CN106927709A - A kind of anion composite powder suitable for construction material - Google Patents
A kind of anion composite powder suitable for construction material Download PDFInfo
- Publication number
- CN106927709A CN106927709A CN201511032230.7A CN201511032230A CN106927709A CN 106927709 A CN106927709 A CN 106927709A CN 201511032230 A CN201511032230 A CN 201511032230A CN 106927709 A CN106927709 A CN 106927709A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- stone flour
- composite powder
- anion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of anion composite powder suitable for construction material, it is obtained by following components according to the mass fraction:30-80 parts of albumen stone flour;Sodium hexametaphosphate 1-8 parts;Cerium oxide 1-5 parts;Rare earth 0-30 parts;Ferric oxide powder 1-30 parts;Water soluble acrylic acid 1-8 parts;Solitary stone flour 1-8 parts.The technical scheme manufacture craft that the present invention is provided is simple, and the prices of raw materials are cheap, and anion plate has persistence, high efficiency, the feature of environmental protection, and obtained anion plate is capable of 2000~3800/scm of anion releasing of efficient stable2, can purify air, eliminate foreign flavor indoors and pernicious gas, be a kind of environment-friendly type anionic additive.
Description
Technical field
The present invention relates to a kind of composite powder, and in particular to a kind of anion composite powder suitable for construction material.
Background technology
Living environment is constantly paid close attention to healthy influence by people, and it is luxurious, attractive in appearance that people pursue indoor decorating
Meanwhile, also pay close attention to indoor pollution influence health, the feature of environmental protection of construction timber, and the influence to health generation.
Therefore, various wholesome novel building functional materials arise at the historic moment.
Anion material has one of multifunctional novel material representatives such as environmental protection, health as one kind, is widely used in spinning
The fields such as fabric, ceramics, construction material.There is biological meaning from Aschkinass in 1902 and Caspan affirmative negative aeroions
Justice, Soviet Union scholar in 1903 has been delivered since eliminating the paper of germ using negative aeroion, and scientific research personnel has carried out largely in succession
Experimental study, has further affirmed the value of negative aeroion.
Negative oxygen ion concentration in the room of city is 100 per cubic centimeter, and the concentration in building office is even as low as every cube
Centimetres 40~50, and the standard that the World Health Organization delimit, the negative oxygen ion content of fresh air is in air per cubic centimeter
1000~1500 are not less than, so tending to induce the discomforts such as headache and insomnia in such environmental work.Many city white collar's works
Work is felt to feel dizzy for one day afterwards, just and air inadequate " nutrition " has certain relation.And forest and waterfall area, high mountain seashore
It is very abundant with " air vitamin " content in park, can reach respectively 10000~20000 per cubic centimeter, 5000~10000
It is individual and 400~1000.Negative oxygen ion can promote human metabolism, flu-prevention, enhancing body resistance against diseases.
CN103805134A Chinese patents disclose a kind of novel negative ion additive, the shortcoming of products obtained therefrom be bearing of producing from
Sub- concentration is not high, efficacy lasting property is poor.
The invention provides there is provided a kind of anion composite powder suitable for construction material, this anion composite powder has
Persistently, high efficiency, and manufacture craft is simple, the prices of raw materials are cheap, is adapted to large-scale production.
The content of the invention
The present invention provides a kind of anion composite powder suitable for construction material, is capable of the anion releasing of efficient stable, can
Purify air, elimination foreign flavor indoors and various pernicious gases, are a kind of new and effective stabilization anionic additives.
The present invention seeks to what is realized using following technical scheme:
A kind of anion composite powder, according to mass fraction meter, the composite powder is obtained by following components:Albumen stone flour 30-80
Part;Sodium hexametaphosphate 1-8 parts;Cerium oxide 1-5 parts;Rare earth 0-30 parts;Ferric oxide powder 1-30 parts;Water soluble acrylic acid 1-8
Part;Solitary stone flour 1-8 parts.
A kind of first preferred scheme of anion composite powder, according to mass fraction meter, the composite powder is obtained by following components:
40-60 parts of albumen stone flour;Sodium hexametaphosphate 3-6 parts;Cerium oxide 2-4 parts;Rare earth 5-20 parts;Ferric oxide powder 5-20 parts;
Water soluble acrylic acid 3-5 parts;Solitary stone flour 2-6 parts.
A kind of second preferred scheme of anion composite powder, according to mass fraction meter, the composite powder is obtained by following components:
50 parts of albumen stone flour;4 parts of sodium hexametaphosphate;3 parts of cerium oxide;16 parts of rare earth;15 parts of ferric oxide powder;Aqueous acrylamide
4 parts of acid;5 parts of solitary stone flour.
A kind of 3rd preferred scheme of anion composite powder, the albumen stone flour is by aqueous acrylamide low-kappa number.
A kind of 4th preferred scheme of anion composite powder, the opal powder footpath is 10~30 μm.
A kind of 5th preferred scheme of anion composite powder, the process of the pretreatment is the albumen stone flour and water soluble acrylic acid
The mixed configuration aqueous solution, water-bath 1 hour at 60~90 DEG C, filtering is dried, and is broken up.
A kind of 6th preferred scheme of anion composite powder, the composite powder is obtained by the way that dry powder blender is well mixed.
Compared with immediate prior art, the technical scheme that the present invention is provided has following excellent effect:
(1) the anion composite powder that the present invention is provided, and manufacture craft is simple, the prices of raw materials are cheap, is adapted to extensive
Production;
(2) the anion composite powder that the present invention is provided has persistence, high efficiency, the feature of environmental protection;
(3) anion plate prepared by the anion composite powder that the present invention is provided be capable of the anion releasing 2000 of efficient stable~
3800/scm2, being capable of purify air, elimination foreign flavor indoors and various pernicious gases.
