CN106867442A - UV solidifications glue composition, soft mold and printing transferring method - Google Patents
UV solidifications glue composition, soft mold and printing transferring method Download PDFInfo
- Publication number
- CN106867442A CN106867442A CN201710026345.8A CN201710026345A CN106867442A CN 106867442 A CN106867442 A CN 106867442A CN 201710026345 A CN201710026345 A CN 201710026345A CN 106867442 A CN106867442 A CN 106867442A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- soft mold
- solidification
- soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a kind of UV solidifications glue composition, soft mold and printing transferring method.In parts by weight, UV solidifications glue composition includes 2~8 parts of 15~35 parts of urethane acrylate oligomer, 5~20 parts of Si modification resin, 30~50 parts of the first monomer and the first light trigger.Urethane acrylate oligomer of the UV solidification glue compositions comprising above-mentioned consumption and Si modification resin, therefore, solidification under uv radiation causes that its surface dynes value is controllable, when being used as soft mold, control the difference of the surface dynes value of its surface dynes value and the decorating film solidifying to form larger, the two purpose for being easy to depart from is capable of achieving, and then solves the problems, such as that the soft mold demoulding is difficult.
Description
Technical field
The present invention relates to transfer field, in particular to a kind of UV solidifications glue composition, soft mold and transfer side
Method.
Background technology
With the high speed development of social economy, the living standard of people is improved constantly, therefore demand to ornament is also got over
Come bigger, it is desirable to also more and more higher.In ornamental glass, pattern structure main method is done on glass mechanical engraving and heat
Transfer, the method for mechanical engraving takes a lot of work and time-consuming, also high to glass oneself requirement;The method of decorative pattern film thermal transfer is moved on to
On glass, operation is simplified, but relatively costly, easily affected by environment or easily come off in cleaning, the life-span is shorter.
The patent application of Application No. 201510443701.7 discloses a kind of glass transfer printing process, including:On glass
One layer of UV glue of coating;The transfer film of the decorative pattern with needed for is sticked in the one side for being coated with UV glue, is struck off;With ultra violet lamp 10~
30s;Transfer film is removed after cooling, required decorative pattern is obtained on glass.But, attachment of the most UV solidified glues to glass
Power is all poor, and be typically necessary improves attachment using the method for primary coat.
The patent application of Application No. 201610031144.2 discloses a kind of ultraviolet curing transfer adhesive and its preparation side
Method has excellent adhesive force to glass, can substitute traditional PUR with application, the ultraviolet curing transfer adhesive prepared by it
Type transfer glue.But transfer film is needed first to carry out pattern structure on soft base material, and transfer glue is coated at the back side, then is fitted in glass
On.Whole process operation is more, and material cost is more, relatively costly.
The patent application of Application No. 200710092834.X discloses a kind of preparation method of glass art picture, including with
Lower step:Glass baseplate is made, paper self-adhesive tape is sticked on the periphery of glass, epoxide-resin glue is mixed up in proportion with curing agent, applied
Levelling on the glass surface;Template is made, decorative pattern is engraved on the facial tissue of Sticky Note, the facial tissue of Sticky Note is attached to plastic sheeting
On, knurling section is torn, decorative pattern module is put on double faced adhesive tape, it is made template;Manufacture craft is drawn on the glass substrate, in epoxy
When resin glue has reached 40~70% state of cure, template is placed on above epoxide-resin glue, is pressed down against decorative pattern module and is formed
Three-dimensional pattern, after epoxy resin adhesive curing, takes away template, coats color, glass art picture.But, the method needs to use
To substantial amounts of artificial operation, be not suitable for mechanization production.
Pattern structure is attached to the method on glass above by thermal transfer, the PUR generally existing for being used some ask
Topic:Heat resistance is not high, and adhesion strength is low, and chemical-resistant is poor, also with a small amount of VOC (VOC), during operation
Special hot melt gun etc. must also be configured;And most UV solidified glues are all poor to the adhesive force of glass.Further, since
Die hard cannot be molded on glass, and general soft mold poor, the low problem of recycling rate of waterused that there is release property.
