CN106820812A - A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof - Google Patents
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof Download PDFInfo
- Publication number
- CN106820812A CN106820812A CN201611198305.3A CN201611198305A CN106820812A CN 106820812 A CN106820812 A CN 106820812A CN 201611198305 A CN201611198305 A CN 201611198305A CN 106820812 A CN106820812 A CN 106820812A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- proof
- nano
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof, including mat body is arranged at the waterproof layer of mat body lower surface, the middle medicine coating for being arranged at mat body upper surface and the fireprotection layer for being arranged at waterproof layer lower surface, wherein：The raw material of fireprotection layer includes epoxy acrylate, vinyl acetate homopolymer emulsion, pure-acrylic emulsion, Styrene acrylic ester copolymeric emulsion, Ludox, nano-zinc borate, nano-sized magnesium hydroxide, sepiolite, expanded vermiculite, expanded perlite, wood fibre, modified additive, talcum powder, aluminium triphosphate, nano barium sulfate, fluorosilicon oil, calgon, dimethylbenzene, propane diols, organic silicon defoamer, hydroxyethyl cellulose, polyurethane thickener, silane coupler KH 560, NPE and deionized water.Health care straw mat of the invention has excellent waterproof fireproofing performance, also has functions that strengthen immunity.
Description
Technical field
The present invention relates to straw mat field, more particularly to a kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof.
Background technology
Straw mat has functions that radiating of cool blood, and permanent use can make one to assemble cold air in vivo, be easily reduced the immunity of people,
Straw mat in the market is mostly by after raw material establishment, fixation is sold after sterilization, and health properties are poor, fire-proof and water-proof
Can cannot meet demand of the prior art, therefore need a kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof of design badly
To solve the problems of the prior art.
The content of the invention
To solve technical problem present in background technology, the present invention proposes that one kind strengthens immunologic function with fire-proof and water-proof
Health care straw mat, with excellent fire-proof and water-proof performance, and there is strengthen immunity.
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that straw mat, rattan seat, bamboo mat, the mat make of thin bamboo strips, one or more braiding of Lin Xizhong are formed；
The raw material of waterproof layer includes by weight：Modified acrylic acid emulsion 80-120 parts, hydroxy propyl methacrylate 30-50
Part, DOTP 10-30 parts, nano titanium oxide 2-8 parts, nano-zinc borate 3-5 parts, magnesium hydroxide 3-9 parts, cunning
Stone flour 2-6 parts, attapulgite 4-8 parts, 6-12 parts of white fused alumina micro mist, fluorocarbons 3-5 parts, sodium peroxydisulfate 2-4 parts, aluminum oxide 3-5
Part, aluminium triphosphate 1-5 parts, nano barium sulfate 2-6 parts, modified filler 4-8 parts, antiseptic 4-8 parts, fluorosilicon oil 1-3 parts, molybdic acid
Sodium 1-5 parts, dimethylbenzene 3-6 parts, propane diols 3-8 parts, organic silicon defoamer 1-3 parts, dispersant 2-4 parts, titanate coupling agent
NDZ-201 3-5 parts, wetting agent 2-5 parts, deionized water 10-30 parts；
The raw material of middle medicine coating includes by weight：Folium panacis japonici cum caule 4-8 parts, Radix Codonopsis 2-5 parts, Chinese yam 1-3 parts, Radix Glycyrrhizae 2-4 parts,
Sealwort 3-5 parts, bur beggar-ticks 2-6 parts, Chinese peashrub root 1-3 parts, broom top 2-4 parts, thizoma curculiginis 1-3 parts, bark of eucommia 4-8 parts, fleece-flower root 2-5
Part, mulberry fruit 1-3 parts, 2-5 parts of paddy tree root skin, fruit of glossy privet 1-3 parts, radix polygonati officinalis 4-8 parts, lily 2-6 parts, rheum officinale 5-15 parts, the root of large-flowered skullcap
2-5 parts, Radix Codonopsis 3-6 parts, radix bupleuri 1-3 parts, stem of noble dendrobium 4-8 parts, dried rhizome of rehmannia 4-8 parts, Chinese ephedra 1-3 parts, Radix Glycyrrhizae 2-4 parts, caulis lonicerae 3-6
Part, rhizoma atractylodis 2-4 parts, rhizoma zingiberis 1-3 parts, fennel seeds 3-5 parts, Chinese cassia tree 2-4 parts, Divine Comedy 1-3 parts, dried orange peel 2-5 parts, Radix Astragali 2-4 parts, when
Return 1-4 parts, rhizome of chuanxiong 2-5 parts, sodium carboxymethylcellulose 2-5 parts, gypsum 2-4 parts, boric acid 1-3 parts, Mecrilate
2-6 parts, 10-20 parts of natural rubber glue；
The raw material of fireprotection layer includes by weight：Epoxy acrylate 80-120 parts, vinyl acetate homopolymer emulsion 15-25
Part, pure-acrylic emulsion 30-50 parts, interpolymer latex of polystyrene and acrylic ester 10-30 parts, Ludox 2-8 parts, nano-zinc borate 3-5
Part, nano-sized magnesium hydroxide 3-9 parts, sepiolite 2-6 parts, expanded vermiculite 4-8 parts, expanded perlite 6-12 parts, wood fibre 3-5
Part, modified additive 2-4 parts, talcum powder 3-5 parts, aluminium triphosphate 1-5 parts, nano barium sulfate 2-6 parts, fluorosilicon oil 1-3 parts, it is six inclined
Sodium phosphate 1-5 parts, dimethylbenzene 3-6 parts, propane diols 3-8 parts, organic silicon defoamer 1-3 parts, hydroxyethyl cellulose 2-4 parts, poly- ammonia
Ester thickener 1-6 parts, 3-5 parts, NPE 2-5 parts, deionized water 16-23 parts of silane coupler KH-560.
Preferably, in the raw material of waterproof layer, the raw material of modified filler includes by weight：Silane coupler KH-560 5-
15 parts, carbon black 2-6 parts, tapioca starch 6-12 parts, montmorillonite 1-5 parts, kaolin 2-4 parts, shitosan 4-8 parts, nanometer silicon carbide 3-5
Part, nano silicon 1-6 parts, Nano diamond 3-5 parts, attapulgite 4-8 parts.
Preferably, in the raw material of waterproof layer, modified filler is prepared by following technique：By silane coupler KH-560 and
Distilled water be well mixed, be then placed in heating 25-35min in water-bath, be subsequently added into carbon black, tapioca starch, montmorillonite, kaolin,
Shitosan, nanometer silicon carbide, nano silicon, Nano diamond and attapulgite, ultrasonic disperse 10-20min, are then adjusted
PH to 2.5-3.5, is then placed in heating 25-35min in water-bath, then carries out separation of solid and liquid, by the solid distillation after separation
Water washing 2-4 times, being subsequently adding n-butanol carries out distillation dehydration, and then the powder after dehydration is put into 100-120 DEG C of baking oven
1-3h is dried, room temperature is cooled to and is obtained modified filler.
