CN106835170A - A kind of stainless steel nurses cleaning agent - Google Patents
A kind of stainless steel nurses cleaning agent Download PDFInfo
- Publication number
- CN106835170A CN106835170A CN201611164599.8A CN201611164599A CN106835170A CN 106835170 A CN106835170 A CN 106835170A CN 201611164599 A CN201611164599 A CN 201611164599A CN 106835170 A CN106835170 A CN 106835170A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- cleaning agent
- water
- nurses
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention mainly relates to chemical technology field, a kind of stainless steel nursing cleaning agent is disclosed, be made up of the raw material of following weight portion：Sodium lignin sulfonate 11 ~ 13, sodium carboxymethylcellulose 3 ~ 5, polyvinyl alcohol 3 ~ 5, calgon 8 ~ 10, AEO 2.3 ~ 2.5, NPE 1.6 ~ 1.8, fatty acid methyl ester ethoxylate 1.1 ~ 1.3, water 70 ~ 75；Environmental protection, safety and Health, decontamination is quick, and soil removal efficiency reaches 98.9%, and income improves 11.4%；Calgon and AEO can promote the infiltration of cleaning fluid, and fast decontaminating prevents stainless steel from getting rusty, and the service life of stainless steel is extended 14.2%, improve the value of stainless steel.
Description
Technical field
The invention mainly relates to chemical technology field, more particularly to a kind of stainless steel nursing cleaning agent.
Background technology
Stainless steel refers to the weak corrosive medium such as resistance to air, steam, water or the steel grade with rustless property, and by resistant to chemical media
The steel grade for corroding (chemical etching such as acid, alkali, salt) is referred to as acid resisting steel, makes theirs due to both differences in chemical composition
Corrosion resistance is different, and acid resisting steel then generally has rustless property, and common stainless steel typically not resistant to chemical media corrosion uses one section
Time just occurs rust staining later.
Spot, oil stain etc. are inevitably infected with during the use of stainless steel products, can generally be used and be washed
It is clean essence or washing powder cleaned, not only cause environmental pollution, wash for a long time it is improper can also cause stainless steel rust staining occur,
Attractive in appearance, reduction of service life is influenceed, accordingly, it would be desirable to a kind of stainless steel Special nursing cleaning agent.
The content of the invention
In order to make up the defect of prior art, it is an object of the invention to provide a kind of stainless steel nursing cleaning agent.
A kind of stainless steel nurses cleaning agent, is made up of the raw material of following weight portion：Sodium lignin sulfonate 11 ~ 13, carboxymethyl
Sodium cellulosate 3 ~ 5, polyvinyl alcohol 3 ~ 5, calgon 8 ~ 10, AEO 2.3 ~ 2.5, Nonyl pheno
Ether 1.6 ~ 1.8, fatty acid methyl ester ethoxylate 1.1 ~ 1.3, water 70 ~ 75.
Described water, is deionized water.
A kind of stainless steel nurses the preparation method of cleaning agent, specifically includes following steps：
（1）Add water in container, add sodium carboxymethylcellulose, be heated to 50 ~ 60 DEG C, stir, be incubated 30 ~ 40 points
Clock, improves the stability of cleaning agent, obtains mixture A；
（2）Sodium lignin sulfonate and calgon are added into mixture A, 65 ~ 70 DEG C, 100 ~ 120 points of insulated and stirred are heated to
Clock, adds AEO and fatty acid methyl ester ethoxylate, in 60 ~ 65 DEG C of insulated and stirreds 100 ~ 120 minutes,
Promote the infiltration of cleaning fluid, fast decontaminating prevents stainless steel from getting rusty, obtains mixture B；
（3）NPE is added into polyvinyl alcohol, 55 ~ 60 DEG C are heated to, insulated and stirred 40 ~ 50 minutes, raising is gone
Dirty ability, obtains mixture C；
（4）Mixture C is added into mixture B, in 60 ~ 65 DEG C of insulated and stirreds 90 ~ 100 minutes, stainless steel nursing cleaning agent is obtained；
（5）Vacuum packaging, obtains finished product.
The stainless steel nurses the application method of cleaning agent, takes appropriate stainless steel nursing cleaning agent, plus running water dilution 300
~ 350 times, it is well mixed, you can carry out the nursing and cleaning of stainless steel, then rinsed well with clear water, spontaneously dries, uses
It is convenient.
It is an advantage of the invention that：A kind of stainless steel nursing cleaning agent that the present invention is provided, environmental protection, safety and Health, system
Health will not be caused damage during standby and use, decontamination is quick, soil removal efficiency reaches 98.9%, and income is improved
11.4%；Calgon and AEO can promote the infiltration of cleaning fluid, and fast decontaminating prevents stainless steel from giving birth to
Rust, makes the service life of stainless steel extend 14.2%, improves the value of stainless steel.
Specific embodiment
Below the present invention is illustrated with specific embodiment.
Embodiment 1
A kind of stainless steel nurses cleaning agent, is made up of the raw material of following weight portion：Sodium lignin sulfonate 11, sodium carboxymethylcellulose
3rd, polyvinyl alcohol 3, calgon 8, AEO 2.3, NPE 1.6, fatty acid methyl ester second
Epoxide compound 1.1, water 70.
Described water, is deionized water.
