CN106865536A - A kind of method and device for preparing Graphene - Google Patents
A kind of method and device for preparing Graphene Download PDFInfo
- Publication number
- CN106865536A CN106865536A CN201710212528.9A CN201710212528A CN106865536A CN 106865536 A CN106865536 A CN 106865536A CN 201710212528 A CN201710212528 A CN 201710212528A CN 106865536 A CN106865536 A CN 106865536A
- Authority
- CN
- China
- Prior art keywords
- conductive metal
- graphene
- reaction vessel
- expanded graphite
- weak acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of device for preparing Graphene, described device includes reaction vessel, expanded graphite cake, conductive metal mesh, conductive metal sheet, weak acid electrolyte and power supply, weak acid electrolyte is full of in reaction vessel, the outer surface of expanded graphite cake is welded with conductive metal mesh.The present invention mainly make use of the principle of electrolysis, and expanded graphite as one end of conductive electrode is electrolysed so that expanded graphite is successively peeled off in the electrolytic solution in access circuit, then filters cleaning, drying and has just obtained required Graphene.Invention mainly make use of the principle of electrolysis, and the proportion that single-layer graphene is accounted for is very big.
Description
Technical field
The invention belongs to technical field of graphene preparation, and in particular to a kind of method that utilization expanded graphite prepares Graphene
And device.
Background technology
Native graphite alkene is the two dimensional crystal for being stripped out from graphite material, being made up of carbon atom.Graphene is both
Most thin material, is also most tough material, 200 times more taller than best steel of fracture strength.It has well again simultaneously
Elasticity, stretch range can reach the 20% of own dimensions.It is that current nature is most thin, intensity highest material, Graphene mesh
Preceding most potential application is the substitute for turning into silicon, manufactures ultra micro transistor npn npn, for producing the supercomputer in future.With
Graphene replaces silicon, and the speed of service of computer processor will hundreds times soon.In addition, Graphene is almost fully transparent,
Only absorb 2.3% light.On the other hand, it is very fine and close, even the gas atom (helium atom) of minimum cannot also be penetrated.This
A little features cause that it is highly suitable as the raw material of transparent electron product, such as transparent touch display screen, luminescent screen and solar energy
Cell panel.As the most strong a kind of novel nano-material of the most thin, maximum intensity, electrical and thermal conductivity performance that have now been found that, Graphene
It is referred to as " dark fund ", is " king of new material ", scientist even foretells that Graphene " will thoroughly change 21 century ".
In the prior art, the synthetic method of Graphene mainly has two kinds：Mechanical means and chemical method.Mechanical means includes
The method of mechanical phonograph recorder separation, epitaxy method and heating SiC, it is chemical reduction method and chemical dissociation method that chemical method is mainly.
Most common is micromechanics partition method, and directly graphene platelet is cut down from larger crystal.2004
Novoselovt etc. has prepared single-layer graphene in this way, it is possible to the stable existence under external environment.It is prepared by typical case
Method is that the pyrolytic graphite of or introducing defect expanded with another material is rubbed, and the surface of body phase graphite can produce wadding
The crystal of sheet, the Graphene containing individual layer in the crystal of these flocculus shapes.But have the disadvantage that this method is using the graphite table that rubs
The thin slice that face obtains filters out the graphene platelet of individual layer, and its size is difficult to control, it is impossible to which reliably factory length is supplied enough
Graphite flake sample.
Epitaxy method is to go out Graphene using growth substrate atomic structure " kind ", allows carbon atom to be oozed at 1150 DEG C first
Enter ruthenium, then cool down, after being cooled to 850 DEG C, a large amount of carbon atoms for absorbing before will float to ruthenium surface, the individual layer of lens shape
Carbon atom " isolated island " be covered with whole stromal surface, it is final they can grow up to a complete layer graphene.Ground floor is covered
After 80%, the second layer starts growth.The Graphene of bottom can produce strong reciprocation with ruthenium, and after the second layer just almost with
Ruthenium is kept completely separate, only remaining light current coupling, and the single-layer graphene thin slice performance for obtaining is satisfactory.But produce in this way
Graphene platelet it is often in uneven thickness, and bonding between Graphene and matrix can influence the characteristic of carbon-coating.