Specific embodiment
Below in conjunction with embodiment, technical scheme is clearly and completely described, it is clear that described implementation
Example is only a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belongs to the scope of protection of the invention.
Case study on implementation 1:
30 parts of the albumen stone flour that particle diameter is 30 μm is weighed, 1 part of water soluble acrylic acid adds appropriate water water-bath 0.5 at 60 DEG C
Hour, filtering is dried, and is broken up, and weighs 1 part of sodium hexametaphosphate, 1 part of cerium oxide, 30 parts of rare earth, ferric oxide powder
30 parts, 8 parts of solitary stone flour, it is well mixed by dry powder blender, you can to obtain negative oxygen ion composite powder.
Case study on implementation 2:
80 parts of the albumen stone flour that particle diameter is 20 μm is weighed, 8 parts of water soluble acrylic acid adds appropriate water water-bath 1 at 90 DEG C
Hour, filtering is dried, and is broken up, and weighs 8 parts of sodium hexametaphosphate, 5 parts of cerium oxide, 1 part of ferric oxide powder, monazite
1 part of powder, it is well mixed by dry powder blender, you can to obtain negative oxygen ion composite powder.
Case study on implementation 3:
40 parts of the albumen stone flour that particle diameter is 10 μm is weighed, 3 parts of water soluble acrylic acid adds appropriate water water-bath 1 at 90 DEG C
Hour, filtering is dried, and is broken up, and weighs 3 parts of sodium hexametaphosphate, 2 parts of cerium oxide, 5 parts of rare earth, ferric oxide powder 5
Part, 2 parts of solitary stone flour, it is well mixed by dry powder blender, you can to obtain negative oxygen ion composite powder.
Case study on implementation 4:
60 parts of the albumen stone flour that particle diameter is 20 μm is weighed, 5 parts of water soluble acrylic acid adds appropriate water water-bath 1 at 90 DEG C
Hour, filtering is dried, and is broken up, and weighs 6 parts of sodium hexametaphosphate, 4 parts of cerium oxide, 20 parts of rare earth, ferric oxide powder
20 parts, 6 parts of solitary stone flour, it is well mixed by dry powder blender, you can to obtain negative oxygen ion composite powder.
Case study on implementation 5:
50 parts of the albumen stone flour that particle diameter is 10 μm is weighed, 4 parts of water soluble acrylic acid adds appropriate water water-bath 1 at 90 DEG C
Hour, filtering is dried, and is broken up, and weighs 4 parts of sodium hexametaphosphate, 3 parts of cerium oxide, 16 parts of rare earth, ferric oxide powder
15 parts, 5 parts of solitary stone flour, it is well mixed by dry powder blender, you can to obtain negative oxygen ion composite powder.
Gained negative oxygen ion composite powder is obtained anion plate as raw material with the various embodiments described above, presses《JCT 2040-2010 bear
Ion functional architecture house decorative material》Standard, the negative aeroion for carrying out induces measurement examination, is as a result listed in the table below:Wherein with
Anion composite powder obtained in component disclosed in prior art CN103805134A is not added with bearing as a control group, to detect
The negative ion amount of ion powder is used as background.
The amount of the anion plate anion releasing of table 1
The above embodiments are merely illustrative of the technical solutions of the present invention rather than its limitations, and those of ordinary skill in the art should
Understand, specific embodiment of the invention can be modified or equivalent with reference to above-described embodiment, these are without departing from this
Any modification of spirit and scope or equivalent are being applied within pending claims.
Claims (7)
1. a kind of anion composite powder, it is characterised in that according to mass fraction meter, the composite powder is obtained by following components:
30-80 parts of albumen stone flour;Sodium hexametaphosphate 1-8 parts;Cerium oxide 1-5 parts;Rare earth 0-30 parts;Ferric oxide powder 1-30 parts;
Water soluble acrylic acid 1-8 parts;Solitary stone flour 1-8 parts.
2. a kind of anion composite powder according to claim 1, it is characterised in that described multiple according to mass fraction meter
Powder is closed to be obtained by following components:40-60 parts of albumen stone flour;Sodium hexametaphosphate 3-6 parts;Cerium oxide 2-4 parts;Rare earth 5-20
Part;Ferric oxide powder 5-20 parts;Water soluble acrylic acid 3-5 parts;Solitary stone flour 2-6 parts.
3. a kind of anion composite powder according to claim 1, it is characterised in that described multiple according to mass fraction meter
Powder is closed to be obtained by following components:50 parts of albumen stone flour;4 parts of sodium hexametaphosphate;3 parts of cerium oxide;16 parts of rare earth;Three oxygen
Change 15 parts of two iron powder;4 parts of water soluble acrylic acid;5 parts of solitary stone flour.
4. according to a kind of any described anion composite powders of claim 1-3, it is characterised in that the albumen stone flour is through water
Property propylene low-kappa number.
5. according to a kind of any described anion composite powders of claim 1-3, it is characterised in that the opal powder footpath
It is 10~30 μm.
6. a kind of anion composite powder according to claim 4, it is characterised in that the pretreatment includes:Will be described
Albumen stone flour and the water soluble acrylic acid mixed configuration aqueous solution, water-bath 1 hour at 60~90 DEG C, filtering are dried, and are broken up.
7. a kind of anion composite powder according to claim 1, it is characterised in that the composite powder is mixed by dry powder
Conjunction machine is well mixed to be obtained.