CN106947202A - The high-strength resistant plastics frame of LCD TV - Google Patents
The high-strength resistant plastics frame of LCD TV Download PDFInfo
- Publication number
- CN106947202A CN106947202A CN201710317226.8A CN201710317226A CN106947202A CN 106947202 A CN106947202 A CN 106947202A CN 201710317226 A CN201710317226 A CN 201710317226A CN 106947202 A CN106947202 A CN 106947202A
- Authority
- CN
- China
- Prior art keywords
- parts
- lcd
- plastics frame
- resistant plastics
- strength resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to television rack technical field, and in particular to the high-strength resistant plastics frame of LCD TV, described alloy material is made up of following raw material:HIPS, TPEE, carry silver-colored cobalt phosphate, fluorosioloxane rubber, glass fibre, modified active magnesium hydroxide, aerosil, antimony oxide, aluminium hydroxide, phosphorous acid hexichol isodecyl ester, EVA, three (2, 4 di-tert-butyl-phenyls) phosphite ester, polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 2, 4 dihydroxy benaophenonels, modified calcium carbonate, solubilizer, curing agent, coupling agent, glass fibre assigns the more preferable mechanical property of material and anti-wear performance, the antibacterial and medium-resistance of material can be obviously improved by carrying silver-colored cobalt phosphate and fluorosioloxane rubber, especially resistance to acids and bases is excellent, the weatherability of material is improved simultaneously, ozone resistance, radiation resistance, meet the high-strength of liquid crystal TV set frame, resistant, the requirement of high performance-price ratio, and product manufacture is simple, it is easy to industrialized production.
Description
Technical field
The present invention relates to television rack technical field, and in particular to the high-strength resistant plastics frame of LCD TV.
Background technology
With the fast development of national economy, the swift and violent hair of the significantly lifting of people's living standard, and TV tech
Open up, the technology such as particularly OLED is in the application of television set relevant industries, and television set is just towards the trend such as giant-screen, ultrathin type hair
Exhibition.At present, the mounting means of liquid crystal TV set mainly has base type and wall-mounted two kinds.Base type needs to buy corresponding TV
Cabinet is supported, and the general volume and weight of cabinet for TV both occupied larger space than larger, haves the shortcomings that mobile inconvenience again.
So increasing family selection in-wall mounting television set, the wall-mounted wall that generally requires carrys out load-bearing, so wall-mounted machine
The features such as frame will have small volume, good mechanical property, toughness.Wall built-up open frame is used to cause the space between television set and wall
It is narrow, be inconvenient to wipe the impurity such as dust, grease in daily life, this, which is accomplished by frame, has good anti-pollution characteristic,
Avoid because of support body deformation, being corroded causes LCD TV to be damaged.
Using steel materials such as steel plate or cast irons more than conventional television frame, it has the disadvantage, and cost is high, weight is big, processing fiber crops
It is tired of.Frame material should also have good insulating properties simultaneously, and insulation spray need to be coated on its outer layer according to metal material
Paint, further increases cost.So providing, one kind is excellent in cushion effect, draftability is good, oil resistant, solvent resistant, low cost, work
The high-strength resistant plastics frame of the simple LCD TV of skill is necessary.
The content of the invention
In order to solve the above technical problems, the invention provides a kind of high-strength resistant plastics frame of LCD TV, it has
The features such as having prominent mechanical property, solvent resistance, weatherability.
To achieve these goals, the present invention is achieved by the following technical programs:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:HIPS 40~60
Part, 10~25 parts of TPEE, silver-colored 12~18 parts of the cobalt phosphate of load, 8~13 parts of fluorosioloxane rubber, 9~15 parts of glass fibre, modified active
2~8 parts of magnesium hydroxide, 3~9 parts of aerosil, 4~11 parts of antimony oxide, 1~5 part of aluminium hydroxide, phosphorous acid two
Benzene -7~11 parts of isodecyl ester, 1~5 part of ethylene-vinyl acetate copolymer (EVA), three (2,4- di-tert-butyl-phenyl) phosphite esters 3
~7 parts, 5~11 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 2~6 parts of 2,4-DihydroxyBenzophenone, 1~4 part of modified calcium carbonate, increase
4~9 parts of solvent, 1~4 part of curing agent, 0.5~3 part of coupling agent.