Preferably, in the raw material of waterproof layer, the raw material of antiseptic includes by weight：Urea 2-8 parts, polyvinylpyrrolidine
Ketone 1-5 parts, deionized water 10-30 parts, sodium chloride 2-8 parts, defoamer 1-6 parts, aluminum nitrate 2-8 parts, 1-4 parts of titanium liquid, zirconium sulfate
3-6 parts, disodium hydrogen phosphate 4-8 parts.
Preferably, in the raw material of waterproof layer, antiseptic is prepared by following technique：By urea, polyvinylpyrrolidone
It is well mixed with deionized water, sodium chloride and defoamer stirring 10-30min are subsequently adding, it is subsequently adding aluminum nitrate and obtains material
a；With separatory funnel to titanium liquid and zirconium sulfate is added in material a, then heating water bath is added to 70-90 DEG C after being cooled to room temperature
Disodium hydrogen phosphate, is then aged, filtration washing, dries, and room temperature is cooled to after calcining and obtains antiseptic.
Preferably, middle medicine coating is prepared by following technique：By folium panacis japonici cum caule, Radix Codonopsis, Chinese yam, Radix Glycyrrhizae, sealwort, wolf handle
Grass, Chinese peashrub root, broom top, thizoma curculiginis, the bark of eucommia, the fleece-flower root, mulberry fruit, paddy tree root skin, the fruit of glossy privet, radix polygonati officinalis, lily, rheum officinale, the root of large-flowered skullcap,
Radix Codonopsis, radix bupleuri, the stem of noble dendrobium, the dried rhizome of rehmannia, Chinese ephedra, Radix Glycyrrhizae, caulis lonicerae, rhizoma atractylodis, rhizoma zingiberis, fennel seeds, Chinese cassia tree, Divine Comedy, dried orange peel, the Radix Astragali, when
Return with rhizome of chuanxiong co-grinding, it is well mixed to obtain material a, during material a then added into ethanol solution, frozen after stirring
Dry-cure obtains material b；Then material b and water are well mixed, 90-100 DEG C of decoction 5-15h is cooled to room temperature and obtains filtrate,
Then filtrate is carried out being concentrated under reduced pressure to give concentrate, then will be cooled to normal temperature after 75-85 DEG C of drying of concentrate, then ground
To 20-40 mesh granular materials, sodium carboxymethylcellulose, gypsum, boric acid, Mecrilate and natural are subsequently adding
Rubber cement is well mixed, and 15-35min is stirred in 2500-3500r/min rotating speeds, obtains middle medicine coating.
Preferably, in the raw material of fireprotection layer, the raw material of modified additive includes by weight：Nanometer antimony-doped stannic oxide powder
4-12 parts, Silane coupling reagent KH-570 2-8 parts, styrene 3-6 parts, butyl acrylate 1.5-4 parts.
Preferably, in the raw material of fireprotection layer, modified additive is prepared by following technique：By styrene, butyl acrylate
It is well mixed with nanometer antimony-doped stannic oxide powder, Silane coupling reagent KH-570 is subsequently adding, 20-28h is stirred in 38-46 DEG C,
It is cooled to room temperature and obtains material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 10-14min obtains modified additive.
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof of the invention, including mat body, are arranged at seat
The waterproof layer of sub- body lower surface, the middle medicine coating for being arranged at mat body upper surface and the fire prevention for being arranged at waterproof layer lower surface
Layer, wherein：Mat body is that straw mat, rattan seat, bamboo mat, the mat make of thin bamboo strips, one or more braiding of Lin Xizhong are formed；The raw material of waterproof layer
Including modified acrylic acid emulsion, hydroxy propyl methacrylate, DOTP, nano titanium oxide, nano-zinc borate,
Magnesium hydroxide, talcum powder, attapulgite, white fused alumina micro mist, fluorocarbons, sodium peroxydisulfate, aluminum oxide, aluminium triphosphate, nano-sulfur
Sour barium, modified filler, antiseptic, fluorosilicon oil, sodium molybdate, dimethylbenzene, propane diols, organic silicon defoamer, dispersant, titanate esters idol
Connection agent NDZ-201, wetting agent and deionized water；In the raw material of waterproof layer, modified filler is prepared by following technique：By silane
Coupling agent KH-560 and distilled water are well mixed, are then placed in being heated in water-bath, are subsequently added into carbon black, tapioca starch, montmorillonite, height
Ridge soil, shitosan, nanometer silicon carbide, nano silicon, Nano diamond and attapulgite, ultrasonic disperse, then adjust pH,
It is then placed in being heated in water-bath, then carries out separation of solid and liquid, by the distillation water washing of the solid after separation, is subsequently adding n-butanol
Distillation dehydration is carried out, then the powder after dehydration is put into baking oven and is dried, be cooled to room temperature and obtain modified filler, applied to anti-
In the preparation of water layer, the water resistance of waterproof layer is effectively increased, and then effectively increase the water proofing property of health care straw mat of the present invention
Energy.In the raw material of waterproof layer, antiseptic is prepared by following technique：Urea, polyvinylpyrrolidone and deionized water are mixed
Close uniform, be subsequently adding sodium chloride and defoamer stirring, be subsequently adding aluminum nitrate and obtain material a；With separatory funnel in material a
Addition titanium liquid and zirconium sulfate, then heating water bath, disodium hydrogen phosphate is added after being cooled to room temperature, is then aged, filtration washing, is done
It is dry, room temperature is cooled to after calcining and obtains antiseptic, apply in the preparation of waterproof layer, effectively increase the antibiotic property of waterproof layer
Can, and then effectively increase the anti-microbial property of health care straw mat of the present invention.Middle medicine coating is prepared by following technique：By ginseng
Leaf, Radix Codonopsis, Chinese yam, Radix Glycyrrhizae, sealwort, bur beggar-ticks, Chinese peashrub root, broom top, thizoma curculiginis, the bark of eucommia, the fleece-flower root, mulberry fruit, paddy tree root skin,
It is the fruit of glossy privet, radix polygonati officinalis, lily, rheum officinale, the root of large-flowered skullcap, Radix Codonopsis, radix bupleuri, the stem of noble dendrobium, the dried rhizome of rehmannia, Chinese ephedra, Radix Glycyrrhizae, caulis lonicerae, rhizoma atractylodis, rhizoma zingiberis, small
Fennel, Chinese cassia tree, Divine Comedy, dried orange peel, the Radix Astragali, Radix Angelicae Sinensis and rhizome of chuanxiong co-grinding, it is well mixed to obtain material a, then material a is added
Frozen dried is carried out in ethanol solution, after stirring obtain material b；Then material b and water are well mixed, are decocted, cooling
Filtrate is obtained to room temperature, then carries out filtrate to be concentrated under reduced pressure to give concentrate, normal temperature is cooled to after then concentrate is dried,
Then abrasive grains shape material, is subsequently adding sodium carboxymethylcellulose, gypsum, boric acid, Mecrilate and natural
Rubber cement is well mixed, stirring, obtains middle medicine coating, and imparting health care straw mat of the present invention has functions that strengthen immunity.