Chemical reduction method is to mix graphite oxide and water with the ratio of 1mg/mL, with supersonic oscillations to the clear nothing of solution
Particulate material, adds appropriate hydrazine in 100 DEG C of backflow 24h, produces black particle shape precipitation, filtering, drying Graphene.Change
It is the method that graphite oxide is prepared Graphene by the method for thermal reduction, the oxygen-containing functional group of graphite oxide interlayer to learn dissociation method
React at a certain temperature.
Wherein, electrolysis be it is the most frequently used prepare the method for Graphene, but have that Graphene yield is too low, purity is not high
Problem.
The content of the invention
The invention aims in solving existing graphene preparation technology, Graphene yield is too low, and purity is not high
Problem, and then a kind of device and method for preparing Graphene is provided.
The technical scheme is that：The present invention includes a kind of device for preparing above-mentioned Graphene, including reaction vessel 1,
Expanded graphite cake 2, conductive metal mesh 3, conductive metal sheet 4, weak acid electrolyte 5 and power supply 6, conductive metal sheet 4 are inlaid in reaction
Weak acid electrolyte 5 is full of in the bottom of container 1, reaction vessel 1, expanded graphite cake 2 is placed in the top of reaction vessel 1, expands stone
The outer surface of black cake 2 is welded with conductive metal mesh 3, and power supply 6 is connected by wire with conductive metal mesh 3 and conductive metal sheet 4 respectively.
Further, connected with suspension bracket between the expanded graphite cake 2 and reaction vessel 1.
Further, glue sticking is used between the conductive metal sheet 4 and reaction vessel 1.
Further, weak acid electrolyte 5 is the weak acid such as dilute oxalic acid or dilute sulfuric acid.
Further, the material of reaction vessel 1 is non-conductive.
Further, the material of conductive metal mesh 3 and conductive metal sheet 4 is copper, iron or aluminium.
The present invention relates to a kind of preparation method of Graphene, comprise the following steps：Conductive metal sheet 4 is inlaid in into reaction to hold
The bottom of device 1, then weak acid electrolyte 5 is full of reaction vessel 1, then expanded graphite cake 2 is inlaid in the top of reaction vessel 1
Portion, power supply 6 is connected by wire with conductive metal mesh 3 and conductive metal sheet 4 respectively, turns on the power 6 switches to expanded graphite cake 2
It is electrolysed, is removed fluid sealant, ultrasonication is carried out after the mixture of Graphene and electrolyte is taken out, filtering drying is obtained final product
To required Graphene.
Further, the voltage of power supply 6 is preferably 8 to 30 volts.
The present invention has the advantages that：The present invention mainly make use of the principle of electrolysis, using expanded graphite as conduction
One end of electrode, is electrolysed so that expanded graphite is successively peeled off in the electrolytic solution, carries out ultrasonication in access electric current,
Filtering drying, that is, in the Graphene for obtaining, the proportion that single-layer graphene is accounted for is very big.This kind of method is simple and easy to apply, to device requirement
It is low, it is not necessary to which that complicated operational means can be completed, and be worthy to be popularized.
Brief description of the drawings
Fig. 1 is the schematic diagram of the device that electrolysis of the present invention prepares Graphene；
Fig. 2 is the top view of the conductive metal mesh of the device that electrolysis of the present invention prepares Graphene.
Specific embodiment
With reference to specific embodiment, the present invention will be further described：
With reference to Fig. 1 and Fig. 2 explanation present embodiments, present embodiment includes reaction vessel 1, expanded graphite cake 2, leads
Electric metal net 3, conductive metal sheet 4, weak acid electrolyte 5 and power supply 6, conductive metal sheet 4 are inlaid in the bottom of reaction vessel 1, instead
Answer full of weak acid electrolyte 5 in container 1, expanded graphite cake 2 is placed in the top of reaction vessel 1, the outer surface weldering of expanded graphite cake 2
There is conductive metal mesh 3, power supply 6 is connected by wire with conductive metal mesh 3 and conductive metal sheet 4 respectively.
Connected with suspension bracket between expanded graphite cake 2 and reaction vessel 1, with gluing between conductive metal sheet 4 and reaction vessel 1
Connect.So it is designed as increasing the sealing effectiveness of reaction vessel 1, and is easy to be repeatedly opened and takes liquid.
Weak acid electrolyte 5 is preferably dilute oxalic acid or dilute sulfuric acid.The material of reaction vessel 1 is non-conductive, it may be preferred to glass
Container.The common cheap metals such as the preferred copper of material of conductive metal mesh 3 and conductive metal sheet 4, iron or aluminium.The voltage of power supply 6
Preferably 8 to 30 volts.
