CN106867374B - Anti-fouling coating and preparation method and application thereof - Google Patents
Anti-fouling coating and preparation method and application thereof Download PDFInfo
- Publication number
- CN106867374B CN106867374B CN201510909441.8A CN201510909441A CN106867374B CN 106867374 B CN106867374 B CN 106867374B CN 201510909441 A CN201510909441 A CN 201510909441A CN 106867374 B CN106867374 B CN 106867374B
- Authority
- CN
- China
- Prior art keywords
- parts
- pollution paint
- substrate
- coating
- pollution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides an anti-fouling coating and a preparation method and application thereof, wherein the anti-fouling coating comprises the following components in parts by weight: 55-60 parts of modified polyester resin, 0.3-0.5 part of hydroxyl modified siloxane, 0.6-0.9 part of titanium dioxide, 6.0-8.0 parts of curing agent, 0.2-0.3 part of flatting agent, 0.1-0.2 part of dispersing agent, 0.1-0.2 part of defoaming agent, 2.5-4.0 parts of pigment, 1.5-2.0 parts of epoxy phosphate, 7.0-8.0 parts of cyclohexanone, 8.0-9.0 parts of propylene glycol methyl ether acetate, 3.0-4.0 parts of ethylene glycol monobutyl ether, 4.0-5.0 parts of n-butyl alcohol and 5.0-7.0 parts of solubilizer. The anti-fouling coating has good hardness and compactness, thereby enhancing the anti-fouling performance of the coating, particularly having obvious anti-fouling effect on greasy dirt sticky substances, and being widely applied to the surfaces of household kitchenware, factory machines and the like.
Description
Technical field
The present invention relates to a kind of coating more particularly to a kind of anti-pollution paint and its preparation method and application.
Background technique
With the development of modern industry, more and more pollution sources are filled in surroundings, for example, dust, greasy dirt etc..
Therefore, people not only only select coating by appearance color, and the pollution resistance of coating itself can be also proposed
Strict requirements.
Existing anti-pollution paint is mostly that the surface of the paint film formed in paint solidification adds Organic fluoride ingredient, and Organic fluoride ingredient is simultaneously
Be not crosslinking in as reactant in the paint film of paint solidification generation, thus paint solidification at paint film internal structure compactness and
Hardness is poor, has still been easy dirt and has penetrated into wherein, antifouling property is not obvious, and cleans decontamination repeatedly to the paint film
Afterwards, paint film is prone to wear, and is further weakened so as to cause pollution resistance.
Summary of the invention
The present invention provides a kind of anti-pollution paint and its preparation method and application, for overcome in the prior art anti-pollution paint it is hard
Spend the unconspicuous defect of antifouling property not enough made.
The present invention provides a kind of anti-pollution paint, includes following component according to parts by weight: 55~60 parts of modified polyester resin, hydroxyl
0.3~0.5 part of base modified siloxane, 0.6~0.9 part of titanium dioxide, 6.0~8.0 parts of curing agent, 0.2~0.3 part of levelling agent,
0.1~0.2 part of dispersing agent, 0.1~0.2 part of defoaming agent, 2.5~4.0 parts of pigment, 1.5~2.0 parts of epoxy phosphate ester, cyclohexanone
7.0~8.0 parts, 8.0~9.0 parts of propylene glycol methyl ether acetate, 3.0~4.0 parts of ethylene glycol monobutyl ether, n-butanol 4.0~5.0
Part, 5.0~7.0 parts of solubilizer.