The raw material of fireprotection layer includes epoxy acrylate, vinyl acetate homopolymer emulsion, pure-acrylic emulsion, cinnamic acrylic ester copolymerization
It is emulsion, Ludox, nano-zinc borate, nano-sized magnesium hydroxide, sepiolite, expanded vermiculite, expanded perlite, wood fibre, modified
Auxiliary agent, talcum powder, aluminium triphosphate, nano barium sulfate, fluorosilicon oil, calgon, dimethylbenzene, propane diols, organosilicon froth breaking
Agent, hydroxyethyl cellulose, polyurethane thickener, silane coupler KH-560, NPE and deionized water.Fire prevention
In the raw material of layer, modified additive is prepared by following technique：By styrene, butyl acrylate and nanometer antimony-doped stannic oxide powder
Body is well mixed, and is subsequently adding Silane coupling reagent KH-570, stirs, and is cooled to room temperature and obtains material a；Then material a is placed in
Crushed in ice-water bath, it is ultrasonically treated to obtain modified additive, apply in the preparation of fireprotection layer, effectively increase the fire prevention of fireprotection layer
Performance, and then effectively increase the fire protecting performance of health care straw mat.
Specific embodiment
The present invention is described in detail with reference to specific embodiment, it should be appreciated that embodiment is served only for illustrating this hair
Bright, rather than for limiting the invention, any modification made on the basis of the present invention, equivalent etc. are in this hair
In bright protection domain.
Embodiment 1
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that straw mat braiding is formed.
The raw material of waterproof layer includes by weight：It is 100 parts of modified acrylic acid emulsion, 40 parts of hydroxy propyl methacrylate, right
20 parts of dioctyl phthalate, 5 parts of nano titanium oxide, 4 parts of nano-zinc borate, 6 parts of magnesium hydroxide, 4 parts of talcum powder, concave convex rod
6 parts of stone, 9 parts of white fused alumina micro mist, 4 parts of fluorocarbons, 3 parts of sodium peroxydisulfate, 4 parts of aluminum oxide, 3 parts of aluminium triphosphate, nano barium sulfate 4
Part, 6 parts of modified filler, 6 parts of antiseptic, 2 parts of fluorosilicon oil, 3 parts of sodium molybdate, 4.5 parts of dimethylbenzene, 5.5 parts of propane diols, organosilicon disappear
2 parts of infusion, 3 parts of dispersant, 4 parts of titanate coupling agent NDZ-201,3.5 parts of wetting agent, 20 parts of deionized water.
Middle medicine coating is prepared by following technique：By weight by 6 parts of folium panacis japonici cum caules, 3.5 parts of Radix Codonopsis, 2 portions of Chinese yams, 3 parts
Radix Glycyrrhizae, 4 portions of sealworts, 4 portions of bur beggar-ticks, 2 portions of Chinese peashrub roots, 3 portions of broom tops, 2 portions of thizoma curculiginises, 6 portions of barks of eucommia, 3.5 portions of fleece-flowers root, 2 portions of mulberries
Mulberry, 3.5 parts of paddy tree root skins, 2 portions of fruit of glossy privets, 6 portions of radix polygonati officinalis, 4 portions of lilies, 10 parts of rheum officinales, 3.5 parts of roots of large-flowered skullcap, 4.5 parts of Radix Codonopsis, 2 parts
Radix bupleuri, 6 parts of stems of noble dendrobium, 6 parts of dried rhizome of rehmannia, 2 parts of Chinese ephedras, 3 parts of Radix Glycyrrhizaes, 4.5 parts of caulis loniceraes, 3 parts of rhizoma atractylodis, 2 parts of rhizoma zingiberis, 4 parts of fennel seeds, 3
Part Chinese cassia tree, 2 parts of Divine Comedy, 3.5 parts of dried orange peels, 3 parts of Radixs Astragali, 2.5 parts of Radix Angelicae Sinensis and 3.5 parts of rhizome of chuanxiong co-grindings, it is well mixed to obtain thing
Material a, then by material a addition ethanol solutions, carries out frozen dried and obtains material b after stirring；Then by material b and water
Well mixed, 95 DEG C of decoction 10h are cooled to room temperature and obtain filtrate, then carry out filtrate to be concentrated under reduced pressure to give concentrate, then
Normal temperature will be cooled to after 80 DEG C of dryings of concentrate, be then ground to 30 mesh granular materials, be subsequently adding 3.5 parts of carboxymethyl celluloses
Plain sodium, 3 parts of gypsums, 2 parts of boric acid, 4 parts of Mecrilates and 15 parts of natural rubber glue are well mixed, in 3000/
Min rotating speeds stir 25min, obtain middle medicine coating.
The raw material of fireprotection layer includes by weight：It is 100 parts of epoxy acrylate, 20 parts of vinyl acetate homopolymer emulsion, pure
40 parts of acrylic emulsion, 20 parts of interpolymer latex of polystyrene and acrylic ester, 5 parts of Ludox, 4 parts of nano-zinc borate, nano-sized magnesium hydroxide 6
Part, 4 parts of sepiolite, 6 parts of expanded vermiculite, 9 parts of expanded perlite, 4 parts of wood fibre, 3 parts of modified additive, 4 parts of talcum powder, trimerization
It is 3 parts of aluminum phosphate, 4 parts of nano barium sulfate, 2 parts of fluorosilicon oil, 3 parts of calgon, 4.5 parts of dimethylbenzene, 5.5 parts of propane diols, organic
2 parts of silicon defoaming agent, 3 parts of hydroxyethyl cellulose, 3.5 parts of polyurethane thickener, 4 parts of silane coupler KH-560, polyoxyethylene nonyl phenyl
3.5 parts of vinethene, 19.5 parts of deionized water.
In the raw material of waterproof layer, modified filler is prepared by following technique：By weight by 10 parts of silane coupler KH-
560 and distilled water it is well mixed, be then placed in heating 30min in water-bath, be subsequently added into 4 parts of carbon blacks, 9 parts of tapioca starch, 3 parts cover de-
Soil, 3 parts of kaolin, 6 parts of shitosans, 4 parts of nanometer silicon carbides, 3.5 parts of nano silicons, 4 parts of Nano diamonds and 6 parts are concavo-convex
Rod soil, ultrasonic disperse 15min then adjusts pH to 3.0, is then placed in heating 30min in water-bath, then carries out separation of solid and liquid,
By the solid after separation with water washing is distilled 3 times, being subsequently adding n-butanol carries out distillation dehydration, then puts the powder after dehydration
Enter and dry 2h in 110 DEG C of baking ovens, be cooled to room temperature and obtain modified filler.
