CN106905663A - A kind of cable material and preparation method thereof - Google Patents
A kind of cable material and preparation method thereof Download PDFInfo
- Publication number
- CN106905663A CN106905663A CN201710181069.2A CN201710181069A CN106905663A CN 106905663 A CN106905663 A CN 106905663A CN 201710181069 A CN201710181069 A CN 201710181069A CN 106905663 A CN106905663 A CN 106905663A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- epoxy resin
- halogen
- cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of cable material, including following weight portion component：20~30 parts of epoxy resin, 15~20 parts of vistanex, 15~35 parts of glass fibre, 5~8 parts of ceramic Firebrake ZB, 15~35 parts of halogen-free expansion fire retardant, 3~7 parts of compatilizer, 0.1~0.2 part of anti-dripping agent, 4~7 parts of silicone oil, 2~3 parts of lubricant, 0.5~2 part of antioxidant, 1~2 part of antiseptic, the each component is that can obtain the cable material by techniques such as kneading, extruding pelletization, dryings, the cable material has good anti-flammability and fire resistance, and excellent moisture resistance and water absorption resistance.
Description
Technical field
The invention belongs to field of cable technology, and in particular to a kind of cable material and preparation method thereof.
Background technology
Existing domestic and international fire-resisting cable mainly has magnesium oxide mineral insulated fireproof cable and Mica tape inorganic insulation
Fire-resisting cable.Though mineral insulated cable has good fire resistance, its manufacturing process is complicated, production cost is high,
Factory length is limited, and cable is stone cannot bend, and joint is complicated, and difficulty of construction is very high, it is difficult to extensive use.Mica tape
Although wrapped fire-resisting cable work process is simple, factory length is unrestricted, one shortcoming of mica tape generally existing, high temperature combustion
The mechanical strength of mica tape is greatly lowered after burning, becomes fragile, and by easy powder of detached after strenuous vibration, causes fire resisting effect not
It is good.And because of easy dry linting when mica tape rubs, cause wrapped live a large amount of dust to the health care belt of operating personnel to threaten.In recent years
To there is scientific research personnel's exploratory development ceramic silicon rubber insulating flame-resistant cable, but because needing special mixing in cable making process
Refine, extrude and vulcanizing equipment, complex process, and be difficult to obtain balance, ceramic journey between isolation layer intensity and fire resistance
Degree is difficult to be tested by the resistance to extreme misery of fire-resisting cable.
The content of the invention
The invention provides a kind of cable material and preparation method thereof, the cable material has good anti-flammability and fire resisting
Property, and excellent moisture resistance and water absorption resistance.
In order to solve the problems, such as prior art, adopt the following technical scheme that：
A kind of cable material, including following weight portion component：20~30 parts of epoxy resin, 15~20 parts of vistanex, glass
15~35 parts of glass fiber, 5~8 parts of ceramic Firebrake ZB, 15~35 parts of halogen-free expansion fire retardant, 3~7 parts of compatilizer, anti-drop
Fall 0.1~0.2 part of agent, 4~7 parts of silicone oil, 2~3 parts of lubricant, 0.5~2 part of antioxidant, 1~2 part of antiseptic.
Preferably, the cable material, including following weight portion component：24~27 parts of epoxy resin, vistanex
17~19 parts, 25~30 parts of glass fibre, 6~7 parts of ceramic Firebrake ZB, 24~27 parts of halogen-free expansion fire retardant, compatilizer 3
~5 parts, 0.1~0.2 part of anti-dripping agent, 5~6 parts of silicone oil, 2~3 parts of lubricant, 0.5~1 part of antioxidant, 1~2 part of antiseptic.
Preferably, the cable material, including following weight portion component：25 parts of epoxy resin, 18 parts of vistanex,
27 parts of glass fibre, 6 parts of ceramic Firebrake ZB, 26 parts of halogen-free expansion fire retardant, 4 parts of compatilizer, 0.1 part of anti-dripping agent, silicon
5 parts of oil, 2 parts of lubricant, 0.6 part of antioxidant, 1.2 parts of antiseptic.
Preferably, the epoxy resin is modified epoxy.