Anti-pollution paint of the invention is low in cost, does not generate layering and in stable condition, the Rockwell after being prepared into coating
Hardness is up to 3H or more.Wherein, curing agent can selected from diaminocyclohexane, diethylenetriamine, ethylenediamine, dipropylenetriamine,
One of dimethylamine propylamine, m-phenylene diamine (MPD), m-xylene diamine and adjacent chlorobenzene diethylenetriamine are a variety of;Levelling agent is selected from acrylic acid tree
One of rouge, Lauxite and melamine resin are a variety of;Dispersing agent be selected from polyethylene wax, polyethylene glycol 200 and
One of polyethylene glycol 400 is a variety of;Defoaming agent is selected from silicone emulsion, polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxy
One in ethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether and dimethyl silicone polymer
Kind is a variety of.In the present invention combination of modified polyester resin and hydroxyl modification siloxanes can greatly enhance the hardness of coating with
And the adhesive rate to coated substrate, to enhance the antifouling property of coating, anti-pollution paint of the invention is particularly with greasy dirt
Class stickum antifouling effect is obvious, can be widely used in the surface of family's kitchen tools, millwork etc..By the present invention it is above-mentioned at
The anti-pollution paint ingredient that is grouped as is simple, stable system, easy to use, and Rockwell hardness has good anti-up to 3H or more
Dirty performance, and it is formed by coating and is also not easy to fall off from substrate.
Further, the modified polyester resin is silanol-modified alkyd resin.Modified polyester resin used in the present invention
Rouge is that polyester resin is formed through silica modified, therefore can significantly increase the hardness of coating, and the present invention is for Starting Material Polyester
Resin is with no restrictions.
Further, the hydroxyl modification siloxanes is hydroxyl modification dimethyl silicone polymer.Specifically, hydroxyl modification silicon
Oxygen alkane is that α-(2- methyl -2- acryloyl group)-w- methoxypolyethylene glycol is grafted to dimethyl silicone polymer and formed.This hair
Hydroxyl modification siloxanes in bright helps to enhance the compactness of coating, therefore the dirts such as extraneous greasy dirt can effectively be avoided to be embedded in
In coating.
Further, the solubilizer is selected from isophorone and 1, at least one of 3- dimethyl-miaow quinoline ketone.Work as solubilising
Agent is isophorone and 1, and when 3- dimethyl-miaow quinoline ketone mixture, the present invention is not particularly limited ratio between the two.
In a specific embodiment, the pigment include the first pigment and the second pigment, first pigment be 2.0~
3.0 parts, the parts by weight of second pigment are 0.3~0.5 part.Pigment can make to beautify coating appearance, specifically, in order to make to apply
The color of material is more bright-coloured, and pigment can be divided into two classes, and the first kind is the first pigment, can select color of object;Second class
For the second pigment, can select with color similar in color of object, further enhance the vividness of color of object.For example, target
Color is sapphire blue coating, and can select transparent blue pigment is the first pigment, and transparent green pigment is the second pigment.
The present invention also provides a kind of preparation methods of any of the above-described anti-pollution paint, include the following steps: under room temperature,
Be added under stirring into the modified polyester resin hydroxyl modification siloxanes, pigment, titanium dioxide, solubilizer, levelling agent,
Curing agent, defoaming agent, dispersing agent, epoxy phosphate ester, cyclohexanone, propylene glycol methyl ether acetate, ethylene glycol monobutyl ether, n-butanol,
It stirs evenly, the anti-pollution paint is made.
In the above preparation method, preparation temperature is room temperature (15~30 DEG C), and preparation condition is simple and easy, sets without large size
Standby auxiliary, operability is high, not only contributes to form stable anti-pollution paint, and in addition there are be conducive to improve the disengaging of anti-pollution paint
Resistance.The present invention has further consolidated the hardness of anti-pollution paint by the sequence of the special addition of restriction.When manufactured anti-pollution applies
Material wouldn't be in use, it can be directly sealed.
Further, the revolving speed for controlling the stirring is 1000~2000r/min, and mixing time is 5~15min.In order to
The emulsifying effectiveness between component is improved, speed of agitator can be controlled in 1000~2000r/min.Have between each component in the present invention
Apparent intersolubility, therefore need to only stir as 5~15min, each component just can be uniformly mixed the anti-pollution paint for being made of the invention.
The present invention also provides the coating method of any of the above-described anti-pollution paint, the step carried out including following sequence
It is rapid:
1) anti-pollution paint is filtered, the anti-pollution paint of 100~200 mesh is obtained;
2) anti-pollution paint that step 1) obtains is coated to substrate surface, control coating rate is 10~30m/min;
3) substrate after coating is cooled to room temperature in 216~232 DEG C of 70-100s that are heating and curing.