The content of the invention
It is a primary object of the present invention to provide a kind of UV solidifications glue composition, soft mold and printing transferring method, to solve
In the prior art heat-transferring method release property difference problem.
To achieve these goals, according to an aspect of the invention, there is provided a kind of UV solidifies glue composition, with weight
Part meter, UV solidification glue compositions include:15~35 parts of urethane acrylate oligomer;5~20 parts of Si modification resin;First is single
30~50 parts of body;And 2~8 parts of the first light trigger.
Further, above-mentioned urethane acrylate oligomer is double bond 583-1, cyanogen spy EB8465, cyanogen spy EB264, length
Formed for one or more in emerging DR-U025, Changxing 6158B-80, the group of Changxing DR-U029 and Ken Meite EO-2238 compositions
Mixture.
Further, above-mentioned Si modification resin is U.S. source SIU2400, the group of cyanogen spy EB1360 and Changxing DR-U188C composition
In one or more formation mixture.
Further, above-mentioned first monomer is trimethylolpropane trimethacrylate, tetrahydrofurfuryl acrylate, ethoxy
Change one or more formation in the group of trimethylol-propane trimethacrylate and 1,6 hexanediol diacrylate composition
Mixture.
Further, above-mentioned first light trigger is α-hydroxyl alkanone photoinitiator or the oxide-based light trigger of acyl group.
Further, above-mentioned UV solidifications glue composition also includes the first auxiliary agent less than or equal to 2 weight portions, and preferably first helps
Agent is organic silicon modified by polyether, and more preferably organic silicon modified by polyether is constituted selected from BYK-333, BYK-UV3500 and BYK-UV3505
Group in one or more formation mixture.
According to another aspect of the present invention, there is provided a kind of soft mold, formed using UV solidification adhesive curings, the UV solidification glues
Formed using any of the above-described kind of UV solidification glue composition solidifications.
Further, the surface dynes value of above-mentioned soft mold is less than 30.
According to another aspect of the present invention, there is provided a kind of printing transferring method, including:Step S1, using any of the above-described kind of UV
Solidification glue composition prepares soft mold;Step S2, is provided for making the glue of decorating film on base material;Step S3, using soft
Mould is modeled to glue, obtains modelling glue-line;And step S4, modelling glue-line is solidified, obtain decorating film.
Further, the surface dynes value of above-mentioned soft mold is less than 30.
Further, above-mentioned steps S1 includes:The mixture that UV solidification glue compositions are formed is set on metal die;
Soft base material is set on mixture, and roll-in is carried out to soft base material;Mixture after roll-in is solidified, is solidified
Layer;And removal metal die, and UV curings are carried out to cured layer, obtain soft mold.
Further, the UV energy that above-mentioned UV curings are used is 20000~100000mj/cm2。
Further, the surface dynes value of above-mentioned decorating film is more than 40, the UV energy that the solidification of preferred steps S4 is used for
10~100mj/cm2。
Further, above-mentioned printing transferring method also includes carrying out decorating film the process of thermal maturation.
Further, weight portion meter, above-mentioned glue includes:45~70 parts of oligomer, 10~30 parts of second comonomers, 2~8 parts
Second light trigger and 0~5 part of second auxiliary agent, wherein, preferably oligomer is urethane acrylate or pure acrylate;It is preferred that
Second comonomer is isobornyl acrylate, Changxing chemistry 2- HEMAs phosphate, tetrahydrofurfuryl propylene
One or more mixture of formation in the group of acid esters composition;It is preferred that the second light trigger be α-hydroxyl alkanone photoinitiator or
The oxide-based light trigger of acyl group;It is preferred that the second auxiliary agent is polyether-modified acrylate or organosilicon-modified acrylate.
Further, above-mentioned base material is glass.
The urethane acrylate oligomer of the UV solidification glue compositions comprising above-mentioned consumption and Si modification resin of the application,
Therefore, solidification causes that its surface dynes value is controllable under uv radiation, when being used as soft mold, controls its surface dynes
The difference of the surface dynes value of the decorating film for being worth and solidifying to form is larger, you can realizes the two purpose for being easy to depart from, and then solves
The difficult problem of the soft mold demoulding.