In the raw material of waterproof layer, antiseptic is prepared by following technique：By weight by 5 parts of urea, 3 parts of polyethylene pyrroles
Pyrrolidone and 20 parts of deionized waters are well mixed, and are subsequently adding 5 parts of sodium chloride and 3.5 parts of defoamer stirring 20min, are subsequently adding
5 parts of aluminum nitrates obtain material a；With separatory funnel to adding 2.5 parts of titanium liquid and 4.5 parts of zirconium sulfates, then heating water bath in material a
To 80 DEG C, 6 parts of disodium hydrogen phosphates are added after being cooled to room temperature, be then aged, filtration washing, dried, room temperature is cooled to after calcining
Obtain antiseptic.
In the raw material of fireprotection layer, modified additive is prepared by following technique：By weight by 4.5 parts of styrene, 2.75
Part butyl acrylate and 8 parts of nanometer antimony-doped stannic oxide powders are well mixed, and are subsequently adding 5 parts of Silane coupling reagent KH-570s, in
42 DEG C of stirring 24h, are cooled to room temperature and obtain material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 12min is obtained
Modified additive.
Embodiment 2
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that the braiding of rattan seat is formed.
The raw material of waterproof layer includes by weight：80 parts of modified acrylic acid emulsion, 50 parts of hydroxy propyl methacrylate, to benzene
10 parts of diformazan dioctyl phthalate, 8 parts of nano titanium oxide, 3 parts of nano-zinc borate, 9 parts of magnesium hydroxide, 2 parts of talcum powder, attapulgite
8 parts, 6 parts of white fused alumina micro mist, 5 parts of fluorocarbons, 2 parts of sodium peroxydisulfate, 5 parts of aluminum oxide, 1 part of aluminium triphosphate, nano barium sulfate 6
Part, 4 parts of modified filler, 8 parts of antiseptic, 1 part of fluorosilicon oil, 5 parts of sodium molybdate, 3 parts of dimethylbenzene, 8 parts of propane diols, organic silicon defoamer
1 part, 4 parts of dispersant, 3 parts of titanate coupling agent NDZ-201,5 parts of wetting agent, 10 parts of deionized water.
Middle medicine coating is prepared by following technique：By weight by 4 parts of folium panacis japonici cum caules, 5 parts of Radix Codonopsis, 1 portion of Chinese yam, 4 parts it is sweet
Grass, 3 parts of sealworts, 6 portions of bur beggar-ticks, 1 part of Chinese peashrub root, 4 portions of broom tops, 1 portion of thizoma curculiginis, 8 parts of barks of eucommia, 2 parts of fleece-flowers root, 3 parts of mulberry fruits,
2 parts of paddy tree root skins, 3 parts of fruit of glossy privets, 4 parts of radix polygonati officinalis, 6 parts of lilies, 5 parts of rheum officinales, 5 parts of roots of large-flowered skullcap, 3 parts of Radix Codonopsis, 3 parts of radix bupleuri, 4 parts of stones
Dry measure used in former times, 8 parts of dried rhizome of rehmannia, 1 part of Chinese ephedra, 4 parts of Radix Glycyrrhizaes, 3 parts of caulis loniceraes, 4 parts of rhizoma atractylodis, 1 part of rhizoma zingiberis, 5 parts of fennel seeds, 2 parts of Chinese cassia trees, 3 parts of god
Bent, 2 parts of dried orange peels, 4 parts of Radixs Astragali, 1 part of Radix Angelicae Sinensis and 5 parts of rhizome of chuanxiong co-grindings, it is well mixed to obtain material a, then material a is added
Frozen dried is carried out in ethanol solution, after stirring obtain material b；Then material b and water are well mixed, 90 DEG C of decoctions
15h, is cooled to room temperature and obtains filtrate, then carries out filtrate to be concentrated under reduced pressure to give concentrate, then by 75 DEG C of dryings of concentrate
After be cooled to normal temperature, be then ground to 40 mesh granular materials, be subsequently adding 2 parts of sodium carboxymethylcelluloses, 4 parts of gypsums, 1 part
Boric acid, 6 parts of Mecrilates and 10 parts of natural rubber glue are well mixed, and 15- is stirred in 3500r/min rotating speeds
35min, obtains middle medicine coating.
The raw material of fireprotection layer includes by weight：80 parts of epoxy acrylate, 25 parts of vinyl acetate homopolymer emulsion, pure third
30 parts of emulsion, 30 parts of interpolymer latex of polystyrene and acrylic ester, 2 parts of Ludox, 5 parts of nano-zinc borate, 3 parts of nano-sized magnesium hydroxide,
6 parts of sepiolite, 4 parts of expanded vermiculite, 12 parts of expanded perlite, 3 parts of wood fibre, 4 parts of modified additive, 3 parts of talcum powder, trimerization phosphorus
5 parts of sour aluminium, 2 parts of nano barium sulfate, 3 parts of fluorosilicon oil, 1 part of calgon, 6 parts of dimethylbenzene, 3 parts of propane diols, organosilicon froth breaking
3 parts of agent, 2 parts of hydroxyethyl cellulose, 6 parts of polyurethane thickener, 3 parts of silane coupler KH-560, NPE 5
Part, 16 parts of deionized water.
In the raw material of waterproof layer, modified filler is prepared by following technique：By weight by 5 parts of silane coupler KH-
560 and distilled water it is well mixed, be then placed in heating 35min in water-bath, be subsequently added into 2 parts of carbon blacks, 12 parts of tapioca starch, 1 part of illiteracy
De- soil, 4 parts of kaolin, 4 parts of shitosans, 5 parts of nanometer silicon carbides, 1 part of nano silicon, 5 parts of Nano diamonds and 4 parts are concavo-convex
Rod soil, ultrasonic disperse 20min then adjusts pH to 2.5, is then placed in heating 35min in water-bath, then carries out separation of solid and liquid,
By the solid after separation with water washing is distilled 2 times, being subsequently adding n-butanol carries out distillation dehydration, then puts the powder after dehydration
Enter and dry 1h in 120 DEG C of baking ovens, be cooled to room temperature and obtain modified filler.
In the raw material of waterproof layer, antiseptic is prepared by following technique：By weight by 2 parts of urea, 5 parts of polyethylene pyrroles
Pyrrolidone and 10 parts of deionized waters are well mixed, and are subsequently adding 8 parts of sodium chloride and 1 part of defoamer stirring 30min, are subsequently adding 2
Part aluminum nitrate obtains material a；With separatory funnel to 4 parts of titanium liquid and 3 parts of zirconium sulfates are added in material a, then heating water bath is to 90
DEG C, 4 parts of disodium hydrogen phosphates are added after being cooled to room temperature, then it is aged, filtration washing, dry, room temperature is cooled to after calcining and is obtained
Antiseptic.
In the raw material of fireprotection layer, modified additive is prepared by following technique：By weight by 3 parts of styrene, 4 parts of propylene
Acid butyl ester and 4 parts of nanometer antimony-doped stannic oxide powders are well mixed, and are subsequently adding 8 parts of Silane coupling reagent KH-570s, are stirred in 38 DEG C
28h is mixed, room temperature is cooled to and is obtained material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 10min obtains modified helping
Agent.
Embodiment 3
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that bamboo mat braiding is formed.