It is preferred that, the high-strength resistant plastics frame of LCD TV is made up of the raw material of following parts by weight:HIPS
47 parts, 16 parts of TPEE, carry silver-colored 13 parts of cobalt phosphate, 10 parts of fluorosioloxane rubber, 11 parts of glass fibre, 5 parts of modified active magnesium hydroxide,
5 parts of aerosil, 7 parts of antimony oxide, 2 parts of aluminium hydroxide, phosphorous acid hexichol -10 parts of isodecyl ester, ethene-vinyl acetate
2 parts of copolymer (EVA), three 4 parts of (2,4- di-tert-butyl-phenyl) phosphite esters, 6 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 2,4- dihydroxies
3 parts of base benzophenone, 2 parts of modified calcium carbonate, 5 parts of solubilizer, 1.5 parts of curing agent, 1.5 parts of coupling agent.
It is preferred that, the modified active magnesium hydroxide refers to heat through wet method, adds zinc stearate and is modified what is be made.
It is preferred that, the glass fibre is grafted to poly- for surface through γ-methacryloxypropyl trimethoxy silane
It is made on butadiene main chain.
It is preferred that, the particle diameter of the aerosil is 10~20nm.
It is preferred that, the modified calcium carbonate is to be used as modifying agent using phosphate.
It is preferred that, the solubilizer is polyadipate isobutyl diester, phenylethylene-maleic anhydride (SMA), ethylene acrylic first
One or more in ester (EMA), ethylene/n-butyl acrylate-glycidyl ester copolymer (PTW).
It is preferred that, the curing agent is in diethylenetriamine, MDA (DDM), biuret polyisocyanate
One or more.
It is preferred that, the coupling agent is one kind in Lü Zuqian, silane coupler, titanate coupling agent
Or more than one.
A kind of preparation method of the high-strength resistant plastics frame of LCD TV, step is as follows:
(1) HIPS is placed in into air circulation oven to do at 80~120 DEG C in dry 5~8h at 110~130 DEG C, TPEE
Dry 6~10h;
(2) in addition to glass fibre, dry HIPS, TPEE and surplus stock is weighed by weight ratio, adds mixed at high speed
Mixed in machine, temperature is 80~110 DEG C, the time is 15~20min;
(3) by the mixture in step (2) and glass fibre at 150 DEG C in twin-roll plastic mixing mill preplasticizing 15~
25min, the mixture of preplasticizing is injected in injection mold, under the conditions of 50~70Mpa, 220~260 DEG C hot pressing 15~
20min;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 190~230 DEG C, pressure
Power is 80~120Mpa, and screw speed is 160~210r/min, is stripped after cooling, produces the LCD TV high-strength resistance to
Dirty plastics frame.
Beneficial effects of the present invention are:
HIPS and TPEE are mixed and made into the high-strength resistant plastics frame of LCD TV, on the one hand, HIPS addition shows
Write the cost for reducing plastics frame.On the other hand, the processing characteristics of HIPS protrusions, dimensional stability, and higher rigidity
And impact strength, substantially increase TPEE erosion-resisting characteristics.Rigidity, polarity and the crystallinity of TPEE polyester hard sections, make it have
Preferable hot property and oil resistant, solvent resistance;The lower glass transition temperatures and saturability of polyester soft segment, make it have excellent
Mechanical property and ageing resistace.TPEE or a kind of macromolecule modifier of excellent performance, carry out blending to HIPS and change simultaneously
Property, improve its erosion-resisting characteristics and stress cracking, toughness, weatherability and oil resistivity.Also, TPEE addition reduces adding for material
Work temperature.
