CN106987970A - The manufacture craft of cuprammonium Silk antistatic spinning fancy suiting - Google Patents
The manufacture craft of cuprammonium Silk antistatic spinning fancy suiting Download PDFInfo
- Publication number
- CN106987970A CN106987970A CN201710367663.0A CN201710367663A CN106987970A CN 106987970 A CN106987970 A CN 106987970A CN 201710367663 A CN201710367663 A CN 201710367663A CN 106987970 A CN106987970 A CN 106987970A
- Authority
- CN
- China
- Prior art keywords
- manufacture craft
- twist
- cuprammonium
- fancy suiting
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacture craft of cuprammonium Silk antistatic spinning fancy suiting, it is characterized in that, comprise the following steps：（1）Raw material proportioning：Australia's hair 50 55%, polyester fiber 20 25%, mulberry silk 6 8%, CUP 17 19%；（2）Australia's hair is subjected to bar dye；（3）Spinning：By Australia's hair and polyester fiber after silver mixing, scalp acupuncture, two pins, three pins, four pins, rove, spun yarn are carried out with mulberry silk again, from winder, doubling, double twisting, yarn steaming, obtain warp thread and the first weft yarn, the second weft yarn uses CUP, 300 twists/m of the twist of second weft yarn, twist direction S；（4）Weaving：Successively through warping → gait, draw reed → weaving → base inspection, obtain fabric；（5）Final finishing：→ flat to boil → shape → middle inspection, and → ripe to repair → bristle → singe → put down and boil → dry → dries soft → middle inspection → dewing → high pressure steaming → tank steaming → dewing → tank steaming, obtains finished product for middle inspection.Fancy worsted feel of the present invention is smooth, moisture transported permeable, drapability are good, smooth appearance, rich in gloss.
Description
Technical field
The present invention relates to a kind of manufacture craft of cuprammonium Silk antistatic spinning fancy suiting, belong to textile technology field.
Background technology
With the development of the society, growth in the living standard, it was recognized that the importance of environmental protection, to environmental protection
More pay close attention to, green is that man and nature height is harmonious, is to have the intuitive knowledge background that love could be takeed good care of forever only together.In life
Production, consumption, life in can feel plus environmental constraints, with it is a kind of to environment be responsible for ethical attitude treat clothing, food, shelter, row,
With, with love life, kind treatment the earth, respect for life attitude practice environmental protection life, be allowed to as drink water with breathing as I
Live in an indispensable part.It is rooted in the hearts of the people with green, environmentally friendly, health requirements, requirement of the people to environmental protection is got over
Come higher, this pure natural idea of green is not only popular on dining table, present this idea also begins to the wardrobe infiltration to people,
They wish the dress of oneself not only fashion, moreover it is possible to bring the enjoyment of health.And our enterprises to be made is how with clothes
For carrier, energy-conservation, green, low-carbon, environmental protection are got up with fashion and healthy perfect adaptation.The cuprammonium emulation that my company is researched and developed
Silk antistatic spinning fancy suiting exactly arises at the historic moment under such circumstances.
The content of the invention
The purpose of the present invention is to overcome the deficiencies in the prior art to be spent there is provided a kind of cuprammonium Silk antistatic spinning
Manufacture craft, feel is smooth, moisture transported permeable, drapability are good, smooth appearance, rich in gloss.
The technical scheme provided according to the present invention, the manufacture craft of the cuprammonium Silk antistatic spinning fancy suiting, it is special
Levying is, comprises the following steps：
（1）Raw material proportioning：Australia hair 50-55%, polyester fiber 20-25%, mulberry silk 6-8%, CUP 17-19%；
（2）Bar contaminates recombing：By Australia's hair through the pinecone, dyeing, after backwashing, silver mixing, grilling, combing, grilling, bar is obtained into, into bar
Carry out bar dye；
（3）Spinning：By Australia hair and polyester fiber after silver mixing, scalp acupuncture, two pins, three pins, four pins, then with mulberry silk carry out rove,
Spun yarn, from winder, doubling, double twisting, yarn steaming, obtain warp thread and the first weft yarn, the second weft yarn uses CUP, the second weft yarn
300 twists/m of the twist, twist direction S；
（4）Weaving：Successively through warping → gait, draw reed → weaving → base inspection, obtain fabric；
（5）Final finishing：Middle inspection → flat to boil → shape → middle inspection → and ripe to repair → bristle → singe → put down and boil → dry → baking is soft →
Middle inspection → dewing → high pressure steaming → tank steaming → dewing → tank steams, and obtains finished product.
Further, the average fineness of Australia's hair is 17.41 μm, and average length is 80.7mm.
