CN106985471A - A kind of weaving face fabric clearly breathed freely and preparation method thereof - Google Patents

A kind of weaving face fabric clearly breathed freely and preparation method thereof Download PDF

Info

Publication number
CN106985471A
CN106985471A CN201710180142.4A CN201710180142A CN106985471A CN 106985471 A CN106985471 A CN 106985471A CN 201710180142 A CN201710180142 A CN 201710180142A CN 106985471 A CN106985471 A CN 106985471A
Authority
CN
China
Prior art keywords
fabric
weaving face
parts
yarn
face fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710180142.4A
Other languages
Chinese (zh)
Inventor
程飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Yundu Cotton Co Ltd
Original Assignee
Hefei Yundu Cotton Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Yundu Cotton Co Ltd filed Critical Hefei Yundu Cotton Co Ltd
Priority to CN201710180142.4A priority Critical patent/CN106985471A/en
Publication of CN106985471A publication Critical patent/CN106985471A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of weaving face fabric clearly breathed freely, the weaving face fabric is made up of fabric and outer shell fabric, and the fabric includes the raw material of following parts by weight：25 36 parts of tencel, 12 28 parts of Lycra cotton, the outer shell fabric includes the raw material of following parts by weight：8 16 parts of polypropylene short fiber, 30 48 parts of bamboo-carbon fibre.The weaving face fabric nexine pro-skin of the present invention feels nice and cool, perspires moisture absorption, and outer layer moisture absorption is ventilative, bacteriostasis antibiosis, adds excellent intensity and ductility, is especially suitable for for manufacturing sportswear.The present invention preparation method include spinning, sizing, knit sand, post-treating and other steps, technique is simple to operation, overcome fiber frictional force greatly, the shortcoming of low intensity so that fabric texture is soft and smooth, and anti-static effect is good.

