CN107030619A - A kind of high-efficient grinding emery cloth and its manufacture method - Google Patents
A kind of high-efficient grinding emery cloth and its manufacture method Download PDFInfo
- Publication number
- CN107030619A CN107030619A CN201710390947.1A CN201710390947A CN107030619A CN 107030619 A CN107030619 A CN 107030619A CN 201710390947 A CN201710390947 A CN 201710390947A CN 107030619 A CN107030619 A CN 107030619A
- Authority
- CN
- China
- Prior art keywords
- resin
- base fabric
- emery cloth
- mass percentage
- primer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-efficient grinding emery cloth and its manufacture method, belong to milling tool technical field.The high-efficient grinding emery cloth, including base fabric, primer layer and frosted layer, the primer layer are covered in base fabric, and the frosted layer is covered on primer.Contain carborundum in frosted layer, boron carbide, zirconium oxide, binding agent, the abrasive material such as diamond contains acrylic acid isocyanate resin in primer layer, zinc oxide, epoxy resin, polyurethane, the material such as phenolic resin.The present invention high-efficient grinding emery cloth by using base fabric, primer layer and frosted layer three-decker; improve the intensity of emery cloth; so that frosted layer is connected more firm with emery cloth; and primer layer can effectively protect base fabric; prevent basic due to the abrasion of stress and frosted layer before emery cloth failure in use, cause base fabric rupture to cause to waste and influence operating efficiency.
Description
Technical field
The present invention relates to a kind of high-efficient grinding emery cloth and its manufacture method, belong to milling tool technical field.
Background technology
The development of nearly 30 years is passed through in emery cloth grinding, as the new processing skill that one more complete and establishes one's own system
Art.Because its is high in machining efficiency, have a wide range of application, strong adaptability, low use cost, easy-to-operate the features such as and it is deep by user
Favor.Abroad, Sand Band Grinding Technique there has been very big progress, and its processing object and application field are increasingly extensive, and it is almost
Can all engineering materials of processing, from general daily life toolses to large-scale aerospace utensil without can not apply, and as obtaining
Take a kind of important means of distinct economic.Its as a kind of process technology why by the increasingly extensive attention of people,
Developed rapidly.
The content of the invention
The technical problem to be solved in the present invention is, in view of the shortcomings of the prior art, propose that a kind of grinding efficiency is high, service life
Long high-efficient grinding emery cloth and its manufacture method.
The present invention is that the technical scheme for solving above-mentioned technical problem proposition is:A kind of high-efficient grinding emery cloth, including base fabric, bottom
Glue-line and frosted layer, the primer layer are covered in base fabric, and the frosted layer is covered on primer;
Frosted layer includes following components by mass percentage:Carborundum:1.77-2.27%, boron carbide:1.12-1.43%, oxidation
Zirconium:0.25-0.44%, white fused alumina:1.32-1.45%, black corundum:1.08-1.17%, Brown Alundum:0.66-0.88%, pink fused alumina:
1.12-1.43%, Pr-Nb fused alumina:3.35-4.16%, binding agent:30.56-35.47%, remaining is:Diamond;Wherein binding agent is pressed
Mass percent meter includes following components:Phenolic resin:10-13%, amino resin:4-7%, polyurethane resin:12-19%,
Epoxy resin:18-20%, acrylic resin:3-5%, acrylic acid epoxy resin:2-4%, surplus is:ABS resin;
Primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:2.3-3.3%, Sodium Polyacrylate:
1.5-2.5%, sodium carboxymethylcellulose:2.1-3.7%, zinc oxide:0.7-1.2%, magnesia:1-2%, aromatic isocyanate:
2.4-3.6%, amino resin:6.7-7.4%, polyurethane resin:2.3-2.7%, epoxy resin:4.3-4.9%, acrylic acid tree
Fat:2.8-3.1%, polyurethane:1.1-1.7%, Lauxite:1.4-2.1%, surplus is:Phenolic resin.