Preferably, the preparation method of the modified epoxy is as follows：25~37 parts of epoxy resin are added by weight
In 100 parts of toluene, 17 parts of bromoacetic acids are stirring evenly and then adding into, 100 parts of methyl alcohol are added after 15~20h of reaction is stirred at room temperature
In, through precipitating, filtering, be dried to obtain material A；By weight by 13 parts of material As 45 parts of toluene of addition, it is stirring evenly and then adding into
40 parts of triphenylphosphines, are stirred at room temperature concentration of reaction solution after 33~37h, are subsequently adding in 100 parts of petroleum ethers, through precipitation, mistake
Filter, be dried to obtain the modified epoxy.
Preferably, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 65~85 DEG C,
Smelting time is 30~50 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization；
（3）Hot wind flow during the material for completing is put into 80~85 DEG C of environment will be granulated to dry 2~3 hours, you can obtain the electricity
Cable material.
Preferably, the temperature range of the extruding and pelletizing process is 100~140 DEG C.
Compared with prior art, it has the advantages that the present invention：
Cable material of the present invention, with good flexibility and elasticity, and excellent moisture resistance and water absorption resistance, burning
The material of ceramic-like afterwards, forms continuous using ceramic Firebrake ZB at high temperature in hard, uniform cellular housing
Glass ceramics tunic, such object has excellent insulating properties, thermal insulation, fire insulation fire resistance, while can also withstand shocks
And vibrations, and the infiltration for preventing water；While the antiseptic by adding proper ratio so that the cable material of preparation both had
Antimycotic effect, while influenceing the performance of original cable material without the addition because of antiseptic；The present invention with the addition of and change
Property epoxy resin, coordinate with vistanex, glass fibre and improve the insulating properties of cable material.
Specific embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of cable material, including following weight portion component：20 parts of epoxy resin, vistanex 15
Part, 15 parts of glass fibre, 5 parts of ceramic Firebrake ZB, 15 parts of halogen-free expansion fire retardant, 3 parts of compatilizer, 0.1 part of anti-dripping agent,
4 parts of silicone oil, 2 parts of lubricant, 0.5 part of antioxidant, 1 part of antiseptic.
Wherein, the epoxy resin is modified epoxy, and the preparation method of the modified epoxy is as follows：By weight
Part adds 25 parts of epoxy resin in 100 parts of toluene, is stirring evenly and then adding into 17 parts of bromoacetic acids, and reaction 15h is stirred at room temperature
Afterwards in 100 parts of methyl alcohol of addition, through precipitating, filtering, be dried to obtain material A；13 parts of material As are added into 45 parts of toluene by weight
In, 40 parts of triphenylphosphines are stirring evenly and then adding into, concentration of reaction solution after 33h is stirred at room temperature, it is subsequently adding 100 parts of petroleum ethers
In, through precipitating, filtering, being dried to obtain the modified epoxy.
Wherein, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 65 DEG C, melting
Time is 30 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization, temperature is 100 DEG C；
（3）Hot wind flow during the material for completing is put into 80 DEG C of environment will be granulated to dry 2 hours, you can obtain the cable material.
Embodiment 2
The present embodiment is related to a kind of cable material, including following weight portion component：30 parts of epoxy resin, vistanex 20
Part, 35 parts of glass fibre, 8 parts of ceramic Firebrake ZB, 35 parts of halogen-free expansion fire retardant, 7 parts of compatilizer, 0.2 part of anti-dripping agent,
7 parts of silicone oil, 3 parts of lubricant, 2 parts of antioxidant, 2 parts of antiseptic.
Wherein, the epoxy resin is modified epoxy, and the preparation method of the modified epoxy is as follows：By weight
Part adds 37 parts of epoxy resin in 100 parts of toluene, is stirring evenly and then adding into 17 parts of bromoacetic acids, and reaction 20h is stirred at room temperature
Afterwards in 100 parts of methyl alcohol of addition, through precipitating, filtering, be dried to obtain material A；13 parts of material As are added into 45 parts of toluene by weight
In, 40 parts of triphenylphosphines are stirring evenly and then adding into, concentration of reaction solution after 37h is stirred at room temperature, it is subsequently adding 100 parts of petroleum ethers
In, through precipitating, filtering, being dried to obtain the modified epoxy.
