CN107034540A - The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net - Google Patents
The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net Download PDFInfo
- Publication number
- CN107034540A CN107034540A CN201710451849.4A CN201710451849A CN107034540A CN 107034540 A CN107034540 A CN 107034540A CN 201710451849 A CN201710451849 A CN 201710451849A CN 107034540 A CN107034540 A CN 107034540A
- Authority
- CN
- China
- Prior art keywords
- parts
- fishing net
- resistance
- agricultural chemicals
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses the preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, including following operating procedure：（1）In the hot water that polyvinyl resin is put into 80 90 DEG C, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive；（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast 34 times of roller stretching；（3）Netting twine after first time stretching is put into after being soaked 23 hours in soak, it is carried out to secondary fast roller stretching under 180 200 DEG C of hot-air, anti-bird pest net filament is made.The preparation method for the anti-bird pest net filament that the present invention is provided, manufacture craft is simple, obtained fishing net monofilament, not only there is extremely excellent mechanical property, larger tensile strength can be born, it is not easy to break, and its resistance to agricultural chemicals corrodes, resistance to oxidation greatly improves the quality of obtained anti-bird pest fishing net.
Description
Technical field
The invention belongs to fishing net preparation field, and in particular to the preparation method that a kind of resistance to agricultural chemicals corrodes fishing net.
Background technology
Fishing net requires higher tensile strength, higher toughness, the wearability of height, low water imbibition, in the past using cotton,
The fishing net that jute fiber plaiting article is knitted, in order to meet above-mentioned requirements, it is necessary to coated with resins.Fishing net is made with plastics, is usually by extruding plastics
Machine extrudes wire drawing, then by braider be made into mesh and tailor into fishing net.Mesh has rhombus, hexagon, oblique rhombus, square
Etc. shape.Fishing net is in addition to for as fishing, the instrument of cultivation, and it is also commonly used to the anti-bird pest net as orchard.Due to fruit
Garden often needs to spray insecticide, after the contamination of some agricultural chemicals is on fishing net, and the phenomenon for changing colour, aoxidizing aggravation easily occurs in fishing net, therefore
It is badly in need of a kind of fishing net that can be resistant to agricultural chemicals corrosion.
The content of the invention
In order to solve the above problems, the present invention provides the preparation method that a kind of resistance to agricultural chemicals corrodes fishing net.
The present invention is achieved by the following technical solutions.
The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, including following operating procedure：
（1）Polyvinyl resin is put into 80-90 DEG C of hot water, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive,
Wherein additive is made up of the component of following parts by weight：10-15 parts of isopropanol pinacol borate, 18-26 parts of nano zine oxide,
3-6 parts of Boratex, 1-2 parts of SILICA FUME；
（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast roller stretching 3-
4 times；
（3）Netting twine after first time stretching is put into after being soaked 2-3 hours in soak, by its hot-air at 180-200 DEG C
It is lower to carry out secondary fast roller stretching, anti-bird pest net filament is made, wherein soak is made up of the component of following parts by weight：Castor oil
13-16 parts, 10-14 parts of 1,8- pungent two mercaptan, 7-9 parts of polyoxyethylene nonylphenol ether -6,5-8 parts of dinonyl phthalate, di(2-ethylhexyl)phosphate it is different pungent
4-6 parts of ester, 30-40 parts of absolute ethyl alcohol.
Specifically, above-mentioned steps（2）The temperature of middle heating is 140-160 DEG C.
Specifically, above-mentioned steps（3）Middle soak is made of following methods：Polyoxyethylene nonylphenol ether -6 is added to absolute ethyl alcohol
In, after being mixed evenly, then add castor oil, pungent two mercaptan of 1,8-, dinonyl phthalate, di(2-ethylhexyl)phosphate thereto successively
Different monooctyl ester, after being mixed evenly, is made soak.