Glass fibre assigns the more preferable mechanical property of material and anti-wear performance as enhancing system.Carry silver-colored cobalt phosphate and fluorine
Silicon rubber can be obviously improved the antibacterial and medium-resistance of material, and especially resistance to acids and bases is excellent, while improving the resistance to of material
Hou Xing, ozone resistance, radiation resistance.The silver-colored phosphorus of the high-strength resistant plastics frame collection HIPS of LCD TV of the present invention, TPEE, load
The advantage of the materials such as sour cobalt, fluorosioloxane rubber, meets the high-strength of liquid crystal TV set frame, resistant, the requirement of high performance-price ratio.And product
Manufacturing process is simple, be easy to industrialized production.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with specific embodiment pair
The present invention is described in detail.It should be pointed out that not making creative work premise to those of ordinary skill in the art
Lower obtained every other embodiment, belongs to the scope of protection of the invention.
Embodiment 1:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:40 parts of HIPS,
Silver-colored 12 parts of the cobalt phosphate of 16 parts of TPEE, load, 13 parts of fluorosioloxane rubber, 9 parts of glass fibre, 5 parts of modified active magnesium hydroxide, gas phase two
9 parts of silica, 4 parts of antimony oxide, 5 parts of aluminium hydroxide, phosphorous acid hexichol -7 parts of isodecyl ester, EVA2 parts, three (2,4- bis- tertiary fourths
Base phenyl) 3~7 parts of phosphite ester, 5~11 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 3 parts of 2,4-DihydroxyBenzophenone, carbon modified
Sour 2 parts of calcium, SMA1 parts, 1 part of EMA, 2 parts of PTW, 4 parts of diethylenetriamine, 0.3 part of Lü Zuqian, silane coupler
0.2 part.
The present embodiment additionally provides the preparation method of modified active magnesium hydroxide, comprises the following steps:
(1) by magnesium hydroxide particles in 110 DEG C of dry 10h, sieving.
(2) magnesium hydroxide of a certain amount of drying is weighed, deionized water is added and is made into the hydroxide that mass fraction is 7% or so
Magnesium slurry, heats while stirring, and heating-up temperature is 80 DEG C, and mixing speed is 500r/min.
(3) after slurry is formed, the zinc stearate of hydroxide magnesium amount 5%, stirring curing 2h are added.
(4) suction filtration obtains white solid, is washed with absolute ethyl alcohol, deionized water repeatedly, and in being dried at 110 DEG C, sieving is produced
The modified active magnesium hydroxide.
The present embodiment additionally provides the preparation method of modified calcium carbonate, comprises the following steps:
A certain amount of calcium carbonate is weighed, 10min is stirred in 140 DEG C of oil baths, a certain amount of phosphate surfactant is added
Agent, continues to stir 10min, cooling, filtering produce the modified calcium carbonate.
The preparation method of the above-mentioned high-strength resistant plastics frame of LCD TV, step is as follows:
(1) HIPS is placed in air circulation oven in dry 8h at 110 DEG C, TPEE dry 10h at 80 DEG C;
(2) in addition to glass fibre, dry HIPS, TPEE and surplus stock is weighed by weight ratio, adds mixed at high speed
Mixed in machine, temperature is 80 DEG C, and the time is 20min;
(3), will by the mixture in step (2) and glass fibre preplasticizing 15min in twin-roll plastic mixing mill at 150 DEG C
In the mixture injection injection mold of preplasticizing, the hot pressing 20min under the conditions of 70Mpa, 220 DEG C;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 190 DEG C, pressure is
120Mpa, screw speed is 160r/min, is stripped after cooling, produces the high-strength resistant plastics frame of the LCD TV.
Embodiment 2:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:47 parts of HIPS,
Silver-colored 18 parts of the cobalt phosphate of 10 parts of TPEE, load, 8 parts of fluorosioloxane rubber, 15 parts of glass fibre, 2 parts of modified active magnesium hydroxide, gas phase two
5 parts of silica, 11 parts of antimony oxide, 2 parts of aluminium hydroxide, phosphorous acid hexichol -10 parts of isodecyl ester, EVA1 parts, three (2,4- bis- uncles
Butyl phenyl) 7 parts of phosphite ester, 5 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 6 parts of 2,4-DihydroxyBenzophenone, modified calcium carbonate 1
Part, SMA3 parts, 6 parts of EMA, 0.5 part of diethylenetriamine, 0.5 part of DDM, 1 part of silane coupler, 2 parts of titanate coupling agent.