Wherein, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 85 DEG C, melting
Time is 50 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization, temperature is 140 DEG C；
（3）Hot wind flow during the material for completing is put into 85 DEG C of environment will be granulated to dry 3 hours, you can obtain the cable material.
Embodiment 3
The present embodiment is related to a kind of cable material, including following weight portion component：24 parts of epoxy resin, vistanex 17
Part, 25 parts of glass fibre, 6 parts of ceramic Firebrake ZB, 24 parts of halogen-free expansion fire retardant, 3 parts of compatilizer, 0.1 part of anti-dripping agent,
5 parts of silicone oil, 2 parts of lubricant, 0.5 part of antioxidant, 1 part of antiseptic.
Wherein, the epoxy resin is modified epoxy, and the preparation method of the modified epoxy is as follows：By weight
Part adds 25 parts of epoxy resin in 100 parts of toluene, is stirring evenly and then adding into 17 parts of bromoacetic acids, and reaction 15h is stirred at room temperature
Afterwards in 100 parts of methyl alcohol of addition, through precipitating, filtering, be dried to obtain material A；13 parts of material As are added into 45 parts of toluene by weight
In, 40 parts of triphenylphosphines are stirring evenly and then adding into, concentration of reaction solution after 33h is stirred at room temperature, it is subsequently adding 100 parts of petroleum ethers
In, through precipitating, filtering, being dried to obtain the modified epoxy.
Wherein, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 65 DEG C, melting
Time is 30 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization, temperature is 100 DEG C；
（3）Hot wind flow during the material for completing is put into 80 DEG C of environment will be granulated to dry 2 hours, you can obtain the cable material.
Embodiment 4
The present embodiment is related to a kind of cable material, including following weight portion component：27 parts of epoxy resin, vistanex 19
Part, 30 parts of glass fibre, 7 parts of ceramic Firebrake ZB, 27 parts of halogen-free expansion fire retardant, 5 parts of compatilizer, 0.2 part of anti-dripping agent,
6 parts of silicone oil, 3 parts of lubricant, 1 part of antioxidant, 2 parts of antiseptic.
Wherein, the epoxy resin is modified epoxy, and the preparation method of the modified epoxy is as follows：By weight
Part adds 37 parts of epoxy resin in 100 parts of toluene, is stirring evenly and then adding into 17 parts of bromoacetic acids, and reaction 20h is stirred at room temperature
Afterwards in 100 parts of methyl alcohol of addition, through precipitating, filtering, be dried to obtain material A；13 parts of material As are added into 45 parts of toluene by weight
In, 40 parts of triphenylphosphines are stirring evenly and then adding into, concentration of reaction solution after 37h is stirred at room temperature, it is subsequently adding 100 parts of petroleum ethers
In, through precipitating, filtering, being dried to obtain the modified epoxy.
Wherein, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 85 DEG C, melting
Time is 50 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization, temperature is 140 DEG C；
（3）Hot wind flow during the material for completing is put into 85 DEG C of environment will be granulated to dry 3 hours, you can obtain the cable material.
Embodiment 5
The present embodiment is related to a kind of cable material, including following weight portion component：25 parts of epoxy resin, vistanex 18
Part, 27 parts of glass fibre, 6 parts of ceramic Firebrake ZB, 26 parts of halogen-free expansion fire retardant, 4 parts of compatilizer, 0.1 part of anti-dripping agent,
5 parts of silicone oil, 2 parts of lubricant, 0.6 part of antioxidant, 1.2 parts of antiseptic.
Wherein, the epoxy resin is modified epoxy, and the preparation method of the modified epoxy is as follows：By weight
Part adds 37 parts of epoxy resin in 100 parts of toluene, is stirring evenly and then adding into 17 parts of bromoacetic acids, and reaction 20h is stirred at room temperature
Afterwards in 100 parts of methyl alcohol of addition, through precipitating, filtering, be dried to obtain material A；13 parts of material As are added into 45 parts of toluene by weight
In, 40 parts of triphenylphosphines are stirring evenly and then adding into, concentration of reaction solution after 37h is stirred at room temperature, it is subsequently adding 100 parts of petroleum ethers
In, through precipitating, filtering, being dried to obtain the modified epoxy.
Wherein, the halogen-free expansion fire retardant is phosphor nitrogen combustion inhibitor.