A kind of stainless steel nurses the preparation method of cleaning agent, specifically includes following steps：
（1）Add water in container, add sodium carboxymethylcellulose, be heated to 50 DEG C, stir, be incubated 40 minutes, improve
The stability of cleaning agent, obtains mixture A；
（2）Sodium lignin sulfonate and calgon are added into mixture A, 70 DEG C are heated to, insulated and stirred 120 minutes, then add
Enter AEO and fatty acid methyl ester ethoxylate, in 60 DEG C of insulated and stirreds 100 minutes, promote oozing for cleaning fluid
Thoroughly, fast decontaminating, prevents stainless steel from getting rusty, and obtains mixture B；
（3）NPE is added into polyvinyl alcohol, 55 DEG C are heated to, insulated and stirred 40 minutes improves dirt-removing power,
Obtain mixture C；
（4）Mixture C is added into mixture B, in 65 DEG C of insulated and stirreds 100 minutes, stainless steel nursing cleaning agent is obtained；
（5）Vacuum packaging, obtains finished product.
The stainless steel nurses the application method of cleaning agent, takes appropriate stainless steel nursing cleaning agent, plus running water dilution 300
Times, it is well mixed, you can carry out the nursing and cleaning of stainless steel, then rinsed well with clear water, spontaneously dry, user
Just.
Embodiment 2
A kind of stainless steel nurses cleaning agent, is made up of the raw material of following weight portion：Sodium lignin sulfonate 12, sodium carboxymethylcellulose
4th, polyvinyl alcohol 4, calgon 9, AEO 2.4, NPE 1.7, fatty acid methyl ester second
Epoxide compound 1.2, water 73.
Described water, is deionized water.
Preparation and application, with embodiment 1.
Embodiment 3
A kind of stainless steel nurses cleaning agent, is made up of the raw material of following weight portion：Sodium lignin sulfonate 13, sodium carboxymethylcellulose
5th, polyvinyl alcohol 5, calgon 10, AEO 2.5, NPE 1.8, fatty acid methyl ester second
Epoxide compound 1.3, water 75.
Described water, is deionized water.
Preparation and application, with embodiment 1.
Comparative example 1
Removal sodium lignin sulfonate and sodium carboxymethylcellulose, remaining preparation and application, with embodiment 1.
Comparative example 2
Removal calgon and AEO, remaining preparation and application, with embodiment 1.
Comparative example 3
Removal NPE and fatty acid methyl ester ethoxylate, remaining preparation and application, with embodiment 1.
Comparative example 4
All raw materials are in step（1）Add, remaining preparation and application, with embodiment 1.
Comparative example 5
Existing commercially available stainless steel nursing cleaning agent.
Embodiment and comparative example stainless steel nurse the cleaning performance of cleaning agent：
Selection identical martensitic stain less steel, is divided into equal-sized 80 pieces, is randomly divided into 8 groups, every group 10 pieces, the spot of contamination
It is identical, to nurse cleaning agent with the stainless steel of the group respectively and carry out nursing and clean, once, the tested time is for nursing cleaning in every 10 days
600 days, embodiment and comparative example stainless steel nursing cleaning agent cleaning performance be shown in Table 1.
Table 1：Embodiment and comparative example stainless steel nurse the cleaning performance of cleaning agent
| Project | Soil removal efficiency/(%) | Scale rate/(%) |
| Embodiment 1 | 98.4 | 0.31 |
| Embodiment 2 | 98.9 | 0.33 |
| Embodiment 3 | 98.2 | 0.27 |
| Comparative example 1 | 86.3 | 1.31 |
| Comparative example 2 | 87.6 | 5.34 |
| Comparative example 3 | 85.7 | 1.66 |
| Comparative example 4 | 91.4 | 1.05 |
| Comparative example 5 | 86.4 | 6.42 |
As it can be seen from table 1 the stainless steel nursing cleaning agent of embodiment, soil removal efficiency is substantially high compared with comparative example, scale rate substantially compared with
Comparative example is low, hence it is evident that the service life of extension stainless steel, illustrates the stainless steel nursing cleaning agent of present invention offer with preferable
Cleaning performance.
Claims (4)
1. a kind of stainless steel nurses cleaning agent, it is characterised in that be made up of the raw material of following weight portion：Sodium lignin sulfonate 11 ~
13rd, sodium carboxymethylcellulose 3 ~ 5, polyvinyl alcohol 3 ~ 5, calgon 8 ~ 10, AEO 2.3 ~ 2.5, nonyl
Phenol polyethenoxy ether 1.6 ~ 1.8, fatty acid methyl ester ethoxylate 1.1 ~ 1.3, water 70 ~ 75.
2. stainless steel according to claim 1 nurses cleaning agent, it is characterised in that described water, is deionized water.
3. stainless steel described in a kind of claim 1 nurses the preparation method of cleaning agent, it is characterised in that specifically include following step
Suddenly：
（1）Add water in container, add sodium carboxymethylcellulose, be heated to 50 ~ 60 DEG C, stir, be incubated 30 ~ 40 points
Clock, obtains mixture A；
（2）Sodium lignin sulfonate and calgon are added into mixture A, 65 ~ 70 DEG C, 100 ~ 120 points of insulated and stirred are heated to
Clock, adds AEO and fatty acid methyl ester ethoxylate, in 60 ~ 65 DEG C of insulated and stirreds 100 ~ 120 minutes,
Obtain mixture B；
（3）NPE is added into polyvinyl alcohol, 55 ~ 60 DEG C are heated to, insulated and stirred 40 ~ 50 minutes must mix
Thing C；
（4）Mixture C is added into mixture B, in 60 ~ 65 DEG C of insulated and stirreds 90 ~ 100 minutes, stainless steel nursing cleaning agent is obtained；
（5）Vacuum packaging, obtains finished product.
4. stainless steel described in a kind of any one of claim 1 ~ 3 nurses the application method of cleaning agent, it is characterised in that take in right amount not
Rust steel nursing cleaning agent, plus running water dilutes 300 ~ 350 times, is well mixed, you can carry out the nursing and cleaning of stainless steel, then use
Clear water is rinsed well, is spontaneously dried.