Further, the polyester fiber is 1.5D*88mm.
Further, the dry fracture strength of the mulberry silk is 3.0-3.5cN/dtex, and wet breaking strength is 1.85-
2.46cN/dtex。
Further, the CUP long filament is 100D/1.
Further, the step（3）In, warp thread single thread is 110,950 twists/m of the twist, twist direction Z；The double yarns of warp thread are
107/2,1230 twists/m of the twist, twist direction S；Weft yarn single thread is 110,950 twists/m of the twist, twist direction Z；The double yarns of weft yarn are 107
Branch/2,1230 twists/m of the twist, twist direction S.
Further, the step（4）In, the warp count of fabric is 446/10 centimetres, weft count is 454/
10 centimetres, breadth：156 centimetres, the grams ms of meter Chong Wei 255.
Further, the parameter of the warping technology：Linear velocity 300m/min, beaming linear velocity 50m/min, yarn tension
3.5 degree, beaming tension force 1kg.
Further, the step（5）In, the flat speed boiled is 60-80 ms/min；The temperature of the fixating shape step
For 170 DEG C, lower machine 155-156cm, upper overfeeding 1%, lower to surpass 0%, hairbrush overfeeding 0%, speed is 25 ms/min；The bristle step：
Using two forward one-reverses；The step of singing：Speed is 115 ms/min, a positive and a negative, and air pressure 13mbar is straight to burn；It is described to dry step
Suddenly：Temperature is 130 DEG C, lower machine 155-156CM, upper overfeeding 1%, lower overfeeding 0%, hairbrush overfeeding 0%, 30 ms/min of speed；It is described to give
Wet step：Get damp again 8-10%, interval 1-2 hours；It is described to dry soft step：Temperature is 130 DEG C, and speed is 28 ms/min, using soft
Soft dose of 0.3kg/ groove, 1 leaching 1 is rolled.
Cuprammonium Silk antistatic worsted fabric feel of the present invention is smooth, moisture transported permeable, drapability are good, outer to go sightseeing
It is clean, rich in gloss.CUP, which has, to be breathed, salubrious characteristic imparts fabric and feels tender thin when with human contact
It is greasy, it is soft and smooth such as silk, there is good sense of touch.The inherent antistatic property of CUP can replace traditional tooling fabric
Add the way of conductive fiber, reduction production difficulty and cost.CUP has larger initial modulus, and fibre deformation is small,
Hook strength and knot strength are big, and with larger resistance capacity to deformation, and the sun-resistant ability of CUP is strong, Anti-mildew capability
Good with resistance to performance of damaging by worms, wearability is splendid, is the high-grade fabric of a great environment-friendlyfashionable fashionable trend.
Embodiment
With reference to specific embodiment, the invention will be further described.
Embodiment one：A kind of manufacture craft of cuprammonium Silk antistatic spinning fancy suiting, comprises the following steps：
（1）Raw material proportioning：90 Australia's hairs 50%, polyester fiber 25%, mulberry silk 8%, CUPs 17%；
The average fineness of Australia's hair is 17.41 μm, and fineness centrifugal pump is 20.6%, and average length is 80.7mm, discrete length
For 36.2%, undercoat coefficient（Below 30mm）For 3.2%, card nailing neps is 2/gram, and regain is 16.8%, and oil content is 0.846%；
The polyester fiber is 1.5D*88mm；
The dry fracture strength of the mulberry silk is 3.0cN/dtex, and wet breaking strength is 1.85cN/dtex, and elastic restoration ratio is
55%, relative density is 1.42, hydroscopicity（20℃ RH65%）For 9%；
The CUP long filament is 100D/1；
（2）Bar contaminates recombing：The pinecone → dyeing → after backwashing → silver mixing → grilling → combing → grilling → into bar, to carrying out bar into bar
Dye；
（3）Spinning：By Australia hair and polyester fiber after silver mixing, scalp acupuncture, two pins, three pins, four pins, then with mulberry silk carry out rove,
Spun yarn, from winder, doubling, double twisting, yarn steaming, obtain warp thread and the first weft yarn, the second weft yarn uses CUP, the second weft yarn
300 twists/m of the twist, twist direction S；
Warp thread：Single thread 110,950 twists/m of the twist, twist direction Z；Double yarns 107/2,1230 twists/m of the twist, twist direction S；
Weft yarn：Single thread 110,950 twists/m of the twist, twist direction Z；Double yarns 107/2,1230 twists/m of the twist, twist direction S；
（4）Weaving：Successively through warping → gait, draw reed → weaving → base inspection, obtain fabric；The warp count of fabric be 446/
10 centimetres, weft count be 454/10 centimetres, breadth：156 centimetres, the grams ms of meter Chong Wei 255；
The parameter of the warping technology：Linear velocity 300m/min, beaming linear velocity 50m/min, 3.5 degree of yarn tension, beaming
Power 1kg；Reasonable adjustment Warp line, it is ensured that opening is clear, solves the faults such as latitude bow yarn, skips, back rest position 105cm, and height-
1cm, menopause height -2cm, front and back position 56CM, tension force 200KG, 315 ° of opening time is more reasonable.