Brief description of the drawings
The Figure of description for constituting the part of the application is used for providing a further understanding of the present invention, of the invention to show
Meaning property and its illustrates, for explaining the present invention, not constitute inappropriate limitation of the present invention embodiment.In the accompanying drawings:
Fig. 1 shows and glue model using soft mold to obtain modelling according to a kind of preferred embodiment of the invention
Glue-line schematic diagram;And
Fig. 2 shows that the utilization metal die provided according to a kind of preferred embodiment of the invention prepares the signal of soft mold
Figure.
Wherein, above-mentioned accompanying drawing is marked including the following drawings:
10th, metal die;20th, soft mold;30th, modelling glue-line.
Specific embodiment
It should be noted that in the case where not conflicting, the feature in embodiment and embodiment in the application can phase
Mutually combination.Describe the present invention in detail below with reference to the accompanying drawings and in conjunction with the embodiments.
As background technology is analyzed, improvement of the prior art to transfer printing process has various, and wherein soft mold transfer is excellent
Gesture is obvious, but when using soft mold to transfer, however it remains the difficult problem of the demoulding, in order to solve the problem, this
Application provides a kind of UV solidifications glue composition, soft mold and printing transferring method.
In a kind of typical implementation method of the application, there is provided a kind of UV solidifies glue composition, and in parts by weight, UV is solid
Changing glue composition includes:15~35 parts of urethane acrylate oligomer;5~20 parts of Si modification resin;First monomer 30~50
Part;And 2~8 parts of the first light trigger.
The urethane acrylate oligomer of the UV solidification glue compositions comprising above-mentioned consumption and Si modification resin of the application,
Therefore, solidification causes that its surface dynes value is controllable under uv radiation, when being used as soft mold, controls its surface dynes
The difference of the surface dynes value of the decorating film for being worth and solidifying to form is larger, you can realizes the two purpose for being easy to depart from, and then solves
The difficult problem of the soft mold demoulding.
Selected in the quasi-oligomer that above-mentioned urethane acrylate oligomer can be commonly used from the prior art, it is excellent
Choose and state urethane acrylate oligomer including double bond 583-1, cyanogen spy EB8465, cyanogen spy EB264, Changxing DR-U025, Changxing
One or more mixture of formation in 6158B-80, the group of Changxing DR-U029 and Ken Meite EO-2238 compositions.
Furthermore it is preferred that above-mentioned Si modification resin include U.S. source SIU2400, cyanogen spy EB1360 and Changxing DR-U188C in extremely
Few one kind.Si modification resin and polyurethane acroleic acid oligomer using mentioned kind are coordinated, further control UV solidifications
The surface dynes value controllability of the soft mold that glue composition is formed.
Above-mentioned first monomer can also refer to the conventional monomer of UV solidification glues in the prior art, in order to preferably and polyurethane
Acrylate oligomer is coordinated, and preferably above-mentioned first monomer is trimethylolpropane trimethacrylate, tetrahydrofurfuryl third
One kind in the group of olefin(e) acid ester, ethoxyquin trimethylol-propane trimethacrylate and 1,6 hexanediol diacrylate composition
Or the mixture of various formation.Such as can be Changxing chemistry EM231 (TMPTA), Changxing chemistry EM214 (THFA), Xinghua long
Learn EM2382 (TMP9EOTMA) and/or Changxing chemistry EM221 (HDDA).
In order to accelerate solidification rate, preferably above-mentioned first light trigger is α-hydroxyl alkanone photoinitiator or acyl group oxide
Photoinitiator.Such as can for Doublecure (enlightening trade Co., Ltd more chemical than happiness) TPO, Doublecure 184,
Doublecure 1173 and/or Doublecure369.
