CN106801334A - The method for sorting of Multifunctional cotton fabric - Google Patents
The method for sorting of Multifunctional cotton fabric Download PDFInfo
- Publication number
- CN106801334A CN106801334A CN201710014162.4A CN201710014162A CN106801334A CN 106801334 A CN106801334 A CN 106801334A CN 201710014162 A CN201710014162 A CN 201710014162A CN 106801334 A CN106801334 A CN 106801334A
- Authority
- CN
- China
- Prior art keywords
- fabric
- solution
- sorting
- primitive
- cotton fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of method for sorting of Multifunctional cotton fabric, the bafta that conductive layer is pre-processed is sequentially placed into the cation prepared by zinc salt and is constructed primitive solution and is constructed by anion prepared by polybasic carboxylic acid and repeatedly soaked in primitive solution, metal organic framework compound is formed by the effect of zinc salt and carboxylic acid, so as to introduce one layer of functional layer with antibacterial, uvioresistant and antistatic property in fabric face, so as to obtain Multifunctional cotton fabric.Species, the species and concentration of thickness and preparation method, reactant zinc salt and carboxylic acid, soak time, the number of repetition of arrangement of the conductive layer for introducing are pre-processed by controlling surface of cotton fabric, it is also possible to obtain the multifunctional fabric of other different qualities.The inventive method is simple, efficiency high;Cost of material is low, easy acquisition, is conducive to industrialized production;The zinc salt and carboxylic acid for using are nontoxic, and reaction need not add any organic solvent;The fabric of preparation has antibacterial, uvioresistant and the multifunctionality such as antistatic.
Description
Technical field
The present invention relates to a kind of method for sorting of bafta, more particularly to a kind of method for sorting of Multifunctional cotton fabric.
Background technology
Used as popular garment material, bafta has the advantages that water imbibition is strong, wear-resisting washable, soft comfortable, passes through
The bafta of arrangement can have widely application.With the development and the progress of science and technology in epoch, the functionalization of bafta is whole
Reason, such as super-hydrophobic arrangement, anti-ultraviolet finishing, low temperature noniron finish, antibiotic finish, anti-crease finishing, flame-proof treatment etc., be
Bafta is applied to link essential in living.
At present, the research to functional finish of cotton fabric is more popular, and the method for arrangement also has a lot, but wherein majority side
Method complex process, time-consuming, high cost.However, up to the present, also finding no pass normal temperature and pressure lower short time repetition and soaking
Obtain the research of Multifunctional cotton fabric.
Uniformly it is distributed due to the multifunctionality of metal organic framework compound and its on fabric, makes fabric in numerous necks
Domain has important application potential, such as can be used for antibacterial, uvioresistant and antistatic field.The present invention is carried based on the principle
Be readily available for a kind of simple for process, raw material, arrangement side with low cost, suitable for large-scale production Multifunctional cotton fabric
Method.
The content of the invention
It is harmless that the technical problem to be solved in the present invention is to provide a kind of advantages of nontoxic raw materials for using during the course of the reaction, cost
It is low, it is readily available, be conducive to the method for sorting of the Multifunctional cotton fabric of industrialized production, the bafta that it is prepared is removed to be had
Outside anti-microbial property, also with certain uvioresistant and antistatic etc. multi-functional.
In order to solve the above-mentioned technical problem, the technical scheme is that providing a kind of arrangement side of Multifunctional cotton fabric
Method, it is characterised in that comprise the following steps:
Step 1:Fabric face is carried out into conductive layer treatment, conductive pretreating fabrics are obtained;
Step 2:Prepare zinc salt solution and construct primitive solution A as cation, the configuration polybasic carboxylic acid aqueous solution is used as the moon
Ion constructs primitive solution B;
Step 3:Pretreating fabrics are soaked in cation constructs primitive solution A, then fabric is constructed from cation
Taken out in primitive solution A, the cation that rinsing removes fabric face physical absorption constructs primitive;
Step 4:The fabric processed through step 3 is soaked in anion constructs primitive solution B, then by fabric from the moon from
Son is constructed in primitive solution B and taken out, and the anion that rinsing removes fabric face physical absorption constructs primitive, so as to complete a week
The preparation of phase;
Step 5:The fabric processed through step 4 is continuously repeated into step 3 and step 4 for several times, finally by after above-mentioned treatment
Fabric takes out, washing, drying, prepare stabilization, it is lasting while there is the multi-functional of antibacterial uvioresistant and antistatic property
Fabric.
Preferably, in the step 1, conductive layer is processed as using Graphene, polyaniline or polypyrrole to process.