In order to enhance the adhesion of anti-pollution paint and substrate, can select mesh number before coating is the filter of 100~200 mesh
Net is filtered operation to anti-pollution paint, by coating control in the mesh number model, can effectively increase connecing for coating and substrate
Contacting surface product makes the coating after coating be not easy to fall off from substrate.
After filtering, the anti-pollution paint of 100~200 mesh can be coated to substrate surface using roll coater, through inventing the National People's Congress
Quantity research shows that the uniformity coefficient that coating rate control can be guaranteed that coating is contacted with substrate in 10~30m/min is maximum
Change, to meet the antifouling effect of coating substrate.It is worth noting that, substrate can also be pre-processed before coating,
It specifically, can be that 5~10% sodium carbonate and sodium hydroxide cleaning agent aqueous solution as main component are heated to by mass concentration
80 DEG C are cleaned substrate, dry substrate after cleaning and passivator is used to be passivated substrate surface, which can
Form oxidation film in substrate surface, so that substrate stability be made to enhance, corrosion resistance is improved, passivator be mass fraction be 20~
40% trivalent chromium solutions, general trivalent chromium are chromium sulfate, and in addition to this, passivator further includes dicarboxylic acids, water-soluble silication
Object and wetting agent.
After substrate after coating is heating and curing, one layer of scratch resistant protective film can be applied on the surface of substrate, then by substrate
It is cut on slitting slicer to the size needed.
Coating method provided by the invention can further increase anti-pollution paint be formed by coating and substrate be detached from it is anti-
Property, be conducive to anti-pollution paint is bonded with the height of substrate, to make substrate have long-acting antifouling property, even across long-term
Friction, anti-pollution paint are formed by coating and are still able to be evenly distributed on the surface of substrate, will not fall off, digital preservation base
The antifouling property of material extends the service life of coating rear substrate.
Further, the coating thickness for controlling anti-pollution paint on the substrate surface is 10~35 μm.Thickness control is existed
Can guarantee the adhesion of coating and substrate within the scope of this, if necessary to improve thickness, can using coating solidification repeatedly into
Capable processing method, such as target coat can divide 3 progress coating processings with a thickness of 40 μm, first coat 15 μm, add for the first time
It is coated with 15 μm after heat cure, 10 μm are coated with after being heating and curing for the second time, then carries out third time and is heating and curing.
Further, the substrate with a thickness of 0.3~1.2mm.Specifically, the aluminium of 1 system, 3 systems or 5 systems can be selected
Alloy sheets, it also may be preferable for secondary operation plasticity requirements reach T1 and Rockwell hardness is the aluminium flake substrate of H24.
The present invention also provides a kind of insulating pots, including bottle body, pot lid and bottom of the pot, are coated on the bottle body surface above-mentioned
Any anti-pollution paint.
The purpose of the present invention and beneficial effect will be more obvious and easy to understand by description of preferred embodiments.
Specific embodiment
Embodiment 1
The anti-pollution paint of the present embodiment includes following component according to parts by weight: 55 parts of modified polyester resin, hydroxyl modification silicon
0.3 part of oxygen alkane, 0.6 part of titanium dioxide, 6.0 parts of diaminocyclohexane, 0.2 part of Lauxite, 0.2 part of polyethylene wax, emulsify silicon
0.1 part of oil, 4.0 parts of red pigment, 2.0 parts of epoxy phosphate ester, 8.0 parts of cyclohexanone, 9.0 parts of propylene glycol methyl ether acetate, second two
3.0 parts of alcohol monobutyl ether, 4.5 parts of n-butanol, 5.0 parts of isophorone.Modified polyester resin is silanol-modified alkyd resin, and hydroxyl changes
Property siloxanes be hydroxyl modification dimethyl silicone polymer.