In a kind of preferred embodiment of the application, above-mentioned UV solidifications glue composition is also included less than or equal to 2 weight portions
First auxiliary agent, preferably first auxiliary agent are organic silicon modified by polyether, and more preferably organic silicon modified by polyether is selected from BYK-333, BYK-
One or more mixture of formation in the group of UV3500 and BYK-UV3505 compositions.Further improve UV using the first auxiliary agent
The surface dynes value performance-adjustable of the soft mold that solidification glue composition is formed.
In another typical implementation method of the application, there is provided a kind of soft mold, formed using UV solidification adhesive curings,
The UV solidification glues solidify glue composition solidification and form using any of the above-described kind of UV.
Using the application UV solidification glue composition formed soft mold under uv radiation when surface dynes value it is controllable, when general
When mould during for transferring is used, the surface dynes value for adjusting its surface dynes value and the decorating film solidifying to form forms larger
Difference, you can realize the two purpose for being easy to depart from, and then solve the problems, such as that the soft mold demoulding is difficult.
In order that the soft mold of the application can be used cooperatively with most decorating films, the surface dynes of preferably above-mentioned soft mold
Value is less than 30.
In the application in another typical implementation method, there is provided a kind of printing transferring method, including:Step S1, using upper
State any one UV solidification glue compositions and prepare soft mold;Step S2, is provided for making the glue of decorating film on base material;Step
S3, is modeled using soft mold 20 to glue, obtains modelling glue-line 30 (referring to Fig. 1);And step S4, by modelling glue-line
Solidified, obtained decorating film.
Due to the application soft mold under uv radiation when surface dynes value it is controllable, when by for transfer when mould use
When, the surface dynes value for adjusting its surface dynes value and the decorating film solidifying to form forms larger difference, you can realize the two easily
In the purpose for departing from, and then solve the problems, such as that the soft mold demoulding is difficult.
Further, it is preferable to control the surface dynes value of above-mentioned soft mold less than 30, the soft mold demoulding can have both been solved difficult
Problem, the anti-pollution characteristic of soft mold can be improved again.
In the application another kind preferred embodiment, there is provided the preparation method of soft mold, i.e., preferred above-mentioned steps S1
Including:The mixture that UV solidification glue compositions are formed is set on metal die 10;Soft base material is set on the mixture, and it is right
Soft base material carries out roll-in;Mixture after roll-in is solidified, cured layer is obtained;And removal metal die, and to solid
Changing layer carries out UV curings, obtains soft mold 20 (referring to Fig. 2).
By way of first solidifying post curing so that the hardness and surface dynes value of soft template can be controlled flexibly,
Such as control surface dyne value < 30, the UV energy that preferably above-mentioned UV curings are used is 20000~100000mj/cm2.This
Outward, above-mentioned surface dynes value also advantageously improves the resistance to soiling of soft mold.On the one hand can fill mantle glue after strong UV curings
Divide reaction, and make up to hardness higher, surface texture is unlikely to deform.On the other hand can migrate auxiliary agent after strong UV curings
To surface, surface smoothness is improved, it is easy to the demoulding.
Additionally, in order to improve recoatability, beneficial to oil surface ink or other coatings, the surface dynes value of preferably decorating film is big
In 40, while the surface dynes value of the surface dynes value and above-mentioned soft template matches, the removing of soft mold is more beneficial for.Enter one
It is 10~100mj/cm to walk the UV energy that the solidification of preferred above-mentioned steps S4 uses2, modelling glue is carried out with the UV irradiation of low energy
The solidification of layer, makes the solidification of modelling adhesive tape sections, surface drying, so as to be easy to and the soft mold demoulding.Soft mold is organic material, central to have
The unreacted double bond in part, UV energy is too high to cause modelling glue-line to produce chemical reaction with soft mold surface, cause adhesive force
Enhancing, is unfavorable for the demoulding.
When the decorating film of the application needs to be applied in the environment higher to hardness requirement, preferably above-mentioned printing transferring method is also
Process including carrying out thermal maturation to decorating film.Decorating film is cured using heat energy, further improves the hardness of decorating film.