A kind of method for preparing the cable material, comprises the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 85 DEG C, melting
Time is 50 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization, temperature is 140 DEG C；
（3）Hot wind flow during the material for completing is put into 85 DEG C of environment will be granulated to dry 3 hours, you can obtain the cable material.
From above-described embodiment as can be seen that cable material of the present invention, with good flexibility and elasticity, Yi Jiyou
Different moisture resistance and water absorption resistance, the material of the ceramic-like after burning is in hard, uniform cellular housing, using ceramic
Firebrake ZB at high temperature, forms continuous glass ceramics tunic, and such object has excellent insulating properties, thermal insulation, fire insulation
Fire resistance, while can also withstand shocks and shake, and prevents the infiltration of water；While the antibacterial by adding proper ratio
Agent so that the cable material of preparation both has antimycotic effect, while influenceing original electricity without the addition because of antiseptic
The performance of cable material；The present invention with the addition of modified epoxy, coordinates with vistanex, glass fibre and improves cable material
Insulating properties.
Specific embodiment of the invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can within the scope of the claims make various deformations or amendments, this not shadow
Sound substance of the invention.
Claims (8)
1. a kind of cable material, it is characterised in that the component including following weight portion：20~30 parts of epoxy resin, polyolefin tree
It is 15~20 parts of fat, 15~35 parts of glass fibre, 5~8 parts of ceramic Firebrake ZB, 15~35 parts of halogen-free expansion fire retardant, compatible
3~7 parts of agent, 0.1~0.2 part of anti-dripping agent, 4~7 parts of silicone oil, 2~3 parts of lubricant, 0.5~2 part of antioxidant, antiseptic 1~2
Part.
2. cable material according to claim 1, it is characterised in that the component including following weight portion：Epoxy resin 24
~27 parts, 17~19 parts of vistanex, 25~30 parts of glass fibre, 6~7 parts of ceramic Firebrake ZB, halogen-free expansion type flame-proof
24~27 parts of agent, 3~5 parts of compatilizer, 0.1~0.2 part of anti-dripping agent, 5~6 parts of silicone oil, 2~3 parts of lubricant, antioxidant 0.5
~1 part, 1~2 part of antiseptic.
3. cable material according to claim 1, it is characterised in that the component including following weight portion：Epoxy resin 25
Part, 18 parts of vistanex, 27 parts of glass fibre, 6 parts of ceramic Firebrake ZB, 26 parts of halogen-free expansion fire retardant, compatilizer 4
Part, 0.1 part of anti-dripping agent, 5 parts of silicone oil, 2 parts of lubricant, 0.6 part of antioxidant, 1.2 parts of antiseptic.
4. cable material according to claim 1, it is characterised in that the epoxy resin is modified epoxy.
5. cable material according to claim 4, it is characterised in that the preparation method of the modified epoxy is as follows：
By weight by 25~37 parts of epoxy resin 100 parts of toluene of addition, 17 parts of bromoacetic acids are stirring evenly and then adding into, stirred at room temperature
Mixing in add after 15~20h of reaction 100 parts of methyl alcohol, through precipitating, filtering, be dried to obtain material A；By weight by 13 parts of material As
Add in 45 parts of toluene, be stirring evenly and then adding into 40 parts of triphenylphosphines, concentration of reaction solution after 33~37h is stirred at room temperature, so
Afterwards in 100 parts of petroleum ethers of addition, through precipitating, filtering, being dried to obtain the modified epoxy.
6. cable material according to claim 1, it is characterised in that the halogen-free expansion fire retardant is that phosphorus nitrogen is fire-retardant
Agent.
7. a kind of method for preparing cable material described in any one of claim 1~6, it is characterised in that comprise the following steps：
（1）It is well mixed after weighing various raw materials by formula, is put into melting machine and is mediated, smelting temperature is 65~85 DEG C,
Smelting time is 30~50 minutes；
（2）By the step（1）Mediate the material for completing and be put into double screw extruder extruding pelletization；
（3）Hot wind flow during the material for completing is put into 80~85 DEG C of environment will be granulated to dry 2~3 hours, you can obtain the electricity
Cable material.
8. preparation method according to claim 7, it is characterised in that the temperature range of the extruding and pelletizing process is 100
~140 DEG C.