CN107095392A - A kind of the elderly's Special shoe pad - Google Patents
A kind of the elderly's Special shoe pad Download PDFInfo
- Publication number
- CN107095392A CN107095392A CN201710539442.7A CN201710539442A CN107095392A CN 107095392 A CN107095392 A CN 107095392A CN 201710539442 A CN201710539442 A CN 201710539442A CN 107095392 A CN107095392 A CN 107095392A
- Authority
- CN
- China
- Prior art keywords
- pad
- shoe
- elderly
- bamboo
- half sole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of the elderly's Special shoe pad, including insole body, from the front end of insole body to rear end, successively including waist and shoe-pad heel in shoe-pad half sole, the shoe-pad pad heart, shoe-pad；The convex grain of 70~150 upper flats is arranged with the upside of the shoe-pad half sole, downside is provided with half sole beam；Side is provided with ovum type convex surface to the shoe-pad pad in the heart, and downside is continuous provided with memory bubble；The both sides of waist are up tilted respectively in the shoe-pad, and corresponding to for waist is arranged with the convex grains of 20~40 upper flats in shoe-pad on the side on the inside of human foot；Round convex surface is provided with the upside of the middle part of the shoe-pad heel, the outer of the shoe-pad heel is up tilted, it tilts and is provided with back heel shock-absorbing pad on the downside of the tilting height that height is less than waist both sides in shoe-pad, the middle part of the shoe-pad heel.Damping of the present invention shield foot effect is strong, can alleviate that medicine, skid resistance are good, can prevent ankle injury, can health care massage.
Description
Technical field
The present invention relates to a kind of shoe-pad, more particularly to a kind of the elderly's Special shoe pad.
Background technology
Shoe-pad is that, using very universal articles for daily use, by effect point, shoe-pad can be divided into health insoles, functional insole and often
Advise shoe-pad.Because the bone of the elderly is calcareous higher, with fragility, therefore, the elderly is in motion process by a relatively large margin, pin
Portion's bone is easily injured, or even cracking.The structure of traditional the elderly's shoe-pad is that the sewing of multilayer cloth forms either multilayer leather
Compacting is formed, and it has certain pliability and shock absorbing effect, substantially conforms to the demand of usual stroll wear shoes.But, when
When the elderly needs to move by a relatively large margin, traditional sock does not apply to then dangerous, has as a drawback that：One, damping, shield foot are made
With poor, during motion, foot's half sole and followed by bottom impulsive force it is big, traditional sock is difficult to absorb in walking, motion process to foot
The impulsive force that portion's bone is produced, it is difficult to protect vola bone, ankle-joint and knee joint；Secondly, to arch portion without effect, it is impossible to it is slow
Solve medicine；Thirdly, skid resistance it is poor, be unfavorable for toe stretch, grab ground；Four, traditional sock each several part thickness is basically identical,
The problem of being difficult to prevention ankle injury；Five, traditional sock is acted on without health care massage.
It six：It is basic continuous without using memory bubble in existing shoe-pad, even if having indivedual continuous using memory bubble, but do not use
Cape jasmine pollen etc. is used for stimulating circulation, the function such as build up resistance.
Bamboo-carbon fibre is to take mao bamboon to be raw material, employs the calcining new technology and new skill of pure oxygen high temperature and nitrogen barrier delay
Art so that the micropore that bamboo charcoal innately has more refine with honeycomb, then again with the polyester with honeycomb microporous structure trend
It is modified section melt spinning and is made.This unique fibre structure design, with moisture absorption is ventilative, bacteriostasis antibiosis, winter warm up the summer
The features such as cool, environmental protection.
The content of the invention
The technical problem to be solved in the present invention is that there is provided a kind of damping shield foot effect for above-mentioned the deficiencies in the prior art
By force, can alleviate that medicine, skid resistance are good, can prevent ankle injury, can health care massage the elderly's Special shoe pad.
