CN106836624A - A kind of prefabricated assembled Ligh compound insulating board wall mounting process - Google Patents
A kind of prefabricated assembled Ligh compound insulating board wall mounting process Download PDFInfo
- Publication number
- CN106836624A CN106836624A CN201710020844.6A CN201710020844A CN106836624A CN 106836624 A CN106836624 A CN 106836624A CN 201710020844 A CN201710020844 A CN 201710020844A CN 106836624 A CN106836624 A CN 106836624A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- parts
- insulating board
- prefabricated assembled
- mounting process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of prefabricated assembled Ligh compound insulating board wall mounting process, for partition wall, filling wall, the not nonload bearing element such as accessible roof.Mainly including the first sheet material, the second sheet material, reinforced mesh, cystosepiment, split bolt, reserved groove etc., sheet material is formulated according to a certain percentage using cement, incinerator ash, sand, gypsum, flyash and water, inside sets one layer of reinforced mesh.Cystosepiment is arranged in the middle of two sheet materials by after fire prevention treatment, and is carried out drawknot by split bolt and fixed, and groove is reserved on the sheet material at split bolt two ends, and brushing grease, is finally sealed with mortar after installing.Rational in infrastructure, low cost of the invention, resource is recycled, light weight, and construction hoisting is quick, factorial praluction, good heat insulating, ensures that plate surface is smooth using reserved groove measure, and good concealment does not influence structure overall appearance.
Description
Technical field
The present invention relates to a kind of prefabricated thermal insulation board wall, and in particular to a kind of prefabricated assembled Ligh compound insulating board wall is installed
Technique.
Background technology
Insulation board wall is wide in building engineering field application, and the heat preservation plate material type for using at present is especially more, Duo Shuoshi
Heat preservation construction is carried out after the construction of engineering secondary structure is finished, cost is too high, the construction occupancy duration of a project, the labour cost for causing,
Machinery cost etc. is costly.
The chemical analysis of city garbage burning ash shows:The main component of bottom ash be SiO2, Al2O3, CaO, Fe2O3 and
The charcoal of uncombusted, wherein main composition is SiO2=34.32%~49.53%, CaO=15.66%~35.23%, Al2O3=8.59%
~13.54%, Fe2O3=5.28%~10.23%;Secondly Na2O, K2O, MgO etc. are also contained.In the U.S. and Holland, bottom ash
The part that (or mixed ash) is used as in concrete substitutes aggregate.Most commonly by bottom ash, water, cement and other aggregates
Concrete brick is made by a certain percentage, and correlation technique is in the existing commercial applications in the U.S..
The present invention using city garbage burning ash as main admixture be used for composite insulating board in, reduce engineering into
This, realizes batch production centralized production, and site machineryization lifting, speed of application quickly, meets current industry policy guidance, energy-conservation
Emission reduction, prefabricated assembled industrialization will be the directions of China's future development.
The content of the invention
Goal of the invention:The invention aims to solve deficiency of the prior art, there is provided a kind of reasonable in design,
Low cost, resource is recycled, light weight, and construction hoisting is quick, and factorial praluction, good heat insulating is arranged using reserved groove
Apply and ensure that plate surface is smooth, good concealment does not influence a kind of prefabricated assembled Ligh compound insulating board of structure overall appearance
Wall and its mounting process.
Technical scheme:A kind of prefabricated assembled Ligh compound insulating board wall mounting process of the present invention, including it is as follows
Step:
(1)The making of sheet material:Sheet material is matched somebody with somebody according to a certain percentage using cement, incinerator ash, sand, gypsum, flyash and water
System is formed, and inside sets one layer of reinforced mesh;The mixing of concrete controls to require in strict accordance with match ratio, incinerator ash is weighed and is missed
Difference cannot be greater than 8%, and reinforced mesh is used and is not less than the@200 of Φ 6, and carries out location measure, can not significantly be shifted during cast, in advance
Staying the size of groove, position should meet design requirement, and last board dimension, flatness, vertical error are no more than 1%;
(2)Cystosepiment treatment:Cystosepiment belongs to combustible material, for fire prevention needs, 1-2 should be brushed all over fireproof coating, in case in fire
In the case of, high temperature destroys internal structure earlier;
(3)Split bolt is selected:Split bolt should select the high-strength bolt for being not less than M8;
(4)Sheet material drills:Bolt hole should be greater than bolt diameter 2-3mm, and spacing should be not more than 1000mm to bolt hole in length and breadth;
(5)Groove treatment, sealing of hole:The brushing grease in groove in time is answered after bolt penetration hole, and is sealed using the mortar for being not less than M15
Hole;
(6)Transport, lifting.
Further, the step(1)The ratio of cement, incinerator ash, sand, gypsum, flyash and water is 1:
1.56:3.07:0.16:1.33:0.46, also can suitably be adjusted according to actual conditions.
