CN107059245A - Graphene film cloth and preparation method thereof - Google Patents
Graphene film cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107059245A CN107059245A CN201710332097.XA CN201710332097A CN107059245A CN 107059245 A CN107059245 A CN 107059245A CN 201710332097 A CN201710332097 A CN 201710332097A CN 107059245 A CN107059245 A CN 107059245A
- Authority
- CN
- China
- Prior art keywords
- base net
- film cloth
- string
- graphene
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Graphene fiber and string are uniformly evacuated tiling by the present invention, are compacted through press, then are perforated with spun-laced machine, are finally dried, are obtained graphene film cloth, the function of sterilized with far infrared, sterilizing, isolate bacterium, the first choice as mask substrate, even more modern female.
Description
Technical field
The present invention relates to cosmetics field, and in particular to a kind of graphene film cloth and preparation method thereof.
Background technology
Facial mask is a kind of cosmetics used widely, is generally made up of mask substrate and beautifying liquid, is led to when using
Cross mask substrate to be applied to beauty essence on the face, base fabric not only plays a part of a carrier here, while also will be certainly
The feature of body is transmitted by means of the skin of close contact, thus base fabric played in facial mask one it is very important
Role.
Mask substrate is usually to be made of non-woven fabrics, is protected using the porous of non-woven fabrics and the moisture absorption of used fiber
Moist and feature, so as to reach more preferable beauty functions.
Fiber used in non-woven fabrics base fabric in the market is mainly cellulose fibre, terylene, nylon and polypropylene fibre, this
A little fibers are in addition to cellulose fibre has certain hygroscopicity, and other synthetic fibers hygroscopicity are poor, while not possessing any
Function or with limited function, can only as beauty essence carrier.
The content of the invention
In view of the above, in order to be adapted to the demand in market, the present invention, which is necessary to provide, a kind of to be had far infrared sterilization, disappears
Poison, the graphene film cloth of the function of isolation bacterium are used as mask substrate.
To reach above-mentioned purpose, the technical scheme that the present invention is provided is as follows：
The preparation method of the graphene film cloth of the present invention is as follows：
（1）Lay graphene fiber base net
After graphene fiber cutting, shredding, graphene fiber base net is made using random web-laying equipment；
（2）Lay string base net
After string cutting, shredding, string base net is made using random web-laying equipment；
（3）Folded net
The step is chosen respectively（1）In graphene fiber base net and the step（2）In string base net according to upper
In lower three layers of mode stack to form film cloth base net, wherein, upper and lower layer is string base net, and intermediate layer is graphene fiber
Base net；
（4）Compacting
By the step（3）In film cloth base net by pressure roller roll to thickness 0.05-0.5 millimeters, weight 30-180 grams/
Between square metre；
（5）Spun lacing is shaped
By the step（4）In film cloth base net pass through spun-laced machine and puncture sizing, film cloth precast body is made；
（6）Drying, shaping
By the step（5）In film cloth precast body drying after, finished product is made.
It is preferred that, the step（1）The weight of middle graphene fiber base net is between 0.3-18 grams/m.
It is preferred that, the step（2）Middle string base net includes the first string base net and the second plant fiber-based
Net, the weight of the first string base net is between 10-110 grams/m, the weight of the second string base net
Between 10-60 grams/m.
It is preferred that, the step（3）It is the first string base net at the middle and upper levels, lower floor is the second string base net.
It is preferred that, the step（4）The line pressure of middle pressure roller is 15-50 oxen/millimeter.
It is preferred that, the step（5）The needling density of middle spun-laced machine be 2000-5000 odd numbers/square metre.
A kind of graphene film cloth prepared by above method, the graphene film cloth includes the graphite of 0.01%-10% contents
The string of alkene fiber and 90%-99.99%.
It is preferred that, the string includes CUP, cellulose fibre, cotton fiber, Lyocell fibers and regeneration element
Fiber one or more therein.
Beneficial effects of the present invention are：
Including the film cloth of graphene fiber has far infrared sterilization, sterilization, the function of isolation bacterium, as mask substrate, more
It is the first choice of modern female.When this method prepares graphene film cloth film cloth, the content of graphene fiber is easily controlled, for control
Cost is highly beneficial；In addition, the present invention is also by graphene fiber is arranged on intermediate layer, and it is very good to graphene fiber to serve
Protective effect.
Embodiment
It should be appreciated that embodiment described herein is merely to illustrate and explain the present invention, it is not used to
The limitation present invention.