（5）Final finishing：Middle inspection → flat to boil → → ripe to repair → bristle → singe → put down and boil → dry → baking that shape → middle inspection
Soft → middle inspection → dewing → high pressure steaming → tank steaming → dewing → tank steaming → finished product.
Described put down is boiled：Machine is boiled using Italian the flat of CIMI companies, it is flat when boiling, joint is boiled using washing, and to use open width
Shape is cleaned, and forbids to clean using traditional rope form, 60 ms/min of speed, middle small tension receiving coil, it is ensured that yarn position does not slide prevents fibre
Dimension scratch.
The fixating shape step：Temperature is 170 DEG C, lower machine 155cm, and upper overfeeding 1% is lower to surpass 0%, hairbrush overfeeding 0%, and speed is
25 ms/min；
The bristle step：It is large-minded using two forward one-reverses；
The step of singing：Speed is 115 ms/min, a positive and a negative, and air pressure 13mbar is straight to burn；
The baking step：Temperature is 130 DEG C, lower machine 155CM, upper overfeeding 1%, lower overfeeding 0%, hairbrush overfeeding 0%, 30 meters of speed/
Point；
The dewing step：Moisture regain 8%, interval 1 hour；
It is described to dry soft step：Temperature is 130 DEG C, and speed is 28 ms/min, using softening agent 0.3kg/ grooves, and 1 leaching 1 is rolled.
Embodiment three：A kind of manufacture craft of cuprammonium Silk antistatic spinning fancy suiting, comprises the following steps：
（1）Raw material proportioning：90 Australia's hairs 55%, polyester fiber 20%, mulberry silk 6%, CUPs 19%；
The average fineness of Australia's hair is 17.41 μm, and fineness centrifugal pump is 20.6%, and average length is 80.7mm, discrete length
For 36.2%, undercoat coefficient（Below 30mm）For 3.2%, card nailing neps is 2/gram, and regain is 16.8%, and oil content is 0.846%；
The polyester fiber is 1.5D*88mm；
The dry fracture strength of the mulberry silk is 3.5cN/dtex, and wet breaking strength is 2.46cN/dtex, and elastic restoration ratio is
55%, relative density is 1.42, hydroscopicity（20℃、RH65%）For 9%；
The CUP long filament is 100D/1；
（2）Bar contaminates recombing：The pinecone → dyeing → after backwashing → silver mixing → grilling → combing → grilling → into bar, to carrying out bar into bar
Dye；
（3）Spinning：By Australia hair and polyester fiber after silver mixing, scalp acupuncture, two pins, three pins, four pins, then with mulberry silk carry out rove,
Spun yarn, from winder, doubling, double twisting, yarn steaming, obtain warp thread and the first weft yarn, the second weft yarn uses CUP, the second weft yarn
300 twists/m of the twist, twist direction S；
Warp thread：Single thread 110,950 twists/m of the twist, twist direction Z；Double yarns 107/2,1230 twists/m of the twist, twist direction S；
Weft yarn：Single thread 110,950 twists/m of the twist, twist direction Z；Double yarns 107/2,1230 twists/m of the twist, twist direction S；
（4）Weaving：Successively through warping → gait, draw reed → weaving → base inspection, obtain fabric；The warp count of fabric be 446/
10 centimetres, weft count be 454/10 centimetres, breadth：156 centimetres, the grams ms of meter Chong Wei 255；
The parameter of the warping technology：Linear velocity 300m/min, beaming linear velocity 50m/min, 3.5 degree of yarn tension, beaming
Power 1kg；Reasonable adjustment Warp line, it is ensured that opening is clear, solves the faults such as latitude bow yarn, skips, back rest position 105cm, and height-
1cm, menopause height -2cm, front and back position 56CM, tension force 200KG, 315 ° of opening time is more reasonable.
（5）Final finishing：Middle inspection → flat to boil → → ripe to repair → bristle → singe → put down and boil → dry → baking that shape → middle inspection
Soft → middle inspection → dewing → high pressure steaming → tank steaming → dewing → tank steaming → finished product.