Description

A kind of weaving face fabric clearly breathed freely and preparation method thereof
Technical field
The present invention relates to field of textile, and in particular to a kind of weaving face fabric clearly breathed freely and preparation method thereof.
Background technology
Weaving face fabric, by method for weaving point, there is Weft knitted fabric and the class of warp knitted fabric two.Weft knitted fabric is normal With low-elasticity terylene fibre or special-shaped dacron thread, Polyamide Yarns, cotton yarn, wool yarn etc. for raw material, using plain stitch, change plain stitch, Rib-loop plain stitch, double rib plain stitch, figured texture weave, pile stitch etc., weave and form on various weft machines.With existing Generation science and technology progress and growth in the living standard, people for garment material Functional Requirement increasingly
Height, this causes functional fabric to turn into new focus, and the exploitation of various functions fabric is produced therewith.
The production method of current functional textile fabric is also more original, or production cost is very high, or working condition requirement It is higher, cause the production and its application of functional fabric limited.Existing fabric is usually to be made up of chemical fibre fabric, the face Expect that moisture is readily volatilized, and heavier mass, not salubrious enough sweat-absorbing breathable, easily sensitive constitution is caused under allergy, dry environment Electrostatic is also also easy to produce, is unfavorable for healthy.Therefore, in the market needs what a kind of weaving face fabric of salubrious ventilative antistatic was made Clothes meets the life requirement of people.
The content of the invention
It is an object of the invention to overcoming above-mentioned the deficiencies in the prior art there is provided a kind of clearly ventilative weaving face fabric and its Preparation method, the weaving face fabric frivolous ventilative perspires non-sticky body, and anti-static effect is good.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides a kind of weaving face fabric clearly breathed freely, it is made up of fabric and outer shell fabric, the fabric Include the raw material of following parts by weight：25-36 parts of tencel, 12-28 parts of Lycra cotton, the outer shell fabric includes the original of following parts by weight Material：8-16 parts of polypropylene short fiber, 30-48 parts of bamboo-carbon fibre.
Preferably, the Lycra cotton is according to cotton of the mass fraction meter comprising 95-97% and 5-3% Lycra.
Preferably, the fineness of the tencel is 1.74dtex, and average length is 51mm.
Preferably, the fineness of the Lycra cotton is 1.65dtex, and average length is 38mm.
Preferably, the fineness of the polypropylene short fiber is 1.66dtex, and average length is 56mm.
Preferably, the fineness of the bamboo-carbon fibre is 1.52dtex, and average length is 35mm.
The preparation method of the above-mentioned weaving face fabric clearly breathed freely, comprises the following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile；
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C of rotation Dried 20-30 minutes in drying box；
（3）Weaving：By step（3）The yarn of sizing processing is woven using the mode of entrying and used between the fabric of double-decker, fabric Adhesive is bonded；
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing process is adopted With 3-5g/L amylase, and use 80-90 DEG C of washing；The mercerizing process uses the sodium hydroxide of 15-20% mass concentrations Solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
Preferably, the step（1）The tension force of entrying of first yarn is 3.8cN, and the tension force of entrying of the second yarn is 6.2cN。
Preferably, the step（3）The adhesive used is epoxy resin, phenolic resin, Lauxite, melamine-first Urea formaldehyde, organic siliconresin or acrylic resin.
Wherein, tencel is pure natural reproducibility fiber, be Acordis companies of Britain to extract from eucalyptus 100% day Right wood pulp for raw material development, be referred to as " dream of the fiber of 21 century ".Its intensity is high, has the comfortableness of cotton concurrently again, is really one The feel of sample and good drapability.
Lycra cotton-wadded quilt is referred to as " friendly " fiber, not only due to it can thoroughly with natural and artificial fiber fusion Together, and the comfort level of fabric or clothing, sense of controling oneself can also be increased, moved freely and service life.Substantially improve The feel of fabric, drapability and folding line recovery capacity, improve the comfort of various clothings and fit sense, make various clothes aobvious Reveal new vitality.
Polypropylene short fiber is a kind of chemical synthetic fiber, and density is smaller, with good extensibility, anticorrosive property, moisture absorption Perspiration discharging performance.
Bamboo-carbon fibre is to take mao bamboon to be raw material, employs the calcining new technology of pure oxygen high temperature and nitrogen barrier delay so that The micropore that bamboo charcoal innately has more refine with honeycomb, then again with honeycomb microporous structure trend polyester modification cut into slices Melt spinning and be made.This unique fibre structure design, with moisture absorption is ventilative, bacteriostasis antibiosis, cool in summer and warm in winter, green ring The features such as guarantor.
Compared with prior art, the present invention has following beneficial effect：
（1）The weaving face fabric of the present invention is used as fabric, polypropylene chopped fiber peacekeeping bamboo-carbon fibre conduct using tencel and Lycra cotton Outer shell fabric, the weaving face fabric nexine pro-skin feels nice and cool, perspires moisture absorption after bonding, and outer layer moisture absorption is ventilative, bacteriostasis antibiosis, adds excellent Good intensity and ductility, is especially suitable for for manufacturing sportswear.
（2）The preparation method of the weaving face fabric of the present invention includes spinning, sizing, knits sand, post-treating and other steps, and technique is simple Easy to operate, the frictional force that overcomes fiber is big, the shortcoming of low intensity so that fabric texture is soft and smooth, and anti-static effect is good.
Embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1.
A kind of weaving face fabric clearly breathed freely, is made up of fabric and outer shell fabric, and the fabric includes following weight The raw material of part：25 parts of tencel, 16 parts of Lycra cotton, the outer shell fabric includes the raw material of following parts by weight：8 parts of polypropylene short fiber, 36 parts of bamboo-carbon fibre.Wherein, Lycra cotton is according to cotton of the mass fraction meter comprising 95-97% and 5-3% Lycra, and the fineness of tencel is 1.74dtex, average length is 51mm.The fineness of Lycra cotton is 1.65dtex, and average length is 38mm.Polypropylene short fiber it is thin Spend for 1.66dtex, average length is 56mm.The fineness of bamboo-carbon fibre is 1.52dtex, and average length is 35mm.