The improvement of above-mentioned technical proposal is:Frosted layer includes following components by mass percentage:Carborundum:1.78%, carbon
Change boron:1.17%, zirconium oxide:0.29%, white fused alumina:1.36%, black corundum:1.12%, Brown Alundum:0.68%, pink fused alumina:1.15%,
Pr-Nb fused alumina:3.36%, binding agent:31.16%, remaining is:Diamond;Wherein binding agent includes with the following group by mass percentage
Point:Phenolic resin:11%, amino resin:4%, polyurethane resin:12%, epoxy resin:18%, acrylic resin:3%, third
Olefin(e) acid epoxy resin:2%, surplus is:ABS resin;
Primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:2.4%, Sodium Polyacrylate:1.6%,
Sodium carboxymethylcellulose:2.5%, zinc oxide:0.8%, magnesia:1%, aromatic isocyanate:2.6%, amino resin:
6.9%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.2%, Lauxite:1.5%,
Surplus is:Phenolic resin.
The improvement of above-mentioned technical proposal is:Frosted layer includes following components by mass percentage:Carborundum:2.12%, carbon
Change boron:1.33%, zirconium oxide:0.34%, white fused alumina:1.42%, black corundum:1.15%, Brown Alundum:0.76%, pink fused alumina:1.21%,
Pr-Nb fused alumina:4.11%, binding agent:34.36%, remaining is:Diamond;Wherein binding agent includes with the following group by mass percentage
Point:Phenolic resin:12%, amino resin:6%, polyurethane resin:17%, epoxy resin:19%, acrylic resin:4%, third
Olefin(e) acid epoxy resin:3%, surplus is:ABS resin;
Primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:3.1%, Sodium Polyacrylate:2.3%,
Sodium carboxymethylcellulose:2.9%, zinc oxide:1.1%, magnesia:2%, aromatic isocyanate:3.4%, amino resin:
7.2%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.7%, Lauxite:1.9%,
Surplus is:Phenolic resin.
The manufacture method of the high-efficient grinding emery cloth, comprises the following steps:
(i) washing stretching is carried out to base fabric, control elongation percentage is in 1-7%;
(ii) base fabric is handled:Aqueous epoxy resins are added into latex, after being stirred at 25-55 DEG C, control temperature is in 30-45
DEG C, base fabric is put into immersion 15-20min;
(iii) dry for the first time:Take out base fabric to be dried, drying temperature is 65-70 DEG C, drying time 13-16min;
(iv) primer on:By the mass percent dispensing of above-mentioned primer layer, accelerator and curing agent are added into dispensing, stirring is equal
It is even, it is coated uniformly on a side surface of base fabric;
(v) second of drying:Base fabric to upper complete primer is dried, and drying temperature is 90-100 DEG C, drying time 5-8min;
(vi) sand is planted:By frosted layer is by predetermined constituent mass percentage dispensing and stirs, the primer layer table of base fabric is coated uniformly on
Face;
(vii) third time is dried:The base fabric after sand will be planted and carry out expanding, drying and processing, drying temperature is 65-80 DEG C, drying time
10-15min;
(viii) solidify:Base fabric after drying is handled using baking and curing, 45-65 DEG C of drying temperature, drying time 40-55min;
(ix) flexure is handled:Base fabric is carried out at flexure using the technique for unreeling-first time flexure-flexure of humidification-second-winding
Reason;
(x) the base fabric after flexure processing cut, arrange obtained high-efficient grinding emery cloth.
