CN107008632A - The new roll coating process that a kind of color steel makes - Google Patents
The new roll coating process that a kind of color steel makes Download PDFInfo
- Publication number
- CN107008632A CN107008632A CN201710272750.8A CN201710272750A CN107008632A CN 107008632 A CN107008632 A CN 107008632A CN 201710272750 A CN201710272750 A CN 201710272750A CN 107008632 A CN107008632 A CN 107008632A
- Authority
- CN
- China
- Prior art keywords
- roller coating
- coating
- layer
- drying
- color steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the new roll coating process that a kind of color steel makes, this method includes：Alkali cleaning degreasing, cleaning, polishing, drying, roller coating smooth surface putty layer, roller coating prime coat, the roller coating of main material enamelled coating, top coat layer roller coating, packaging；The greasy dirt and impurity of substrate are cleaned, it is ensured that plate face is cleaned, then the sheet material substrate that cleaning is finished is polished and dried；One layer of putty layer of the first roller coating in the surface of substrate after the drying; after putty layer is dried; last layer priming paint is applied on the surface of putty layer; last layer fire proofing material is being applied after priming paint is dried; fire proofing material rolls the main material paint of last layer steel plate again after drying; after the completion of roll on an aspect paint again, after drying, will be sticked on the steel plate finally completed diaphragm carry out packaging storage.The color steel of production technology production of the present invention has good thickness of thin, lightweight, intensity, waterproof fireproofing and that corrosivity strong.
Description
Technical field
The present invention relates to a kind of color steel roll coating process, more precisely, being the new roller coating work that a kind of color steel makes
Skill.
Background technology
Color painted steel strip（It is commonly called as color steel）Refer to that surface grease is sloughed, through surface passivation by metal base tandem mill county
After Coating Pretreatment, composite is formed after applying last layer or multilayer organic coating on the surface.
Color steel is divided into veneer, color-steel composite board, floor support plate etc..It is widely used in large public building, public factory building, work
The metope and roofing of dynamic board house and integrated house.
Common color steel is unshielded just now with other, and general fire endurance is 15 minutes, is not fire proofing material
Also be far from being the grade of fire resisting, using there are some potential safety hazards in safety.
The content of the invention
The present invention mainly solves the technical problem present in prior art, so as to provide a kind of the new of color steel making
Roll coating process.
The above-mentioned technical problem of the present invention is mainly what is be addressed by following technical proposals：
The new roll coating process that a kind of color steel makes, including following processing steps：
A, alkali cleaning degreasing：The greasy dirt and impurity of cleaning base plate, it is ensured that plate face is cleaned, and is prepared for the late stage process of japanning；
B, cleaning：Because the raffinate that plate face is retained must the no raffinate retention of clear water cleaning guarantee after degreasing；
C, polishing：The sheet material substrate that cleaning is finished is polished;
Further, polished using sander, polishing number of times is 2 times.
D, drying：Polishing is dried after finishing by drying oven；
Further, polishing post-baking temperature is 60 DEG C ~ 70 DEG C, and drying time is 10 minutes.
E, roller coating smooth surface putty layer:In the basal plane roller coating resin of substrate, toasted again after drying in the shade naturally；
F, roller coating prime coat:After the completion of smooth surface putty layer, then one layer of priming paint of roller coating, dried again after being dried in the shade naturally after roller coating
It is roasting；
G, fireprotection layer roller coating：After the completion of priming paint, dried in the shade after the surface roller coating fireproof coating of prime paint；
H, main material lacquer painting roller coating：Main material lacquer painting roller coating is carried out after the completion of fireprotection layer again, is toasted after drying in the shade naturally；
I, top coat layer roller coating：In the substrate surface roller coating emulsion of main material lacquer painting roller coating, then toasted；
J is packed：Diaphragm will be sticked on the steel plate finally completed, carry out cutting rear packaging and storage according to size.
Preferably, the roller coating smooth surface putty layer described in the step D is substrate surface one layer of ternary of spraying in substrate
Vinyl chloride-vinyl acetate copolymer resin, is placed in ventilation and dries in the shade naturally 1 ~ 2H, then is dried by drying oven, and drying temperature is 65 DEG C ~ 75 DEG C,
Drying time is 10-15 minutes, and the smooth surface putty coating thickness is 100 μm -120 μm.
Preferably, the roller coating prime coat described in the step E uses epoxy anticorrosion coating, mainly using fatty amine,
Epoxy resin stir and quartz sand mixing after even application in be placed in smooth surface putty layer, after roller coating ventilation dry in the shade 1.5 naturally ~
2H, is toasted by drying oven again after drying in the shade, and baking temperature is at 65 DEG C ~ 75 DEG C, and drying time is 10-15 minutes, the bottom
Enamelled coating coating layer thickness is 130 μm -150 μm.