After according to above-mentioned composition ingredient, 25 DEG C, by hydroxyl modification siloxanes, red pigment, titanium dioxide, different under stirring
Fluorine that ketone, Lauxite, diaminocyclohexane, silicone emulsion, polyethylene wax, epoxy phosphate ester, cyclohexanone, propylene glycol monomethyl ether vinegar
Acid esters, ethylene glycol monobutyl ether, n-butanol sequentially add in modified polyester resin, in the case where revolving speed is 1500r/min, stir 10min,
Generate anti-pollution paint.
The coating method of the present embodiment anti-pollution paint includes the steps that following sequence carries out:
1) selecting mesh number is that the strainer of 100~200 mesh is filtered the anti-pollution paint of the present embodiment, by after filtering 100
In the anti-pollution paint injection roll coater cutting disc of~200 mesh;
2) it is H24 by the Rockwell hardness after Cleaning and Passivation, is loaded in roll coater with a thickness of the aluminium flake substrate of 0.3mm, control
The rate of roll shaft is 20m/min, and anti-pollution paint is coated on substrate, and coating thickness is 15 μm;
3) substrate after coating is put into in 220 DEG C of high temperature furnace the 80s that is heating and curing, it is cooling, anti-pollution substrate 1# is made.
Hardness test: it uses 3H pencil (Chinese board or Mitsubishi's board), pen core is whittled into cylinder and is ground on 400 mesh sand paper
After flat, (load on pen tip is applied to as 750g, the angle of pencil and horizontal plane is on dedicated pencil hardness tester
45 °), about 1cm long is pushed on the anti-pollution surface substrate 1# with the speed of 1mm/s, draws 5 altogether, then wiped pencil trace with erasing rubber
Completely.By aforesaid operations, the present embodiment anti-pollution substrate surface does not occur rupture and exposes substrate, therefore manufactured in the present embodiment anti-
Dirty coating Rockwell hardness reaches 3H.
Wearability test: being stained with 5% abluent solution on scouring pad, and bear a heavy burden 20N, on the anti-pollution surface substrate 1# with resistance to
Grind instrument with 10 rates per minute rub 10cm, totally 100 times (one be primary back and forth), if coat side do not expose substrate show
As then wearability is good.By aforesaid operations, the present embodiment anti-pollution substrate surface does not occur rupture and exposes substrate, therefore this implementation
The anti-pollution paint wearability of example preparation is good.
Solvent resistance test: alcohol is picked respectively with cotton, n-hexane (two solvents can not be at same position) is soaked in corner
The face bear of 10mm weighs 500 gram forces and is applied to coating surface to rub 30 times/30S repeatedly, if dissolution phenomena does not occur for coat side,
Solvent resistance is good.By aforesaid operations, the present embodiment anti-pollution substrate surface does not occur dissolution phenomena, therefore prepared by the present embodiment
Anti-pollution paint solvent resistance it is good.
Adhesive force test: with cross-cut tester, on the surface anti-pollution substrate 1#, (lattice for marking 10 10 vertical spacing 1mm wide of cross (is drawn
Trace depth and substrate), surface debris is removed, indentation is covered with 3M (250) adhesive plaster, is rubbed back and forth on adhesive tape with mother's finger pulp
(can not have bubble), with test surfaces at an angle of 90 degrees degree rapidly it is vertical by adhesive tape from surface pull-up, same position is tested 3 times, if
It is each test lattice fall off area be no more than lattice area 1/3, and at most only have non-conterminous 3 lattices fall off
Area is no more than the 1/3 of lattice area, then adhesive force is good.By aforesaid operations, the present embodiment anti-pollution substrate surface does not go out
Existing obscission, therefore adhesive force is good for anti-pollution paint manufactured in the present embodiment.
Embodiment 2
The anti-pollution paint of the present embodiment includes following component according to parts by weight: 58 parts of modified polyester resin, hydroxyl modification silicon
0.5 part of oxygen alkane, 0.9 part of titanium dioxide, 7.5 parts of mixture of diethylenetriamine and m-phenylene diamine (MPD), melamine resin
0.25 part, 0.15 part of mixture of polyethylene glycol 200 and polyethylene glycol 400,0.1 part of dimethyl silicone polymer, viridine green 4.0
Part, 1.5 parts of epoxy phosphate ester, 7.5 parts of cyclohexanone, 8.0 parts of propylene glycol methyl ether acetate, 3.5 parts of ethylene glycol monobutyl ether, n-butanol
4.0 parts, 5.5 parts of isophorone.Modified polyester resin is silanol-modified alkyd resin, and hydroxyl modification siloxanes is poly- for hydroxyl modification
Dimethyl siloxane.