Further, the step(2)Fireproof coating is made of the component of following mass fraction:
18 parts~30 parts of asphalt mixtures modified by epoxy resin, 15 parts~25 parts of cellulose ether, 2 parts~8 parts of expanded vermiculite, 3 parts of magnesium hydroxide~6 parts, silicon
1 part~8 parts of sour sodium, 5 parts~10 parts of dimethicone, 25 parts~45 parts of isobutyl ketone, 1 part~6 parts of chlorinated paraffin.
Further, the step(2)Fireproof coating is made of the component of following mass fraction:
24 parts of epoxy resin, 20 parts of cellulose ether, 2 parts of expanded vermiculite, 4 parts of magnesium hydroxide, 5 parts of sodium metasilicate, dimethicone 7
Part, 35 parts of isobutyl ketone, 1 part of chlorinated paraffin.
The structure that a kind of above-mentioned prefabricated assembled Ligh compound insulating board wall is installed includes the first sheet material, the second sheet material, steel
Muscle mesh sheet, cystosepiment, split bolt and reserved groove, first sheet material and the second sheet material are respectively provided at cystosepiment both sides, institute
State the first sheet material, the second sheet material and cystosepiment to be fixedly clamped by split bolt, also set in first sheet material and the second sheet material
There is reinforced mesh, first sheet material and the second sheet material outside are additionally provided with multiple reserved grooves passed through for split bolt.
Further, bolt hole is provided with the reserved groove, spacing is not more than 1000mm to bolt hole in length and breadth.
Further, split bolt both ends extension elongation 1-2mm smaller than reserved depth of groove.
Further, the thickness of the cystosepiment more than the first sheet material or the second sheet material thickness, first sheet material with
The thickness of the second sheet material is equal or unequal.
Further, bar diameter is not less than 6mm in the reinforced mesh.
Beneficial effect:Rational in infrastructure, low cost of the invention, resource is recycled, light weight, and construction hoisting is quick, factory
Metaplasia is produced, good heat insulating, ensures that plate surface is smooth using reserved groove measure, and good concealment does not influence structure integrated beauty
See.
Brief description of the drawings
Fig. 1 is the structural representation of present invention insulation board wall.
Specific embodiment
The structure that a kind of prefabricated assembled Ligh compound insulating board wall as shown in Figure 1 is installed includes the first sheet material 1, second
Sheet material 2, reinforced mesh 3, cystosepiment 4, split bolt 5 and reserved groove 6, the sheet material 2 of first sheet material 1 and second are respectively provided at
The both sides of cystosepiment 4, first sheet material 1, the second sheet material 2 are fixedly clamped with cystosepiment 4 by split bolt 5, first plate
Reinforced mesh 3 is additionally provided with the sheet material 2 of material 1 and second, the outside of 1 and second sheet material of the first sheet material 2 is additionally provided with multiple for drawing
The reserved groove 6 that bolt 5 is passed through.
Further, bolt hole is provided with the reserved groove 6, spacing is not more than 1000mm to bolt hole in length and breadth.
Further, the both ends extension elongation of the split bolt 5 is than the small 1-2mm of the depth of reserved groove 6.
Further, the thickness of the cystosepiment 4 is more than the first sheet material 1 or the thickness of the second sheet material 2, first sheet material
1 is equal or unequal with the thickness of the second sheet material 2.
Further, bar diameter is not less than 6mm in the reinforced mesh.
A kind of above-mentioned prefabricated assembled Ligh compound insulating board wall mounting process, comprises the following steps:
(1)The making of sheet material:Sheet material is matched somebody with somebody according to a certain percentage using cement, incinerator ash, sand, gypsum, flyash and water
System is formed, and inside sets one layer of reinforced mesh;The mixing of concrete controls to require in strict accordance with match ratio, incinerator ash is weighed and is missed
Difference cannot be greater than 8%, and reinforced mesh is used and is not less than the@200 of Φ 6, and carries out location measure, can not significantly be shifted during cast, in advance
Staying the size of groove, position should meet design requirement, and last board dimension, flatness, vertical error are no more than 1%;
(2)Cystosepiment treatment:Cystosepiment belongs to combustible material, for fire prevention needs, 1-2 should be brushed all over fireproof coating, in case in fire
In the case of, high temperature destroys internal structure earlier;
(3)Split bolt is selected:Split bolt should select the high-strength bolt for being not less than M8;
(4)Sheet material drills:Bolt hole should be greater than bolt diameter 2-3mm, and spacing should be not more than 1000mm to bolt hole in length and breadth;
(5)Groove treatment, sealing of hole:Bolt penetration hole post-sampling nut 7 is fixed and answers the brushing grease in groove in time, and using not
Mortar sealing of hole less than M15;
(6)Transport, lifting.
Further, the step(1)The ratio of cement, incinerator ash, sand, gypsum, flyash and water is 1:
1.56:3.07:0.16:1.33:0.46.