Preferably, the fireprotection layer roller coating described in the step F uses water-based fireproof material, by water-based fireproof material roller coating
After on prime coat, polished after the 3H ~ 4H that dried in the shade naturally in ventilation, roller coating brush mark is being polished off, fireprotection layer roller coating time
Number is 2-3 times, and each roller coating thickness is 200 μm -500 μm.
Further, the fire endurance of the water-based fireproof material is 105 minutes, and sticking strength is 0.63MPa.
Preferably, the coloured paint needed for color steel is chosen in the main material paint roller coating described in the step H, in fireprotection layer
Surface carries out roller coating, and dry in the shade 1 ~ 2H naturally after roller coating in ventilation, and baking temperature is at 70 DEG C ~ 80 DEG C, and drying time is 5-10 points
Clock, the main material enamelled coating coating layer thickness is 100 μm -150 μm.
Preferably, the pure emulsion coatings of water soluble acrylic acid that the top coat layer roller coating described in the step F is used, in main material enamelled coating
Roller coating is carried out on surface, carries out being toasted after roller coating, 60 DEG C -70 DEG C of baking temperature, drying time is 10-15 minutes, institute
Top coat layer coating layer thickness is stated for 100 μm -120 μm.
The new roll coating process that a kind of color steel makes, the color steel that the preparation technology according to any of the above-described is obtained
Plate.
The preferably closed ventilation after the completion of preparation of the color steel of the present invention is preserved.
In the present invention, above-mentioned priority condition can be combined on the basis of common sense in the field is met, and produce the present invention's
Most preferred embodiment.
The positive effect of the present invention is：
1st, color steel of the invention is lightweight, and heat-insulation and heat-preservation is attractive in appearance, fire prevention, anticorrosion, the advantages of waterproof, is that building is melted with decoration
The senior building being integrated is quick for installation.The construction cleaning of color steel prefabricated house, is widely used in large-span industrial building, warehouse, office building,
Roof adds layer, air cleaning room, freezer, retail kiosk and temporary house.Light color steel weight is low to be substantially reduced structural load, drop
Low prefabricated house structural cost.
2nd, color steel prefabricated house is from heavy and light, spliced installation and the characteristics of can arbitrarily cut, and determines the letter that its prefabricated house is installed
Just, benefit can be greatly improved, the duration is saved.Fireproof color steel disclosure satisfy that prefabricated house fire safety rules, reduce fire risk,
The life of support personnel.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is the accompanying drawing used required in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, on the premise of not paying creative work, can be with
Other accompanying drawings are obtained according to these accompanying drawings.
The new roll coating process flow chart that Fig. 1 makes for a kind of color steel of the present invention；
Fig. 2 is cross section structure schematic diagram of the invention；
1st, substrate, 2, smooth surface putty layer, 3, prime coat, 4 fireprotection layers, 5 main material enamelled coatings, 6 top coat layers.
Embodiment
The preferred embodiments of the present invention are described in detail below in conjunction with the accompanying drawings, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, apparent is clearly defined so as to be made to protection scope of the present invention.
The new roll coating process that a kind of color steel of embodiment 1 makes：
A, alkali cleaning degreasing：The greasy dirt and impurity of cleaning base plate, it is ensured that plate face is cleaned, and is prepared for the late stage process of japanning；
B, cleaning：Because the raffinate that plate face is retained must the no raffinate retention of clear water cleaning guarantee after degreasing；
C, polishing：The sheet material substrate that cleaning is finished is polished;
Further, polished using sander, polishing number of times is 2 times.
D, drying：Polishing is dried after finishing by drying oven；
Further, polishing post-baking temperature is 70 DEG C, and drying time is 10 minutes.
E, roller coating smooth surface putty layer:In the basal plane roller coating resin of substrate, toasted again after drying in the shade naturally；
F, roller coating prime coat:After the completion of smooth surface putty layer, then one layer of priming paint of roller coating, dried again after being dried in the shade naturally after roller coating
It is roasting；
G, fireprotection layer roller coating：After the completion of priming paint, dried in the shade after the surface roller coating fireproof coating of prime paint；
H, main material lacquer painting roller coating：Main material lacquer painting roller coating is carried out after the completion of fireprotection layer again, is toasted after drying in the shade naturally；
I, top coat layer roller coating：In the substrate surface roller coating emulsion of main material lacquer painting roller coating, then toasted；
J is packed：Diaphragm will be sticked on the steel plate finally completed, carry out cutting rear packaging and storage according to size.
Preferably, the roller coating smooth surface putty layer described in the step D is substrate surface one layer of ternary of spraying in substrate
Vinyl chloride-vinyl acetate copolymer resin, is placed in ventilation and dries in the shade naturally 2H, then is dried by drying oven, and drying temperature is 75 DEG C, during drying
Between be 10 minutes, the smooth surface putty coating thickness be 100 μm.
