CN106950722A - A kind of cloudy surface Sunglasses lenses sun clips and its production technology - Google Patents
A kind of cloudy surface Sunglasses lenses sun clips and its production technology Download PDFInfo
- Publication number
- CN106950722A CN106950722A CN201710236655.2A CN201710236655A CN106950722A CN 106950722 A CN106950722 A CN 106950722A CN 201710236655 A CN201710236655 A CN 201710236655A CN 106950722 A CN106950722 A CN 106950722A
- Authority
- CN
- China
- Prior art keywords
- layer
- sunglasses lenses
- sun clips
- lenses sun
- fog
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of cloudy surface Sunglasses lenses sun clips, it includes base material, and the substrate outer surface is sequentially provided with fog surface layer and stiffening layer, and the fog surface layer is coated on face outside base material and formed after being atomized by polysilicon.The present invention sets fog surface layer on Sunglasses lenses sun clips, and the fog surface layer can make light carry out diffusing reflection, so that effectively barrier high light line is emitted directly toward glasses, realizes the function of anti-dazzle and eyeshield.
Description
Technical field
The present invention relates to sunglasses field, and in particular to a kind of cloudy surface Sunglasses lenses sun clips and its production technology.
Background technology
Sunglasses, also referred to as sunshade mirror, are used as sunshade.People will generally adjust light by regulation pupil size and lead in the sun
Amount, when light intensity exceedes human eye regulating power, will be damaged to human eye.So playground out of doors, particularly exists
Summer, many people are kept the sun off using sunshade mirror, and the tired or high light caused with mitigating eyes regulation stimulates the wound caused
Evil.
But current sunglasses still can be present, such as, in the case where light is stronger, though light
A part can be so blocked by sunglasses, but its effect blocked is limited, and most of light still can be emitted directly toward eye through sunglasses
Eyeball, can make people produce glare, and getting off can cause damage for a long time to the glasses of people.
The content of the invention
It is an object of the invention to provide a kind of cloudy surface Sunglasses lenses sun clips and its production technology, it sets mist on Sunglasses lenses sun clips
Surface layer, the fog surface layer can make light carry out diffusing reflection, can effectively obstruct high light line and be emitted directly toward glasses, thus realize anti-dazzle and
The function of eyeshield.
A kind of cloudy surface Sunglasses lenses sun clips, including base material, the substrate outer surface are sequentially provided with the fog surface layer formed by polysilicon
And stiffening layer.
The fog surface layer includes several spherical silicon bodies.
The spherical silicon body is irregular alignment.
The eyeglass also includes an at least reflexed light film, and the reflexed light film is arranged between fog surface layer and stiffening layer.
The reflexed light film is coloured reflexed light film.
A kind of production technology of cloudy surface Sunglasses lenses sun clips, comprises the following steps：
Step 1, the outer surface that liquid polysilicon is sprayed to lens substrate by gas atomization, do by 118-122 high temperature
I.e. in substrate outer surface formation fog surface layer after dry 4.8-5.2 hours.
Step 2, eyeglass is immersed in organic silicon solution, at the uniform velocity lifting makes organic silicon solution be coated on lens surface,
Then it is to form cloudy surface Sunglasses lenses sun clips by the high temperature drying of 118-122 degree.
The liquid polysilicon enters after spray gun makes it be sprayed on substrate surface in mist-like and be formed using 4KG pressure
Fog surface layer.
Increase by a step between step 1 and step 2, i.e., at least one is coated on fog surface layer using optical vacuum coating machine
Layer reflexed light film.
When light enters eyes through Sunglasses lenses sun clips, light can sequentially pass through stiffening layer, reflexed light film, fog surface layer and base
Material, finally just enters eyes.The harmful light of light part when through reflexed light film can be predominantly absorbed, and pass through fog surface layer
When, a part of light can form diffusing reflection light and filter out, and so enter the pipelines of eyes just than milder by base material, so that
Reach the effect of anti-dazzle and protect eyes.
Further, since when the setting of fog surface layer is caused in terms of the outer surface of cloudy surface sunglasses, cloudy surface is presented in minute surface, and increase is too
The aesthetic property of positive eyeglass.And it from polysilicon in terms of the low coverage of inner side is not block vision that wearer, which is, so from the inner surface of sunglasses
See, be clearly, the visual effect of eyeglass wearer not to be influenceed.
Brief description of the drawings
Fig. 1 is schematic structural view of the invention；
Fig. 2 is the combination schematic diagram of fog surface layer and base material.
Embodiment
Shown referring to Figures 1 and 2, present invention is disclosed a kind of cloudy surface Sunglasses lenses sun clips, it includes base material 1, in the appearance of base material 1
Face is sequentially provided with fog surface layer 2 and stiffening layer 4.
Wherein, fog surface layer 2 can be coated on substrate outer surface using polysilicon atomization and be formed, and polysilicon will not increase eyeglass
Haze value.The fog surface layer 2 being consequently formed makes the outer surface of base material 1 form the miniature spherical silicon body 21 of numerous irregular alignment,
It can carry out diffusing reflection to external direct projection light and various reflection lights, and the effectively stronger light of barrier enters glasses.