The preparation method of the graphene film cloth of the present invention is as follows：
（1）Lay graphene fiber base net
After graphene fiber cutting, shredding, graphene fiber base net is made using random web-laying equipment；
（2）Lay string base net
After string cutting, shredding, string base net is made using random web-laying equipment；
（3）Folded net
The step is chosen respectively（1）In graphene fiber base net and the step（2）In string base net according to upper
In lower three layers of mode stack to form film cloth base net, wherein, upper and lower layer is string base net, and intermediate layer is graphene fiber
Base net；
（4）Compacting
By the step（3）In film cloth base net by pressure roller roll to thickness 0.05-0.5 millimeters, weight 30-180 grams/
Between square metre；
（5）Spun lacing is shaped
By the step（4）In film cloth base net pass through spun-laced machine and puncture sizing, film cloth precast body is made；
（6）Drying, shaping
By the step（5）In film cloth precast body drying after, finished product is made.
The step（1）The weight of middle graphene fiber base net is between 0.3-18 grams/m.
The step（2）Middle string base net includes the first string base net and the second string base net, described
The weight of first string base net is between 10-110 grams/m, and the weight of the second string base net is in 10-60
Between gram/m.
The step（3）It is the first string base net at the middle and upper levels, lower floor is the second string base net.
The step（4）The line pressure of middle pressure roller is 15-50 oxen/millimeter.
The step（5）The needling density of middle spun-laced machine be 2000-5000 odd numbers/square metre.
A kind of graphene film cloth prepared by above method, the graphene film cloth includes the graphite of 0.01%-10% contents
The string of alkene fiber and 90%-99.99%.
The string includes CUP, cellulose fibre, cotton fiber, Lyocell fibers and regeneration cellulose fiber wherein
One or more.
Wherein, a kind of specific embodiment is：
A kind of graphene film cloth, includes the graphene fiber and 90%-99.99% string of 0.01%-10% contents, the plant
Fibres are Lyocell fibers.
Wherein, another specific embodiment is：
A kind of graphene film cloth, includes the graphene fiber and 90%-99.99% string of 0.01%-10% contents, the plant
Fibres include Lyocell fibers and regeneration cellulose fiber, and the upper strata of the graphene film cloth is Lyocell fibers, the graphene
The lower floor of film cloth is regeneration cellulose fiber.
Without departing from the thought of the invention, the various not be the same as Examples to the present invention are combined, all should
When being considered as present disclosure；In the range of the technology design of the present invention, a variety of simple modifications are carried out to technical scheme
And not be the same as Example carry out the thought without prejudice to the invention any combination, all should protection scope of the present invention it
It is interior.
Claims (8)
1. a kind of preparation method of graphene film cloth, it is characterised in that methods described includes：
（1）Lay graphene fiber base net
After graphene fiber cutting, shredding, graphene fiber base net is made using random web-laying equipment；
（2）Lay string base net
After string cutting, shredding, string base net is made using random web-laying equipment；
（3）Folded net
The step is chosen respectively（1）In graphene fiber base net and the step（2）In string base net according to upper
In lower three layers of mode stack to form film cloth base net, wherein, upper and lower layer is string base net, and intermediate layer is graphene fiber
Base net；
（4）Compacting
By the step（3）In film cloth base net by pressure roller roll to thickness 0.05-0.5 millimeters, weight 30-180 grams/
Between square metre；
（5）Spun lacing is shaped
By the step（4）In film cloth base net pass through spun-laced machine and puncture sizing, film cloth precast body is made；
（6）Drying, shaping
By the step（5）In film cloth precast body drying after, finished product is made.
2. the preparation method of graphene film cloth according to claim 1, it is characterised in that the step（1）Middle graphene
The weight of fiber base net is between 0.3-18 grams/m.
3. the preparation method of graphene film cloth according to claim 2, it is characterised in that the step（2）Middle plant is fine
Wiki net includes the first string base net and the second string base net, and the weight of the first string base net is in 10-
Between 110 grams/m, the weight of the second string base net is between 10-60 grams/m.
4. the preparation method of graphene film cloth according to claim 3, it is characterised in that the step（3）It is at the middle and upper levels
First string base net, lower floor is the second string base net.
5. the preparation method of graphene film cloth according to claim 4, it is characterised in that the step（4）Middle pressure roller
Line pressure is 15-50 oxen/millimeter.
6. the preparation method of graphene film cloth according to claim 5, it is characterised in that the step（5）Middle spun-laced machine
Needling density for 2000-5000 odd numbers/square metre.
7. a kind of graphene film cloth, it is characterised in that the graphene film cloth is as the method preparation described in claim 1-6
Into the graphene film cloth includes the graphene fiber of 0.01%-10% contents and 90%-99.99% string.
8. graphene film cloth according to claim 7, it is characterised in that the string includes CUP, fiber
Cellulose fiber, cotton fiber, Lyocell fibers and regeneration cellulose fiber one or more therein.