Preferably, the roller coating prime coat described in the step E uses epoxy anticorrosion coating, mainly using fatty amine,
Epoxy resin stir and quartz sand mixing after even application dry in the shade naturally 2H in being placed in ventilation in smooth surface putty layer, after roller coating,
Toasted again by drying oven after drying in the shade, baking temperature is at 75 DEG C, and drying time is 10 minutes, the Primer Layer Coatings thickness
For 130 μm.
Preferably, the fireprotection layer roller coating described in the step F uses water-based fireproof material, by water-based fireproof material roller coating
After on prime coat, polished after the 4H that dried in the shade naturally in ventilation, roller coating brush mark is being polished off, fireprotection layer roller coating number of times is
2 times, each roller coating thickness is 200 μm
Further, the fire endurance of the water-based fireproof material is 105 minutes, and sticking strength is 0.63MPa.
Preferably, the coloured paint needed for color steel is chosen in the main material paint roller coating described in the step H, in fireprotection layer
Surface carries out roller coating, 2H is toasted after roller coating, baking temperature is at 80 DEG C, and drying time is 10 minutes, and the main material enamelled coating applies thickness
Spend for 100 μm.
Preferably, the pure emulsion coatings of water soluble acrylic acid that the top coat layer roller coating described in the step F is used, in main material enamelled coating
Roller coating is carried out on surface, carries out being toasted after roller coating, 70 DEG C of baking temperature, drying time is 10 minutes, the top coat layer
Coating layer thickness is 100 μm.
The new roll coating process that a kind of color steel of embodiment 2 makes, including following processing steps：
A, alkali cleaning degreasing：The greasy dirt and impurity of cleaning base plate, it is ensured that plate face is cleaned, and is prepared for the late stage process of japanning；
B, cleaning：Because the raffinate that plate face is retained must the no raffinate retention of clear water cleaning guarantee after degreasing；
C, polishing：The sheet material substrate that cleaning is finished is polished;
Further, polished using sander, polishing number of times is 2 times.
D, drying：Polishing is dried after finishing by drying oven；
Further, polishing post-baking temperature is 60 DEG C, and drying time is 10 minutes.
E, roller coating smooth surface putty layer:In the basal plane roller coating resin of substrate, toasted again after drying in the shade naturally；
F, roller coating prime coat:After the completion of smooth surface putty layer, then one layer of priming paint of roller coating, dried again after being dried in the shade naturally after roller coating
It is roasting；
G, fireprotection layer roller coating：After the completion of priming paint, dried in the shade after the surface roller coating fireproof coating of prime paint；
H, main material lacquer painting roller coating：Main material lacquer painting roller coating is carried out after the completion of fireprotection layer again, is toasted after drying in the shade naturally；
I, top coat layer roller coating：In the substrate surface roller coating emulsion of main material lacquer painting roller coating, then toasted；
J is packed：Diaphragm will be sticked on the steel plate finally completed, carry out cutting rear packaging and storage according to size.
Preferably, the roller coating smooth surface putty layer described in the step D is substrate surface one layer of ternary of spraying in substrate
Vinyl chloride-vinyl acetate copolymer resin, is placed in ventilation and dries in the shade naturally 1H, then is dried by drying oven, and drying temperature is 65 DEG C, during drying
Between be 15 minutes, the smooth surface putty coating thickness be 120 μm.
Preferably, the roller coating prime coat described in the step E uses epoxy anticorrosion coating, mainly using fatty amine,
Epoxy resin stir and quartz sand mixing after even application dry in the shade naturally in being placed in ventilation in smooth surface putty layer, after roller coating
1.5H, is toasted by drying oven again after drying in the shade, and baking temperature is at 65 DEG C, and drying time is 15 minutes, and the prime coat is applied
Thickness degree is 150 μm.
Preferably, the fireprotection layer roller coating described in the step F uses water-based fireproof material, by water-based fireproof material roller coating
After on prime coat, polished after the 3H that dried in the shade naturally in ventilation, roller coating brush mark is being polished off, fireprotection layer roller coating number of times is
3 times, each roller coating thickness is 500 μm.
Further, the fire endurance of the water-based fireproof material is 105 minutes, and sticking strength is 0.63MPa.
Preferably, the coloured paint needed for color steel is chosen in the main material paint roller coating described in the step H, in fireprotection layer
Surface carries out roller coating, and dry in the shade 1H naturally after roller coating in ventilation, and baking temperature is at 70 DEG C, and drying time is 10 minutes, the master
Material enamelled coating coating layer thickness is 150 μm.
Preferably, the pure emulsion coatings of water soluble acrylic acid that the top coat layer roller coating described in the step F is used, in main material enamelled coating
Roller coating is carried out on surface, carries out being toasted after roller coating, 60 DEG C of baking temperature, drying time is 15 minutes, the top coat layer
Coating layer thickness is 120 μm.
