CN107118435A - Polypropylene blending modified material and preparation method thereof - Google Patents
Polypropylene blending modified material and preparation method thereof Download PDFInfo
- Publication number
- CN107118435A CN107118435A CN201710339816.0A CN201710339816A CN107118435A CN 107118435 A CN107118435 A CN 107118435A CN 201710339816 A CN201710339816 A CN 201710339816A CN 107118435 A CN107118435 A CN 107118435A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- modified material
- blending
- blending modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of polypropylene blending modified material and preparation method thereof, according to the number of parts by weight, including following components:0.2~0.6 part of 80~90 parts of polypropylene, 10~20 parts of polyethylene, 5~10 parts of iso-cyanuric acid triallyl ester, 20~26 parts of bulking agent, 1~3 part of coupling agent, 1~10 part of filler and antioxidant;Wherein, bulking agent is made up of ethylene methyl acrylate GMA terpolymer and polyacrylic acid.Preparation method:Cross-linking radiation is carried out after each component is well mixed, is placed into screw extruder, blending extrusion, blending temperature is 180 DEG C~210 DEG C, that is, obtains product.This it is material modified have rigid toughening effect have shock resistance again.
Description
Technical field
The invention belongs to field of high polymer material modification, and in particular to a kind of polypropylene blending modified material and its system
Preparation Method.
Background technology
Polypropylene (PP) is one of fastest-rising kind in general thermoplastic resin, is widely used in industrial each
Individual field.It is as the important source material of blow molded product, and abundance is cheap, good processability, using quite varied.But
It is because its black brittleness, dimensional stability particularly notch sensitivity are poor, using receiving certain limitation.
The features such as method of PP blending toughenings industrializes small investment, rapid easy and notable effect with it and extensively should
With.Blending Toughening Modification refers to that elastomer or other plastics are blended as modifying agent and PP, improves PP toughness with this.Often
Modifying agent is broadly divided into plastics, rubber or elastomer and several major classes of inorganic rigid particle.
It is too late to reach toughness reinforcing purpose using plasticized modifier of the plastics as PP, and the wear-resisting of material can be made
Property, dyeability etc. are largely improved, and price is more cheap.There is high density polyethylene (HDPE) using more
(HDPE), LLDPE (ILDPE), ethylene-vinyl acetate copolymer (EVA), polyvinyl chloride (PVC), polyamide
(PA) etc..But it is due to their poor compatibilities with PP, system is reached higher toughness, generally requires to increase modifying agent
Consumption adds compatilizer.PP and PE are crystalline polymers, do not form eutectic between them, but each crystallization,
Form the bad heterogeneous system of compatibility.
The content of the invention
The present invention proposes a kind of polypropylene blending modified material, and this is material modified, and there is rigid toughening effect to have shock resistance again
Performance.
The technical proposal of the invention is realized in this way:
A kind of polypropylene blending modified material, according to the number of parts by weight, including following components:
80~90 parts of polypropylene, 10~20 parts of polyethylene, 5~10 parts of iso-cyanuric acid triallyl ester, bulking agent 20~
0.2~0.6 part of 26 parts, 1~3 part of coupling agent, 1~10 part of filler and antioxidant;Wherein, bulking agent is by ethylene-acrylic acid
Methyl esters-GMA terpolymer is constituted with polyacrylic acid.
Preferably, the quality of ethylene-methyl acrylate-glyceryl methacrylate terpolymer and polyacrylic acid
Than for 80~90:10~20.
Preferably, polyethylene is one kind or several in high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density of polyethylene
The mixture planted.
Preferably, coupling agent is titanate coupling agent.
Preferably, filler is one kind or several in calcium carbonate, silica, kaolin, talcum powder, barium sulfate, wollastonite
The mixture planted.
Preferably, antioxidant is phenolic antioxidant or phosphoric acid ester antioxidant.
, proportionally, will it is a further object to provide a kind of preparation method of polypropylene blending modified material
Cross-linking radiation is carried out after each component is well mixed, is placed into screw extruder, blending extrusion, blending temperature is 180 DEG C~
210 DEG C, that is, obtain product.
Cross-linking radiation method is referred to the refined equality of sieve 2016 and existed《Chinese Tissue Engineering Study》What magazines were delivered
The Radiation Crosslinking Method that entitled " present Research of ultra high molecular weight polyethylene crosslinking with radiation " is introduced.
Beneficial effects of the present invention:
1st, the present invention is improved between polypropylene and polyethylene using iso-cyanuric acid triallyl ester by cross-linking radiation
Compatibility, by ethylene-methyl acrylate-glyceryl methacrylate terpolymer and polyacrylic acid constitute it is mixed
On the premise of compound, being mutually bonded for incompatible thing is improved, the compatibility of blend is improved, and improves its mechanical property
Energy.