After according to above-mentioned composition ingredient, 30 DEG C, by hydroxyl modification siloxanes, viridine green, titanium dioxide, different under stirring
Fluorine your ketone, melamine resin, diethylenetriamine and m-phenylene diamine (MPD) mixture, dimethyl silicone polymer, polyethylene glycol
200 and the mixture of polyethylene glycol 400, epoxy phosphate ester, cyclohexanone, propylene glycol methyl ether acetate, ethylene glycol monobutyl ether, positive fourth
Alcohol sequentially adds in modified polyester resin, in the case where revolving speed is 1000r/min, stirs 15min, generates anti-pollution paint.
The coating method of the present embodiment anti-pollution paint includes the steps that following sequence carries out:
1) selecting mesh number is that the strainer of 100~200 mesh is filtered the anti-pollution paint of the present embodiment, by after filtering 100
In the anti-pollution paint injection roll coater cutting disc of~200 mesh;
2) it is H24 by the Rockwell hardness after Cleaning and Passivation, is loaded in roll coater with a thickness of the aluminium flake substrate of 1.2mm, control
The rate of roll shaft is 10m/min, and anti-pollution paint is coated on substrate, and coating thickness is 10 μm;
3) substrate after coating is put into in 230 DEG C of high temperature furnace the 70s that is heating and curing, it is cooling, anti-pollution substrate 2# is made.
Test method same as Example 1 is taken to carry out hardness, wearability, solvent resistant and attachment to anti-pollution substrate 2#
Power test, test result show that the Rockwell hardness of the anti-pollution paint of the present embodiment reaches 3H, wearability, solvent resistant and adhesive force
It is good.
Embodiment 3
The anti-pollution paint of the present embodiment includes following component according to parts by weight: 60 parts of modified polyester resin, hydroxyl modification silicon
0.35 part of oxygen alkane, 0.7 part of titanium dioxide, 7.0 parts of ethylenediamine, the mixture 0.2 of acrylic resin and melamine resin
Part, 0.2 part of mixture of polyethylene glycol 200 and polyethylene wax, polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxyethylene are poly-
0.1 part of the mixture of oxygen propyl alcohol amidogen ether, 2.5 parts of transparent blue pigment, 0.5 part of transparent green pigment, 2.0 parts of epoxy phosphate ester, ring
7.0 parts of ketone, 8.5 parts of propylene glycol methyl ether acetate, 4.0 parts of ethylene glycol monobutyl ether, 5.0 parts of n-butanol, 1,3- dimethyl-miaow quinoline
7.0 parts of ketone.Modified polyester resin is silanol-modified alkyd resin, and hydroxyl modification siloxanes is hydroxyl modification polydimethylsiloxanes
Alkane.
After according to above-mentioned composition ingredient, 30 DEG C, by hydroxyl modification siloxanes, transparent blue pigment, transparent green face under stirring
Material, titanium dioxide, 1,3- dimethyl-miaow quinoline ketone, ethylenediamine, gather the mixture of acrylic resin and melamine resin
Mixture, polyethylene glycol 200 and the polyethylene wax of ethylene oxide polyoxypropylene pentaerythrite ether and polyoxyethylene polyoxy propyl alcohol amidogen ether
Mixture, epoxy phosphate ester, cyclohexanone, propylene glycol methyl ether acetate, ethylene glycol monobutyl ether, n-butanol sequentially add it is modified poly-
In ester resin, in the case where revolving speed is 2000r/min, 15min is stirred, generates anti-pollution paint.
