CN106946546A - 一种耐磨透水广场砖及其制备方法 - Google Patents

一种耐磨透水广场砖及其制备方法 Download PDF

Info

Publication number
CN106946546A
CN106946546A CN201710219770.9A CN201710219770A CN106946546A CN 106946546 A CN106946546 A CN 106946546A CN 201710219770 A CN201710219770 A CN 201710219770A CN 106946546 A CN106946546 A CN 106946546A
Authority
CN
China
Prior art keywords
parts
square brick
wear
temperature
resisting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710219770.9A
Other languages
English (en)
Inventor
曹智远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Oukesi New Building Material Co Ltd
Original Assignee
Hefei Oukesi New Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Oukesi New Building Material Co Ltd filed Critical Hefei Oukesi New Building Material Co Ltd
Priority to CN201710219770.9A priority Critical patent/CN106946546A/zh
Publication of CN106946546A publication Critical patent/CN106946546A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种耐磨透水广场砖及其制备方法，涉及到广场砖领域，该种广场砖以重量份数计，包括以下原料：复合硅酸盐水泥80‑120份、凹凸棒粘土40‑60份、废矿尾砂30‑40份、煤矸石20‑30份、脱硫石膏粉15‑25份、硬脂酸钙10‑20份、椰壳炭10‑20份、助剂4‑6份，其中，所述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%。该种广场砖通过混料、搅拌、压制成型、自然养护、高温烘干以及高温煅烧等步骤制得。本发明的有益之处在于原料成本低，节能环保，不仅具有良好的抗折抗压强度、耐磨性和抗冻性，还具有一定的透水吸水性，当环境温度过高时，其内部孔洞储存的水分蒸发吸热，降低了环境温度，在城市内使用能够有效地防止城市热岛效应的产生。