In order to solve the above technical problems, the technical scheme is that：A kind of the elderly's Special shoe pad, including shoe-pad sheet
Body, from the front end of insole body to rear end, successively including waist and shoe-pad heel, the footwear in shoe-pad half sole, the shoe-pad pad heart, shoe-pad
The convex grain of 70~150 upper flats is arranged with the upside of pad half sole, the downside of the shoe-pad half sole is provided with half sole beam；Institute
The upside for stating the shoe-pad pad heart is provided with ovum type convex surface, and ovum type convex surface is provided with the downside of pad heart spiral grooves, the shoe-pad pad heart and set
There is memory bubble continuous, the continuous shape of memory bubble is corresponding with the shape on ovum type convex surface；The both sides of waist are past respectively in the shoe-pad upwarps
Rise, and corresponding to for waist is arranged with the convex grains of 20~40 upper flats in shoe-pad on the side on the inside of human foot；The footwear
Pad and round convex surface is provided with the upside of the middle part of heel, the round convex surface is provided with followed by spiral grooves, outside the shoe-pad heel
Along up tilting, its tilting height is less than the tilting of waist both sides in shoe-pad highly, after being provided with the downside of the middle part of the shoe-pad heel
With beam, the shape of back heel shock-absorbing pad is corresponding with the shape on round convex surface.
It is expanded on further as to the present invention：
Preferably, it is arranged with the upside of the shoe-pad half sole between the convex grain of 100~130 upper flats, convex grain and is equipped with a S
Type exhaust trench, the front end of the S type exhaust trench extends to the front end of shoe-pad half sole, and the rear end of the S type exhaust trench is extended to
The rear end of shoe-pad half sole；Corresponding on the side on the inside of human foot for waist is arranged with 28~32 upper flats in the shoe-pad
Convex grain.
Preferably, it is arranged between the convex grain of 100~130 upper flats, convex grain and wears on the upside of the shoe-pad half sole
There is a S type exhaust trench, the front end of the S type exhaust trench extends to the front end of shoe-pad half sole, and the rear end of the S type exhaust trench is prolonged
Extend the rear end of shoe-pad half sole；Corresponding on the side on the inside of human foot for waist is arranged with 28~32 tops in the shoe-pad
Smooth convex grain.
Preferably, the insole body includes bamboo, the first PU polyurethane foams layer and the successively from top to bottom
Two PU polyurethane foams layers；The thickness of the bamboo is 0.3~0.8mm, the thickness of the first PU polyurethane foams layer
Spend for 3~6mm, the thickness of the 2nd PU polyurethane foams layer is 3~6mm.
Preferably, the downside of the 2nd PU polyurethane foams layer is respectively equipped with preceding accommodating cavity, middle accommodating cavity and housed afterwards
Chamber, before the half sole beam is set in accommodating cavity, the memory bubble silk floss is set in middle accommodating cavity, and the back heel shock-absorbing pad is set in
Afterwards in accommodating cavity.
Preferably, the memory bubble is continuous steeps continuous for polyetherurethane foam；The half sole beam and back heel shock-absorbing pad
Thickness be respectively 1~12.7mm, the continuous thickness of memory bubble is 3~6mm.
Memory bubble is continuous to react what foaming was made by the following raw material：100 parts of PPG, methyl diphenylene diisocyanate
5~15 parts, 1-3 parts of cape jasmine pollen, 5-10 parts of IPDI, 2~3 parts of water, 0.5~3 part of silicone oil, catalyst
0.2~1 part, 0.5~1 part of foaming agent, 2~5 parts of crosslinking agent.
Memory foam sponge layer preparation method be：By the PPG of corresponding parts by weight, diphenylmethane diisocyanate
Ester, cape jasmine pollen and IPDI are added to stir in blender, is heated to 35~38 degrees Celsius, will
Other raw materials of corresponding number are added in blender, and high-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and is obtained
Corresponding memory foam sponge layer.
The hydroxyl value of the PPG is 50~90 mgKOH/g, and molecular weight is 8000~10000, and the silicone oil is
Two kinds of mass ratioes of BF-2370 and B-4900 are 3：1 mixture.
The catalyst is N, and N- dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1
Mixture.
The foaming agent is normal heptane；Crosslinking agent is ethylenediamine, triethylene glycol and dipropyl（Support）Three kinds of mixtures of glycol.