The preparation method of the above-mentioned weaving face fabric clearly breathed freely, comprises the following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile, the tension force of entrying of the first yarn is 3.8cN, the second yarn The tension force of entrying of line is 6.2cN.
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C Dried 20-30 minutes in rotation drying box.
（3）Weaving：By step（3）The yarn of sizing processing weaves the fabric of double-decker, fabric using the mode of entrying Between bonded with epoxy resin.
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing work Sequence uses 3-5g/L amylase, and uses 80-90 DEG C of washing；The mercerizing process uses the hydrogen-oxygen of 15-20% mass concentrations Change sodium solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
Embodiment 2.
A kind of weaving face fabric clearly breathed freely, is made up of fabric and outer shell fabric, and the fabric includes following weight The raw material of part：30 parts of tencel, 18 parts of Lycra cotton, the outer shell fabric includes the raw material of following parts by weight：12 parts of polypropylene short fiber, 38 parts of bamboo-carbon fibre.Wherein, Lycra cotton is according to cotton of the mass fraction meter comprising 95-97% and 5-3% Lycra, and the fineness of tencel is 1.74dtex, average length is 51mm.The fineness of Lycra cotton is 1.65dtex, and average length is 38mm.Polypropylene short fiber it is thin Spend for 1.66dtex, average length is 56mm.The fineness of bamboo-carbon fibre is 1.52dtex, and average length is 35mm.
The preparation method of the above-mentioned weaving face fabric clearly breathed freely, comprises the following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile, the tension force of entrying of the first yarn is 3.8cN, the second yarn The tension force of entrying of line is 6.2cN.
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C Dried 20-30 minutes in rotation drying box.
（3）Weaving：By step（3）The yarn of sizing processing weaves the fabric of double-decker, fabric using the mode of entrying Between use phenolic resin adhesion.
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing work Sequence uses 3-5g/L amylase, and uses 80-90 DEG C of washing；The mercerizing process uses the hydrogen-oxygen of 15-20% mass concentrations Change sodium solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
Embodiment 3.
A kind of weaving face fabric clearly breathed freely, is made up of fabric and outer shell fabric, and the fabric includes following weight The raw material of part：32 parts of tencel, 22 parts of Lycra cotton, the outer shell fabric includes the raw material of following parts by weight：14 parts of polypropylene short fiber, 40 parts of bamboo-carbon fibre.Wherein, Lycra cotton is according to cotton of the mass fraction meter comprising 95-97% and 5-3% Lycra, and the fineness of tencel is 1.74dtex, average length is 51mm.The fineness of Lycra cotton is 1.65dtex, and average length is 38mm.Polypropylene short fiber it is thin Spend for 1.66dtex, average length is 56mm.The fineness of bamboo-carbon fibre is 1.52dtex, and average length is 35mm.
The preparation method of the above-mentioned weaving face fabric clearly breathed freely, comprises the following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile, the tension force of entrying of the first yarn is 3.8cN, the second yarn The tension force of entrying of line is 6.2cN.
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C Dried 20-30 minutes in rotation drying box.
（3）Weaving：By step（3）The yarn of sizing processing weaves the fabric of double-decker, fabric using the mode of entrying Between bonded with organic siliconresin.
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing work Sequence uses 3-5g/L amylase, and uses 80-90 DEG C of washing；The mercerizing process uses the hydrogen-oxygen of 15-20% mass concentrations Change sodium solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
Embodiment 4.
A kind of weaving face fabric clearly breathed freely, is made up of fabric and outer shell fabric, and the fabric includes following weight The raw material of part：36 parts of tencel, 24 parts of Lycra cotton, the outer shell fabric includes the raw material of following parts by weight：16 parts of polypropylene short fiber, 25 parts of bamboo-carbon fibre.Wherein, Lycra cotton is according to cotton of the mass fraction meter comprising 95-97% and 5-3% Lycra, and the fineness of tencel is 1.74dtex, average length is 51mm.The fineness of Lycra cotton is 1.65dtex, and average length is 38mm.Polypropylene short fiber it is thin Spend for 1.66dtex, average length is 56mm.The fineness of bamboo-carbon fibre is 1.52dtex, and average length is 35mm.
The preparation method of the above-mentioned weaving face fabric clearly breathed freely, comprises the following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile, the tension force of entrying of the first yarn is 3.8cN, the second yarn The tension force of entrying of line is 6.2cN.
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C Dried 20-30 minutes in rotation drying box.
（3）Weaving：By step（3）The yarn of sizing processing weaves the fabric of double-decker, fabric using the mode of entrying Between use acrylic binder.
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing work Sequence uses 3-5g/L amylase, and uses 80-90 DEG C of washing；The mercerizing process uses the hydrogen-oxygen of 15-20% mass concentrations Change sodium solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
Performance detection：Antistatic, inspection that is antibacterial, perspiring moisture pick-up properties have been carried out to above-described embodiment 1-4 weaving face fabric Survey, wherein, control group selects common polyester fabric, and the bacteriostasis rate of staphylococcus aureus is the testing result of 50 days.
As can be seen from the above table, compared with common polyester fabric, the weaving face fabric charge density of the embodiment of the present invention is smaller, i.e., Anti-static effect is more excellent；Exceed 99.6% to the staphylococcus aureus bacteriostasis rate of 50 days, bacteriostat degerming effect is preferable； Hydrofuge amount perspires moisture absorption efficiency high, is especially suitable for for making gym suit obviously higher than ordinary polyester fabric.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications It should be regarded as protection scope of the present invention.