2nd, the present invention obtains polypropylene blending modified material using the method for PP and PE blending and modifyings.This is polypropene blended
Material modified surface gloss reduction, extinction effect are good, can be applied to the fields such as packaging, commodity and construction material.
Embodiment
Embodiment 1
A kind of polypropylene blending modified material, according to the number of parts by weight, including following components:
86 parts of polypropylene, 14 parts of low density polyethylene (LDPE), 6 parts of iso-cyanuric acid triallyl ester, 23 parts of bulking agent, titanate esters
0.4 part of 2 parts of coupling agent, 4 parts of calcium carbonate and phenolic antioxidant.
Wherein, bulking agent is 80 by mass ratio:20 ethylene-methyl acrylate-glyceryl methacrylate ternary
Copolymer is constituted with polyacrylic acid.
Preparation method:
Proportionally, cross-linking radiation is carried out after each component is well mixed, is placed into screw extruder, blending is squeezed
Go out, blending temperature is 180 DEG C, that is, obtains product.
Embodiment 2
A kind of polypropylene blending modified material, according to the number of parts by weight, including following components:
80 parts of polypropylene, 20 parts of high density polyethylene (HDPE), 5 parts of iso-cyanuric acid triallyl ester, 20 parts of bulking agent, titanate esters
0.2 part of 1 part of coupling agent, 5 parts of calcium carbonate, 5 parts of kaolin and phosphate-based antioxidants.
Wherein, bulking agent is 90 by mass ratio:10 ethylene-methyl acrylate-glyceryl methacrylate ternary
Copolymer is constituted with polyacrylic acid.
Preparation method:
Proportionally, cross-linking radiation is carried out after each component is well mixed, is placed into screw extruder, blending is squeezed
Go out, blending temperature is 200 DEG C, that is, obtains product.
Embodiment 3
A kind of polypropylene blending modified material, according to the number of parts by weight, including following components:
90 parts of polypropylene, 4 parts of LLDPE, 6 parts of high density polyethylene (HDPE), iso-cyanuric acid triallyl ester 10
Part, 26 parts of bulking agent, 3 parts of titanate coupling agent, 1 part of kaolin and 0.6 part of phosphate-based antioxidants.
Wherein, bulking agent is 85 by mass ratio:15 ethylene-methyl acrylate-glyceryl methacrylate ternary
Copolymer is constituted with polyacrylic acid.
Preparation method:
Proportionally, cross-linking radiation is carried out after each component is well mixed, is placed into screw extruder, blending is squeezed
Go out, blending temperature is 210 DEG C, that is, obtains product.
Test example
Embodiment 1-3 polypropylene blending modified material is tested using ASTM standard, test result is shown in Table 1:
The material modified the performance test results of table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
Notch impact strength (KJ/m2) | 35 | 33 | 37 |
Bending modulus (MPa) | 1126 | 1176 | 1234 |
Tensile strength (MPa) | 32.1 | 34.2 | 33.5 |
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (7)
1. a kind of polypropylene blending modified material, it is characterised in that according to the number of parts by weight, including following components:
80~90 parts of polypropylene, 10~20 parts of polyethylene, 5~10 parts of iso-cyanuric acid triallyl ester, 20~26 parts of bulking agent,
0.2~0.6 part of 1~3 part of coupling agent, 1~10 part of filler and antioxidant;Wherein, bulking agent by ethylene-methyl acrylate-
GMA terpolymer is constituted with polyacrylic acid.
2. polypropylene blending modified material according to claim 1, it is characterised in that ethylene-methyl acrylate-methyl-prop
The mass ratio of olefin(e) acid ethylene oxidic ester terpolymer and polyacrylic acid is 80~90:10~20.
3. polypropylene blending modified material according to claim 1, it is characterised in that polyethylene be high density polyethylene (HDPE),
One or more of mixtures in low density polyethylene (LDPE), linear low density of polyethylene.
4. polypropylene blending modified material according to claim 1, it is characterised in that coupling agent is titanate coupling agent.
5. polypropylene blending modified material according to claim 1, it is characterised in that filler be calcium carbonate, silica,
One or more of mixtures in kaolin, talcum powder, barium sulfate, wollastonite.
6. polypropylene blending modified material according to claim 1, it is characterised in that antioxidant is phenolic antioxidant or phosphorus
Acid esters kind antioxidant.
7. the preparation method of polypropylene blending modified material as claimed in claim 1, it is characterised in that proportionally, will be each
Cross-linking radiation is carried out after individual component is well mixed, is placed into screw extruder, blending extrusion, blending temperature is 180 DEG C~210
DEG C, that is, obtain product.