Preferably, in the step 2, zinc salt is one or more in zinc acetate, zinc chloride, zinc nitrate and zinc sulfate.
Preferably, in the step 2, the concentration of zinc salt solution is 0.05-0.4mol/L.
Preferably, in the step 2, polybasic carboxylic acid be terephthalic acid (TPA), trimesic acid, Pyromellitic Acid, succinic acid,
One or more in glutaric acid, citric acid, BTCA.
Preferably, in the step 2, the concentration of the polybasic carboxylic acid aqueous solution is 0.05-0.2mol/L.
Preferably, in the step 2, cation constructs zinc salt and anion in primitive solution A and constructs many in primitive solution B
The mol ratio of first carboxylic acid is 5: 1-1: 5.
Preferably, in the step 3, bath raio is 1: 5-1: 20, soak time is 5-15min;In the step 4, bath raio
It is 1: 5-1: 20, soak time is 5-15min.
The present invention is arranged using conductive layer to fabric first, and film preparation is conducive to so as to introduce one layer in fabric face
Conductive layer, obtain pretreating fabrics;Pretreatment bafta is soaked first in the cation containing zinc salt constructs primitive solution A
Bubble, the negative electrical charge having using pretreating fabrics surface conductive layer reacts with zinc ion;Again by bafta containing polynary
The anion of carboxylic acid is constructed in primitive solution B and soaked, and the zinc ion for making polybasic carboxylic acid be introduced with fabric face reacts;Afterwards
The fabric continuous several times are soaked in cation constructs primitive solution A and anion constructs primitive solution B respectively, by zinc salt
The compound with ad hoc structure and composition is formed with the effect of polybasic carboxylic acid, so as to introduce one layer with anti-in fabric face
The functional layer of bacterium, uvioresistant and antistatic property, prepares multifunctional fabric.
During arrangement, species, thickness and the preparation side of the conductive layer for introducing are pre-processed by controlling surface of cotton fabric
The species and concentration of method, reactant zinc salt and carboxylic acid, soak time, the number of repetition of arrangement, it is also possible to obtain having and remove anti-
The multifunctional fabric of beyond bacterium, uvioresistant and antistatic property, other different qualities.The method for sorting is not restricted to cotton and knits
Thing, by certain method after non-surface of cotton fabric introducing conductive layer carries out surface preparation, walks using in the inventive method
The technique of rapid 2 to step 5, can also obtain non-cotton multifunctional fabric.
Compared to existing technology, the method that the present invention is provided has the advantages that:
(1) method and technical process are simple, efficiency high, without special installation;Cost of material is low, easy acquisition, is conducive to work
Industry metaplasia is produced.
(2) zinc salt and carboxylic acid for being used in course of reaction are nontoxic, and reaction is carried out in water phase, any without adding
Organic solvent, it is environment-friendly.
(3) there is the multifunctionality such as uvioresistant, antibacterial, antistatic after Cotton Fabric, has a good application prospect.
(4) by changing the preprocess method of fabric, the method for sorting is also applied for other non-cotton fabrics.
Brief description of the drawings
Fig. 1 is the scanning electron microscope (SEM) photograph of the Multifunctional cotton fabric that embodiment 1 is prepared.
Specific embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.In addition, it is to be understood that after the content for having read instruction of the present invention, people in the art
Member can make various changes or modifications to the present invention, and these equivalent form of values equally fall within the application appended claims and limited
Scope.
Embodiment 1
Fabric is surface-treated using Graphene, Graphene pretreating fabrics are obtained.Prepare the acetic acid of 0.25mol/L
The zinc aqueous solution constructs primitive solution A as cation, and the aqueous terephthalic acid solution for preparing 0.15mol/L is constructed as anion
Primitive solution B.Pretreatment bafta is put into cation and constructed 5min is soaked in primitive solution A, bath raio is 1: 5, take out rinsing,
Place into anion and construct and 5min is soaked in primitive solution B, bath raio is 1: 5, take out rinsing;Continuously repeat in solution A and solution B
Taken out after middle immersion 8 times, wash, dry, prepare stabilization, it is lasting while there is the multi-functional of antibacterial and uvioresistant performance
Fabric.The SEM figures of product are shown in accompanying drawing 1.Fabric bacteriostasis rate is more than 99%, and uvioresistant performance UPF 50+, antistatic effect is excellent.