The coating method of the present embodiment anti-pollution paint includes the steps that following sequence carries out:
1) selecting mesh number is that the strainer of 100~200 mesh is filtered the anti-pollution paint of the present embodiment, by after filtering 100
In the anti-pollution paint injection roll coater cutting disc of~200 mesh;
2) it is H24 by the Rockwell hardness after Cleaning and Passivation, is loaded in roll coater with a thickness of the aluminium flake substrate of 0.4mm, control
The rate of roll shaft is 30m/min, and anti-pollution paint is coated on substrate, and coating thickness is 20 μm;
3) substrate after coating is put into in 225 DEG C of high temperature furnace the 85s that is heating and curing, it is cooling, anti-pollution substrate 3# is made.
Test method same as Example 1 is taken to carry out hardness, wearability, solvent resistant and attachment to anti-pollution substrate 3#
Power test, test result show that the Rockwell hardness of the anti-pollution paint of the present embodiment reaches 3H, wearability, solvent resistant and adhesive force
It is good.
Embodiment 4
The anti-pollution paint of the present embodiment includes following component according to parts by weight: 58 parts of modified polyester resin, hydroxyl modification silicon
0.5 part of oxygen alkane, 0.6 part of titanium dioxide, 8.0 parts of mixture of dipropylenetriamine and dimethylamine propylamine, acrylic resin 0.25
Part .1 parts of Macrogol 4000,0.17 part of polyoxyethylene polyoxypropylene glycerin ether, 3.0 parts of transparent blue pigment, transparent green pigment
0.5 part, 1.5 parts of epoxy phosphate ester, 7.0 parts of cyclohexanone, 8.0 parts of propylene glycol methyl ether acetate, 3.0 parts of ethylene glycol monobutyl ether, just
4.5 parts of butanol, 6.0 parts of mixture of 1,3- dimethyl-miaow quinoline ketone and isophorone.Modified polyester resin is silanol-modified alkyd
Resin, hydroxyl modification siloxanes are hydroxyl modification dimethyl silicone polymer.
After according to above-mentioned composition ingredient, 25 DEG C, by hydroxyl modification siloxanes, transparent blue pigment, transparent green face under stirring
Material, titanium dioxide, 1,3- dimethyl-miaow quinoline ketone and isophorone mixture, acrylic resin, dipropylenetriamine and dimethylamine
The mixture of base propylamine, polyoxyethylene polyoxypropylene glycerin ether, polyethylene glycol 400, epoxy phosphate ester, cyclohexanone, propylene glycol first
Ether acetate, ethylene glycol monobutyl ether, n-butanol sequentially add in modified polyester resin, in the case where revolving speed is 1800r/min, stirring
15min generates anti-pollution paint.
The coating method of the present embodiment anti-pollution paint includes the steps that following sequence carries out:
1) selecting mesh number is that the strainer of 100~200 mesh is filtered the anti-pollution paint of the present embodiment, by after filtering 100
In the anti-pollution paint injection roll coater cutting disc of~200 mesh;
2) it is H24 by the Rockwell hardness after Cleaning and Passivation, is loaded in roll coater with a thickness of the aluminium flake substrate of 1.2mm, control
The rate of roll shaft is 30m/min, and anti-pollution paint is coated on substrate, and coating thickness is 35 μm;
3) substrate after coating is put into in 225 DEG C of high temperature furnace the 100s that is heating and curing, it is cooling, anti-pollution substrate 4# is made.
Test method same as Example 1 is taken to carry out hardness, wearability, solvent resistant and attachment to anti-pollution substrate 4#
Power test, test result show that the Rockwell hardness of the anti-pollution paint of the present embodiment reaches 3H, wearability, solvent resistant and adhesive force
It is good.
Test example
Gone out at two on the anti-pollution substrate surface of embodiment 1# using specific " CPM-150 " number signature pen picture and is handed in length and breadth
Three wrong cross three are perpendicular, and after picture, wherein taking operation a at one, another place takes operation b:
A: being wiped 10 times using clean cotton back and forth immediately, repeats 10 periods;
B: after person's handwriting air-dries completely, using the tooling cubing of 10N power, (tip wraps up single layer cleaning cotton and connects with person's handwriting
Touching) it wipes 10 times back and forth, repeat 10 periods.
