CN107022898A - A kind of inflaming retarding fabric Final finishing rubber cement - Google Patents
A kind of inflaming retarding fabric Final finishing rubber cement Download PDFInfo
- Publication number
- CN107022898A CN107022898A CN201710407029.5A CN201710407029A CN107022898A CN 107022898 A CN107022898 A CN 107022898A CN 201710407029 A CN201710407029 A CN 201710407029A CN 107022898 A CN107022898 A CN 107022898A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber cement
- final finishing
- inflaming retarding
- retarding fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inflaming retarding fabric Final finishing rubber cement, including：Auxiliary rheological agents, solvent, dispersant, antistatic additive, fire retardant and deionized water, the antistatic additive is the one or two kinds of mixture in hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy base ether, the fire retardant is that the accounting of each composition in cycli phosphate esters organic synthesis thing or brominated Polystyrene, the inflaming retarding fabric Final finishing rubber cement is：69 ~ 83 parts of 1 ~ 2 part of auxiliary rheological agents, 2 ~ 5 parts of solvent, 6 ~ 11 parts of dispersant, 3 ~ 5 parts of antistatic additive, 5 ~ 8 parts of fire retardant and deionized water.Through the above way, inflaming retarding fabric Final finishing rubber cement of the present invention, the antistatic effect of fabric is lifted using antistatic additive, avoid the generation of spark during fabric use, recycle fire retardant to strengthen the flame retardant effect of fabric, leave naked light and extinguish immediately, it is to avoid the intensity of a fire spreads, the security used is improved, it is applied widely.
Description
Technical field
The present invention relates to textile finish field, more particularly to a kind of inflaming retarding fabric Final finishing rubber cement.
Background technology
Common fabric be usually it is inflammable, fabric production and use process, encounter naked light and be readily ignited, and
And the intensity of a fire spreads rapidly along fabric, trigger fire incident.
Fabric is used extensively in automotive seat, interior trim and interior decoration field, and these fields are also the multiple area of fire,
The accident that self-burning of vehicle, factory catch fire or family catches fire is of common occurrence, and fabric is not supported substantially in these fire incidents
Anti- ability is, it is necessary to improve.
The content of the invention
The present invention solves the technical problem of a kind of inflaming retarding fabric Final finishing rubber cement is provided, the fire-retardant effect of fabric is lifted
Really, the security used is lifted.
In order to solve the above technical problems, one aspect of the present invention is：A kind of inflaming retarding fabric Final finishing is provided
Rubber cement, including：Auxiliary rheological agents, solvent, dispersant, antistatic additive, fire retardant and deionized water, the antistatic additive are 16
One or two kinds of mixture in alkyl trimethyl ammonium chloride and alkylphenol-polyethenoxy base ether, the fire retardant is ring phosphorus
The accounting of each composition is in esters of gallic acid organic synthesis thing or brominated Polystyrene, the inflaming retarding fabric Final finishing rubber cement：Rheology
1 ~ 2 part of auxiliary agent, 2 ~ 5 parts of solvent, 6 ~ 11 parts of dispersant, 3 ~ 5 parts of antistatic additive, 5 ~ 8 parts of fire retardant and deionized water 69 ~ 83
Part.
In a preferred embodiment of the present invention, the antistatic additive is that hexadecyltrimethylammonium chloride and alkyl phenol are poly-
The proportion of the mixture of oxyethylene group ether, hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy base ether is 1:2.
In a preferred embodiment of the present invention, the inflaming retarding fabric Final finishing rubber cement also includes regulator so that fire-retardant
The Ph values of fabric Final finishing rubber cement are 6 ~ 7.
In a preferred embodiment of the present invention, the regulator is sodium hydroxide.
In a preferred embodiment of the present invention, the auxiliary rheological agents are polyacrylate.
In a preferred embodiment of the present invention, the solvent is acetone.
In a preferred embodiment of the present invention, the accounting of each composition is in the inflaming retarding fabric Final finishing rubber cement：Rheology
83 parts of 1 part of auxiliary agent, 2 parts of solvent, 6 parts of dispersant, 3 parts of antistatic additive, 5 parts of fire retardant and deionized water.
In a preferred embodiment of the present invention, the accounting of each composition is in the inflaming retarding fabric Final finishing rubber cement：Rheology
69 parts of 2 parts of auxiliary agent, 5 parts of solvent, 11 parts of dispersant, 5 parts of antistatic additive, 8 parts of fire retardant and deionized water.