Embodiment 2
Fabric is surface-treated using polyaniline, polyaniline pretreating fabrics are obtained.Prepare the chlorination of 0.20mol/L
The zinc aqueous solution constructs primitive solution A as cation, and the butanetetra-carboxylic acid aqueous solution for preparing 0.10mol/L constructs base as anion
First solution B.Pretreatment bafta is put into cation and constructed 5min is soaked in primitive solution A, bath raio is 1: 15, take out rinsing,
Place into anion and construct and 5min is soaked in primitive solution B, bath raio is 1: 15, take out rinsing;Continuously repeat in solution A and solution
Taken out after soaking 8 times in B, wash, dry, prepare stabilization, it is lasting while there are many work(of antibacterial and uvioresistant performance
Can fabric.Fabric bacteriostasis rate is more than 99%, and uvioresistant performance UPF 50+, antistatic effect is excellent.
Embodiment 3
Fabric is surface-treated using polypyrrole, polypyrrole pretreating fabrics are obtained.Prepare the sulfuric acid of 0.1mol/L
The zinc aqueous solution constructs primitive solution A as cation, and the aqueous citric acid solution for preparing 0.05mol/L constructs primitive as anion
Solution B.Pretreatment bafta is put into cation and constructed 15min is soaked in primitive solution A, bath raio is 1: 20, take out rinsing, then
It is put into anion and constructs and 15min is soaked in primitive solution B, bath raio is 1: 20, takes out rinsing;Continuously repeat in solution A and solution B
Taken out after middle immersion 12 times, wash, dry, prepare stabilization, it is lasting while there are many work(of antibacterial and uvioresistant performance
Can fabric.Fabric bacteriostasis rate is more than 99%, and uvioresistant performance UPF 50+, antistatic effect is excellent.
Embodiment 4
Fabric is surface-treated using polypyrrole, polypyrrole pretreating fabrics are obtained.Prepare the nitric acid of 0.15mol/L
The zinc aqueous solution constructs primitive solution A as cation, and the Pyromellitic Acid aqueous solution for preparing 0.1mol/L is constructed as anion
Primitive solution B.Pretreatment bafta is put into cation and constructed 10min is soaked in primitive solution A, bath raio is 1: 10, take out drift
Wash, place into anion and construct and 10min is soaked in primitive solution B, bath raio is 1: 10, take out rinsing;Continuously repeat in solution A and
Taken out after soaking 10 times in solution B, wash, dry, prepare stabilization, it is lasting while there is antibacterial and uvioresistant performance
Multifunctional fabric.Fabric bacteriostasis rate is more than 99%, and uvioresistant performance UPF 50+, antistatic effect is excellent.
Claims (8)
1. a kind of method for sorting of Multifunctional cotton fabric, it is characterised in that comprise the following steps:
Step 1:Fabric face is carried out into conductive layer treatment, conductive pretreating fabrics are obtained;
Step 2:Prepare zinc salt solution and construct primitive solution A as cation, the configuration polybasic carboxylic acid aqueous solution is used as anion
Construct primitive solution B;
Step 3:Pretreating fabrics are soaked in cation constructs primitive solution A, fabric is then constructed into primitive from cation
Taken out in solution A, the cation that rinsing removes fabric face physical absorption constructs primitive;
Step 4:The fabric processed through step 3 is soaked in anion constructs primitive solution B, then by fabric from anion structure
Taking-up in primitive solution B is built, the anion that rinsing removes fabric face physical absorption constructs primitive, so as to complete a cycle
Prepare;
Step 5:The fabric processed through step 4 is continuously repeated into step 3 and step 4 for several times, finally by the fabric after above-mentioned treatment
Take out, washing, drying, prepare stabilization, it is lasting while there is the multi-functional of antibacterial, uvioresistant and antistatic property to knit
Thing.
2. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:It is conductive in the step 1
Layer is processed as using Graphene, polyaniline or polypyrrole to process.
3. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:In the step 2, zinc salt
It is one or more in zinc acetate, zinc chloride, zinc nitrate and zinc sulfate.
4. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:In the step 2, zinc salt
The concentration of the aqueous solution is 0.05-0.4mol/L.
5. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:It is polynary in the step 2
Carboxylic acid is in terephthalic acid (TPA), trimesic acid, Pyromellitic Acid, succinic acid, glutaric acid, citric acid, BTCA
Plant or several.
6. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:It is polynary in the step 2
The concentration of carboxylic acid aqueous solution is 0.05-0.2mol/L.
7. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:In the step 2, sun from
Son construct zinc salt and anion in primitive solution A construct polybasic carboxylic acid in primitive solution B mol ratio be 5: 1-1: 5.
8. a kind of method for sorting of Multifunctional cotton fabric as claimed in claim 1, it is characterised in that:In the step 3, bath raio
It is 1: 5-1: 20, soak time is 5-15min;In the step 4, bath raio is 1: 5-1: 20, soak time is 5-15min.