CN106978026A - 二氧化硅气凝胶保温隔热乳胶漆及其制备方法 - Google Patents
二氧化硅气凝胶保温隔热乳胶漆及其制备方法 Download PDFInfo
- Publication number
- CN106978026A CN106978026A CN201710167789.3A CN201710167789A CN106978026A CN 106978026 A CN106978026 A CN 106978026A CN 201710167789 A CN201710167789 A CN 201710167789A CN 106978026 A CN106978026 A CN 106978026A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- aerosil
- titanium dioxide
- aerosil insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种二氧化硅气凝胶保温隔热乳胶漆及其制备方法，该乳胶漆按照重量份包括：去离子水20～35份、分散剂0.5～0.8份、二氧化硅气凝胶粉体4～9份、消泡剂0.1～0.2份、润湿剂0.3～0.5份、中空微珠填料15～30份、钛白粉8～15份、高岭土8～12份、滑石粉2～5份、轻质碳酸钙5～10份、重质碳酸钙10～15份、丙烯酸乳液30～60份、防霉剂0.3～0.5份、多功能助剂0.2～0.4份、成膜助剂2～4份、增稠剂0.5～1.5份、流平剂0.3～0.5份。本发明所制备的二氧化硅气凝胶保温隔热乳胶漆具有良好的隔热性、高遮盖率、高渗透性和附着力、不燃等特性，是一种优良的保温隔热乳胶漆。
Description
技术领域
本申请属于建筑涂料技术领域，特别是涉及一种二氧化硅气凝胶保温隔热乳胶漆及其制备方法。
背景技术
自20世纪80年代以来，建筑行业的迅速发展，人们逐渐意识到建筑能耗占人类能源消耗的比重之大，达到30～40％，而在发达城市夏季制冷、冬季取暖所消耗的能源已占建筑物总能耗的40～50％。为了降低建筑物表面温度、改善工作环境等，对隔热涂料的需求越来越迫切。
照射到建筑物***结构的太阳光主要是通过与***结构的传递、对流和辐射作用对***机构的热量产生影响，进而影响建筑物内部的热环境。近年来，对建筑物***采用具有节能性能的保温砂浆、保温涂料的方法已经引起越来越广泛的关注。目前常用的保温隔热乳胶漆中多采用海泡石、膨胀蛭石等粉体作为保温添加物进行制备，所制得的保温乳胶漆往往存在其图层厚、易开裂、易沾污等缺陷，无法满足人类发展的需求。
二氧化硅气凝胶是一种防热隔热性能非常优越的轻质纳米多孔非晶固体材料，其孔隙率高达80～99.8％，空洞的典型尺寸为1～100nm，比表面积为200～1000m2/g，而密度低至3kg/m3，室温导热系数可低至0.012W/(m·K)。正是由于这些特点，使得二氧化硅气胶凝材料在热学方面有很广阔的应用潜力。
发明内容
本发明的目的在于将具有优越防热隔热性能的二氧化硅气凝胶引入到建筑乳胶漆中，提供一种二氧化硅气凝胶保温隔热乳胶漆及其制备方法，赋予乳胶漆卓越的保温隔热性能。
为实现上述目的，本发明提供如下技术方案：
本申请实施例公开一种二氧化硅气凝胶保温隔热乳胶漆，按照重量份包括：去离子水20～35份、分散剂0.5～0.8份、二氧化硅气凝胶粉体4～9份、消泡剂0.1～0.2份、润湿剂0.3～0.5份、中空微珠填料15～30份、钛白粉8～15份、高岭土8～12份、滑石粉2～5份、轻质碳酸钙5～10份、重质碳酸钙10～15份、丙烯酸乳液30～60份、防霉剂0.3～0.5份、多功能助剂0.2～0.4份、成膜助剂2～4份、增稠剂0.5～1.5份、流平剂0.3～0.5份。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的丙烯酸乳液为纯丙乳液、硅丙乳液、苯丙乳液中的任意一种。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的二氧化硅气凝胶的导热系数低于0.02W/(m·K)。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的中空微珠填料为中空玻璃微珠、粉煤灰漂珠、纳米空心陶瓷微珠、膨胀珍珠岩中的一种或多种混合。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的钛白粉为金红石型或锐钛型。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的多功能助剂为乙醇胺类中和剂。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的流平剂为非离子型疏水改性聚氨酯流平剂。
优选的，在上述的二氧化硅气凝胶保温隔热乳胶漆中，所述的增稠剂为碱溶胀型增稠剂。
相应的，本申请还公开了一种二氧化硅气凝胶保温隔热乳胶漆的制备方法，包括：
步骤1)：在分散转速为1500～2000转/分钟的状态下，依次加入去离子水、分散剂、二氧化硅气凝胶粉体、消泡剂、润湿剂、中空微珠填料、钛白粉、高岭土、滑石粉、轻质碳酸钙、重质碳酸钙，至搅拌均匀；
步骤2)：将分散转速设置为800～1200转/分钟，在步骤1)的基础上依次加入丙烯酸乳液、防霉剂、多功能助剂、成膜助剂、增稠剂、流平剂，至搅拌均匀，即得到一种二氧化硅气凝胶保温隔热乳胶漆。
与现有技术相比，本发明的优点在于：本发明所制备的二氧化硅气凝胶保温隔热乳胶漆具有良好的隔热性、高遮盖率、高渗透性和附着力、不燃等特性，是一种优良的保温隔热乳胶漆。