Bamboo is made up of bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon；Viscose rayon
In contain 0.8-1% ceramic powders and coupling agent, coupling agent be ceramic powders weight 0.1-0.3%；Ceramic powders by weighing as follows
Amount percent composition is made：Zirconium dioxide 50-60%, silica 35-40%, titanium dioxide 5-15%；Coupling agent is that stearic acid is sweet
Grease.
The preparation method of the viscose rayon is：（1）, by zirconium dioxide, silica and titanium dioxide mix, it is sintered
The ceramic powders that average grain diameter is 1-2 μm are crushed to afterwards；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic
Powder；（3）, by the modified ceramic powder and viscose glue blending, viscose glue section is made in extrusion, section；（4）, the viscose glue cut
Piece heating melting, extruding, spinneret shaping, you can viscose rayon is made.
The preparation method of bamboo is：
（1）, bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be well mixed, add dispersant, viscous
Knot agent, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained bamboo.
The beneficial effects of the invention are as follows：One, damping, shield foot, because the downside of shoe-pad half sole and shoe-pad heel is set respectively
There is beam, therefore, shoe-pad elasticity is good, and hardness is moderate, can effectively absorb in walking, motion process and foot bones generation is rushed
Hit power, protection vola bone, ankle-joint and knee joint；Secondly, alleviate medicine, the present invention according to principle of human engineering,
Shoe-pad pad center portion position sets ovum type convex surface, arch portion of fitting, and sole center of gravity is redistributed, makes full sole stress equalization, is alleviated
Motion, walking, the stress fatigue for standing produced；Thirdly, stablize anti-skidding, it is low early and high after, outer it is thick in it is thin, gravity leans forward so that
Toe has bigger activity space, is stretched beneficial to toe, grabs ground, convex grain and spiral grooves design, significantly enhanced frictional force, subtract
Rear cunning and the sideslip in motion process are lacked, biped is more balanced, support body is more balanced；Four, prevent ankle injury, this hair
Bright low early and high after, outer thick interior thin, middle waist both sides, which thicken, to be surrounded, and is wrapped up foot, can be prevented the joint displacements in motion process, prevents
Only turn up, pin situation of rivering bend, the effectively risk injured unexpectedly of reduction podarthrum；Five, health care massage, shoe-pad pad center portion position is set
The ovum type convex surface with spiral grooves is put, arch of the foot acupuncture point can be massaged, vola blood circulation is effectively facilitated.
Memory bubble is continuous to have outstanding memory function, can recover original form, and good permeability after deformation rapidly, use
Cape jasmine pollen have stimulate circulation, the function of building up resistance.
The special preparation method of bamboo, makes shoe-pad have stronger self-cleaning function and odor-resistant result, and have
The effects such as anti-inflammatory analgetic, fatigue-relieving and prevention spur.
Brief description of the drawings
Fig. 1 is dispersed structure schematic diagram of the invention.
Fig. 2 is upside overall structure diagram of the invention.
Fig. 3 is downside overall structure diagram of the invention.
In figure：100. insole body；1. shoe-pad half sole；11. convex grain；12. half sole beam；13.S type exhaust trench；2.
The shoe-pad pad heart；21. ovum type convex surface；22. pad heart spiral grooves；23. memory bubble is continuous；3. waist in shoe-pad；31. convex grain；4. after shoe-pad
With；41. round convex surface；42. followed by spiral grooves；43. outer；44. back heel shock-absorbing pad；5. bamboo；6. the first PU gathers
Urethane foam sponge layer；7. the 2nd PU polyurethane foams layer.
Embodiment
The structural principle and operation principle of the present invention are described in further detail below in conjunction with the accompanying drawings.
