CN107058814A - A kind of motorcycle aluminium alloy - Google Patents
A kind of motorcycle aluminium alloy Download PDFInfo
- Publication number
- CN107058814A CN107058814A CN201710430847.7A CN201710430847A CN107058814A CN 107058814 A CN107058814 A CN 107058814A CN 201710430847 A CN201710430847 A CN 201710430847A CN 107058814 A CN107058814 A CN 107058814A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium alloy
- motorcycle
- aluminium
- tungsten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of motorcycle aluminium alloy, include the component of following parts by weight:70 80 parts of aluminium;0.5 0.8 parts of manganese;58 parts of sodium;0.3 0.6 parts of cobalt;0.2 0.5 parts of magnesium;0.12 0.35 parts of tungsten.The beneficial effects of the invention are as follows:Proportioning is scientific and reasonable, using aluminium as main metal element, and increased magnesium, tungsten and sodium increase the intensity of aluminium alloy, increase abrasion resistant effect and corrosion resistance, it is adaptable to motorcycle, improve the stability of metal material.
Description
Technical field
The present invention relates to a kind of aluminium alloy, more particularly to a kind of motorcycle aluminium alloy.
Background technology
In motorcycle many parts be all by the motorcycle stamping parts for welding or being machined after stamped or punching press,
The motorcycle hardware stamping part of different purposes selects the metal material of different mechanical properties according to its handling characteristics, so as to ensure it
Product quality.In recent years, motorcycle industry energy-saving and emission-reduction policy is widelyd popularize so that the alternative materials such as high strength steel are in vehicle
Begin to use in manufacture, high strength steel can mitigate part quality by reducing the modes such as thickness of slab or sectional dimension, in reality
Had a clear superiority in terms of existing vehicle lightweight and raising security performance, current steel motor vehicle material generally existing wearability
The problem of difference, difference of hardness.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of motorcycle aluminium alloy.
The technical solution adopted by the present invention is:
A kind of motorcycle aluminium alloy, includes the component of following parts by weight:
70-80 parts of aluminium;
0.5-0.8 parts of manganese;
5-8 parts of sodium;
0.3-0.6 parts of cobalt;
0.2-0.5 parts of magnesium;
0.12-0.35 parts of tungsten.
Further, the parts by weight of the cobalt are 0.4-0.5 parts.
Further, the parts by weight of the sodium are 5.5-6.5 parts.
Further, the parts by weight of the tungsten are 0.2-0.35 parts.
Further, the parts by weight of the manganese are 0.65 part.
The beneficial effects of the invention are as follows:Proportioning is scientific and reasonable, and using aluminium as main metal element, increased magnesium, tungsten and sodium add
The big intensity of aluminium alloy, increase abrasion resistant effect and corrosion resistance, it is adaptable to motorcycle, improve the stability of metal material.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of motorcycle aluminium alloy, includes the component of following parts by weight:
70 parts of aluminium;
0.5 part of manganese;
5 parts of sodium;
0.3 part of cobalt;
0.2 part of magnesium;
0.12 part of tungsten.
The beneficial effects of the invention are as follows:Proportioning is scientific and reasonable, and using aluminium as main metal element, increased magnesium, tungsten and sodium add
The big intensity of aluminium alloy, increase abrasion resistant effect and corrosion resistance, it is adaptable to motorcycle, improve the stability of metal material.
Embodiment 2
A kind of motorcycle aluminium alloy, includes the component of following parts by weight:
75 parts of aluminium;
0.65 part of manganese;
6.5 parts of sodium;
0.45 part of cobalt;
0.35 part of magnesium;
0.2 part of tungsten.
The beneficial effects of the invention are as follows:Proportioning is scientific and reasonable, and using aluminium as main metal element, increased magnesium, tungsten and sodium add
The big intensity of aluminium alloy, increase abrasion resistant effect and corrosion resistance, it is adaptable to motorcycle, improve the stability of metal material.
Embodiment 3
A kind of motorcycle aluminium alloy, includes the component of following parts by weight:
80 parts of aluminium;
0.8 part of manganese;
8 parts of sodium;
0.6 part of cobalt;
0.5 part of magnesium;
0.35 part of tungsten.
The beneficial effects of the invention are as follows:Proportioning is scientific and reasonable, and using aluminium as main metal element, increased magnesium, tungsten and sodium add
The big intensity of aluminium alloy, increase abrasion resistant effect and corrosion resistance, it is adaptable to motorcycle, improve the stability of metal material.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (5)
1. a kind of motorcycle aluminium alloy, it is characterised in that:Include the component of following parts by weight:
70-80 parts of aluminium;
0.5-0.8 parts of manganese;
5-8 parts of sodium;
0.3-0.6 parts of cobalt;
0.2-0.5 parts of magnesium;
0.12-0.35 parts of tungsten.
2. a kind of motorcycle aluminium alloy according to claim 1, it is characterised in that:The parts by weight of the cobalt are 0.4-
0.5 part.
3. a kind of motorcycle aluminium alloy according to claim 1, it is characterised in that:The parts by weight of the sodium are 5.5-
6.5 part.
4. a kind of motorcycle aluminium alloy according to claim 1, it is characterised in that:The parts by weight of the tungsten are 0.2-
0.35 part.
5. a kind of motorcycle aluminium alloy according to claim 1, it is characterised in that:The parts by weight of the manganese are 0.65
Part.