The above-mentioned formation raw material that decorating film in the prior art is may be referred to for forming the glue of decorating film, in order to adapt to this
The printing transferring method of application and the cooperation with soft mold, preferably in parts by weight, glue includes:45~70 parts of oligomer, 10~
30 parts of second comonomers, 2~8 part of second light trigger and 0~5 part of second auxiliary agent, wherein, preferably oligomer is polyurethane acroleic acid
Ester or pure acrylate;It is preferred that second comonomer is isobornyl acrylate, Changxing chemistry EM39 (HEMAP) 2- hydroxy ethyl methyls
One or more mixture of formation in acrylate phosphate, the group of tetrahydrofurfuryl acrylate composition;It is preferred that second
Light trigger is α-hydroxyl alkanone photoinitiator or the oxide-based light trigger of acyl group;It is preferred that the second auxiliary agent is polyether-modified propylene
Acid esters or organosilicon-modified acrylate.Wherein, made using above-mentioned polyether-modified acrylate or organosilicon-modified acrylate
It is the second auxiliary agent, is favorably improved the surface dynes value of decorating film.
Above-mentioned printing transferring method is applied to transfer of the decorating film on various base materials, especially glass baseplate, such as common glass
Glass or safety glass, its thickness is preferably in 0.5~5cm.
Soft base material employed in above-mentioned formation soft mold process can be PET, PMMA or PC etc. with certain flexible
Property plastic basis material, for the ease of removing preferably its thickness between 25~250 μm.
Below with reference to embodiment and comparative example, the beneficial effect of the application is further illustrated.
Embodiment 1
The preparation of decorating film
(1) by 20 parts of urethane acrylates EO-2238,10 parts of urethane acrylate 6158B-80,15 parts of Si modifications
Resin SIU2400,20 parts of monomer EM214,30 parts of monomer EM221,4 parts of initiators, 184,1 part of auxiliary agent B YK-UV3505 mixing is stirred
Mix 30min and obtain master mold glue.
(2) by 40 parts of urethane acrylates EB8210,10 parts of urethane acrylate XP2765,17 parts of pure acrylates
353L, 10 parts of monomers EM39,15 parts of monomer EM214,4 parts of initiators, 184,1 part of initiator TPO, 3 parts of auxiliary agent B YK-3560 mixing
Stirring 30min obtains decorating film glue.
(3) PET from 188 μ m-thicks is soft base material, and master mold glue is set on metal die, sets soft on master mold glue
Matter base material, roll-in is carried out with pair of rollers soft base material makes master mold glue uniform;The master mold glue after roll-in is consolidated using ultraviolet light
Change, soft mold sheet material is obtained, using preceding by soft mold piece timber-used 50000mj/cm2Energy cured.
(4) it is base material from 0.5cm thick safety glass, decorating film glue is coated on base material, using soft mold piece
Material is modeled to decorating film glue, then using 50mj/cm2The ultraviolet light polymerization decorating film glue of energy, tears soft mold
Sheet material, you can obtain the decorating film of embodiment 1.
Embodiment 2
The preparation of decorating film
(1) by 20 parts of urethane acrylates EO-2238,10 parts of urethane acrylate 6158B-80,15 parts of Si modifications
Resin SIU2400,20 parts of monomer EM214,30 parts of monomer EM221,4 parts of initiators, 184,1 part of auxiliary agent B YK-UV3505 mixing is stirred
Mix 30min and obtain master mold glue.
(2) by 40 parts of urethane acrylates EB8210,10 parts of urethane acrylate XP2765,17 parts of pure acrylates
353L, 10 parts of monomers EM39,15 parts of monomer EM214,4 parts of initiators, 184,1 part of initiator TPO, 3 parts of auxiliary agent B YK-3560 mixing
Stirring 30min obtains decorating film glue.
(3) PET from 188 μ m-thicks is soft base material, and master mold glue is set on metal die, sets soft on master mold glue
Matter base material, roll-in is carried out with pair of rollers soft base material makes master mold glue uniform;The master mold glue after roll-in is consolidated using ultraviolet light
Change, soft mold sheet material is obtained, using preceding by soft mold piece timber-used 50000mj/cm2Energy cured.