The beneficial effects of the invention are as follows：A kind of inflaming retarding fabric Final finishing rubber cement that the present invention is pointed out, using antistatic additive come
Lift the antistatic effect of fabric, it is to avoid the generation of spark during fabric use, recycle fire retardant to strengthen the resistance of fabric
Fuel efficiency fruit, leaves naked light and extinguishes immediately, it is to avoid spreading for the intensity of a fire, improve the security used, applied widely.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
The embodiment of the present invention includes：
A kind of inflaming retarding fabric Final finishing rubber cement, including：Auxiliary rheological agents, solvent, dispersant, antistatic additive, fire retardant and go from
Sub- water, the antistatic additive is the one or two kinds of in hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy base ether
Mixture, the fire retardant is cycli phosphate esters organic synthesis thing or brominated Polystyrene, the inflaming retarding fabric Final finishing glue
The accounting of each composition is in slurry：1 ~ 2 part of auxiliary rheological agents, 2 ~ 5 parts of solvent, 6 ~ 11 parts of dispersant, 3 ~ 5 parts of antistatic additive, fire retardant 5
~ 8 parts and 69 ~ 83 parts of deionized water.
The antistatic additive is the mixture of hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy base ether, hexadecane
The proportion of base trimethyl ammonium chloride and alkylphenol-polyethenoxy base ether is 1:2.Hexadecyltrimethylammonium chloride be a kind of sun from
Sub- surfactant, used in fabric field, can cause fiber softening, minimizing electrostatic, and alkylphenol-polyethenoxy base ether is to fabric
When being arranged, strengthen antistatic effect.
The inflaming retarding fabric Final finishing rubber cement also includes regulator so that the Ph values of inflaming retarding fabric Final finishing rubber cement are 6 ~ 7,
The stabilization of Ph values, is conducive to being lifted the effect of fabric Final finishing.The regulator is sodium hydroxide, and sodium hydroxide is soluble in water,
Quickly Ph values are adjusted.
The auxiliary rheological agents are polyacrylate, and the dispersion effect of polyacrylate is good, lift the uniformity of rubber cement, are reduced
Particulate matter, the solvent is acetone, and acetone is soluble in water, is suitable as solvent and uses.
Embodiment 1：
83 parts of 1 part of auxiliary rheological agents, 2 parts of solvent, 6 parts of dispersant, 3 parts of antistatic additive, 5 parts of fire retardant and deionized water are taken, is mixed
It is combined, is heated to 60 DEG C, then measure Ph values, adds sodium hydroxide, adjustment Ph values to 6.5.
Embodiment 2：
69 parts of 2 parts of auxiliary rheological agents, 5 parts of solvent, 11 parts of dispersant, 5 parts of antistatic additive, 8 parts of fire retardant and deionized water are taken, is mixed
It is combined, is heated to 65 DEG C, then measure Ph values, adds sodium hydroxide, adjustment Ph values to 6.
Embodiment 3：
Take 1.5 parts of auxiliary rheological agents, 4 parts of solvent, 8.5 parts of dispersant, 4 parts of antistatic additive, 7 parts of fire retardant and deionized water 75
Part, mix, be heated to 65 DEG C, then measure Ph values, add sodium hydroxide, adjustment Ph values to 7.
In summary, a kind of inflaming retarding fabric Final finishing rubber cement that the present invention is pointed out, good flame retardation effect, after material is carried out over there
When phase arranges, the antistatic and fire resistance of fabric can be lifted, the scope of application is more extensive, safe to use.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (8)
1. a kind of inflaming retarding fabric Final finishing rubber cement, it is characterised in that including：Auxiliary rheological agents, solvent, dispersant, antistatic additive, resistance
Agent and deionized water are fired, the antistatic additive is in hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy base ether
One or two kinds of mixture, the fire retardant be cycli phosphate esters organic synthesis thing or brominated Polystyrene, it is described fire-retardant
The accounting of each composition is in fabric Final finishing rubber cement：1 ~ 2 part of auxiliary rheological agents, 2 ~ 5 parts of solvent, 6 ~ 11 parts of dispersant, antistatic additive 3
69 ~ 83 parts of ~ 5 parts, 5 ~ 8 parts of fire retardant and deionized water.
2. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the antistatic additive is cetyl
The mixture of trimethyl ammonium chloride and alkylphenol-polyethenoxy base ether, hexadecyltrimethylammonium chloride and alkylphenol-polyethenoxy
The proportion of base ether is 1:2.
3. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the inflaming retarding fabric Final finishing rubber cement
Also include regulator so that the Ph values of inflaming retarding fabric Final finishing rubber cement are 6 ~ 7.
4. inflaming retarding fabric Final finishing rubber cement according to claim 3, it is characterised in that the regulator is sodium hydroxide.
5. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the auxiliary rheological agents are polyacrylic acid
Salt.
6. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the solvent is acetone.
7. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the inflaming retarding fabric Final finishing rubber cement
In the accounting of each composition be：1 part of auxiliary rheological agents, 2 parts of solvent, 6 parts of dispersant, 3 parts of antistatic additive, 5 parts of fire retardant and go from
Sub- 83 parts of water.
8. inflaming retarding fabric Final finishing rubber cement according to claim 1, it is characterised in that the inflaming retarding fabric Final finishing rubber cement
In the accounting of each composition be：2 parts of auxiliary rheological agents, 5 parts of solvent, 11 parts of dispersant, 5 parts of antistatic additive, 8 parts of fire retardant and go from
Sub- 69 parts of water.