The influence for the new roll coating process that the color steel of comparative example 1 makes
The new roll coating process made using the color steel in embodiment 1, the difference is that comparative result is the rolling using embodiment 1
Apply the thickness of color steel that technique obtained thinner, but the roller coating number of times of waterproof layer 2 times, fire rating does not have embodiment 2
Fire rating is high, and the roller coating number of times of the fireprotection layer in embodiment 2 is 3 times, but the coloured silk obtained according to the roll coating process of embodiment 2
The thickness ratio of steel plate is thicker.So the number of times and roller coating thickness in roll coating process can be adjusted according to demand, client's needs are reached
Color steel.
Only illustrate the mentality of designing of the present invention in one embodiment above, in the case where system allows, the present invention can
To expand to external more functional modules simultaneously, so as to extend its function to greatest extent.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, should all be included within the scope of the present invention.Therefore, it is of the invention
Protection domain should be determined by the scope of protection defined in the claims.
Claims (7)
1. the new roll coating process that a kind of color steel makes, it is characterised in that including following processing steps：A, alkali cleaning degreasing：Clearly
Wash the greasy dirt and impurity of substrate, it is ensured that plate face is cleaned, and is prepared for the late stage process of japanning；B, cleaning：After degreasing due to
The raffinate that plate face is retained must the no raffinate retention of clear water cleaning guarantee；
C, polishing：The sheet material substrate that cleaning is finished is polished;D, drying：Polishing is dried after finishing by drying oven
It is dry；E, roller coating smooth surface putty layer:In the basal plane roller coating resin of substrate, toasted again after drying in the shade naturally；F, roller coating prime coat:In smooth surface
After the completion of putty layer, then one layer of priming paint of roller coating, toasted again after being dried in the shade naturally after roller coating；G, fireprotection layer roller coating：It is complete in priming paint
Cheng Hou, is dried in the shade after the surface roller coating fireproof coating of prime paint；H, main material lacquer painting roller coating：Led again after the completion of fireprotection layer
Material lacquer painting roller coating, is toasted after drying in the shade naturally；I, top coat layer roller coating：In the substrate surface roller coating emulsion of main material lacquer painting roller coating, then enter
Row baking；J is packed：Diaphragm will be sticked on the steel plate finally completed, carry out cutting rear packaging and storage according to size.
2. the new roll coating process that color steel according to claim 1 makes, it is characterised in that described in the step D
Roller coating smooth surface putty layer be substrate substrate surface spray one layer of ternary chlorine vinegar copolymer resins, be placed in ventilation and dry in the shade naturally
1 ~ 2H, then dried by drying oven, drying temperature is 65 DEG C ~ 75 DEG C, and drying time is 10-15 minutes, and the smooth surface is greasy
Sub- coating layer thickness is 100 μm -120 μm.
3. the new roll coating process that color steel according to claim 2 makes, it is characterised in that described in the step E
Roller coating prime coat use epoxy anticorrosion coating, mainly using uniform after fatty amine, epoxy resin stirring and quartz sand mixing
It is sprayed in smooth surface putty layer, ventilation is placed in after roller coating and is dried in the shade naturally 1.5 ~ 2H, is toasted again by drying oven after drying in the shade,
Baking temperature is at 65 DEG C ~ 75 DEG C, and drying time is 10-15 minutes, and the Primer Layer Coatings thickness is 130 μm -150 μm.
4. the new roll coating process that color steel according to claim 3 makes, it is characterised in that described in the step F
Fireprotection layer roller coating use water-based fireproof material, by water-based fireproof material roller coating after on prime coat, dried in the shade naturally in ventilation
Polished after 3H ~ 4H, roller coating brush mark polished off, fireprotection layer roller coating number of times be 2-3 time, each roller coating thickness for 200 μm-
500μm。
5. the new roll coating process that color steel according to claim 4 makes, it is characterised in that described in the step H
The roller coating of main material paint choose color steel needed for coloured paint, fireprotection layer surface carry out roller coating, after roller coating ventilation from
So dry in the shade 1 ~ 2H, and baking temperature is at 70 DEG C ~ 80 DEG C, and drying time is 5-10 minutes, and the main material enamelled coating coating layer thickness is 100 μ
m-150μm。
6. the new roll coating process that color steel according to claim 6 makes, it is characterised in that described in the step F
The pure emulsion coatings of water soluble acrylic acid that top coat layer roller coating is used, roller coating is carried out on main material enamelled coating surface, after roller coating need to enter
Row baking, 60-70 DEG C of baking temperature, drying time is 10-15 minutes, and the top coat layer coating layer thickness is 100 μm -120 μm.
7. a kind of novel color steel plate, the new roller coating work that the color steel described in any one according to claim 1-6 makes
The color steel that skill is obtained.