Described put down is boiled：Machine is boiled using Italian the flat of CIMI companies, it is flat when boiling, joint is boiled using washing, and to use open width
Shape is cleaned, and forbids to clean using traditional rope form, 80 ms/min of speed, middle small tension receiving coil, it is ensured that yarn position does not slide prevents fibre
Dimension scratch.
The fixating shape step：Temperature is 170 DEG C, lower machine 156cm, and upper overfeeding 1% is lower to surpass 0%, hairbrush overfeeding 0%, and speed is
25 ms/min；
The bristle step：It is large-minded using two forward one-reverses；
The step of singing：Speed is 115 ms/min, a positive and a negative, and air pressure 13mbar is straight to burn；
The baking step：Temperature is 130 DEG C, lower machine 156CM, upper overfeeding 1%, lower overfeeding 0%, hairbrush overfeeding 0%, 30 meters of speed/
Point；
The dewing step：Moisture regain 10%, interval 2 hours；
It is described to dry soft step：Temperature is 130 DEG C, and speed is 28 ms/min, using softening agent 0.3kg/ grooves, and 1 leaching 1 is rolled.
Cuprammonium Silk antistatic spinning fancy suiting product quality of the present invention is according to People's Republic of China's textile industry
GB/T26382-2011《Combing worsted spinning》Standard is performed, and indices are through national textile product Quality Supervision and Inspection Center（River
It is cloudy）Laboratory tests, and reaches the requirement of Grade A standard.
Claims (9)
1. a kind of manufacture craft of cuprammonium Silk antistatic spinning fancy suiting, it is characterized in that, comprise the following steps：
（1）Raw material proportioning：Australia hair 50-55%, polyester fiber 20-25%, mulberry silk 6-8%, CUP 17-19%；
（2）Bar contaminates recombing：By Australia's hair through the pinecone, dyeing, after backwashing, silver mixing, grilling, combing, grilling, bar is obtained into, into bar
Carry out bar dye；
（3）Spinning：By Australia hair and polyester fiber after silver mixing, scalp acupuncture, two pins, three pins, four pins, then with mulberry silk carry out rove,
Spun yarn, from winder, doubling, double twisting, yarn steaming, obtain warp thread and the first weft yarn, the second weft yarn uses CUP, the second weft yarn
300 twists/m of the twist, twist direction S；
（4）Weaving：Successively through warping → gait, draw reed → weaving → base inspection, obtain fabric；
（5）Final finishing：Middle inspection → flat to boil → shape → middle inspection → and ripe to repair → bristle → singe → put down and boil → dry → baking is soft →
Middle inspection → dewing → high pressure steaming → tank steaming → dewing → tank steams, and obtains finished product.
2. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：Australia's hair
Average fineness is 17.41 μm, and average length is 80.7mm.
3. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The polyester is fine
Tie up as 1.5D*88mm.
4. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The mulberry silk
Dry fracture strength be 3.0-3.5cN/dtex, wet breaking strength is 1.85-2.46cN/dtex.
5. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The cuprammonium is fine
Dimension long filament is 100D/1.
6. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The step
（3）In, warp thread single thread is 110,950 twists/m of the twist, twist direction Z；The double yarns of warp thread are 107/2,1230 twists/m of the twist, twist direction
S；Weft yarn single thread is 110,950 twists/m of the twist, twist direction Z；The double yarns of weft yarn are 107/2,1230 twists/m of the twist, twist direction S.
7. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The step
（4）In, the warp count of fabric is 446/10 centimetres, weft count is 454/10 centimetres, breadth：156 centimetres, meter Chong Wei
255 grams ms.
8. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The warping work
The parameter of skill：Linear velocity 300m/min, beaming linear velocity 50m/min, 3.5 degree of yarn tension, beaming tension force 1kg.
9. the manufacture craft of cuprammonium Silk antistatic spinning fancy suiting as claimed in claim 1, it is characterized in that：The step
（5）In, the flat speed boiled is 60-80 ms/min；The temperature of the fixating shape step is 170 DEG C, lower machine 155-156cm, upper super
1% is fed, lower to surpass 0%, hairbrush overfeeding 0%, speed is 25 ms/min；The bristle step：Using two forward one-reverses；The step of singing：
Speed is 115 ms/min, a positive and a negative, and air pressure 13mbar is straight to burn；The baking step：Temperature is 130 DEG C, lower machine 155-
156CM, upper overfeeding 1%, lower overfeeding 0%, hairbrush overfeeding 0%, 30 ms/min of speed；The dewing step：Get damp again 8-10%, interval 1-2
Hour；It is described to dry soft step：Temperature is 130 DEG C, and speed is 28 ms/min, using softening agent 0.3kg/ grooves, and 1 leaching 1 is rolled.