CN106906639A - Cotton fabric waterproofing refuses oil corrugation finishing agent - Google Patents
Cotton fabric waterproofing refuses oil corrugation finishing agent Download PDFInfo
- Publication number
- CN106906639A CN106906639A CN201610521848.8A CN201610521848A CN106906639A CN 106906639 A CN106906639 A CN 106906639A CN 201610521848 A CN201610521848 A CN 201610521848A CN 106906639 A CN106906639 A CN 106906639A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing agent
- corrugation
- cotton fabric
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses cotton fabric waterproofing refuse oil corrugation finishing agent, including following weight portion component, 100~160 parts of dimethylol urea, 40~60 parts of magnesium chloride hexahydrate, 100~160 parts of aluminum sulfate, 80~100 parts of trimethylol melamine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide, 600~800 parts of deionized water.The cotton fabric waterproofing that the present invention is provided refuses oil corrugation finishing agent, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of cotton fabric waterproofing refuses oil corrugation finishing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people
Attention and have a good application prospect;The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
Oil corrugation finishing agent is refused it is an object of the invention to provide cotton fabric waterproofing, in above-mentioned prior art problem is solved
Or it is multiple.
According to an aspect of the present invention, cotton fabric waterproofing refuse oil corrugation finishing agent, including following weight portion component:
100~160 parts of dimethylol urea, 40~60 parts of magnesium chloride hexahydrate, 100~160 parts of aluminum sulfate, trihydroxy methyl trimerization
80~100 parts of cyanamide, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, hydrogen
20~40 parts of aluminum oxide, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide, go from
600~800 parts of sub- water.
The cotton fabric waterproofing that the present invention is provided refuses oil corrugation finishing agent, makes simple, and the raw materials for production selection of use is nontoxic
Property, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with Water-proof and oil-proof, well-pressed, rich
Full, not dirty the features such as.
Specific embodiment
Embodiment 1
By 100 parts of dimethylol urea, 40 parts of magnesium chloride hexahydrate, 100 parts of aluminum sulfate, 80 parts of trimethylol melamine, first
20 parts of base lauryl acrylate, 20 parts of zinc nitrate hexahydrate, 40 parts of poly- isobutyl ester, 20 parts of aluminium hydroxide, 12 parts of phosphotriester, three oxygen
Change 12 parts of two antimony, 10 parts of benzoyl peroxide, 600 parts of deionized water is put into reactor, is stirred continuously, heating after mixing completely
To 60 DEG C, product is obtained final product after uniform stirring.
Embodiment 2
By 130 parts of dimethylol urea, 50 parts of magnesium chloride hexahydrate, 130 parts of aluminum sulfate, 90 parts of trimethylol melamine, first
25 parts of base lauryl acrylate, 25 parts of zinc nitrate hexahydrate, 50 parts of poly- isobutyl ester, 30 parts of aluminium hydroxide, 18 parts of phosphotriester, three oxygen
Change 15 parts of two antimony, 15 parts of benzoyl peroxide, 700 parts of deionized water is put into reactor, is stirred continuously, heating after mixing completely
To 60 DEG C, product is obtained final product after uniform stirring.
Embodiment 3
By 160 parts of dimethylol urea, 60 parts of magnesium chloride hexahydrate, 160 parts of aluminum sulfate, 100 parts of trimethylol melamine, first
30 parts of base lauryl acrylate, 30 parts of zinc nitrate hexahydrate, 60 parts of poly- isobutyl ester, 40 parts of aluminium hydroxide, 24 parts of phosphotriester, three oxygen
Change 18 parts of two antimony, 20 parts of benzoyl peroxide, 800 parts of deionized water is put into reactor, is stirred continuously, heating after mixing completely
To 60 DEG C, product is obtained final product after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. cotton fabric waterproofing refuses oil corrugation finishing agent, it is characterised in that:Component including following weight portion:
100~160 parts of dimethylol urea, 40~60 parts of magnesium chloride hexahydrate, 100~160 parts of aluminum sulfate, trimethylol melamine
80~100 parts, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, hydroxide
20~40 parts of aluminium, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide, deionized water
600~800 parts.