Embodiment 1# anti-pollution substrate is examined to be whether surface has person's handwriting residual.
After above-mentioned detection, equal noresidue at embodiment 1# anti-pollution substrate surface two.
Above-mentioned same operating method is taken, same detection is made to the anti-pollution substrate of embodiment 2#~4#, as a result table
It is bright, equal noresidue at embodiment 2#~4# anti-pollution substrate surface two.
Above-mentioned test result shows: anti-pollution paint antifouling effect of the invention is excellent.
Above-mentioned anti-pollution paint preferably can be used on household appliances, for example people's everyday exposure is more, surface is easy
The kettle or electromagnetic oven of contamination.By taking kettle as an example, kettle includes bottle body, pot lid and bottom of the pot, and anti-pollution paint is coated in above-mentioned bottle body
Surface.
Finally, it should be noted that the above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent
Pipe present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: its according to
So be possible to modify the technical solutions described in the foregoing embodiments, or to some or all of the technical features into
Row equivalent replacement;And these are modified or replaceed, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (10)
1. a kind of anti-pollution paint, which is characterized in that according to parts by weight include following component: 55~60 parts of modified polyester resin, hydroxyl
0.3~0.5 part of base modified siloxane, 0.6~0.9 part of titanium dioxide, 6.0~8.0 parts of curing agent, 0.2~0.3 part of levelling agent,
0.1~0.2 part of dispersing agent, 0.1~0.2 part of defoaming agent, 2.5~4.0 parts of pigment, 1.5~2.0 parts of epoxy phosphate ester, cyclohexanone
7.0~8.0 parts, 8.0~9.0 parts of propylene glycol methyl ether acetate, 3.0~4.0 parts of ethylene glycol monobutyl ether, n-butanol 4.0~5.0
Part, 5.0~7.0 parts of solubilizer;
The pigment is selected from one of the mixture of transparent blue pigment and transparent green pigment, red pigment, viridine green;
The hydroxyl modification siloxanes is hydroxyl modification dimethyl silicone polymer, and the hydroxyl modification dimethyl silicone polymer is logical
It crosses and α-(2- methyl -2- acryloyl group)-ω-methoxypolyethylene glycol is grafted to dimethyl silicone polymer and obtained.
2. anti-pollution paint according to claim 1, which is characterized in that the modified polyester resin is silanol-modified alkyd tree
Rouge.
3. anti-pollution paint according to claim 1, which is characterized in that the solubilizer is selected from isophorone and 1,3- diformazan
At least one of base-imidazolone.
4. the preparation method of any anti-pollution paint of claims 1 to 3, which comprises the steps of:
Under room temperature, be added under stiring into the modified polyester resin hydroxyl modification siloxanes, pigment, titanium dioxide,
Solubilizer, levelling agent, curing agent, defoaming agent, dispersing agent, epoxy phosphate ester, cyclohexanone, propylene glycol methyl ether acetate, ethylene glycol
Monobutyl ether, n-butanol, stir evenly, and the anti-pollution paint is made.
5. the preparation method according to claim 4, which is characterized in that the revolving speed for controlling the stirring is 1000~2000r/
Min, mixing time are 5~15min.
6. the coating method of any anti-pollution paint of claims 1 to 3, which is characterized in that carried out including following sequence
Step:
1) anti-pollution paint is filtered, the anti-pollution paint of 100~200 mesh is obtained;
2) anti-pollution paint that step 1) obtains is coated to substrate surface, control coating rate is 10~30m/min;
3) substrate after coating is cooled to room temperature in 216~232 DEG C of 70~100s that are heating and curing.
7. coating method according to claim 6, which is characterized in that control the coating of anti-pollution paint on the substrate surface
With a thickness of 10~35 μm.
8. coating method according to claim 6, which is characterized in that the substrate with a thickness of 0.3~1.2mm.
9. coating method according to claim 6, which is characterized in that the substrate is aluminium flake substrate.
10. a kind of insulating pot, including bottle body, pot lid and bottom of the pot, it is characterised in that: be coated with claim on the bottle body surface
1~3 any anti-pollution paint.