Description

一种耐磨透水广场砖及其制备方法
技术领域
本发明涉及广场砖领域，尤其是涉及一种耐磨透水广场砖及其制备方法。
背景技术
随着国民经济的快速发展，人民生活水平的不断提高，对能源的消耗也越来越大，能源短缺问题日益突出，因此，节能环保型的建筑材料逐渐被人们所重视，广场砖作为新型建筑材料中的一种，应用广泛，已经成为城市道路、广场、居住小区、旅游区等路面铺设的结构砖，其砖体色彩简单，砖面广场砖体积小，多采用凹凸面的形式。需要具有防滑、耐磨、强度高等特点，也已成为现代化城市美化的一种新型建筑材料，而现如今普通的广场砖大都是以水泥和沙石为原料制备而成的，这种砖体资源浪费大、价格高、抗冻性差、吸水性差，并且，在抗折抗压强度以及耐磨性上依然存在诸多不足，造成广场砖出现掉粒、凹坑、断裂等现象，达不到广场砖必要的性能。因此，研制出一种能够解决上述性能问题的广场砖非常有必要。
发明内容
本发明的目的是针对现有技术的问题，提供一种耐磨透水广场砖及其制备方法，该种广场砖具有良好的抗折抗压强度、耐磨性、抗冻性及吸水性，满足了广场砖在实际环境中应用的需求。
为了达到上述目的，本发明通过以下技术方案来实现的：
一种耐磨透水广场砖，以重量份数计，包括以下原料：复合硅酸盐水泥80-120份、凹凸棒粘土40-60份、废矿尾砂30-40份、煤矸石20-30份、脱硫石膏粉15-25份、硬脂酸钙10-20份、椰壳炭10-20份、助剂4-6份。
进一步地，上述广场砖以重量份数计，包括以下原料：复合硅酸盐水泥100份、凹凸棒粘土50份、废矿尾砂35份、煤矸石25份、脱硫石膏粉20份、硬脂酸钙15份、椰壳炭15份、助剂5份。
优选地，所述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%。
优选地，所述减水剂为木质素磺酸钙、聚丙烯酸钠、氨基磺酸钠中的一种或者多种。
优选地，所述憎水剂为有机硅乳液。
优选地，所述发泡剂按重量百分比计由65%的十二烷基硫酸钠和35%的脂肪醇聚氧乙烯醚硫酸钠组成。
进一步地，将所述废矿尾砂、煤矸石和椰壳炭粉碎至粒度1-2mm。
上述的耐磨透水广场砖的制备方法，按照以下步骤进行：
（1）按照配比称重上述原料，先将煤矸石、脱硫石膏粉、硬脂酸钙、椰壳炭和助剂搅拌混合均匀后加入到主料复合硅酸盐水泥、凹凸棒粘土和废矿尾砂的混合物中，加入适量水搅拌混合，之后输送至搅拌机中进行搅拌处理，搅拌转速70-80r/min，搅拌时间为50-60min，得含水量在7-9wt％的浆料；
（2）将所述浆料倒入模具中，通过压力机进行压制成型；
（3）将成型后的广场砖置于干燥室温的条件下自然养护2-4天；
（4）将养护后的广场砖放置于高温烘干机内进行高温烘干处理，且烘干温度设定为75-85℃，烘干时间24-32h；
（5）将烘干后的广场砖放置于高温煅烧炉中进行高温煅烧处理，且煅烧温度为1100-1300℃，高温煅烧时间为12-16h。
进一步地，所述压制成型的压制强度为18-24MPa，压制时间为20-30s。
本发明与现有技术相比，具有如下的有益效果：
（1）本发明以凹凸棒粘土、废矿尾砂、脱硫石膏粉以及椰壳炭作为广场砖的原料，替代传统的天然碎石和石英砂等生产的广场砖，有效利用了固体废弃物以及高性价比的原料，不仅节能环保，降低生产成本，还具有明显的社会、经济和环保效益；
（2）本发明的广场砖达到了《广场用陶瓷砖》国家标准（GB／T234582009）对广场砖性能要求，具有良好的抗折抗压强度、耐磨性、抗冻性，经实施例检测本发明的广场砖破坏强度≥1680N，断裂模数单值≥20MPa，断裂模数平均值高达24MPa，经反复摩擦实验后测得磨损量≤0.07g，经抗冻实验后无裂纹、剥落或破损，强度损失量≤12%。
（3）本发明因含有凹凸棒粘土和椰壳炭等成分原因，成品广场砖结构内部含有丰富的气孔，具有很好的透水吸水性，当环境温度过高时，其内部水分蒸发吸热，降低了环境温度，在城市内使用能够有效地防止城市热岛效应的产生。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例１
一、原料选取
一种耐磨透水广场砖，包括以下原料：复合硅酸盐水泥80kg、凹凸棒粘土40kg、废矿尾砂30kg、煤矸石20kg、脱硫石膏粉15kg、硬脂酸钙10kg、椰壳炭10kg和助剂4kg。
其中，上述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%，减水剂采用木质素磺酸钙，憎水剂采用有机硅乳液，发泡剂按重量百分比计由65%的十二烷基硫酸钠和35%的脂肪醇聚氧乙烯醚硫酸钠组成。
并且在具体实施中将上述原料的废矿尾砂、煤矸石和椰壳炭通过锤式破碎机粉碎至粒度1-2mm。
二、制备方法
上述的耐磨透水广场砖的制备方法，按照以下步骤进行：
（1）按照配比称重上述原料，先将煤矸石、脱硫石膏粉、硬脂酸钙、椰壳炭和助剂搅拌混合均匀后加入到主料复合硅酸盐水泥、凹凸棒粘土和废矿尾砂的混合物中，加入适量水搅拌混合，之后输送至搅拌机中进行搅拌处理，搅拌转速70r/min，搅拌时间为60min，得含水量在7wt％的浆料；
（2）将所述浆料倒入模具中，通过压力机进行压制成型，其中，压制强度为18MPa，压制时间为30s；
（3）将成型后的广场砖置于干燥室温的条件下自然养护2天；
（4）将养护后的广场砖放置于高温烘干机内进行高温烘干处理，且烘干温度设定为75℃，烘干时间32h；
（5）将烘干后的广场砖放置于高温煅烧炉中进行高温煅烧处理，且煅烧温度为1100℃，高温煅烧时间为16h，便制得本发明的广场砖。
实施例2
一、原料选取
一种耐磨透水广场砖，包括以下原料：复合硅酸盐水泥100kg、凹凸棒粘土50kg、废矿尾砂35kg、煤矸石25kg、脱硫石膏粉20kg、硬脂酸钙15kg、椰壳炭15kg、助剂5kg。
其中，上述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%，减水剂采用木质素磺酸钙和聚丙烯酸钠的混合物，且两者的质量比为2:1，憎水剂采用有机硅乳液，发泡剂按重量百分比计由65%的十二烷基硫酸钠和35%的脂肪醇聚氧乙烯醚硫酸钠组成。
并且在具体实施中将上述原料的废矿尾砂、煤矸石和椰壳炭通过锤式破碎机粉碎至粒度1-2mm。
二、制备方法
上述的耐磨透水广场砖的制备方法，按照以下步骤进行：
（1）按照配比称重上述原料，先将煤矸石、脱硫石膏粉、硬脂酸钙、椰壳炭和助剂搅拌混合均匀后加入到主料复合硅酸盐水泥、凹凸棒粘土和废矿尾砂的混合物中，加入适量水搅拌混合，之后输送至搅拌机中进行搅拌处理，搅拌转速75r/min，搅拌时间为55min，得含水量在8wt％的浆料；
（2）将所述浆料倒入模具中，通过压力机进行压制成型，其中，压制强度为21MPa，压制时间为25s；
（3）将成型后的广场砖置于干燥室温的条件下自然养护3天；
（4）将养护后的广场砖放置于高温烘干机内进行高温烘干处理，且烘干温度设定为80℃，烘干时间28h；
（5）将烘干后的广场砖放置于高温煅烧炉中进行高温煅烧处理，且煅烧温度为1200℃，高温煅烧时间为14h，便制得本发明的广场砖。
实施例3
一、原料选取
一种耐磨透水广场砖，包括以下原料：复合硅酸盐水泥120kg、凹凸棒粘土60kg、废矿尾砂40kg、煤矸石30kg、脱硫石膏粉25kg、硬脂酸钙20kg、椰壳炭20kg、助剂6kg。
其中，上述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%，减水剂采用氨基磺酸钠，憎水剂采用有机硅乳液，发泡剂按重量百分比计由65%的十二烷基硫酸钠和35%的脂肪醇聚氧乙烯醚硫酸钠组成。
并且在具体实施中将上述原料的废矿尾砂、煤矸石和椰壳炭通过锤式破碎机粉碎至粒度1-2mm。
二、制备方法
上述的耐磨透水广场砖的制备方法，按照以下步骤进行：
（1）按照配比称重上述原料，先将煤矸石、脱硫石膏粉、硬脂酸钙、椰壳炭和助剂搅拌混合均匀后加入到主料复合硅酸盐水泥、凹凸棒粘土和废矿尾砂的混合物中，加入适量水搅拌混合，之后输送至搅拌机中进行搅拌处理，搅拌转速80r/min，搅拌时间为50min，得含水量在9wt％的浆料；
（2）将所述浆料倒入模具中，通过压力机进行压制成型，其中，压制强度为24MPa，压制时间为20s；
（3）将成型后的广场砖置于干燥室温的条件下自然养护4天；
（4）将养护后的广场砖放置于高温烘干机内进行高温烘干处理，且烘干温度设定为85℃，烘干时间24h；
（5）将烘干后的广场砖放置于高温煅烧炉中进行高温煅烧处理，且煅烧温度为1300℃，高温煅烧时间为12h，便制得本发明的广场砖。
性能检测
将实施例1-3制得广场砖进行性能检测与《广场用陶瓷砖》国家标准（GB／T234582009）进行对比，检测数据见下表1：
表1
这里指出，上述磨损量指的是砖块顶面经300次往复摩擦砖料的磨损量。
由上表1可知，本发明的广场砖相对GB／T234582009，在破坏强度上提高了180-260MPa，断裂模数平均值提高了4MPa，磨损量减少了0.03-0.04g，冻后强度损失量降低了8-9个百分点。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (9)

