CN107118689A - A kind of liquid crystal display antifouling paint and its application method with antibacterial effect - Google Patents
A kind of liquid crystal display antifouling paint and its application method with antibacterial effect Download PDFInfo
- Publication number
- CN107118689A CN107118689A CN201710498003.6A CN201710498003A CN107118689A CN 107118689 A CN107118689 A CN 107118689A CN 201710498003 A CN201710498003 A CN 201710498003A CN 107118689 A CN107118689 A CN 107118689A
- Authority
- CN
- China
- Prior art keywords
- liquid crystal
- crystal display
- antibacterial effect
- antifouling paint
- application method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of liquid crystal display antifouling paint with antibacterial effect, main component includes:Fluorinated polyether silicone compounds, silicon powder, nano titanium oxide, catalyst, fluorescent material, siloxanes, dispersant and solvent.The coating is by the scientific matching and rational application method of each raw material, with good antifouling, heat-resisting quantity, wearability, impact resistance and adhesive force;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, and there is the fluorescent material power to cause ratio fluorescent metachromatism, and the phenomenon has contrast high, and the characteristics of fluorescence color transformation is obvious is especially suitable for touch-screen and used.
Description
Technical field
Paint field of the present invention, and in particular to a kind of liquid crystal display antifouling paint and its application method with antibacterial effect.
Background technology
With the development of electronics industry, particularly smart mobile phone, large screen television, can only tablet personal computer etc. promote and should
With after the popularization of various touch screen technologies, due to high-frequency using these products, the display surface of product is easy to become
Dirty, scratch and corroded by some chemical solvents, therefore improve the waterproofs of these products, antifouling, anti-chemical reagent, improve wear-resisting
Property it is very necessary, it is very necessary to develop a kind of protecting LCD screen material of each side excellent combination property, in the market
Coating can not meet its requirement.
The content of the invention
It is an object of the invention to provide a kind of liquid crystal display antifouling paint and application method with antibacterial effect.
A kind of liquid crystal display antifouling paint with antibacterial effect, is made up of the component of following percentage by weight:
Fluorinated polyether silicone compounds 30-50%
Silicon powder 5-10%
Nano titanium oxide 0.2-0.5%
Catalyst 0.5-1%
Fluorescent material 1-3%
Siloxanes 2-5%
Dispersant 1-2%
Balance of solvent.
It is preferred that, the molecular weight of fluorinated polyether silicone compounds is 3000-5000.
It is preferred that, described catalyst is zinc oxide;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, tool
Strong to cause ratio fluorescent metachromatism, the phenomenon has contrast high, the characteristics of fluorescence color transformation is obvious, is especially suitable for touching
Screen is used.
It is preferred that, described dispersant is wetting agent X-405.
It is preferred that, described solvent is organic solvent, more preferably ethyl acetate.
Present invention also offers a kind of application method of the liquid crystal display antifouling paint with antibacterial effect, following step is included
Suddenly:
Step one:Stirred after all raw materials in addition to zinc oxide are mixed, obtain coating solution;
Step 2:Using adding zinc oxide in the coating solution of step one in preceding 20min, stir, obtain coating;
Step 3:By the coating dilution in step 2, and it is sprayed on liquid crystal screen surfaces;
Step 4:10-15min is toasted under the conditions of liquid crystal display is put into 130-150 DEG C, you can.
It is preferred that, in described step three, coating is diluted using organic solvent.
It is preferred that, in described step three, 8-10 times is diluted to coating using organic solvent.
The beneficial of the present invention is effectively:Liquid crystal display antifouling paint of the present invention with antibacterial effect passes through each original
The scientific matching of material and rational application method, described powdery paints has good antifouling, heat-resisting quantity, wearability, anti-
Impact and adhesive force.
Embodiment
Embodiment 1
A kind of liquid crystal display antifouling paint with antibacterial effect, is made up of the component of following percentage by weight:
Fluorinated polyether silicone compounds 42%
Silicon powder 7%
Nano titanium oxide 0.3%
Catalyst 0.5%
Fluorescent material 2%
Siloxanes 3.5%
Dispersant 1.5%
Balance of solvent.
The molecular weight of fluorinated polyether silicone compounds is 3000-5000.
Described catalyst is zinc oxide;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, with cause ratio
Rate fluorescence metachromatism.
Described dispersant is wetting agent X-405.
Described solvent is ethyl acetate.