Stiffening layer 4 is arranged on the outer surface of fog surface layer 2, and it protects fog surface layer 2 and base material 1 not frayed.
One reflexed light film 3 can also be set on Sunglasses lenses sun clips, and the reflexed light film 3 can use coloured reflexed light film, its
It is arranged between fog surface layer 2 and stiffening layer 4.It can absorb some harmful light in light, such as ultraviolet etc., thus strengthen
The anti-dazzle light effect of Sunglasses lenses sun clips.
When light enters eyes through Sunglasses lenses sun clips, light can sequentially pass through stiffening layer 4, reflexed light film 3, fog surface layer 2
With base material 1, finally just enter eyes.The harmful light of light part when through reflexed light film 3 can be predominantly absorbed, and pass through mist
During surface layer 2, a part of light can form diffusing reflection light and filter out, and so the light by base material 1 into eyes is just more soft
With so as to reach the effect of anti-dazzle and protect eyes.
Further, since when the setting of fog surface layer 2 is caused in terms of the outer surface of cloudy surface sunglasses, cloudy surface, increase is presented in minute surface
The aesthetic property of Sunglasses lenses sun clips.And it from polysilicon in terms of the low coverage of inner side is not block vision that wearer, which is, so from the interior table of sunglasses
Face is seen, is clearly, the visual effect of eyeglass wearer not to be influenceed.
The manufacturing process of the cloudy surface Sunglasses lenses sun clips is：
Step 1, the outer surface of base material 1 coat fog surface layer 2
Liquid polysilicon is sprayed to the outer surface of lens substrate by gas atomization, after the high temperature drying of 110-130 degree
Fog surface layer is formed after 3-5 hours.
Liquid polysilicon is water white transparency liquid of vicidity, and the liquid polysilicon enters after spray gun the pressure for using 4KG
It is set to be sprayed on substrate surface in mist-like.
Step 2, the coating reflexed light film 3 on fog surface layer 2
At least one layer of reflexed light film 3 is coated on fog surface layer using optical vacuum coating machine, the reflexed light film 3 can use coloured
Reflexed light film.
Under vacuum conditions, electron gun evaporates the materials such as SIO2 and TIO2 by electric current makes it be attached to cloudy surface layer surface,
Form reflexed light film 3.
Step 3, to the surface of reflexed light film 3 carry out cure process
The eyeglass coated after reflexed light film 3 is immersed in organic silicon solution, at the uniform velocity lifting makes it be spread evenly across product surface,
Then stiffening layer 4 can be formed in the outer surface of reflexed light film 3 by the high temperature drying of 110-130 degree, also just completes cloudy surface too
Positive eyeglass makes.
The above, is only the embodiment of the present invention, and not the technical scope of the present invention is imposed any restrictions, therefore every
Any trickle amendment, equivalent variations and modification that technical spirit according to the present invention is made to above example, still fall within this
In the range of inventive technique scheme.
Claims (8)
1. a kind of cloudy surface Sunglasses lenses sun clips, including base material, it is characterised in that：The substrate outer surface is sequentially provided with to be formed by polysilicon
Fog surface layer and stiffening layer.
2. a kind of cloudy surface Sunglasses lenses sun clips according to claim 1, it is characterised in that：It is spherical that the fog surface layer includes several
Silicon body.
3. a kind of cloudy surface Sunglasses lenses sun clips according to claim 2, it is characterised in that：The spherical silicon body is irregular row
Row.
4. a kind of cloudy surface Sunglasses lenses sun clips according to claim 1, it is characterised in that：It is reflective that the eyeglass also includes at least one
Film layer, the reflexed light film is arranged between fog surface layer and stiffening layer.
5. a kind of cloudy surface Sunglasses lenses sun clips according to claim 4, it is characterised in that：The reflexed light film is coloured reflective membrane
Layer.
6. a kind of production technology of cloudy surface Sunglasses lenses sun clips, it is characterised in that：Comprise the following steps：
Step 1, the outer surface that liquid polysilicon is sprayed to lens substrate by gas atomization, by the high temperature of 110-130 degree
I.e. in substrate outer surface formation fog surface layer after drying 3-5 hours；
Step 2, eyeglass is immersed in organic silicon solution, at the uniform velocity lifting makes organic silicon solution be coated on lens surface, then
It is to form cloudy surface Sunglasses lenses sun clips by the high temperature drying of 110-130 degree.
7. a kind of production technology of cloudy surface Sunglasses lenses sun clips according to claim 6, it is characterised in that：The liquid polysilicon
It is set to be sprayed on substrate surface in mist-like and form fog surface layer using 4KG pressure after into spray gun.
8. a kind of production technology of cloudy surface Sunglasses lenses sun clips according to claim 6, it is characterised in that：In step 1 and step 2
Between increase by a step, i.e., using optical vacuum coating machine coat on fog surface layer at least one layer reflexed light film.