The raw material of waterproof layer includes by weight：It is 120 parts of modified acrylic acid emulsion, 30 parts of hydroxy propyl methacrylate, right
30 parts of dioctyl phthalate, 2 parts of nano titanium oxide, 5 parts of nano-zinc borate, 3 parts of magnesium hydroxide, 6 parts of talcum powder, concave convex rod
4 parts of stone, 12 parts of white fused alumina micro mist, 3 parts of fluorocarbons, 4 parts of sodium peroxydisulfate, 3 parts of aluminum oxide, 5 parts of aluminium triphosphate, nano barium sulfate
2 parts, 8 parts of modified filler, 4 parts of antiseptic, 3 parts of fluorosilicon oil, 1 part of sodium molybdate, 6 parts of dimethylbenzene, 3 parts of propane diols, organosilicon froth breaking
3 parts of agent, 2 parts of dispersant, 5 parts of titanate coupling agent NDZ-201,2 parts of wetting agent, 30 parts of deionized water.
Middle medicine coating is prepared by following technique：By weight by 8 parts of folium panacis japonici cum caules, 2 parts of Radix Codonopsis, 3 portions of Chinese yams, 2 parts it is sweet
Grass, 5 parts of sealworts, 2 portions of bur beggar-ticks, 3 parts of Chinese peashrub roots, 2 portions of broom tops, 3 portions of thizoma curculiginises, 4 parts of barks of eucommia, 5 parts of fleece-flowers root, 1 part of mulberry fruit,
5 parts of paddy tree root skins, 1 part of fruit of glossy privet, 8 parts of radix polygonati officinalis, 2 parts of lilies, 15 parts of rheum officinales, 2 parts of roots of large-flowered skullcap, 6 parts of Radix Codonopsis, 1 part of radix bupleuri, 8 parts of stones
Dry measure used in former times, 4 parts of dried rhizome of rehmannia, 3 parts of Chinese ephedras, 2 parts of Radix Glycyrrhizaes, 6 parts of caulis loniceraes, 2 parts of rhizoma atractylodis, 3 parts of rhizoma zingiberis, 3 parts of fennel seeds, 4 parts of Chinese cassia trees, 1 part of god
Bent, 5 parts of dried orange peels, 2 parts of Radixs Astragali, 4 parts of Radix Angelicae Sinensis and 2 parts of rhizome of chuanxiong co-grindings, it is well mixed to obtain material a, then material a is added
Frozen dried is carried out in ethanol solution, after stirring obtain material b；Then material b and water are well mixed, 100 DEG C of decoctions
5h, is cooled to room temperature and obtains filtrate, then carries out filtrate to be concentrated under reduced pressure to give concentrate, then by after 85 DEG C of dryings of concentrate
Normal temperature is cooled to, 20 mesh granular materials are then ground to, 5 parts of sodium carboxymethylcelluloses, 2 parts of gypsums, 3 parts of boron are subsequently adding
Acid, 2 parts of Mecrilates and 20 parts of natural rubber glue are well mixed, and 35min is stirred in 2500r/min rotating speeds, are obtained
To middle medicine coating.
The raw material of fireprotection layer includes by weight：It is 120 parts of epoxy acrylate, 15 parts of vinyl acetate homopolymer emulsion, pure
50 parts of acrylic emulsion, 10 parts of interpolymer latex of polystyrene and acrylic ester, 8 parts of Ludox, 3 parts of nano-zinc borate, nano-sized magnesium hydroxide 9
Part, 2 parts of sepiolite, 8 parts of expanded vermiculite, 6 parts of expanded perlite, 5 parts of wood fibre, 2 parts of modified additive, 5 parts of talcum powder, trimerization
1 part of aluminum phosphate, 6 parts of nano barium sulfate, 1 part of fluorosilicon oil, 5 parts of calgon, 3 parts of dimethylbenzene, 8 parts of propane diols, organosilicon disappear
1 part of infusion, 4 parts of hydroxyethyl cellulose, 1 part of polyurethane thickener, 5 parts of silane coupler KH-560, NPE
2 parts, 23 parts of deionized water.
In the raw material of waterproof layer, modified filler is prepared by following technique：By weight by 15 parts of silane coupler KH-
560 and distilled water it is well mixed, be then placed in heating 25min in water-bath, be subsequently added into 6 parts of carbon blacks, 6 parts of tapioca starch, 5 parts cover de-
Soil, 2 parts of kaolin, 8 parts of shitosans, 3 parts of nanometer silicon carbides, 6 parts of nano silicons, 3 parts of Nano diamonds and 8 parts of concave convex rods
Soil, ultrasonic disperse 10min then adjusts pH to 3.5, is then placed in heating 25min in water-bath, then carries out separation of solid and liquid, will
With water washing is distilled 4 times, be subsequently adding n-butanol carries out distillation dehydration to solid after separation, is then put into the powder after dehydration
3h is dried in 100 DEG C of baking ovens, room temperature is cooled to and is obtained modified filler.
In the raw material of waterproof layer, antiseptic is prepared by following technique：By weight by 8 parts of urea, 1 part of polyethylene pyrrole
Pyrrolidone and 30 parts of deionized waters are well mixed, and are subsequently adding 2 parts of sodium chloride and 6 parts of defoamer stirring 10min, are subsequently adding 8
Part aluminum nitrate obtains material a；With separatory funnel to 1 part of titanium liquid and 6 parts of zirconium sulfates are added in material a, then heating water bath is to 70
DEG C, 8 parts of disodium hydrogen phosphates are added after being cooled to room temperature, then it is aged, filtration washing, dry, room temperature is cooled to after calcining and is obtained
Antiseptic.
In the raw material of fireprotection layer, modified additive is prepared by following technique：By weight by 6 parts of styrene, 1.5 part third
Olefin(e) acid butyl ester and 12 parts of nanometer antimony-doped stannic oxide powders are well mixed, and 2 parts of Silane coupling reagent KH-570s are subsequently adding, in 46 DEG C
Stirring 20h, is cooled to room temperature and obtains material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 14min is modified
Auxiliary agent.
Embodiment 4
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that mat make of thin bamboo strips braiding is formed.
The raw material of waterproof layer includes by weight：85 parts of modified acrylic acid emulsion, 45 parts of hydroxy propyl methacrylate, to benzene
15 parts of diformazan dioctyl phthalate, 7 parts of nano titanium oxide, 3.5 parts of nano-zinc borate, 8 parts of magnesium hydroxide, 3 parts of talcum powder, concave convex rod
7 parts of stone, 7 parts of white fused alumina micro mist, 4.5 parts of fluorocarbons, 2.5 parts of sodium peroxydisulfate, 4.5 parts of aluminum oxide, aluminium triphosphate 2 part, nanometer
5 parts of barium sulfate, 5 parts of modified filler, 7 parts of antiseptic, 1.5 parts of fluorosilicon oil, 4 parts of sodium molybdate, 4 parts of dimethylbenzene, 7 parts of propane diols, have
1.5 parts of machine silicon defoaming agent, 3.5 parts of dispersant, 3.5 parts of titanate coupling agent NDZ-201,4 parts of wetting agent, 15 parts of deionized water.