The preparation method of the above-mentioned high-strength resistant plastics frame of LCD TV, step is as follows:
(1) HIPS is placed in air circulation oven in dry 5h at 130 DEG C, TPEE dry 6h at 120 DEG C;
(2) in addition to glass fibre, dry HIPS, TPEE and surplus stock is weighed by weight ratio, adds mixed at high speed
Mixed in machine, temperature is 110 DEG C, and the time is 15min;
(3), will by the mixture in step (2) and glass fibre preplasticizing 25min in twin-roll plastic mixing mill at 150 DEG C
In the mixture injection injection mold of preplasticizing, the hot pressing 15min under the conditions of 50Mpa, 260 DEG C;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 230 DEG C, pressure is
80Mpa, screw speed is 210r/min, is stripped after cooling, produces the high-strength resistant plastics frame of the LCD TV.
Embodiment 3:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:47 parts of HIPS,
Silver-colored 13 parts of the cobalt phosphate of 16 parts of TPEE, load, 11 parts of fluorosioloxane rubber, 11 parts of glass fibre, 5 parts of modified active magnesium hydroxide, gas phase two
5 parts of silica, 7 parts of antimony oxide, 2 parts of aluminium hydroxide, phosphorous acid hexichol -10 parts of isodecyl ester, 2 parts of EVA, three (2,4- bis- uncles
Butyl phenyl) 4 parts of phosphite ester, 6 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 3 parts of 2,4-DihydroxyBenzophenone, modified calcium carbonate 2
Part, 1 part of SMA, PTW 3 parts 5 parts, 0.5 part of diethylenetriamine, 1 part of MDA, 1 part of Lü Zuqian, silicon
0.5 part of alkane coupling agent.
The preparation method be the same as Example 1 of the above-mentioned high-strength resistant plastics frame of LCD TV.
Embodiment 4:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:60 parts of HIPS,
Silver-colored 13 parts of the cobalt phosphate of 25 parts of TPEE, load, 11 parts of fluorosioloxane rubber, 11 parts of glass fibre, 8 parts of modified active magnesium hydroxide, gas phase two
3 parts of silica, 7 parts of antimony oxide, 1 part of aluminium hydroxide, phosphorous acid hexichol -11 parts of isodecyl ester, 5 parts of EVA, three (2,4- bis- uncles
Butyl phenyl) 4 parts of phosphite ester, 6 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 2 parts of 2,4-DihydroxyBenzophenone, modified calcium carbonate 4
Part, 1 part of SMA, PTW 3 parts 5 parts, 0.5 part of diethylenetriamine, 1 part of MDA, 0.5 part of silane coupler, aluminum-zirconium
1 part of acid esters coupling agent.
The preparation method be the same as Example 2 of the above-mentioned high-strength resistant plastics frame of LCD TV.
Embodiment 5:
A kind of high-strength resistant plastics frame of LCD TV, is made up of the raw material of following parts by weight:50 parts of HIPS,
Silver-colored 16 parts of the cobalt phosphate of 20 parts of TPEE, load, 9 parts of fluorosioloxane rubber, 13 parts of glass fibre, 7 parts of modified active magnesium hydroxide, stearic acid
5 parts of zinc, 3 parts of p-phenylenediamine, 6 parts of ethylene methyl acrylate, 5 parts of pentaerythritol ester, 2.5 parts of EVA, three (2,4- di-tert-butyls
Base) 6 parts of phosphite ester, 8 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 5 parts of 2,4-DihydroxyBenzophenone, 3 parts of modified calcium carbonate, EMA2
Part, 3 parts of PTW, 3 parts of biuret polyisocyanate, 2.5 parts of titanate coupling agent.