It is of the invention to be using the beneficial effect of above-mentioned technical proposal:
(1)The high-efficient grinding emery cloth of the present invention improves emery cloth by using the three-decker of base fabric, primer layer and frosted layer
Intensity so that frosted layer is connected more firm with emery cloth, and primer layer can effectively protect base fabric, prevent in use
It is basic due to the abrasion of stress and frosted layer before emery cloth failure, cause base fabric rupture to cause to waste and influence operating efficiency;
(2)The high-efficient grinding emery cloth of the present invention has used carborundum, boron carbide, the mill such as zirconium oxide and diamond due to frosted layer
Material, intensity is had nothing in common with each other, focused on emery cloth so that emery cloth of the invention can process surface or the workpiece of various intensity,
Realize preliminary polishing simultaneously when grinding first, substantially increase the efficiency of attrition process;
(3)The high-efficient grinding emery cloth of the present invention improves the resistance to of emery cloth due to having used phenolic resin and ABS resin in binding agent
Corrode resistant to elevated temperatures combination property so that emery cloth can tackle more complicated operating mode;
(4)Acrylic acid isocyanate resin, Sodium Polyacrylate, carboxymethyl cellulose in the high-efficient grinding emery cloth primer layer of the present invention
Sodium, zinc oxide, magnesia, aromatic isocyanate, amino resin, polyurethane resin, epoxy resin, acrylic resin,
Polyurethane, Lauxite and phenolic resin is used in combination, the structure characteristic and advantage of multiple material, relative to traditional list
The primer of one material, substantially increases the structural strength of emery cloth, extends service life;
(5)The high-efficient grinding emery cloth of the present invention during fabrication, first by washing stretching, controls the elongation percentage of base fabric, prevents base
Seriously cause final emery cloth size and off quality due to shrinking in process of the cloth after, reduce defect rate;
(6)The present invention is handled by base fabric so that emery cloth intensity is greatly improved, and extends service life;
(7)During the emery cloth baking and curing of the present invention, using relatively low temperature so that more preferably, solidification is more thorough for solidification effect, prevents
Only because temperature is too high, cause frosted layer surface rapid curing, frosted layer internal moisture can not be distributed, so as to influence the strong of emery cloth
Degree;
(8)Handled by flexure so that the pliability of high-efficient grinding emery cloth of the invention is more preferable so that more square when emery cloth is used
Just, grind more efficient.
Embodiment
Embodiment one
The high-efficient grinding emery cloth of the present embodiment includes base fabric, primer layer and frosted layer, and primer layer is covered in base fabric, and frosted layer covers
Cover on primer;Frosted layer includes following components by mass percentage:Carborundum:1.78%, boron carbide:1.17%, zirconium oxide:
0.29%, white fused alumina:1.36%, black corundum:1.12%, Brown Alundum:0.68%, pink fused alumina:1.15%, Pr-Nb fused alumina:3.36%, bond
Agent:31.16%, remaining is:Diamond;Wherein binding agent includes following components by mass percentage:Phenolic resin:11%, ammonia
Base plastic resin:4%, polyurethane resin:12%, epoxy resin:18%, acrylic resin:3%, acrylic acid epoxy resin:2%, it is remaining
Measure and be:ABS resin;
Primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:2.4%, Sodium Polyacrylate:1.6%,
Sodium carboxymethylcellulose:2.5%, zinc oxide:0.8%, magnesia:1%, aromatic isocyanate:2.6%, amino resin:
6.9%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.2%, Lauxite:1.5%,
Surplus is:Phenolic resin.
The manufacture method of the high-efficient grinding emery cloth, comprises the following steps:
(i) washing stretching is carried out to base fabric, control elongation percentage is in 1-7%;
(ii) base fabric is handled:Aqueous epoxy resins are added into latex, after being stirred at 25-55 DEG C, temperature are controlled at 35 DEG C,
Base fabric is put into immersion 15min;
(iii) dry for the first time:Take out base fabric to be dried, drying temperature is 65 DEG C, drying time 15min;
(iv) primer on:By the mass percent dispensing of above-mentioned primer layer, accelerator and curing agent are added into dispensing, stirring is equal
It is even, it is coated uniformly on a side surface of base fabric;
(v) second of drying:Base fabric to upper complete primer is dried, and drying temperature is 90 DEG C, drying time 8min;
(vi) sand is planted:By frosted layer is by predetermined constituent mass percentage dispensing and stirs, the primer layer table of base fabric is coated uniformly on
Face;
(vii) third time is dried:The base fabric after sand will be planted and carry out expanding, drying and processing, drying temperature is 75 DEG C, drying time
14min;
(viii) solidify:Base fabric after drying is handled using baking and curing, 45 DEG C of drying temperature, drying time 55min;
(ix) flexure is handled:Base fabric is carried out at flexure using the technique for unreeling-first time flexure-flexure of humidification-second-winding
Reason;
(x) the base fabric after flexure processing cut, arrange obtained high-efficient grinding emery cloth.