Middle medicine coating is prepared by following technique：By weight by 5 parts of folium panacis japonici cum caules, 4 parts of Radix Codonopsis, 1.5 parts of Chinese yams, 3.5
Part Radix Glycyrrhizae, 3.5 parts of sealworts, 5 parts of bur beggar-ticks, 1.5 parts of Chinese peashrub roots, 3.5 parts of broom tops, 1.5 parts of thizoma curculiginises, 7 parts of barks of eucommia, 3 parts of what head
Crow, 2.5 parts of mulberry fruits, 3 parts of paddy tree root skins, 2.5 parts of fruit of glossy privets, 5 parts of radix polygonati officinalis, 5 parts of lilies, 8 parts of rheum officinales, 4 parts of roots of large-flowered skullcap, 4 parts of parties
Ginseng, 2.5 parts of radix bupleuri, 5 parts of stems of noble dendrobium, 7 parts of dried rhizome of rehmannia, 1.5 portions of Chinese ephedras, 3.5 portions of Radix Glycyrrhizaes, 4 portions of caulis loniceraes, 3.5 parts of rhizoma atractylodis, 1.5 parts do
Ginger, 4.5 parts of fennel seeds, 2.5 parts of Chinese cassia trees, 2.5 parts of Divine Comedy, 3 parts of dried orange peels, 3.5 parts of Radixs Astragali, 2 parts of Radix Angelicae Sinensis and 4 parts of rhizome of chuanxiong mixed powders
It is broken, it is well mixed to obtain material a, then by material a addition ethanol solutions, carry out frozen dried after stirring and obtain material
b；Then material b and water are well mixed, 92 DEG C of decoction 12h are cooled to room temperature and obtain filtrate, it is dense that filtrate then is carried out into decompression
Contracting obtains concentrate, then will be cooled to normal temperature after 78 DEG C of dryings of concentrate, is then ground to 35 mesh granular materials, Ran Houjia
Enter 3 parts of sodium carboxymethylcelluloses, 3.5 parts of gypsums, 1.5 parts of boric acid, 5 parts of Mecrilates and 12 parts of natural rubber latexes
Water is well mixed, and 32min is stirred in 3200r/min rotating speeds, obtains middle medicine coating.
The raw material of fireprotection layer includes by weight：85 parts of epoxy acrylate, 22 parts of vinyl acetate homopolymer emulsion, pure third
35 parts of emulsion, 25 parts of interpolymer latex of polystyrene and acrylic ester, 3 parts of Ludox, 4.5 parts of nano-zinc borate, nano-sized magnesium hydroxide 4
Part, 5 parts of sepiolite, 5 parts of expanded vermiculite, 11 parts of expanded perlite, 3.5 parts of wood fibre, 3.5 parts of modified additive, talcum powder 3.5
Part, 4 parts of aluminium triphosphate, 3 parts of nano barium sulfate, 2.5 parts of fluorosilicon oil, 2 parts of calgon, 5 parts of dimethylbenzene, 4 parts of propane diols,
2.5 parts of organic silicon defoamer, 2.5 parts of hydroxyethyl cellulose, 5 parts of polyurethane thickener, silane coupler KH-5603.5 parts, nonyl
4 parts of base phenol polyethenoxy ether, 17 parts of deionized water.
In the raw material of waterproof layer, modified filler is prepared by following technique：By weight by 8 parts of silane coupler KH-
560 and distilled water it is well mixed, be then placed in heating 32min in water-bath, be subsequently added into 3 parts of carbon blacks, 10 parts of tapioca starch, 2 parts of illiteracies
De- soil, 3.5 parts of kaolin, 5 parts of shitosans, 4.5 parts of nanometer silicon carbides, 2 parts of nano silicons, 4.5 parts of Nano diamonds and 5
Part attapulgite, ultrasonic disperse 18min then adjusts pH to 2.8, is then placed in heating 32min in water-bath, then carries out solid-liquid
Separate, by the solid after separation with water washing is distilled 2 times, being subsequently adding n-butanol carries out distillation dehydration, then by after dehydration
Powder dries 1.5h in being put into 115 DEG C of baking ovens, is cooled to room temperature and obtains modified filler.
In the raw material of waterproof layer, antiseptic is prepared by following technique：By weight by 3 parts of urea, 4 parts of polyethylene pyrroles
Pyrrolidone and 15 parts of deionized waters are well mixed, and are subsequently adding 7 parts of sodium chloride and 2 parts of defoamer stirring 25min, are subsequently adding 3
Part aluminum nitrate obtains material a；With separatory funnel to 3 parts of titanium liquid and 4 parts of zirconium sulfates are added in material a, then heating water bath is to 85
DEG C, 5 parts of disodium hydrogen phosphates are added after being cooled to room temperature, then it is aged, filtration washing, dry, room temperature is cooled to after calcining and is obtained
Antiseptic.
In the raw material of fireprotection layer, modified additive is prepared by following technique：By weight by 4 parts of styrene, 3.8 part third
Olefin(e) acid butyl ester and 5 parts of nanometer antimony-doped stannic oxide powders are well mixed, and 7 parts of Silane coupling reagent KH-570s are subsequently adding, in 39 DEG C
Stirring 26h, is cooled to room temperature and obtains material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 11min is modified
Auxiliary agent.
Embodiment 5
A kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof proposed by the present invention, including mat body, are set
In the waterproof layer of mat body lower surface, it is arranged at the middle medicine coating of mat body upper surface and is arranged at waterproof layer lower surface
Fireprotection layer, wherein：
Mat body is that the braiding of Lin's seat is formed.
The raw material of waterproof layer includes by weight：It is 115 parts of modified acrylic acid emulsion, 35 parts of hydroxy propyl methacrylate, right
It is 25 parts of dioctyl phthalate, 3 parts of nano titanium oxide, 4.5 parts of nano-zinc borate, 4 parts of magnesium hydroxide, 5 parts of talcum powder, concavo-convex
5 parts of rod stone, 11 parts of white fused alumina micro mist, 3.5 parts of fluorocarbons, 3.5 parts of sodium peroxydisulfate, 3.5 parts of aluminum oxide, 4 parts of aluminium triphosphate, receive
3 parts of nano-barium sulfate, 7 parts of modified filler, 5 parts of antiseptic, 2.5 parts of fluorosilicon oil, 2 parts of sodium molybdate, 5 parts of dimethylbenzene, 4 parts of propane diols,
2.5 parts of organic silicon defoamer, 2.5 parts of dispersant, 4.5 parts of titanate coupling agent NDZ-201,3 parts of wetting agent, deionized water 25
Part.