As shown in Figure 1, Figure 2 and Figure 3, the present invention is a kind of the elderly's Special shoe pad, including insole body 100, from shoe-pad
The front end of body 100 to rear end, successively including waist 3 and shoe-pad heel 4, the shoe-pad in shoe-pad half sole 1, the shoe-pad pad heart 2, shoe-pad
The upside of half sole 1 is arranged with the convex grain 11 of 70~150 upper flats, and the downside of the shoe-pad half sole 1 is provided with half sole beam
12；The upside of the shoe-pad pad heart 2 is provided with ovum type convex surface 21, and ovum type convex surface 21 is provided with pad heart spiral grooves 22, the shoe-pad
The downside of the heart 2 is padded provided with memory bubble silk floss 23, the shape of memory bubble silk floss 23 is corresponding with the shape on ovum type convex surface 21；In the shoe-pad
The both sides of waist 3 are up tilted respectively, and corresponding on the side on the inside of human foot for waist 3 is arranged with 20~40 tops in shoe-pad
The smooth convex grain 31 in portion；Round convex surface 41 is provided with the upside of the middle part of the shoe-pad heel 4, the round convex surface 41 is provided with heel
Spiral grooves 42, the outer 43 of the shoe-pad heel 4 is up tilted, and it tilts the tilting height that height is less than the both sides of waist 3 in shoe-pad
Back heel shock-absorbing pad 44, the shape of back heel shock-absorbing pad 44 and the shape on round convex surface 41 are provided with the downside of degree, the middle part of the shoe-pad heel 4
Shape is corresponding.
As shown in Figure 1, Figure 2 and Figure 3, the upside of the shoe-pad half sole 1 is arranged with the convex grain of 100~130 upper flats
11, a S types exhaust trench 13 is equipped between convex grain 11, and the front end of the S types exhaust trench 13 is extended to before shoe-pad half sole 1
End, the rear end of the S types exhaust trench 13 extends to the rear end of shoe-pad half sole 1；Waist 3 corresponds in human foot in the shoe-pad
The convex grain 31 that waist 3 in the convex grain 31 of 28~32 upper flats, shoe-pad is arranged with the side of side concentrates on one and a half months shape area
In domain.
As shown in figure 1, the insole body 100 includes bamboo 5, the first PU polyurethane foams successively from top to bottom
The PU polyurethane foams layer 7 of layer 6 and the 2nd.The thickness of the bamboo 5 be 0.3~0.8mm, preferably 0.5~0.6mm,
The thickness of first PU polyurethane foams layer 6 is 3~6mm, preferably 4~5mm, the 2nd PU polyurethane foams layer 7
Thickness is 3~6mm, preferably 4~5mm.Bamboo 5 has ventilative moisture absorption, bacteriostasis antibiosis, cool in summer and warm in winter, environmental protection
The characteristics of；First PU polyurethane foams layer 6 and the 2nd PU polyurethane foams layer 7 have environmentally friendly degradable, ventilative, deodorization, perspired
Effect.
As shown in figure 3, the downside of the 2nd PU polyurethane foams layer 7 be respectively equipped with preceding accommodating cavity, middle accommodating cavity and after
Accommodating cavity, before the half sole beam 12 is set in accommodating cavity, the memory bubble silk floss 23 is set in middle accommodating cavity, and the heel subtracts
Shake pad 44 is set in rear accommodating cavity.
As shown in figures 1 and 3, the memory bubble silk floss 23 is that polyetherurethane foam bubble is continuous；The half sole beam 12
And the thickness of back heel shock-absorbing pad 44 is respectively 1~12.7mm, preferably 4~7mm, the thickness of memory bubble silk floss 23 for 3~
6mm, preferably 4~5mm.
It is material prescription and process example below.
Embodiment 1
Memory bubble is continuous to react what foaming was made by the following raw material：PPG 10kg, methyl diphenylene diisocyanate
0.5kg, cape jasmine pollen 0.2kg, IPDI 1kg, water 0.2kg, silicone oil 0.1kg, catalyst 0.05kg, foaming
Agent 0.08kg, crosslinking agent 0.3kg.
Preparation method is：By the PPG of corresponding parts by weight, methyl diphenylene diisocyanate, cape jasmine pollen and
IPDI is added to stir in blender, 35~38 degrees Celsius is heated to, by its of corresponding number
Its raw material is added in blender, and high-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and obtains corresponding memory bubble
Continuous layer.
Bamboo is made up of bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon；Viscose rayon
In contain 0.8% ceramic powders and coupling agent, coupling agent be ceramic powders weight 0.1%；Ceramic powders are by following weight percent
It is made than composition：Zirconium dioxide 60%, silica 35%, titanium dioxide 5%；Coupling agent is tristerin.