Embodiment two
The high-efficient grinding emery cloth of the present embodiment includes base fabric, primer layer and frosted layer, and primer layer is covered in base fabric, and frosted layer covers
Cover on primer;Frosted layer includes following components by mass percentage:Carborundum:2.12%, boron carbide:1.33%, zirconium oxide:
0.34%, white fused alumina:1.42%, black corundum:1.15%, Brown Alundum:0.76%, pink fused alumina:1.21%, Pr-Nb fused alumina:4.11%, bond
Agent:34.36%, remaining is:Diamond;Wherein binding agent includes following components by mass percentage:Phenolic resin:12%, ammonia
Base plastic resin:6%, polyurethane resin:17%, epoxy resin:19%, acrylic resin:4%, acrylic acid epoxy resin:3%, it is remaining
Measure and be:ABS resin;
Primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:3.1%, Sodium Polyacrylate:2.3%,
Sodium carboxymethylcellulose:2.9%, zinc oxide:1.1%, magnesia:2%, aromatic isocyanate:3.4%, amino resin:
7.2%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.7%, Lauxite:1.9%,
Surplus is:Phenolic resin.
The manufacture method of the high-efficient grinding emery cloth, comprises the following steps:
(i) washing stretching is carried out to base fabric, control elongation percentage is in 1-7%;
(ii) base fabric is handled:Aqueous epoxy resins are added into latex, after being stirred at 45 DEG C, control temperature, will at 45 DEG C
Base fabric is put into immersion 15min;
(iii) dry for the first time:Take out base fabric to be dried, drying temperature is 70 DEG C, drying time 13min;
(iv) primer on:By the mass percent dispensing of above-mentioned primer layer, accelerator and curing agent are added into dispensing, stirring is equal
It is even, it is coated uniformly on a side surface of base fabric;
(v) second of drying:Base fabric to upper complete primer is dried, and drying temperature is 100 DEG C, drying time 5min;
(vi) sand is planted:By frosted layer is by predetermined constituent mass percentage dispensing and stirs, the primer layer table of base fabric is coated uniformly on
Face;
(vii) third time is dried:The base fabric after sand will be planted and carry out expanding, drying and processing, drying temperature is 80 DEG C, drying time
10min;
(viii) solidify:Base fabric after drying is handled using baking and curing, 65 DEG C of drying temperature, drying time 40min;
(ix) flexure is handled:Base fabric is carried out at flexure using the technique for unreeling-first time flexure-flexure of humidification-second-winding
Reason;
(x) the base fabric after flexure processing cut, arrange obtained high-efficient grinding emery cloth.
The present invention is not limited to above-described embodiment.The technical scheme of all use equivalent substitution formation, all falling within the present invention will
The protection domain asked.
Claims (4)
1. a kind of high-efficient grinding emery cloth, including base fabric, primer layer and frosted layer, the primer layer are covered in base fabric, the mill
Layer of sand is covered on primer;It is characterized in that:
The frosted layer includes following components by mass percentage:Carborundum:1.77-2.27%, boron carbide:1.12-1.43%,
Zirconium oxide:0.25-0.44%, white fused alumina:1.32-1.45%, black corundum:1.08-1.17%, Brown Alundum:0.66-0.88%, chromium is firm
It is beautiful:1.12-1.43%, Pr-Nb fused alumina:3.35-4.16%, binding agent:30.56-35.47%, remaining is:Diamond;Wherein bond
Agent includes following components by mass percentage:Phenolic resin:10-13%, amino resin:4-7%, polyurethane resin:12-
19%, epoxy resin:18-20%, acrylic resin:3-5%, acrylic acid epoxy resin:2-4%, surplus is:ABS resin;
The primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:2.3-3.3%, polyacrylic acid
Sodium:1.5-2.5%, sodium carboxymethylcellulose:2.1-3.7%, zinc oxide:0.7-1.2%, magnesia:1-2%, aromatic series isocyanic acid
Ester:2.4-3.6%, amino resin:6.7-7.4%, polyurethane resin:2.3-2.7%, epoxy resin:4.3-4.9%, propylene
Acid resin:2.8-3.1%, polyurethane:1.1-1.7%, Lauxite:1.4-2.1%, surplus is:Phenolic resin.