具体实施方式
本发明通过下列实施例作进一步说明：根据下述实施例，可以更好地理解本发明。然而，本领域的技术人员容易理解，实施例所描述的具体的物料比、工艺条件及其结果仅用于说明本发明，而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1
一种二氧化硅气凝胶保温隔热乳胶漆，由以下重量份的组分构成：去离子水25份、分散剂0.5份、二氧化硅气凝胶粉体4份、消泡剂0.1份、润湿剂0.3份、中空玻璃微珠20份、金红石型钛白粉10份、高岭土9份、滑石粉3份、轻质碳酸钙8份、重质碳酸钙10份、硅丙乳液40份、防霉剂0.3份、HT-95多功能助剂0.2份、成膜助剂2份、SN636增稠剂0.5份、RJ-600流平剂0.3份。
制备步骤如下：
步骤1)：在分散转速为1800转/分钟的状态下，依次加入去离子水、分散剂、二氧化硅气凝胶粉体、消泡剂、润湿剂、中空微珠填料、钛白粉、高岭土、滑石粉、轻质碳酸钙、重质碳酸钙，至搅拌均匀。
步骤2)：将分散转速为800转/分钟，在步骤1的基础上依次加入丙烯酸乳液、防霉剂、多功能助剂、成膜助剂、增稠剂、流平剂，至搅拌均匀，即得到一种二氧化硅气凝胶保温隔热乳胶漆。
实施例2
一种二氧化硅气凝胶保温隔热乳胶漆，由以下重量份的组分构成：去离子水35份、分散剂0.8份、二氧化硅气凝胶粉体9份、消泡剂0.2份、润湿剂0.5份、纳米空心陶瓷微珠30份、金红石型钛白粉15份、高岭土12份、滑石粉5份、轻质碳酸钙10份、重质碳酸钙15份、苯丙乳液60份、防霉剂0.5份、HT-96多功能助剂0.4份、成膜助剂4份、TT-935增稠剂1.5份、RJ-600流平剂0.5份；
制备步骤如下：
步骤1)：在分散转速为2000转/分钟的状态下，依次加入去离子水、分散剂、二氧化硅气凝胶粉体、消泡剂、润湿剂、中空微珠填料、钛白粉、高岭土、滑石粉、轻质碳酸钙、重质碳酸钙，至搅拌均匀。
步骤2)：将分散转速为900转/分钟，在步骤1的基础上依次加入丙烯酸乳液、防霉剂、多功能助剂、成膜助剂、增稠剂、流平剂，至搅拌均匀，即得到一种二氧化硅气凝胶保温隔热乳胶漆。
实施例3
一种二氧化硅气凝胶保温隔热乳胶漆，由以下重量份的组分构成：去离子水20份、分散剂0.5份、二氧化硅气凝胶粉体4份、消泡剂0.1份、润湿剂0.3份、膨胀珍珠岩15份、锐钛型钛白粉8份、高岭土8份、滑石粉2份、轻质碳酸钙5份、重质碳酸钙10份、纯丙乳液30份、防霉剂0.3份、HT-96多功能助剂0.2份、成膜助剂2份、UCAR POLYPHONE T-901增稠剂0.5份、RJ-600流平剂0.3份；
制备步骤如下：
步骤1)：在分散转速为2000转/分钟的状态下，依次加入去离子水、分散剂、二氧化硅气凝胶粉体、消泡剂、润湿剂、中空微珠填料、钛白粉、高岭土、滑石粉、轻质碳酸钙、重质碳酸钙，至搅拌均匀。
步骤2)：将分散转速为1200转/分钟，在步骤1的基础上依次加入丙烯酸乳液、防霉剂、多功能助剂、成膜助剂、增稠剂、流平剂，至搅拌均匀，即得到一种二氧化硅气凝胶保温隔热乳胶漆。
经涂料研究所检验中心检测，本发明实施例1、2和3制备的二氧化硅气凝胶保温隔热乳胶漆主要技术参数如下：
最后，还需要说明的是，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
Claims (9)
1.一种二氧化硅气凝胶保温隔热乳胶漆，其特征在于，按照重量份包括：去离子水20～35份、分散剂0.5～0.8份、二氧化硅气凝胶粉体4～9份、消泡剂0.1～0.2份、润湿剂0.3～0.5份、中空微珠填料15～30份、钛白粉8～15份、高岭土8～12份、滑石粉2～5份、轻质碳酸钙5～10份、重质碳酸钙10～15份、丙烯酸乳液30～60份、防霉剂0.3～0.5份、多功能助剂0.2～0.4份、成膜助剂2～4份、增稠剂0.5～1.5份、流平剂0.3～0.5份。
2.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的丙烯酸乳液为纯丙乳液、硅丙乳液、苯丙乳液中的任意一种。
3.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的二氧化硅气凝胶的导热系数低于0.02W/(m·K)。
4.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的中空微珠填料为中空玻璃微珠、粉煤灰漂珠、纳米空心陶瓷微珠、膨胀珍珠岩中的一种或多种混合。
5.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的钛白粉为金红石型或锐钛型。
6.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的多功能助剂为乙醇胺类中和剂。
7.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的流平剂为非离子型疏水改性聚氨酯流平剂。
8.根据权利要求1所述的二氧化硅气凝胶保温隔热乳胶漆，其特征在于：所述的增稠剂为碱溶胀型增稠剂。
9.权利1至8任一所述的二氧化硅气凝胶保温隔热乳胶漆的制备方法，其特征在于，包括：
步骤1)：在分散转速为1500～2000转/分钟的状态下，依次加入去离子水、分散剂、二氧化硅气凝胶粉体、消泡剂、润湿剂、中空微珠填料、钛白粉、高岭土、滑石粉、轻质碳酸钙、重质碳酸钙，至搅拌均匀；
步骤2)：将分散转速设置为800～1200转/分钟，在步骤1)的基础上依次加入丙烯酸乳液、防霉剂、多功能助剂、成膜助剂、增稠剂、流平剂，至搅拌均匀，即得到一种二氧化硅气凝胶保温隔热乳胶漆。