The preparation method of the viscose rayon is：（1）, by zirconium dioxide, silica and titanium dioxide mix, it is sintered
The ceramic powders that average grain diameter is 1-2 μm are crushed to afterwards；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic
Powder；（3）, by the modified ceramic powder and viscose glue blending, viscose glue section is made in extrusion, section；（4）, the viscose glue cut
Piece heating melting, extruding, spinneret shaping, you can viscose rayon is made.
The preparation method of bamboo is：（1）, by bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Fiber is well mixed, and is added dispersant, binding agent, softening agent and is stirred, dries processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35 DEG C, wash 5min；
（5）, adjustment pH value to 7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut the bamboo-carbon fibre of obtained embodiment 1
Layer.
Embodiment 2
Memory bubble is continuous to react what foaming was made by the following raw material：PPG 10kg, methyl diphenylene diisocyanate 1kg,
Cape jasmine pollen 0.1kg, IPDI 0.5kg, water 0.2kg, silicone oil 0.1kg, catalyst 0.05kg, foaming agent
0.08kg, crosslinking agent 0.3kg.
Memory foam sponge layer preparation method be：By the PPG of corresponding parts by weight, diphenylmethane diisocyanate
Ester, cape jasmine pollen and IPDI are added to stir in blender, is heated to 35~38 degrees Celsius, will
Other raw materials of corresponding number are added in blender, and high-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and is obtained
Corresponding memory foam sponge layer.
Bamboo is made up of bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon；Viscose rayon
In contain 0.8-1% ceramic powders and coupling agent, coupling agent be ceramic powders weight 0.2%；Ceramic powders are by following weight hundred
Divide and be made than composition：Zirconium dioxide 50%, silica 40%, titanium dioxide 10%；Coupling agent is tristerin.
The preparation method of the viscose rayon is：（1）, by zirconium dioxide, silica and titanium dioxide mix, it is sintered
The ceramic powders that average grain diameter is 1-2 μm are crushed to afterwards；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic
Powder；（3）, by the modified ceramic powder and viscose glue blending, viscose glue section is made in extrusion, section；（4）, the viscose glue cut
Piece heating melting, extruding, spinneret shaping, you can viscose rayon is made.
The preparation method of bamboo is：（1）, by bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Fiber is well mixed, and is added dispersant, binding agent, softening agent and is stirred, dries processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 38 DEG C, wash 8min；
（5）, adjustment pH value to 6, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut the bamboo-carbon fibre of obtained embodiment 2
Layer.
Embodiment 3
Memory bubble is continuous to react what foaming was made by the following raw material：PPG 10kg, methyl diphenylene diisocyanate
0.8kg, cape jasmine pollen 0.1kg, IPDI 0.8kg, water 0.3kg, silicone oil 0.08kg, catalyst 0.05kg,
Foaming agent 0.05kg, crosslinking agent 0.5kg.
Memory foam sponge layer preparation method be：By the PPG of corresponding parts by weight, diphenylmethane diisocyanate
Ester, cape jasmine pollen and IPDI are added to stir in blender, is heated to 35~38 degrees Celsius, will
Other raw materials of corresponding number are added in blender, and high-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and is obtained
Corresponding memory foam sponge layer.
Bamboo is made up of bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon；Viscose rayon
In contain 0.8-1% ceramic powders and coupling agent, coupling agent be ceramic powders weight 0.3%；Ceramic powders are by following weight hundred
Divide and be made than composition：Zirconium dioxide 55%, silica 40%, titanium dioxide 5%；Coupling agent is tristerin.
The preparation method of the viscose rayon is：（1）, by zirconium dioxide, silica and titanium dioxide mix, it is sintered
The ceramic powders that average grain diameter is 1-2 μm are crushed to afterwards；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic
Powder；（3）, by the modified ceramic powder and viscose glue blending, viscose glue section is made in extrusion, section；（4）, the viscose glue cut
Piece heating melting, extruding, spinneret shaping, you can viscose rayon is made.
The preparation method of bamboo is：（1）, by bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Fiber is well mixed, and is added dispersant, binding agent, softening agent and is stirred, dries processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35 DEG C, wash 5min；
（5）, adjustment pH value to 5, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut the bamboo-carbon fibre of obtained embodiment 3
Layer.