Technical scheme more than, the beneficial effects of the invention are as follows：
The preparation method for the anti-bird pest net fishing net that the present invention is provided, manufacture craft is simple, not only with extremely excellent mechanical property
Can, larger tensile strength can be born, it is not easy to break, and its resistance to agricultural chemicals corrosion, resistance to oxidation, greatly improve obtained anti-
The quality of bird pest fishing net.After nano zine oxide and SILICA FUME synergy in additive, fishing net surface can be effectively lifted
Active force between compactness, lifting fishing net molecule, can effectively reduce residual quantity and residence time of the agricultural chemicals on fishing net surface,
Agricultural chemicals is avoided to chemically react with the molecule in fishing net；Isopropanol pinacol borate and Boratex collaboration in additive
After effect, when can be in Pesticide Infiltration to fishing net, be chemically reacted instead of the composition in fishing net and farm chemical ingredients, it is ensured that fishing
The molecular structure of net is not destroyed；In conventional technology, after fishing net one-off drawing, directly heated up, carry out two
Secondary stretching, the invention netting twine carry out first time stretching after, put it into specific soak soak, effectively
The effect for improving stretching, both reduced the appearance number of stomata in fishing net drawing process, improve again fishing net stretching it is equal
Even property.
Embodiment
Following examples are used to illustrate the present invention, but can not be used for limiting the scope of the present invention.The reality used in embodiment
The condition of applying can be for further adjustments according to the condition of producer, and unaccounted implementation condition is usually conventional laboratory conditions.
Embodiment 1
The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, including following operating procedure：
（1）In the hot water that polyvinyl resin is put into 80 DEG C, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive, wherein
Additive is made up of the component of following parts by weight：10 parts of isopropanol pinacol borate, 18 parts of nano zine oxide, 3 parts of Boratex,
1 part of SILICA FUME；
（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast roller stretching 3
Times；
（3）Netting twine after first time stretching is put into after being soaked 2 hours in soak, it is carried out under 180 DEG C of hot-air
Secondary fast roller stretching, is made anti-bird pest net filament, and wherein soak is made up of the component of following parts by weight：13 parts of castor oil, 1,
10 parts of pungent two mercaptan of 8-, 7 parts of polyoxyethylene nonylphenol ether -6,5 parts of dinonyl phthalate, 4 parts of di (isooctyl) phosphate, absolute ethyl alcohol 30
Part.
Specifically, above-mentioned steps（2）The temperature of middle heating is 140 DEG C.
Specifically, above-mentioned steps（3）Middle soak is made of following methods：Polyoxyethylene nonylphenol ether -6 is added to absolute ethyl alcohol
In, after being mixed evenly, then add castor oil, pungent two mercaptan of 1,8-, dinonyl phthalate, di(2-ethylhexyl)phosphate thereto successively
Different monooctyl ester, after being mixed evenly, is made soak.
Embodiment 2
The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, including following operating procedure：
（1）In the hot water that polyvinyl resin is put into 85 DEG C, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive, wherein
Additive is made up of the component of following parts by weight：13 parts of isopropanol pinacol borate, 22 parts of nano zine oxide, 5 parts of Boratex,
1 part of SILICA FUME；
（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast roller stretching 3
Times；
（3）Netting twine after first time stretching is put into after being soaked 2 hours in soak, it is carried out under 190 DEG C of hot-air
Secondary fast roller stretching, is made anti-bird pest net filament, and wherein soak is made up of the component of following parts by weight：15 parts of castor oil, 1,
12 parts of pungent two mercaptan of 8-, 8 parts of polyoxyethylene nonylphenol ether -6,7 parts of dinonyl phthalate, 5 parts of di (isooctyl) phosphate, absolute ethyl alcohol 35
Part.
Specifically, above-mentioned steps（2）The temperature of middle heating is 150 DEG C.
Specifically, above-mentioned steps（3）Middle soak is made of following methods：Polyoxyethylene nonylphenol ether -6 is added to absolute ethyl alcohol
In, after being mixed evenly, then add castor oil, pungent two mercaptan of 1,8-, dinonyl phthalate, di(2-ethylhexyl)phosphate thereto successively
Different monooctyl ester, after being mixed evenly, is made soak.
Embodiment 3
The preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, including following operating procedure：
（1）In the hot water that polyvinyl resin is put into 90 DEG C, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive, wherein
Additive is made up of the component of following parts by weight：15 parts of isopropanol pinacol borate, 26 parts of nano zine oxide, 6 parts of Boratex,
2 parts of SILICA FUME；
（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast roller stretching 4
Times；
（3）Netting twine after first time stretching is put into after being soaked 3 hours in soak, it is carried out under 200 DEG C of hot-air
Secondary fast roller stretching, is made anti-bird pest net filament, and wherein soak is made up of the component of following parts by weight：16 parts of castor oil, 1,
14 parts of pungent two mercaptan of 8-, 9 parts of polyoxyethylene nonylphenol ether -6,8 parts of dinonyl phthalate, 6 parts of di (isooctyl) phosphate, absolute ethyl alcohol 40
Part.