(4) it is, base material from 0.5cm thick safety glass, decorating film glue is coated on base material, using soft mold piece
Material is modeled to decorating film glue, then using 100mj/cm2The ultraviolet light polymerization decorating film glue of energy, tears soft mold
Sheet material, you can obtain the decorating film of embodiment 2.
Embodiment 3
The preparation of decorating film
(1) by 20 parts of urethane acrylates EO-2238,10 parts of urethane acrylate 6158B-80,15 parts of Si modifications
Resin SIU2400,20 parts of monomer EM214,30 parts of monomer EM221,4 parts of initiators, 184,1 part of auxiliary agent B YK-UV3505 mixing is stirred
Mix 30min and obtain master mold glue.
(2) by 40 parts of urethane acrylates EB8210,10 parts of urethane acrylate XP2765,17 parts of pure acrylates
353L, 10 parts of monomers EM39,15 parts of monomer EM214,4 parts of initiators, 184,1 part of initiator TPO, 3 parts of auxiliary agent B YK-3560 mixing
Stirring 30min obtains decorating film glue.
(3) PET from 188 μ m-thicks is base material, and master mold glue is set on metal die, and soft base is set on master mold glue
Material, roll-in is carried out with pair of rollers soft base material makes master mold glue uniform;The master mold glue after roll-in is solidified using ultraviolet light, is obtained
To soft mold sheet material, using preceding by soft mold piece timber-used 50000mj/cm2Energy cured.
(4) it is base material from 0.5cm thick safety glass, decorating film glue is coated on base material, using soft mold piece
Material is modeled to decorating film glue, then using 500mj/cm2The ultraviolet light polymerization decorating film glue of energy, tears soft mold
Sheet material, you can obtain the decorating film of embodiment 3.
Embodiment 4
(1) by 20 parts of urethane acrylates EO-2238,10 parts of urethane acrylate 6158B-80,15 parts of Si modifications
Resin SIU2400,20 parts of monomer EM214,30 parts of monomer EM221,4 parts of initiators, 184,1 part of auxiliary agent B YK-UV3505 mixing is stirred
Mix 30min and obtain master mold glue.
(2) by 40 parts of urethane acrylates EB8210,10 parts of urethane acrylate XP2765,20 parts of pure acrylates
353L, 10 parts of monomers EM39,15 parts of monomer EM214,4 parts of initiators, 184,1 part of initiator TPO, mix 30min and are filled
Decorations film glue.
(3) PET from 188 μ m-thicks is soft base material, and master mold glue is set on metal die, sets soft on master mold glue
Matter base material, roll-in is carried out with pair of rollers soft base material makes master mold glue uniform;The master mold glue after roll-in is consolidated using ultraviolet light
Change, soft mold sheet material is obtained, using preceding by soft mold piece timber-used 50000mj/cm2Energy cured.
(4) it is base material from 0.5cm thick safety glass, decorating film glue is coated on base material, using soft mold piece
Material is modeled to decorating film glue, then using 50mj/cm2The ultraviolet light polymerization decorating film glue of energy, tears soft mold
Sheet material, you can obtain the decorating film of embodiment 4.
Embodiment 5
Difference with embodiment 1 is, by soft mold piece timber-used 20000mj/cm2Energy cured.
Embodiment 6
Difference with embodiment 1 is, by soft mold piece timber-used 100000mj/cm2Energy cured.
Embodiment 7
Difference with embodiment 1 is, by soft mold piece timber-used 10000mj/cm2Energy cured.
Embodiment 8
Difference with embodiment 1 is, by soft mold piece timber-used 110000mj/cm2Energy cured.
Embodiment 9
Difference with embodiment 1 is, using 200mj/cm2The ultraviolet light polymerization decorating film glue of energy.
Embodiment 10
Difference with embodiment 1 is, using 10mj/cm2The ultraviolet light polymerization decorating film glue of energy.
Embodiment 11
Difference with embodiment 1 is:
By 20 parts of urethane acrylates EO-2238,5 parts of urethane acrylate 6158B-80,5 parts of Si modification resins
SIU2400,20 parts of monomer EM214,20 parts of monomer EM221,8 parts of initiators 184 mix 30min and obtain master mold glue.