1.一种耐磨透水广场砖，其特征在于，以重量份数计，包括以下原料：复合硅酸盐水泥80-120份、凹凸棒粘土40-60份、废矿尾砂30-40份、煤矸石20-30份、脱硫石膏粉15-25份、硬脂酸钙10-20份、椰壳炭10-20份、助剂4-6份。
2.根据权利要求1所述的一种耐磨透水广场砖，其特征在于，以重量份数计，包括以下原料：复合硅酸盐水泥100份、凹凸棒粘土50份、废矿尾砂35份、煤矸石25份、脱硫石膏粉20份、硬脂酸钙15份、椰壳炭15份、助剂5份。
3.根据权利要求1-2任意一项所述的一种耐磨透水广场砖，其特征在于，所述助剂按重量百分比计包括减水剂35%、憎水剂35%和发泡剂30%。
4.根据权利要求3所述的一种耐磨透水广场砖，其特征在于，所述减水剂为木质素磺酸钙、聚丙烯酸钠、氨基磺酸钠中的一种或者多种。
5.根据权利要求3所述的一种耐磨透水广场砖，其特征在于，所述憎水剂为有机硅乳液。
6.根据权利要求3所述的一种耐磨透水广场砖，其特征在于，所述发泡剂按重量百分比计由65%的十二烷基硫酸钠和35%的脂肪醇聚氧乙烯醚硫酸钠组成。
7.根据权利要求1所述的一种耐磨透水广场砖，其特征在于，将所述废矿尾砂、煤矸石和椰壳炭粉碎至粒度1-2mm。
8.一种如权利要求1-7任意一项所述的耐磨透水广场砖的制备方法，其特征在于，包括以下步骤：
（1）按照配比称重上述原料，先将煤矸石、脱硫石膏粉、硬脂酸钙、椰壳炭和助剂搅拌混合均匀后加入到主料复合硅酸盐水泥、凹凸棒粘土和废矿尾砂的混合物中，加入适量水搅拌混合，之后输送至搅拌机中进行搅拌处理，搅拌转速70-80r/min，搅拌时间为50-60min，得含水量在7-9wt％的浆料；
（2）将所述浆料倒入模具中，通过压力机进行压制成型；
（3）将成型后的广场砖置于干燥室温的条件下自然养护2-4天；
（4）将养护后的广场砖放置于高温烘干机内进行高温烘干处理，且烘干温度设定为75-85℃，烘干时间24-32h；
（5）将烘干后的广场砖放置于高温煅烧炉中进行高温煅烧处理，且煅烧温度为1100-1300℃，高温煅烧时间为12-16h。
9.根据权利要求8所述的一种耐磨透水广场砖的制备方法，其特征在于，所述压制成型的压制强度为18-24MPa，压制时间为20-30s。
CN201710219770.9A 2017-04-06 2017-04-06 一种耐磨透水广场砖及其制备方法 Withdrawn CN106946546A (zh)