The preparation method be the same as Example 2 of the above-mentioned high-strength resistant plastics frame of LCD TV.
Comparative example 1:
A kind of LCD TV plastics frame, is made up of the raw material of following parts by weight:47 parts of ABS, 16 parts of PVC, gas
5 parts of aerosil, 6 parts of silicone master batch, 10 parts of hydroxy silicon oil, 5 parts of carbon black, three (2,4- di-tert-butyl-phenyl) phosphite esters 4
Part, 6 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 3 parts of 2,4-DihydroxyBenzophenone, 2 parts of modified calcium carbonate, 5 parts of zinc stearate, PTW
3 parts, 0.5 part of diethylenetriamine, 1 part of MDA, 0.5 part of silane coupler.
The preparation method of above-mentioned LCD TV plastics frame, step is as follows:
(1) ABS, PVC are placed in air circulation oven in dry 5h at 130 DEG C;
(2) dry ABS, PVC and surplus stock is weighed by weight ratio, adds in high-speed mixer and mixes, and temperature is
100 DEG C, the time is 16min;
(3) by the mixture in step (2) at 150 DEG C the preplasticizing 22min in twin-roll plastic mixing mill, by the mixed of preplasticizing
In compound injection injection mold, the hot pressing 18min under the conditions of 60Mpa, 230 DEG C;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 240 DEG C, pressure is
90Mpa, screw speed is 260r/min, is stripped after cooling, produces the LCD TV plastics frame.
Comparative example 2:
A kind of LCD TV plastics frame, is made up of the raw material of following parts by weight:53 parts of ABS, 21 parts of PVC, gas
6 parts of aerosil, 5 parts of silicone master batch, 12 parts of hydroxy silicon oil, 3 parts of carbon black, three (2,4- di-tert-butyl-phenyl) phosphite esters 5
Part, 2 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 7 parts of 2,4-DihydroxyBenzophenone, 3 parts of modified calcium carbonate, 4 parts of zinc stearate, PTW
6 parts, 1 part of diethylenetriamine, 3 parts of MDA, 2 parts of silane coupler.
The preparation method of above-mentioned LCD TV plastics frame, step is as follows:
(1) ABS, PVC are placed in air circulation oven in dry 6h at 130 DEG C;
(2) dry ABS, PVC and surplus stock is weighed by weight ratio, adds in high-speed mixer and mixes, and temperature is
120 DEG C, the time is 16min;
(3) by the mixture in step (2) at 160 DEG C the preplasticizing 20min in twin-roll plastic mixing mill, by the mixed of preplasticizing
In compound injection injection mold, the hot pressing 15min under the conditions of 50Mpa, 200 DEG C;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 220 DEG C, pressure is
80Mpa, screw speed is 210r/min, is stripped after cooling, produces the LCD TV plastics frame.
Comparative example 3:
A kind of LCD TV plastics frame, is made up of the raw material of following parts by weight:57 parts of ABS, 21 parts of PVC, gas
6 parts of aerosil, 5 parts of silicone master batch, 8.5 parts of hydroxy silicon oil, 3.5 parts of carbon black, three (2,4- di-tert-butyl-phenyl) phosphorous acid
5 parts of ester, 8 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 1 part of 2,4-DihydroxyBenzophenone, 5 parts of modified calcium carbonate, 3 parts of zinc stearate,
6 parts of PTW, 2.5 parts of diethylenetriamine, 1 part of MDA, 0.5 part of silane coupler.
The preparation process of above-mentioned LCD TV plastics frame is with comparative example 1.
Performance test:
By a kind of high-strength resistant plastics frame of LCD TV made from embodiment of the present invention 1-5 and comparative example 1-3 systems
The LCD TV plastics frame obtained is contrasted under the same conditions, and indices data are as shown in table 1 below:
The performance test of table 1
Note:Corrosivity (water, ethanol, butanone) is tested by GB/T 1154743-2008, and observing time is 24h.