A kind of application method of the liquid crystal display antifouling paint with antibacterial effect, is comprised the steps of:
Step one:Stirred after all raw materials in addition to zinc oxide are mixed, obtain coating solution;
Step 2:Using adding zinc oxide in the coating solution of step one in preceding 20min, stir, obtain coating;
Step 3:By the coating dilution in step 2, and it is sprayed on liquid crystal screen surfaces;
Step 4:Liquid crystal display is put under the conditions of 140 DEG C and toasts 12min, you can.
In described step three, 8.5 times are diluted to coating using organic solvent.
Embodiment 2
A kind of liquid crystal display antifouling paint with antibacterial effect, is made up of the component of following percentage by weight:
Fluorinated polyether silicone compounds 30%
Silicon powder 10%
Nano titanium oxide 0.2%
Catalyst 0.5%
Fluorescent material 3%
Siloxanes 2%
Dispersant 2%
Balance of solvent.
The molecular weight of fluorinated polyether silicone compounds is 3000-5000.
Described catalyst is zinc oxide;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, with cause ratio
Rate fluorescence metachromatism.
Described dispersant is wetting agent X-405.
Described solvent is ethyl acetate.
A kind of application method of the liquid crystal display antifouling paint with antibacterial effect, is comprised the steps of:
Step one:Stirred after all raw materials in addition to zinc oxide are mixed, obtain coating solution;
Step 2:Using adding zinc oxide in the coating solution of step one in preceding 20min, stir, obtain coating;
Step 3:By the coating dilution in step 2, and it is sprayed on liquid crystal screen surfaces;
Step 4:Liquid crystal display is put under the conditions of 130 DEG C and toasts 15min, you can.
In described step three, 8 times are diluted to coating using organic solvent.
Embodiment 3
A kind of liquid crystal display antifouling paint with antibacterial effect, is made up of the component of following percentage by weight:
Fluorinated polyether silicone compounds 50%
Silicon powder 5%
Nano titanium oxide 0.5%
Catalyst 1%
Fluorescent material 1%
Siloxanes 5%
Dispersant 1%
Balance of solvent.
The molecular weight of fluorinated polyether silicone compounds is 3000-5000.
Described catalyst is zinc oxide;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, with cause ratio
Rate fluorescence metachromatism.
Described dispersant is wetting agent X-405.
Described solvent is ethyl acetate.
A kind of application method of the liquid crystal display antifouling paint with antibacterial effect, is comprised the steps of:
Step one:Stirred after all raw materials in addition to zinc oxide are mixed, obtain coating solution;
Step 2:Using adding zinc oxide in the coating solution of step one in preceding 20min, stir, obtain coating;
Step 3:By the coating dilution in step 2, and it is sprayed on liquid crystal screen surfaces;
Step 4:Liquid crystal display is put under the conditions of 130 DEG C and toasts 15min, you can.
In described step three, 8 times are diluted to coating using organic solvent.
The antifouling paint of the present invention, using after 3 years, to Candida albicans, staphylococcus aureus, Escherichia coli suppression
Bacterium rate is more than 99%, and antibacterial effect is very good.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (9)
1. a kind of liquid crystal display antifouling paint with antibacterial effect, it is characterised in that by the component group of following percentage by weight
Into:
Fluorinated polyether silicone compounds 30-50%
Silicon powder 5-10%
Nano titanium oxide 0.2-0.5%
Catalyst 0.5-1%
Fluorescent material 1-3%
Siloxanes 2-5%
Dispersant 1-2%
Balance of solvent.
2. there is the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that fluorinated polyether siloxanes
The molecular weight of compound is 3000-5000.
3. there is the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that described catalyst is
Zinc oxide;The primary raw material of described fluorescent material is diphenyl ethylene derivatives, with cause ratio fluorescent metachromatism.
4. there is the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that described dispersant is
Wetting agent X-405.
5. there is the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that described solvent is to have
Machine solvent.
6. as claimed in claim 1 have antibacterial effect liquid crystal display antifouling paint, it is characterised in that described solvent be for
Ethyl acetate.
7. a kind of application method of the liquid crystal display antifouling paint with antibacterial effect, it is characterised in that comprise the steps of:
Step one:Stirred after all raw materials in addition to zinc oxide are mixed, obtain coating solution;
Step 2:Using adding zinc oxide in the coating solution of step one in preceding 20min, stir, obtain coating;
Step 3:By the coating dilution in step 2, and it is sprayed on liquid crystal screen surfaces;
Step 4:10-15min is toasted under the conditions of liquid crystal display is put into 130-150 DEG C, you can.
8. there is the application method of the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that described
The step of three in, coating is diluted using organic solvent.
9. there is the application method of the liquid crystal display antifouling paint of antibacterial effect as claimed in claim 1, it is characterised in that described
The step of three in, 8-10 times is diluted to coating using organic solvent.