CN106825080A - A kind of method for removing Automobile Plate steel red rust defect - Google Patents
A kind of method for removing Automobile Plate steel red rust defect Download PDFInfo
- Publication number
- CN106825080A CN106825080A CN201710018587.2A CN201710018587A CN106825080A CN 106825080 A CN106825080 A CN 106825080A CN 201710018587 A CN201710018587 A CN 201710018587A CN 106825080 A CN106825080 A CN 106825080A
- Authority
- CN
- China
- Prior art keywords
- straightening
- red rust
- pickling
- steel
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of steel rolling, a kind of method for removing Automobile Plate steel red rust defect is disclosed, including：In control steel rolling process flow, pickling process speed, straightening insertion, straightening elongation percentage, acid strength and acid liquor temperature parameter；Wherein, the pickling process velocity interval：80~110m/min；The straightening insertion scope：28~40mm；The straightening elongation percentage scope：1%~1.5%；The pickling concentration range：50±5g/L；The acid liquor temperature parameter area：75~85 DEG C.The present invention can provide a kind of removal strip red rust defect, the method for lifting surface quality.
Description
Technical field
The present invention relates to technical field of steel rolling, more particularly to a kind of method for removing Automobile Plate steel red rust defect.
Background technology
As auto industry develops towards loss of weight, energy-conservation and raising security direction, with dual phase steel and phase-change induced plastic
Steel is that the application of the high strength car sheet of representative is more and more extensive, and the application of dual phase steel and transformation induced plasticity steel Automobile Plate not only may be used
It is the important materials for realizing body lightening with saving steel, moreover it is possible to reduce oil consumption.
However, dual phase steel and transformation induced plasticity steel to realize the characteristics such as high intensity, low surrender, high-elongation, it is necessary to
Matrix adds certain Si elements, and Si elements easily cause belt steel surface to produce red rust defect.Red rust defect is mainly Si units
Element forms fayalite phase Fe2SiO4 between band steel matrix and iron oxide cortex, and fayalite has adhesion with respect to iron scale
Effect, makes the scale defect of belt steel surface be difficult to remove.
The content of the invention
The present invention provides a kind of method for removing Automobile Plate steel red rust defect, solves the oxidation of steel surface in the prior art
Iron sheet defect is difficult to the technical problem to remove.
In order to solve the above technical problems, the invention provides a kind of method for removing Automobile Plate steel red rust defect, including：
In control steel rolling process flow, pickling process speed, straightening insertion, straightening elongation percentage, acid strength and acid
Liquid temperature parameter；
Wherein, the pickling process velocity interval：80~110m/min；The straightening insertion scope：- 28~-40mm；
The straightening elongation percentage scope：1%~1.5%；The pickling concentration range：50±5g/L；The acid liquor temperature parameter area：
75~85 DEG C.
Further, the pickling process speed is 100m/min；The straightening insertion is -35mm；The straightening is prolonged
It is 1% to stretch rate；The pickling concentration is 55g/L；80 DEG C of the acid liquor temperature parameter.
Further, the pickling process speed is 115m/min；The straightening insertion is -37mm；The straightening is prolonged
It is 1.1% to stretch rate；The pickling concentration is 52g/L；78 DEG C of the acid liquor temperature parameter.
Further, the pickling process speed is 97m/min；The straightening insertion is -38mm；The straightening extends
Rate is 1.1%；The pickling concentration is 54g/L；82 DEG C of the acid liquor temperature parameter.
Further, the acid solution is hydrochloric acid.
One or more technical schemes provided in the embodiment of the present application, at least have the following technical effect that or advantage：
The removal Automobile Plate provided in the embodiment of the present application method of steel red rust defect, for dual phase steel and phase-change induced
Plasticity steel, using rational pickling parameter combination, obtains the red rust of belt steel surface and crushes to a certain extent, and improves and acid solution
Time of contact and area so that the scale defect of belt steel surface is easily removed, so that the red rust area of belt steel surface is reduced,
Improve the surface quality of final finished.
Specific embodiment
The embodiment of the present application solves steel in the prior art by providing a kind of method for removing Automobile Plate steel red rust defect
The scale defect on surface is difficult to the technical problem to remove；The technique effect of lifting strip surface quality is reached.
In order to be better understood from above-mentioned technical proposal, above-mentioned technical proposal is carried out below in conjunction with specific embodiment
Describe in detail, it should be understood that the specific features in the embodiment of the present invention and embodiment are to the detailed of technical scheme
Illustrate, rather than the restriction to technical scheme, in the case where not conflicting, in the embodiment of the present application and embodiment
Technical characteristic can be mutually combined.
A kind of method for removing Automobile Plate steel red rust defect, including：
In control steel rolling process flow, pickling process speed, straightening insertion, straightening elongation percentage, acid strength and acid
Liquid temperature parameter；
Wherein, the pickling process velocity interval：80~110m/min；The straightening insertion scope：- 28~-40mm；
The straightening elongation percentage scope：1%~1.5%；The pickling concentration range：50±5g/L；The acid liquor temperature parameter area：
75~85 DEG C.