Embodiment 4
Memory bubble is continuous to react what foaming was made by the following raw material：PPG 10kg, methyl diphenylene diisocyanate
1.2kg, cape jasmine pollen 0.2kg, IPDI 0.6kg, water 0.2kg, silicone oil 0.1kg, catalyst 0.08kg, hair
Infusion 0.08kg, crosslinking agent 0.5kg.
Memory foam sponge layer preparation method be：By the PPG of corresponding parts by weight, diphenylmethane diisocyanate
Ester, cape jasmine pollen and IPDI are added to stir in blender, is heated to 35~38 degrees Celsius, will
Other raw materials of corresponding number are added in blender, and high-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and is obtained
Corresponding memory foam sponge layer.
Bamboo is made up of bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon；Viscose rayon
In contain 0.8-1% ceramic powders and coupling agent, coupling agent be ceramic powders weight 0.2%；Ceramic powders are by following weight hundred
Divide and be made than composition：Zirconium dioxide 50%, silica 35%, titanium dioxide 15%；Coupling agent is tristerin.
The preparation method of the viscose rayon is：（1）, by zirconium dioxide, silica and titanium dioxide mix, it is sintered
The ceramic powders that average grain diameter is 1-2 μm are crushed to afterwards；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic
Powder；（3）, by the modified ceramic powder and viscose glue blending, viscose glue section is made in extrusion, section；（4）, the viscose glue cut
Piece heating melting, extruding, spinneret shaping, you can viscose rayon is made.
The preparation method of bamboo is：（1）, by bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Fiber is well mixed, and is added dispersant, binding agent, softening agent and is stirred, dries processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using a cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 37 DEG C, wash 7min；
（5）, adjustment pH value to 7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut the bamboo-carbon fibre of obtained embodiment 4
Layer.
The memory bubble of embodiment 5 is continuous same as Example 1, but uses common bamboo.
The memory bubble of embodiment 6 is continuous same as Example 2, but uses common bamboo.
The bamboo of embodiment 7 is same as Example 1, but it is that conventional polyurethanes bubble is continuous that memory bubble is continuous.
The tender bamboo of the memory bubble of embodiment 8 is made using common existing material and method.
Memory bubble silk floss, bamboo and other structures made from above example 1-8 are assembled into shoe-pad, pass through footwear
Bottom wear-resistant tester test result is the good anti-bacterial effect of embodiment 1-6 feels more comfortableness, embodiment 1-4 and embodiment 7,
Placed 72 hours in 37 DEG C of incubators after wearing, less than 3 every square centimeter of detection bacterium content, and the detection of embodiment 5,6
As a result it is every square centimeter at 20-30.
It is described above, only it is better embodiment of the present invention, every implementation according to technical scheme to more than
Any subtle modifications, equivalent variations and modifications that mode is made, are belonged in the range of technical solution of the present invention.
Claims (10)
1. a kind of the elderly's Special shoe pad, including insole body, from the front end of insole body to rear end, successively including shoe-pad before
Waist and shoe-pad heel in the palm, the shoe-pad pad heart, shoe-pad, it is characterised in that：70~150 tops are arranged with the upside of the shoe-pad half sole
The smooth convex grain in portion, the downside of the shoe-pad half sole is provided with half sole beam；The upside of the shoe-pad pad heart is provided with ovum type convex surface,
Ovum type convex surface is provided with pad heart spiral grooves, and the downside of the shoe-pad pad heart is continuous provided with memory bubble, the continuous shape of memory bubble and ovum
The shape on type convex surface is corresponding；The both sides of waist are up tilted respectively in the shoe-pad, and in shoe-pad waist correspond to human foot
The convex grain of 20~40 upper flats is arranged with the side of inner side；Round convex surface is provided with the upside of the middle part of the shoe-pad heel,
The round convex surface is provided with followed by spiral grooves, and the outer of the shoe-pad heel is up tilted, and it tilts height and is less than shoe-pad
Back heel shock-absorbing pad, the shape and circle of back heel shock-absorbing pad are provided with the downside of the tilting height of middle waist both sides, the middle part of the shoe-pad heel
The shape on type convex surface is corresponding.