Claims (9)

1. a kind of weaving face fabric clearly breathed freely, is made up of, it is characterised in that the fabric fabric and outer shell fabric Include the raw material of following parts by weight：25-36 parts of tencel, 12-28 parts of Lycra cotton, the outer shell fabric includes the original of following parts by weight Material：8-16 parts of polypropylene short fiber, 30-48 parts of bamboo-carbon fibre.
2. the weaving face fabric according to claim 1 clearly breathed freely, it is characterised in that the Lycra cotton is according to mass fraction Cotton of the meter comprising 95-97% and 5-3% Lycra.
3. clearly ventilative weaving face fabric according to claim 1, it is characterised in that the fineness of the tencel is 1.74dtex, average length is 51mm.
4. clearly ventilative weaving face fabric according to claim 1, it is characterised in that the fineness of the Lycra cotton is 1.65dtex, average length is 38mm.
5. clearly ventilative weaving face fabric according to claim 1, it is characterised in that the fineness of the polypropylene short fiber is 1.66dtex, average length is 56mm.
6. clearly ventilative weaving face fabric according to claim 1, it is characterised in that the fineness of the bamboo-carbon fibre is 1.52dtex, average length is 35mm.
7. the preparation method of the clearly ventilative weaving face fabric according to claim 1-6 any one, it is characterised in that bag Include following steps：
（1）Spinning：By blowing, cotton carding, drafting, rove, spinning process, it is the first yarn that tencel and Lycra cotton are mixed into weaving Line, is the second yarn by polypropylene chopped fiber peacekeeping bamboo-carbon fibre mixed textile；
（2）Sizing：First yarn and the second yarn are impregnated into slurries, is taken out after 50-60 minutes, is put into 50-60 DEG C of rotation Dried 20-30 minutes in drying box；
（3）Weaving：By step（3）The yarn of sizing processing is woven using the mode of entrying and used between the fabric of double-decker, fabric Adhesive is bonded；
（4）Post processing：The fabric of double-decker is subjected to desizing, mercerising, stentering forming, shrinking processes, the desizing process is adopted With 3-5g/L amylase, and use 80-90 DEG C of washing；The mercerizing process uses the sodium hydroxide of 15-20% mass concentrations Solution；The stentering forming process preliminary drying temperature is 100 DEG C, and baking temperature is 160 DEG C；Breadth is made in the shrinking processes 160mm, grammes per square metre 180g/m2, the weaving face fabric of contracting cloth rate 5%.
8. the preparation method of the weaving face fabric according to claim 7 clearly breathed freely, it is characterised in that the step（1） The tension force of entrying of first yarn is 3.8cN, and the tension force of entrying of the second yarn is 6.2cN.
9. the preparation method of the weaving face fabric according to claim 7 clearly breathed freely, it is characterised in that the step（3） The adhesive used is epoxy resin, phenolic resin, Lauxite, melamine-formaldehyde resin, organic siliconresin or acrylic acid tree Fat.
CN201710180142.4A 2017-03-24 2017-03-24 A kind of weaving face fabric clearly breathed freely and preparation method thereof Withdrawn CN106985471A (en)