The preparation method of expanded graphite cake 2 is as follows：
Natural flake graphite is taken, in the mixed acid solution of sulfuric acid and nitric acid is added under being stirred continuously, Gao Meng is added
Sour potassium, controls uniform temperature, then adds ferric trichloride, stirs, and after reaction certain hour, dilute alkaline soln is used in centrifugation
Embathe, be washed to acidity, expanded graphite is obtained by drying carries out high temperature puffing again after dehydration.Need that stone will be expanded further according to device
It is that can be used into different shape that ink is tightly compacted.
The invention further relates to a kind of preparation method of Graphene, comprise the following steps：Conductive metal sheet 4 is inlaid in reaction
The bottom of container 1, then weak acid electrolyte 5 is full of reaction vessel 1, then expanded graphite cake 2 is inlaid in the top of reaction vessel 1
Portion, power supply 6 is connected by wire with conductive metal mesh 3 and conductive metal sheet 4 respectively, turns on the power 6 switches to expanded graphite cake 2
It is electrolysed, is removed fluid sealant, ultrasonication is carried out after the mixture of Graphene and electrolyte is taken out, filtering drying is obtained final product
To required Graphene.
The principle of present embodiment：Power supply 6 leads to 8 to 10 volt voltages, and conductive metal mesh 3 can be electrolysed expanded graphite cake after being powered
2, Graphene is peeled off into, the mixture of weak acid electrolyte 5 and Graphene is poured out from reaction vessel 1, using filter
Mixture is filtered, the Graphene for leaching is cleaned using Ultrasound Instrument, filtered after ultrasonication, using dryer pair
Graphene is dried, and obtains required Graphene.
The above is only presently preferred embodiments of the present invention, is not intended to limit embodiment of the present invention, and this area is general
Logical technical staff's central scope of the invention and spirit, can very easily carry out corresponding flexible or modification, therefore originally
The protection domain of invention should be defined by the protection domain required by claims.
Claims (9)
1. a kind of device for preparing Graphene, it is characterised in that described device include reaction vessel (1), expanded graphite cake (2),
Conductive metal mesh (3), conductive metal sheet (4), weak acid electrolyte (5) and power supply (6), conductive metal sheet (4) is inlaid in reaction to be held
Weak acid electrolyte (5) is full of in the bottom of device (1), reaction vessel (1), expanded graphite cake (2) is placed in the upper of reaction vessel (1)
Side, the outer surface of expanded graphite cake (2) is welded with conductive metal mesh (3), and power supply (6) is respectively by wire and conductive metal mesh (3)
Connected with conductive metal sheet (4).
2. a kind of device for preparing Graphene according to claim 1, it is characterised in that the expanded graphite cake (2) is used
Suspension bracket is placed in reaction vessel (1) top.
3. a kind of device for preparing Graphene according to claim 1, it is characterised in that：The conductive metal sheet (4) with
Reaction vessel uses glue sticking between (1).
4. a kind of device for preparing Graphene according to claim 1, it is characterised in that weak acid electrolyte (5) is dilute grass
The weak acid such as acid or dilute sulfuric acid.
5. a kind of device for preparing Graphene according to claim 1, it is characterised in that the material of reaction vessel (1) is not
It is conductive.
6. a kind of device for preparing Graphene according to claim 1, it is characterised in that conductive metal mesh (3) and conduction
The material of metallic plate (4) is copper, iron or aluminium.
7. a kind of method that any one of utilization the claims 1 to 6 prepares Graphene, it is characterised in that comprise the following steps：
Conductive metal sheet (4) is inlaid in the bottom of reaction vessel (1), then by weak acid electrolyte (5) full of reaction vessel (1), then
Expanded graphite cake (2) is inlaid in the top of reaction vessel (1), power supply (6) by wire and conductive metal mesh (3) and is led respectively
Electric metal plate (4) connect, turn on the power (6) switch expanded graphite cake (2) is electrolysed, fully electrolysis after, by Graphene with
Ultrasonication after the mixture taking-up of electrolyte, cleans filtering drying, that is, obtain required Graphene.
8. the method that a kind of electrolysis according to claim 7 prepares Graphene, it is characterised in that weak acid electrolyte (5)
It is the weak acid such as dilute oxalic acid or dilute sulfuric acid.
9. the method that a kind of electrolysis according to claim 8 prepares Graphene, it is characterised in that the voltage of power supply (6)
It is 8 to 30 volts.