Further, the step(2)Fireproof coating is made of the component of following mass fraction:
18 parts~30 parts of asphalt mixtures modified by epoxy resin, 15 parts~25 parts of cellulose ether, 2 parts~8 parts of expanded vermiculite, 3 parts of magnesium hydroxide~6 parts, silicon
1 part~8 parts of sour sodium, 5 parts~10 parts of dimethicone, 25 parts~45 parts of isobutyl ketone, 1 part~6 parts of chlorinated paraffin.
Further, the step(2)Fireproof coating is made of the component of following mass fraction:
24 parts of epoxy resin, 20 parts of cellulose ether, 2 parts of expanded vermiculite, 4 parts of magnesium hydroxide, 5 parts of sodium metasilicate, dimethicone 7
Part, 35 parts of isobutyl ketone, 1 part of chlorinated paraffin.
The above, is only presently preferred embodiments of the present invention, and any formal limitation is not made to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, without departing from the scope of the present invention, when making a little change or modification using the technology contents of the disclosure above
It is the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, according to technical spirit of the invention
Any simple modification, equivalent variations and the modification made to above example, still fall within the range of technical solution of the present invention.
Claims (9)
1. a kind of prefabricated assembled Ligh compound insulating board wall mounting process, it is characterised in that:Comprise the following steps:
(1)The making of sheet material:Sheet material is matched somebody with somebody according to a certain percentage using cement, incinerator ash, sand, gypsum, flyash and water
System is formed, and inside sets one layer of reinforced mesh;The mixing of concrete controls to require in strict accordance with match ratio, incinerator ash is weighed and is missed
Difference cannot be greater than 8%, and reinforced mesh is used and is not less than the@200 of Φ 6, and carries out location measure, can not significantly be shifted during cast, in advance
Staying the size of groove, position should meet design requirement, and last board dimension, flatness, vertical error are no more than 1%;
(2)Cystosepiment treatment:Cystosepiment belongs to combustible material, for fire prevention needs, 1-2 should be brushed all over fireproof coating, in case in fire
In the case of, high temperature destroys internal structure earlier;
(3)Split bolt is selected:Split bolt should select the high-strength bolt for being not less than M8;
(4)Sheet material drills:Bolt hole should be greater than bolt diameter 2-3mm, and spacing should be not more than 1000mm to bolt hole in length and breadth;
(5)Groove treatment, sealing of hole:The brushing grease in groove in time is answered after bolt penetration hole, and is sealed using the mortar for being not less than M15
Hole;
(6)Transport, lifting.
2. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 1, it is characterised in that:Institute
State step(1)The ratio of cement, incinerator ash, sand, gypsum, flyash and water is 1:1.56:3.07:0.16:1.33:
0.46, also can suitably be adjusted according to actual conditions.
3. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 1, it is characterised in that:Institute
State step(2)Fireproof coating is made of the component of following mass fraction:
18 parts~30 parts of asphalt mixtures modified by epoxy resin, 15 parts~25 parts of cellulose ether, 2 parts~8 parts of expanded vermiculite, 3 parts of magnesium hydroxide~6 parts, silicon
1 part~8 parts of sour sodium, 5 parts~10 parts of dimethicone, 25 parts~45 parts of isobutyl ketone, 1 part~6 parts of chlorinated paraffin.
4. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 3, it is characterised in that:Institute
State step(2)Fireproof coating is made of the component of following mass fraction:
24 parts of epoxy resin, 20 parts of cellulose ether, 2 parts of expanded vermiculite, 4 parts of magnesium hydroxide, 5 parts of sodium metasilicate, dimethicone 7
Part, 35 parts of isobutyl ketone, 1 part of chlorinated paraffin.
5. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 1, it is characterised in that:Institute
Stating a kind of structure of prefabricated assembled Ligh compound insulating board wall installation includes the first sheet material(1), the second sheet material(2), bar-mat reinforcement
Piece(3), cystosepiment(4), split bolt(5)With reserved groove(6), first sheet material(1)With the second sheet material(2)It is respectively provided at
Cystosepiment(4)Both sides, first sheet material(1), the second sheet material(2)With cystosepiment(4)By split bolt(5)It is fixedly clamped,
First sheet material(1)With the second sheet material(2)Inside it is additionally provided with reinforced mesh(3), first sheet material(1)With the second sheet material(2)
Outside is additionally provided with multiple and supplies split bolt(5)The reserved groove for passing through(6).
6. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 5, it is characterised in that:Institute
State reserved groove(6)Bolt hole is inside provided with, spacing is not more than 1000mm to bolt hole in length and breadth.
7. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 5, it is characterised in that:Institute
State split bolt(5)Both ends extension elongation is than reserved groove(6)The small 1-2mm of depth.
8. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 5, it is characterised in that:Institute
State cystosepiment(4)Thickness be more than the first sheet material(1)Or second sheet material(2)Thickness, first sheet material(1)With the second sheet material
(2)Thickness it is equal or unequal.
9. a kind of prefabricated assembled Ligh compound insulating board wall mounting process according to claim 5, it is characterised in that:Institute
State reinforced mesh(3)Middle bar diameter is not less than 6mm.