Middle medicine coating is prepared by following technique：By weight by 7 parts of folium panacis japonici cum caules, 3 parts of Radix Codonopsis, 2.5 parts of Chinese yams, 2.5
Part Radix Glycyrrhizae, 4.5 parts of sealworts, 3 parts of bur beggar-ticks, 2.5 parts of Chinese peashrub roots, 2.5 parts of broom tops, 2.5 parts of thizoma curculiginises, 5 parts of barks of eucommia, 4 parts of what head
Crow, 1.5 parts of mulberry fruits, 4 parts of paddy tree root skins, 1.5 parts of fruit of glossy privets, 7 parts of radix polygonati officinalis, 3 parts of lilies, 12 parts of rheum officinales, 3 parts of roots of large-flowered skullcap, 5 parts of parties
Ginseng, 1.5 parts of radix bupleuri, 7 parts of stems of noble dendrobium, 5 parts of dried rhizome of rehmannia, 2.5 portions of Chinese ephedras, 2.5 portions of Radix Glycyrrhizaes, 5 portions of caulis loniceraes, 2.5 parts of rhizoma atractylodis, 2.5 parts do
Ginger, 3.5 parts of fennel seeds, 3.5 parts of Chinese cassia trees, 1.5 parts of Divine Comedy, 4 parts of dried orange peels, 2.5 parts of Radixs Astragali, 3 parts of Radix Angelicae Sinensis and 3 parts of rhizome of chuanxiong mixed powders
It is broken, it is well mixed to obtain material a, then by material a addition ethanol solutions, carry out frozen dried after stirring and obtain material
b；Then material b and water are well mixed, 98 DEG C of decoction 8h are cooled to room temperature and obtain filtrate, it is dense that filtrate then is carried out into decompression
Contracting obtains concentrate, then will be cooled to normal temperature after 82 DEG C of dryings of concentrate, is then ground to 25 mesh granular materials, Ran Houjia
Enter 4 parts of sodium carboxymethylcelluloses, 2.5 parts of gypsums, 2.5 parts of boric acid, 3 parts of Mecrilates and 18 parts of natural rubber latexes
Water is well mixed, and 32min is stirred in 2800r/min rotating speeds, obtains middle medicine coating.
The raw material of fireprotection layer includes by weight：It is 115 parts of epoxy acrylate, 18 parts of vinyl acetate homopolymer emulsion, pure
45 parts of acrylic emulsion, 15 parts of interpolymer latex of polystyrene and acrylic ester, 7 parts of Ludox, 3.5 parts of nano-zinc borate, nano-sized magnesium hydroxide
8 parts, 3 parts of sepiolite, 7 parts of expanded vermiculite, 7 parts of expanded perlite, 4.5 parts of wood fibre, 2.5 parts of modified additive, talcum powder 4.5
Part, 2 parts of aluminium triphosphate, 5 parts of nano barium sulfate, 1.5 parts of fluorosilicon oil, 4 parts of calgon, 4 parts of dimethylbenzene, 7 parts of propane diols,
1.5 parts of organic silicon defoamer, 3.5 parts of hydroxyethyl cellulose, 2 parts of polyurethane thickener, 4.5 parts of silane coupler KH-560, nonyl
3 parts of base phenol polyethenoxy ether, 22 parts of deionized water.
In the raw material of waterproof layer, modified filler is prepared by following technique：By weight by 12 parts of silane coupler KH-
560 and distilled water it is well mixed, be then placed in heating 28min in water-bath, be subsequently added into 5 parts of carbon blacks, 8 parts of tapioca starch, 4 parts cover de-
Soil, 2.5 parts of kaolin, 7 parts of shitosans, 3.5 parts of nanometer silicon carbides, 5 parts of nano silicons, 3.5 parts of Nano diamonds and 7 parts
Attapulgite, ultrasonic disperse 12min then adjusts pH to 3.2, is then placed in heating 28min in water-bath, then carries out solid-liquid point
From by the solid after separation with water washing is distilled 4 times, being subsequently adding n-butanol carries out distillation dehydration, then by the powder after dehydration
End dries 2.5h in being put into 105 DEG C of baking ovens, is cooled to room temperature and obtains modified filler.
In the raw material of waterproof layer, antiseptic is prepared by following technique：By weight by 7 parts of urea, 2 parts of polyethylene pyrroles
Pyrrolidone and 25 parts of deionized waters are well mixed, and are subsequently adding 3 parts of sodium chloride and 5 parts of defoamer stirring 15min, are subsequently adding 7
Part aluminum nitrate obtains material a；With separatory funnel to 2 parts of titanium liquid and 5 parts of zirconium sulfates are added in material a, then heating water bath is to 75
DEG C, 7 parts of disodium hydrogen phosphates are added after being cooled to room temperature, then it is aged, filtration washing, dry, room temperature is cooled to after calcining and is obtained
Antiseptic.
In the raw material of fireprotection layer, modified additive is prepared by following technique：By weight by 5 parts of styrene, 1.6 part third
Olefin(e) acid butyl ester and 11 parts of nanometer antimony-doped stannic oxide powders are well mixed, and 3 parts of Silane coupling reagent KH-570s are subsequently adding, in 45 DEG C
Stirring 22h, is cooled to room temperature and obtains material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 13min is modified
Auxiliary agent.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept is subject to equivalent or change, should all be included within the scope of the present invention.