By 20 parts of urethane acrylates EB8210,15 parts of urethane acrylate XP2765,10 parts of pure acrylates
353L, 20 parts of monomers EM39,10 parts of monomer EM214,4 parts of initiators, 184,4 parts of initiator TPO, 3 parts of auxiliary agent B YK-3560 mixing
Stirring 30min obtains decorating film glue.
Embodiment 12
Difference with embodiment 1 is:
By 10 parts of urethane acrylates EO-2238,5 parts of urethane acrylate 6158B-80,20 parts of Si modification resins
SIU2400,20 parts of monomers EM214,10 parts of monomer EM221,2 parts of initiators, 184,2 parts of auxiliary agent B YK-UV3505 mixings
30min obtains master mold glue.
By 40 parts of urethane acrylates EB8210,10 parts of urethane acrylate XP2765,10 parts of pure acrylates
353L, 5 parts of monomer EM39,5 parts of monomer EM214,1 part of initiator, 184,1 part of initiator TPO, 5 parts of auxiliary agent B YK-3560 mixing are stirred
Mix 30min and obtain decorating film glue.
Comparative example 1
Difference with embodiment 1 is, by 20 parts of urethane acrylate EO-2238,20 parts of urethane acrylates
6158B-80,2 parts of Si modification resin SIU2400,20 parts of monomer EM214,20 parts of monomer EM221,4 parts of initiators 184, mixing is stirred
Mix 30min and obtain master mold glue.
Comparative example 2
Difference with embodiment 1 is, by 20 parts of urethane acrylate EO-2238,10 parts of urethane acrylates
6158B-80,25 parts of Si modification resin SIU2400,10 parts of monomer EM214,10 parts of monomer EM221,4 parts of 184,1 part of initiators are helped
Agent BYK-UV3505 mixes 30min and obtains master mold glue.
The overall merit of embodiment 1~12 and the preparation process of comparative example 1~2 and decoration film properties, wherein, a dyne value is used
German arcotest dynes of pen.Line is evenly distributed, and the maximum number dyne pen for not playing any pearl point in 3 seconds is a dyne value survey
Examination, hardness is tested using pencil hardometer according to GB/T 6739-1996, and test result is referring to table 1.
Table 1
Can be seen that what is solidify to form using the UV solidification glue compositions of the application by the comparing of each embodiment and comparative example
The surface dynes value of soft mold changes with the difference of solidification energy, but, less than 30 are can be controlled in, and can be with decoration
The separation of glued membrane is easier.
In addition, the comparing according to embodiment 1,2,3,9 and 10 can be seen that carrying with the solidification energy of decoration glued membrane
Height, the hardness for decorating glued membrane is improved, but UV energy is too high that decorating film glue can be caused to be chemically reacted with decorating film surface, leads
Cause Adhesion enhancement so that the difficult increase of the demoulding, but, still there is clear superiority relative to the demoulding of comparative example.
Ratio according to embodiment 1 and embodiment 5~8 can be seen that the raising of energy is cured with soft mold, and UV is solid
The hardness for changing glue composition is improved, and decoration membrane superficial tissue is unlikely to deform, and on the other hand can migrate auxiliary agent after strong UV curings
To surface, surface smoothness is improved, it is easy to the demoulding.
Meanwhile, the contrast according to embodiment 1 and embodiment 4 can be seen that the auxiliary agent for improving surface due to eliminating, decoration
Film surface dyne value is decreased obviously, therefore can influence to decorate the recoatability of film surface.
As can be seen from the above description, the above embodiments of the present invention realize following technique effect:
The urethane acrylate oligomer of the UV solidification glue compositions comprising above-mentioned consumption and Si modification resin of the application,
Therefore, solidification causes that its surface dynes value is controllable under uv radiation, when being used as soft mold, controls its surface dynes
The difference of the surface dynes value of the decorating film for being worth and solidifying to form is larger, you can realizes the two purpose for being easy to depart from, and then solves
The difficult problem of the soft mold demoulding.