2. the elderly's Special shoe pad according to claim 1, it is characterised in that：It is arranged with the upside of the shoe-pad half sole
A S type exhaust trench, the front end extension of the S type exhaust trench are equipped between the convex grain of 100~130 upper flats, convex grain
To the front end of shoe-pad half sole, the rear end of the S type exhaust trench extends to the rear end of shoe-pad half sole；Waist corresponds in the shoe-pad
The convex grain of 28~32 upper flats is arranged with side on the inside of human foot.
3. the elderly's Special shoe pad according to claim 1, it is characterised in that：The insole body is wrapped successively from top to bottom
Include bamboo, the first PU polyurethane foams layer and the 2nd PU polyurethane foams layer；The thickness of the bamboo is 0.3
~0.8mm, the thickness of the first PU polyurethane foams layer is 3~6mm, and the thickness of the 2nd PU polyurethane foams layer is 3
~6mm.
4. the elderly's Special shoe pad according to claim 3, it is characterised in that：Under the 2nd PU polyurethane foams layer
Side is respectively equipped with preceding accommodating cavity, middle accommodating cavity and rear accommodating cavity, before the half sole beam is set in accommodating cavity, the memory bubble
Silk floss is set in middle accommodating cavity, and the back heel shock-absorbing pad is set in rear accommodating cavity.
5. the elderly's Special shoe pad according to any one in Claims 1 to 4, it is characterised in that：The memory bubble is continuous
Steep continuous for polyetherurethane foam；The thickness of the half sole beam and back heel shock-absorbing pad is respectively 1~12.7mm, the note
It is 3~6mm to recall the continuous thickness of bubble.
6. the elderly's Special shoe pad according to claim 1, it is characterised in that：Continuous reacted by the following raw material of memory bubble is foamed
It is made：100 parts of PPG, 5~15 parts of methyl diphenylene diisocyanate, 1-3 parts of cape jasmine pollen, isophorone two are different
5-10 parts of cyanate, 2~3 parts of water, 0.5~3 part of silicone oil, 0.2~1 part of catalyst, 0.5~1 part of foaming agent, crosslinking agent 2~5
Part.
7. the elderly's Special shoe pad according to claim 6, it is characterised in that：Memory foam sponge layer preparation method be：Will
PPG, methyl diphenylene diisocyanate, cape jasmine pollen and the IPDI of corresponding parts by weight add
Enter in blender and stir, be heated to 35~38 degrees Celsius, other raw materials of corresponding number are added in blender,
High-speed stirred is poured into after 6~8 seconds after mould foams and solidify, and obtains remembering foam sponge layer accordingly；The PPG
Hydroxyl value is 50~90 mgKOH/g, and molecular weight is 8000~10000, and the silicone oil is two kinds of mass ratioes of BF-2370 and B-4900
For 3：1 mixture；The catalyst is N, and N- dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are
0.5：1 mixture；The foaming agent is normal heptane；Crosslinking agent is ethylenediamine, triethylene glycol and dipropyl（Support）Three kinds of mixing of glycol
Thing.
8. the elderly's Special shoe pad according to claim 3, it is characterised in that：The bamboo by bamboo-carbon fibre,
Nano silver fibre, monocrystalline sapphire whisker and viscose rayon composition；Contain 0.8-1% ceramic powders and coupling agent in viscose rayon,
Coupling agent is the 0.1-0.3% of ceramic powders weight；Ceramic powders are made up of following weight percent composition：Zirconium dioxide 50-
60%th, silica 35-40%, titanium dioxide 5-15%；Coupling agent is tristerin.
9. the elderly's Special shoe pad according to claim 8, it is characterised in that：The preparation method of the viscose rayon is：
（1）, zirconium dioxide, silica and titanium dioxide mixed, it is sintered after to be crushed to average grain diameter be 1-2 μm of ceramic powder
End；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic powder；（3）, by the modified ceramic powder with it is viscous
Glue is blended, extrusion, section, and viscose glue section is made；（4）, by the viscose glue section heating melting, extruding, spinneret shaping, you can system
Obtain viscose rayon.
10. the elderly's Special shoe pad according to claim 8, it is characterised in that：The preparation method of bamboo is
（1）, bamboo-carbon fibre, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be well mixed, add dispersant, viscous
Knot agent, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained bamboo.