Specifically, above-mentioned steps（2）The temperature of middle heating is 160 DEG C.
Specifically, above-mentioned steps（3）Middle soak is made of following methods：Polyoxyethylene nonylphenol ether -6 is added to absolute ethyl alcohol
In, after being mixed evenly, then add castor oil, pungent two mercaptan of 1,8-, dinonyl phthalate, di(2-ethylhexyl)phosphate thereto successively
Different monooctyl ester, after being mixed evenly, is made soak.
Comparative example 1
Isopropanol pinacol borate and SILICA FUME composition are not contained in additive, remaining step is identical with embodiment 1.
Comparative example 2
Nano zine oxide, SILICA FUME composition are not contained in additive, remaining step is identical with embodiment 2.
Comparative example 3
After stretching for the first time, directly heating stretch for the second time, is soaked without soak, remaining operating procedure is with implementing
Example 3 is identical.
Fishing net monofilament is made with the method for each embodiment and comparative example respectively, these fishing net monofilament are then used into identical
Weaving is woven into fishing net, and obtained fishing net is placed in 800 times of liquid of effective cypermethrin and soaked 48 hours, is then tested
The properties of fishing net, test result is as shown in table 1：
The resistance to agricultural chemicals of table 1 corrodes fishing net the performance test results
| Project | Fracture strength（MPa） | Elongation at break（%） | Cosmetic variation |
| Embodiment 1 | 69 | 37.2 | Nondiscolouring, pore-free |
| Comparative example 1 | 54 | 34.0 | Discoloration is serious, and surface pores is more |
| Embodiment 2 | 71 | 37.8 | Nondiscolouring, pore-free |
| Comparative example 2 | 60 | 35.9 | Discoloration is more serious, and surface pores is more |
| Embodiment 3 | 72 | 37.8 | Nondiscolouring, pore-free |
| Comparative example 3 | 65 | 36.1 | Discoloration is more serious, and surface pores is more |
As shown in Table 1, the method provided using the present invention, can effectively lift the ability of the resistance to agricultural chemicals corrosion of fishing net, greatly
Improve the quality of fishing net.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, in the essential scope of the present invention, the change made, changes, addition or replace, should all belong to of the invention
Protection domain.
Claims (3)
1. the preparation method that a kind of resistance to agricultural chemicals corrodes fishing net, it is characterised in that including following operating procedure：
（1）Polyvinyl resin is put into 80-90 DEG C of hot water, heat-insulation soaking takes out after 2 hours and carries out ball milling with additive,
Wherein additive is made up of the component of following parts by weight：10-15 parts of isopropanol pinacol borate, 18-26 parts of nano zine oxide,
3-6 parts of Boratex, 1-2 parts of SILICA FUME；
（2）By the mixture after ball milling, by extruder spinneret, then cooled down, heated after traction, fast roller stretching 3-
4 times；
（3）Netting twine after first time stretching is put into after being soaked 2-3 hours in soak, by its hot-air at 180-200 DEG C
It is lower to carry out secondary fast roller stretching, anti-bird pest net filament is made, wherein soak is made up of the component of following parts by weight：Castor oil
13-16 parts, 10-14 parts of 1,8- pungent two mercaptan, 7-9 parts of polyoxyethylene nonylphenol ether -6,5-8 parts of dinonyl phthalate, di(2-ethylhexyl)phosphate it is different pungent
4-6 parts of ester, 30-40 parts of absolute ethyl alcohol.
2. the preparation method that a kind of resistance to agricultural chemicals according to claim 1 corrodes fishing net, it is characterised in that step（2）In
The temperature of heating is 140-160 DEG C.
3. the preparation method that a kind of resistance to agricultural chemicals according to claim 1 corrodes fishing net, it is characterised in that step（3）In
Soak is made of following methods：Polyoxyethylene nonylphenol ether -6 is added into absolute ethyl alcohol, after being mixed evenly, then successively to it
Middle addition castor oil, pungent two mercaptan of 1,8-, dinonyl phthalate, di (isooctyl) phosphate, after being mixed evenly, are made leaching
Steep liquid.