From data in table, the high-strength resistant plastics frame of LCD TV produced by the present invention in tensile strength, lack
Comparative example is superior in terms of mouth impact strength, heat resistance, corrosion resistance, and product preparation process is more perfect, is worthy to be popularized.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic;And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (10)
1. the high-strength resistant plastics frame of LCD TV, it is characterised in that:It is made up of the raw material of following parts by weight:HIPS 40
~60 parts, 10~25 parts of TPEE, carry silver-colored 12~18 parts of cobalt phosphate, it is 8~13 parts of fluorosioloxane rubber, 9~15 parts of glass fibre, modified
Active 2~8 parts of magnesium hydroxide, 3~9 parts of aerosil, 4~11 parts of antimony oxide, 1~5 part of aluminium hydroxide, phosphorous acid
Hexichol -7~11 parts of isodecyl ester, 1~5 part of EVA, three 3~7 parts of (2,4- di-tert-butyl-phenyl) phosphite esters, polyphenylene phosphonic acids two
5~11 parts of benzene sulfone ester, 2~6 parts of 2,4-DihydroxyBenzophenone, 1~4 part of modified calcium carbonate, 4~9 parts of solubilizer, curing agent 1
~4 parts, 0.5~3 part of coupling agent.
2. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:By following parts by weight
Raw material be made:Silver-colored 13 parts of the cobalt phosphate of 47 parts of HIPS, 16 parts of TPEE, load, 10 parts of fluorosioloxane rubber, 11 parts of glass fibre, modification
Active 5 parts of magnesium hydroxide, 5 parts of aerosil, 7 parts of antimony oxide, 2 parts of aluminium hydroxide, phosphorous acid hexichol-isodecyl ester 10
Part, 2 parts of EVA, three 4 parts of (2,4- di-tert-butyl-phenyl) phosphite esters, 6 parts of polyphenylene phosphonic acids diphenyl sulphone (DPS) ester, 2,4- dihydroxy two
3 parts of Benzophenone, 2 parts of modified calcium carbonate, 5 parts of solubilizer, 1.5 parts of curing agent, 1.5 parts of coupling agent.
3. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The modified active
Magnesium hydroxide refers to heat through wet method, adds zinc stearate and is modified what is be made.
4. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The glass fibre
It is grafted to what is be made on polybutadiene main chain through γ-methacryloxypropyl trimethoxy silane for surface.
5. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The gas phase dioxy
The particle diameter of SiClx is 10~20nm.
6. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The modified carbonic acid
Calcium is to be used as modifying agent using phosphate.
7. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The solubilizer is
One or more in polyadipate isobutyl diester, SMA, EMA, PTW.
8. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The curing agent is
One or more in diethylenetriamine, DDM, biuret polyisocyanate.
9. the high-strength resistant plastics frame of LCD TV according to claim 1, it is characterised in that:The coupling agent is
One or more in Lü Zuqian, silane coupler, titanate coupling agent.
10. the high-strength resistant plastics frame of LCD TV according to claim any one of 1-9, it is characterised in that:System
Preparation Method comprises the following steps:
(1) by HIPS be placed in air circulation oven at 110~130 DEG C dry 5~8h, TPEE at 80~120 DEG C dry 6~
10h;
(2) in addition to glass fibre, dry HIPS, TPEE and surplus stock is weighed by weight ratio, is added in high-speed mixer
Mix, temperature is 80~110 DEG C, the time is 15~20min;
(3), will by the mixture in step (2) and glass fibre 15~25min of preplasticizing in twin-roll plastic mixing mill at 150 DEG C
In the mixture injection injection mold of preplasticizing, 15~20min of hot pressing under the conditions of 50~70Mpa, 220~260 DEG C;
(4) and then by material grain it is expelled to by parallel dual-screw extruding machine in mould, injection temperature is 190~230 DEG C, pressure is
80~120Mpa, screw speed is 160~210r/min, is stripped after cooling, produces the high-strength resistant modeling of the LCD TV
Expect frame.