The preferred embodiments of the present invention are the foregoing is only, is not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.It is all within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (11)
1. a kind of UV solidifies glue composition, it is characterised in that in parts by weight, and the UV solidifications glue composition includes:
15~35 parts of urethane acrylate oligomer;
5~20 parts of Si modification resin;
First 30~50 parts of monomer;And
First 2~8 parts of light trigger.
2. UV according to claim 1 solidification glue composition, it is characterised in that the urethane acrylate oligomer is
Double bond 583-1, cyanogen spy EB8465, cyanogen spy EB264, Changxing DR-U025, Changxing 6158B-80, Changxing DR-U029 and Ken Meite
One or more mixture of formation in the group of EO-2238 compositions;It is preferred that the Si modification resin is U.S. source SIU2400, cyanogen
One or more mixture of formation in the group of special EB1360 and Changxing DR-U188C compositions.
3. UV according to claim 1 solidifies glue composition, it is characterised in that first monomer is trimethylolpropane
Triacrylate, tetrahydrofurfuryl acrylate, ethoxyquin trimethylol-propane trimethacrylate and 1,6-HD two
One or more mixture of formation in the group of acrylate composition;It is preferred that first light trigger is α-hydroxyl alkanone class light
Initiator or the oxide-based light trigger of acyl group.
4. UV according to claim 1 solidifies glue composition, it is characterised in that the UV solidifications glue composition also includes small
In the first auxiliary agent equal to 2 weight portions, preferably described first auxiliary agent is organic silicon modified by polyether, more preferably described polyether-modified to have
Machine silicon is selected from one or more mixture of formation in the group of BYK-333, BYK-UV3500 and BYK-UV3505 composition.
5. a kind of soft mold, is formed, it is characterised in that the UV solidification glues use Claims 1-4 using UV solidification adhesive curings
Any one of UV solidification glue composition solidification form.
6. soft mold according to claim 5, it is characterised in that the surface dynes value of the soft mold is less than 30.
7. a kind of printing transferring method, it is characterised in that including:
Step S1, soft mold is prepared using the UV solidification glue compositions any one of Claims 1-4;
Step S2, is provided for making the glue of decorating film on base material;
Step S3, is modeled using the soft mold to glue, obtains modelling glue-line;And
Step S4, the modelling glue-line is solidified, and obtains the decorating film.
8. printing transferring method according to claim 7, it is characterised in that the surface dynes value of the soft mold is less than 30;It is excellent
Selecting the step S1 includes:
The mixture that the UV solidifications glue composition is formed is set on metal die;
Soft base material is set on the mixture, and roll-in is carried out to the soft base material;
The mixture after to the roll-in solidifies, and obtains cured layer;And
The metal die is removed, and UV curings are carried out to the cured layer, obtain the soft mold;
Wherein, the UV energy that preferably described UV curings are used is 20000~100000mj/cm2。
9. printing transferring method according to claim 7, it is characterised in that the surface dynes value of the decorating film is more than 40, excellent
The UV energy for selecting the solidification of the step S4 to use is 10~100mj/cm2;It is preferred that the printing transferring method also includes to the dress
Decorations film carries out the process of thermal maturation.
10. the printing transferring method according to claim 7 or 9, it is characterised in that in parts by weight, the glue includes:45~
70 parts of oligomer, 10~30 parts of second comonomers, 2~8 part of second light trigger and 0~5 part of second auxiliary agent, wherein, it is preferably described
Oligomer is urethane acrylate or pure acrylate;It is preferred that the second comonomer is isobornyl acrylate, Changxing chemistry
What is formed for one or more in 2- HEMAs phosphate, the group of tetrahydrofurfuryl acrylate composition is mixed
Compound;It is preferred that second light trigger is α-hydroxyl alkanone photoinitiator or the oxide-based light trigger of acyl group;It is preferred that described
Second auxiliary agent is polyether-modified acrylate or organosilicon-modified acrylate.
11. printing transferring methods according to claim 7, it is characterised in that the base material is glass.