Claims (8)
1. a kind of health care straw mat for strengthening immunologic function with fire-proof and water-proof, including mat body, is arranged at mat body following table
The waterproof layer in face, the middle medicine coating for being arranged at mat body upper surface and the fireprotection layer for being arranged at waterproof layer lower surface, its feature
It is, wherein：
Mat body is that straw mat, rattan seat, bamboo mat, the mat make of thin bamboo strips, one or more braiding of Lin Xizhong are formed；
The raw material of waterproof layer includes by weight：Modified acrylic acid emulsion 80-120 parts, hydroxy propyl methacrylate 30-50 parts,
DOTP 10-30 parts, nano titanium oxide 2-8 parts, nano-zinc borate 3-5 parts, magnesium hydroxide 3-9 parts, talcum
Powder 2-6 parts, attapulgite 4-8 parts, 6-12 parts of white fused alumina micro mist, fluorocarbons 3-5 parts, sodium peroxydisulfate 2-4 parts, aluminum oxide 3-5 parts,
Aluminium triphosphate 1-5 parts, nano barium sulfate 2-6 parts, modified filler 4-8 parts, antiseptic 4-8 parts, fluorosilicon oil 1-3 parts, sodium molybdate
1-5 parts, dimethylbenzene 3-6 parts, propane diols 3-8 parts, organic silicon defoamer 1-3 parts, dispersant 2-4 parts, titanate coupling agent NDZ-
201 3-5 parts, wetting agent 2-5 parts, deionized water 10-30 parts；
The raw material of middle medicine coating includes by weight：Folium panacis japonici cum caule 4-8 parts, Radix Codonopsis 2-5 parts, Chinese yam 1-3 parts, Radix Glycyrrhizae 2-4 parts, sealwort
3-5 parts, bur beggar-ticks 2-6 parts, Chinese peashrub root 1-3 parts, broom top 2-4 parts, thizoma curculiginis 1-3 parts, bark of eucommia 4-8 parts, fleece-flower root 2-5 parts, mulberry
Mulberry 1-3 parts, 2-5 parts of paddy tree root skin, fruit of glossy privet 1-3 parts, radix polygonati officinalis 4-8 parts, lily 2-6 parts, rheum officinale 5-15 parts, root of large-flowered skullcap 2-5 parts,
Radix Codonopsis 3-6 parts, radix bupleuri 1-3 parts, stem of noble dendrobium 4-8 parts, dried rhizome of rehmannia 4-8 parts, Chinese ephedra 1-3 parts, Radix Glycyrrhizae 2-4 parts, caulis lonicerae 3-6 parts, rhizoma atractylodis
2-4 parts, rhizoma zingiberis 1-3 parts, fennel seeds 3-5 parts, Chinese cassia tree 2-4 parts, Divine Comedy 1-3 parts, dried orange peel 2-5 parts, Radix Astragali 2-4 parts, Radix Angelicae Sinensis 1-4
Part, rhizome of chuanxiong 2-5 parts, sodium carboxymethylcellulose 2-5 parts, gypsum 2-4 parts, boric acid 1-3 parts, Mecrilate 2-6 parts,
10-20 parts of natural rubber glue；
The raw material of fireprotection layer includes by weight：Epoxy acrylate 80-120 parts, 15-25 parts of vinyl acetate homopolymer emulsion,
Pure-acrylic emulsion 30-50 parts, interpolymer latex of polystyrene and acrylic ester 10-30 parts, Ludox 2-8 parts, nano-zinc borate 3-5 parts, receive
Rice 3-9 part of magnesium hydroxide, sepiolite 2-6 parts, expanded vermiculite 4-8 parts, expanded perlite 6-12 parts, wood fibre 3-5 parts, be modified
Auxiliary agent 2-4 parts, talcum powder 3-5 parts, aluminium triphosphate 1-5 parts, nano barium sulfate 2-6 parts, fluorosilicon oil 1-3 parts, calgon
1-5 parts, dimethylbenzene 3-6 parts, propane diols 3-8 parts, organic silicon defoamer 1-3 parts, hydroxyethyl cellulose 2-4 parts, polyurethane thickening
Agent 1-6 parts, 3-5 parts, NPE 2-5 parts, deionized water 16-23 parts of silane coupler KH-560.
2. it is according to claim 1 with fire-proof and water-proof strengthen immunologic function health care straw mat, it is characterised in that waterproof layer
Raw material in, the raw material of modified filler includes by weight：5-15 parts of silane coupler KH-560, carbon black 2-6 parts, tapioca starch
6-12 parts, montmorillonite 1-5 parts, kaolin 2-4 parts, shitosan 4-8 parts, nanometer silicon carbide 3-5 parts, nano silicon 1-6 parts,
Nano diamond 3-5 parts, attapulgite 4-8 parts.
3. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim 1 and 2, it is characterised in that anti-
In the raw material of water layer, modified filler is prepared by following technique：Silane coupler KH-560 and distilled water are well mixed, so
After be put into water-bath and heat 25-35min, be subsequently added into carbon black, tapioca starch, montmorillonite, kaolin, shitosan, nanometer silicon carbide,
Nano silicon, Nano diamond and attapulgite, ultrasonic disperse 10-20min then adjust pH to 2.5-3.5, Ran Houfang
Enter and heat 25-35min in water-bath, then carry out separation of solid and liquid, by distillation water washing 2-4 times of the solid after separation, Ran Houjia
Entering n-butanol carries out distillation dehydration, then the powder after dehydration is put into 100-120 DEG C of baking oven and dries 1-3h, is cooled to room temperature
Obtain modified filler.
4. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim any one of 1-3, its feature exists
In in the raw material of waterproof layer, the raw material of antiseptic includes by weight：Urea 2-8 parts, polyvinylpyrrolidone 1-5 parts, go from
Sub- water 10-30 parts, sodium chloride 2-8 parts, defoamer 1-6 parts, aluminum nitrate 2-8 parts, 1-4 parts of titanium liquid, zirconium sulfate 3-6 parts, phosphoric acid hydrogen
Disodium 4-8 parts.
5. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim any one of 1-4, its feature exists
In in the raw material of waterproof layer, antiseptic is prepared by following technique：Urea, polyvinylpyrrolidone and deionized water are mixed
Close uniform, be subsequently adding sodium chloride and defoamer stirring 10-30min, be subsequently adding aluminum nitrate and obtain material a；Use separatory funnel
To titanium liquid and zirconium sulfate is added in material a, then heating water bath adds disodium hydrogen phosphate to 70-90 DEG C after being cooled to room temperature, connects
Ageing, filtration washing dries, room temperature is cooled to after calcining and obtains antiseptic.
6. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim any one of 1-5, its feature exists
In middle medicine coating is prepared by following technique：By folium panacis japonici cum caule, Radix Codonopsis, Chinese yam, Radix Glycyrrhizae, sealwort, bur beggar-ticks, Chinese peashrub root, goldspink
Flower, thizoma curculiginis, the bark of eucommia, the fleece-flower root, mulberry fruit, paddy tree root skin, the fruit of glossy privet, radix polygonati officinalis, lily, rheum officinale, the root of large-flowered skullcap, Radix Codonopsis, radix bupleuri, stone
The mixing of dry measure used in former times, the dried rhizome of rehmannia, Chinese ephedra, Radix Glycyrrhizae, caulis lonicerae, rhizoma atractylodis, rhizoma zingiberis, fennel seeds, Chinese cassia tree, Divine Comedy, dried orange peel, the Radix Astragali, Radix Angelicae Sinensis and rhizome of chuanxiong
Crush, it is well mixed to obtain material a, then by material a addition ethanol solutions, carry out frozen dried after stirring and obtain thing
Material b；Then material b and water are well mixed, 90-100 DEG C of decoction 5-15h is cooled to room temperature and obtains filtrate, then enters filtrate
Row is concentrated under reduced pressure to give concentrate, then will be cooled to normal temperature after 75-85 DEG C of drying of concentrate, is then ground to 20-40 mesh
Granular material, is subsequently adding sodium carboxymethylcellulose, gypsum, boric acid, Mecrilate and natural rubber glue and mixes
Close uniform, 15-35min is stirred in 2500-3500r/min rotating speeds, obtain middle medicine coating.
7. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim any one of 1-6, its feature exists
In in the raw material of fireprotection layer, the raw material of modified additive includes by weight：4-12 parts of nanometer antimony-doped stannic oxide powder, silane
Coupling agent kh-570 2-8 parts, styrene 3-6 parts, butyl acrylate 1.5-4 parts.
8. the health care straw mat for strengthening immunologic function with fire-proof and water-proof according to claim any one of 1-7, its feature exists
In in the raw material of fireprotection layer, modified additive is prepared by following technique：By styrene, butyl acrylate and nano antimony doped two
Tin oxide powder is well mixed, and is subsequently adding Silane coupling reagent KH-570, and 20-28h is stirred in 38-46 DEG C, is cooled to room temperature and is obtained
To material a；Then material a is placed in ice-water bath and is crushed, ultrasonically treated 10-14min obtains modified additive.