The acid solution is hydrochloric acid.
Combined by above-mentioned parameter, dual phase steel and transformation induced plasticity steel belt steel surface red rust phenomenon, red rust face can be reduced
Product at least reduces 10%.
Lower mask body provides three embodiment explanation parameter combination schemes.
Embodiment 1
The product specification of the present embodiment is：Trimmed size 1250mm × 1.5mm；The percentage by weight of product composition is：C：
0.084%th, Mn：1.80%th, Si：0.45%th, P：0.014%th, S：0.001%, remaining is impurity and Fe.
Manufacturing parameter：
Pickling speed is 100m/min.
Straightening insertion is -35mm.
Straightening elongation percentage is 1.0%.
The free acid concentration of 1# groove hydrochloric acid is 55g/l.
Hydrochloric acid temperature is 80 DEG C.
The surface of steel plate table inspection instrument detection more conventional control method of red rust area reduces 15%.
Embodiment 2
The product specification of the present embodiment is：Trimmed size 1200mm × 1.7mm；The percentage by weight of product composition is：C：
0.081%th, Mn：1.81%th, Si：0.47%th, P：0.009%th, S：0.003%, remaining is impurity and Fe.
Manufacturing parameter：
Pickling speed is 115m/min.
Straightening insertion is -37mm.
Straightening elongation percentage is 1.1%.
The free acid concentration of 1# groove hydrochloric acid is 52g/l.
Hydrochloric acid temperature is 78 DEG C.
The surface of steel plate table inspection instrument detection more conventional control method of red rust area reduces 12%.
Embodiment 3
The product specification of the present embodiment is：Trimmed size 1320mm × 1.0mm；The percentage by weight of product composition is：C：
0.075%th, Mn：1.83%th, Si：0.47%th, P：0.009%th, S：0.001%, remaining is impurity and Fe.
Manufacturing parameter：
Pickling speed is 97m/min.
Straightening insertion is -38mm.
Straightening elongation percentage is 1.1%.
The free acid concentration of 1# groove hydrochloric acid is 54g/l.
Hydrochloric acid temperature is 82 DEG C.
The surface of steel plate table inspection instrument detection more conventional control method of red rust area reduces 14%.
One or more technical schemes provided in the embodiment of the present application, at least have the following technical effect that or advantage：
The removal Automobile Plate provided in the embodiment of the present application method of steel red rust defect, for dual phase steel and phase-change induced
Plasticity steel, using rational pickling parameter combination, obtains the red rust of belt steel surface and crushes to a certain extent, and improves and acid solution
Time of contact and area so that the scale defect of belt steel surface is easily removed, so that the red rust area of belt steel surface is reduced,
Improve the surface quality of final finished.
It should be noted last that, above specific embodiment is merely illustrative of the technical solution of the present invention and unrestricted,
Although being described in detail to the present invention with reference to example, it will be understood by those within the art that, can be to the present invention
Technical scheme modify or equivalent, without deviating from the spirit and scope of technical solution of the present invention, it all should cover
In the middle of scope of the presently claimed invention.
Claims (5)
1. it is a kind of to remove the Automobile Plate method of steel red rust defect, it is characterised in that including：
In control steel rolling process flow, pickling process speed, straightening insertion, straightening elongation percentage, acid strength and acid solution temperature
Degree parameter；
Wherein, the pickling process velocity interval：80~110m/min；The straightening insertion scope：- 28~-40mm；It is described
Straightening elongation percentage scope：1%~1.5%；The pickling concentration range：50±5g/L；The acid liquor temperature parameter area：75~
85℃。
2. the method for removing Automobile Plate steel red rust defect as claimed in claim 1, it is characterised in that：The pickling process speed
It is 100m/min to spend；The straightening insertion is -35mm；The straightening elongation percentage is 1%；The pickling concentration is 55g/L；Institute
State 80 DEG C of acid liquor temperature parameter.
3. the method for removing Automobile Plate steel red rust defect as claimed in claim 1, it is characterised in that：The pickling process speed
It is 115m/min to spend；The straightening insertion is -37mm；The straightening elongation percentage is 1.1%；The pickling concentration is 52g/L；
78 DEG C of the acid liquor temperature parameter.
4. the method for removing Automobile Plate steel red rust defect as claimed in claim 1, it is characterised in that：The pickling process speed
It is 97m/min to spend；The straightening insertion is -38mm；The straightening elongation percentage is 1.1%；The pickling concentration is 54g/L；
82 DEG C of the acid liquor temperature parameter.
5. the method for steel red rust defect of the removal Automobile Plate as described in 1~any one of claim, it is characterised in that：The acid
Liquid is hydrochloric acid.