2. high-efficient grinding emery cloth according to claim 1, it is characterised in that:The frosted layer includes by mass percentage
Following components:Carborundum:1.78%, boron carbide:1.17%, zirconium oxide:0.29%, white fused alumina:1.36%, black corundum:1.12%, palm fibre
Corundum:0.68%, pink fused alumina:1.15%, Pr-Nb fused alumina:3.36%, binding agent:31.16%, remaining is:Diamond;Wherein binding agent
Include following components by mass percentage:Phenolic resin:11%, amino resin:4%, polyurethane resin:12%, asphalt mixtures modified by epoxy resin
Fat:18%, acrylic resin:3%, acrylic acid epoxy resin:2%, surplus is:ABS resin;
The primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:2.4%, Sodium Polyacrylate:
1.6%, sodium carboxymethylcellulose:2.5%, zinc oxide:0.8%, magnesia:1%, aromatic isocyanate:2.6%, aminoplast tree
Fat:6.9%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.2%, Lauxite:
1.5%, surplus is:Phenolic resin.
3. high-efficient grinding emery cloth according to claim 2, it is characterised in that:The frosted layer includes by mass percentage
Following components:Carborundum:2.12%, boron carbide:1.33%, zirconium oxide:0.34%, white fused alumina:1.42%, black corundum:1.15%, palm fibre
Corundum:0.76%, pink fused alumina:1.21%, Pr-Nb fused alumina:4.11%, binding agent:34.36%, remaining is:Diamond;Wherein binding agent
Include following components by mass percentage:Phenolic resin:12%, amino resin:6%, polyurethane resin:17%, asphalt mixtures modified by epoxy resin
Fat:19%, acrylic resin:4%, acrylic acid epoxy resin:3%, surplus is:ABS resin;
The primer layer includes following components by mass percentage:Acrylic acid isocyanate resin:3.1%, Sodium Polyacrylate:
2.3%, sodium carboxymethylcellulose:2.9%, zinc oxide:1.1%, magnesia:2%, aromatic isocyanate:3.4%, aminoplast tree
Fat:7.2%, polyurethane resin:2.6%, epoxy resin:4.5%, acrylic resin:2.9%, polyurethane:1.7%, Lauxite:
1.9%, surplus is:Phenolic resin.
4. the manufacture method of the high-efficient grinding emery cloth according to any claim in claim 1-3, it is characterised in that:Bag
Include following steps:
(i) washing stretching is carried out to base fabric, control elongation percentage is in 1-7%;
(ii) base fabric is handled:Aqueous epoxy resins are added into latex, after being stirred at 25-55 DEG C, control temperature is in 30-45
DEG C, base fabric is put into immersion 15-20min;
(iii) dry for the first time:Take out base fabric to be dried, drying temperature is 65-70 DEG C, drying time 13-16min;
(iv) primer on:By the mass percent dispensing of above-mentioned primer layer, accelerator and curing agent are added into dispensing, stirring is equal
It is even, it is coated uniformly on a side surface of base fabric;
(v) second of drying:Base fabric to upper complete primer is dried, and drying temperature is 90-100 DEG C, drying time 5-8min;
(vi) sand is planted:By frosted layer is by predetermined constituent mass percentage dispensing and stirs, the primer layer table of base fabric is coated uniformly on
Face;
(vii) third time is dried:The base fabric after sand will be planted and carry out expanding, drying and processing, drying temperature is 65-80 DEG C, drying time
10-15min;
(viii) solidify:Base fabric after drying is handled using baking and curing, 45-65 DEG C of drying temperature, drying time 40-55min;
(ix) flexure is handled:Base fabric is carried out at flexure using the technique for unreeling-first time flexure-flexure of humidification-second-winding
Reason;
(x) the base fabric after flexure processing cut, arrange obtained high-efficient grinding emery cloth.