CN106751888A - A kind of high connductivity organic silicon rubber - Google Patents
A kind of high connductivity organic silicon rubber Download PDFInfo
- Publication number
- CN106751888A CN106751888A CN201611089581.6A CN201611089581A CN106751888A CN 106751888 A CN106751888 A CN 106751888A CN 201611089581 A CN201611089581 A CN 201611089581A CN 106751888 A CN106751888 A CN 106751888A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone oil
- silicon rubber
- methyl
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high connductivity organic silicon rubber, it is prepared from by the raw material of following weight parts:100 parts of methyl vinyl silicon kautschuk, 4 16 parts of siloxanes, 10 30 parts of methyl-silicone oil, 2 18 parts of vinyl silicone oil, 3 15 parts of aluminum oxide, 4 16 parts of silica, 18 parts of silane coupler, 30 80 parts of gas-phase silica, 1 15 parts of crosslinking agent, 0.02 1 parts of Graphene, 3 10 parts of nano zircite.High-conductivity silicon rubber of the present invention has the thermal conductivity of superelevation, is not available for existing conventional silicone rubber, can have and more be widely applied space.
Description
Technical field
The application belongs to organic silicon rubber technical field, more particularly to a kind of high connductivity organic silicon rubber.
Background technology
Special conductive particle is filled in usual silicone rubber and can be made into conductive silicon rubber, conductive electricity silicon rubber is common except having
Outside the characteristics such as the high-low temperature resistant of silicon rubber, the processing of ageing-resistant, easy-formation, its conductive stability and good thermal stability, volume electricity
Resistance rate is general in 3~10 Ω cm, and 50~80,5~7MPa of tensile strength, specific elongation rate is up to hardness (shore A)
265%, therefore it is widely used in conducting silica gel key, conductive silicon rubber roller, printed circuit and integrated circuit and aobvious
Show the connection between device.
The content of the invention
It is an object of the invention to provide a kind of high connductivity organic silicon rubber, to overcome deficiency of the prior art.
To achieve the above object, the present invention provides following technical scheme:
The embodiment of the present application discloses a kind of high connductivity organic silicon rubber, is prepared from by the raw material of following weight parts:Methyl
100 parts of vinyl silicon kautschuk, siloxanes 4-16 parts, methyl-silicone oil 10-30 parts, vinyl silicone oil 2-18 parts, aluminum oxide 3-
15 parts, silica 4-16 parts, silane coupler 1-8 parts, gas-phase silica 30-80 parts, crosslinking agent 1-15 parts, Graphene
0.02-1 parts, nano zircite 3-10 parts.
Additionally, the present invention also provides following technical scheme:
The high connductivity organic silicon rubber is prepared from by the raw material of following weight parts:Methyl vinyl silicon kautschuk 100
Part, 6 parts of siloxanes, 10 parts of methyl-silicone oil, 8 parts of vinyl silicone oil, 5 parts of aluminum oxide, 6 parts of silica, 6 parts of silane coupler,
30 parts of conductive carbon black, 15 parts of crosslinking agent, 0.5 part of Graphene, 10 parts of nano zircite.
Compared with prior art, invention high-conductivity silicon rubber has the thermal conductivity of superelevation, be existing conventional silicone rubber institute not
Possess, can have and more be widely applied space.
Specific embodiment
The technical scheme in the embodiment of the present invention is described in detail below, it is clear that described embodiment is only
It is a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill people
The every other embodiment that member is obtained on the premise of creative work is not made, belongs to the scope of protection of the invention.
Embodiment 1
A kind of preparation of high-conductivity silicon rubber, by weight, is prepared from the following components:Methyl vinyl silicone rubber
It is 100 parts of rubber, 6 parts of siloxanes, 10 parts of methyl-silicone oil, 8 parts of vinyl silicone oil, 5 parts of aluminum oxide, 6 parts of silica, silane coupled
6 parts of agent, 30 parts of gas-phase silica, 15 parts of crosslinking agent, 0.5 part of Graphene, 10 parts of nano zircite.
Embodiment 2
A kind of preparation of high-conductivity silicon rubber, by weight, is prepared from the following components:Methyl vinyl silicone rubber
100 parts of rubber, 10 parts of siloxanes, 10 parts of methyl-silicone oil, 2 parts of vinyl silicone oil, 5 parts of aluminum oxide, 0 part of silica 1, silane idol
4 parts of agent of connection, 40 parts of gas-phase silica, 10 parts of crosslinking agent, 0.2 part of Graphene, 6 parts of nano zircite.
Embodiment 3
A kind of preparation of high thermal conductive silicon rubber, by weight, is prepared from the following components:Methyl vinyl silicone rubber
100 parts of rubber, 4 parts of siloxanes, 12 parts of methyl-silicone oil, 12 parts of vinyl silicone oil, 15 parts of aluminum oxide, 5 parts of silica 1, silane
8 parts of coupling agent, 50 parts of gas-phase silica, 15 parts of crosslinking agent, 0.1 part of Graphene, 8 parts of nano zircite.
Comparative example 1
A kind of preparation of conventional silicone rubber, by weight, is prepared from the following components:Methyl vinyl silicone rubber is given birth to
100 parts of glue, 4 parts of siloxanes, 18 parts of methyl-silicone oil, 5 parts of vinyl silicone oil, 5 parts of calcium carbonate, 2 parts of silica, silane coupler
2 parts, 40 parts of gas-phase silica, 4 parts of crosslinking agent.
Title | Specific insulation (Ω cm) | Environmental condition |
Embodiment 1 | 5 powers of 2*10 | Normal temperature and pressure |
Embodiment 2 | 5 powers of 6*10 | Normal temperature and pressure |
Embodiment 3 | 6 powers of 1*10 | Normal temperature and pressure |
Comparative example 1 | 14 powers of 1*10 | Normal temperature and pressure |
Compared with prior art, invention high-conductivity silicon rubber has the thermal conductivity of superelevation, be existing conventional silicone rubber institute not
Possess, can have and more be widely applied space.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality
Body or operation make a distinction with another entity or operation, and not necessarily require or imply these entities or deposited between operating
In any this actual relation or order.And, term " including ", "comprising" or its any other variant be intended to
Nonexcludability is included, so that process, method, article or equipment including a series of key elements not only will including those
Element, but also other key elements including being not expressly set out, or also include being this process, method, article or equipment
Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that
Also there is other identical element in process, method, article or equipment including the key element.
The above is only the specific embodiment of the application, it is noted that for the ordinary skill people of the art
For member, on the premise of the application principle is not departed from, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as the protection domain of the application.
Claims (2)
1. a kind of high connductivity organic silicon rubber, it is characterised in that be prepared from by the raw material of following weight parts:Methyl ethylene silicon
100 parts of rubber raw rubber, siloxanes 4-16 parts, methyl-silicone oil 10-30 parts, vinyl silicone oil 2-18 parts, aluminum oxide 3-15 parts, dioxy
SiClx 4-16 parts, silane coupler 1-8 parts, gas-phase silica 30-80 parts, crosslinking agent 1-15 parts, Graphene 0.02-1 parts, nanometer
Zirconium oxide 3-10 parts.
2. high connductivity organic silicon rubber according to claim 1, it is characterised in that prepared by the raw material of following weight parts and
Into:100 parts of methyl vinyl silicon kautschuk, 6 parts of siloxanes, 10 parts of methyl-silicone oil, 8 parts of vinyl silicone oil, 5 parts of aluminum oxide,
6 parts of silica, 6 parts of silane coupler, 30 parts of conductive carbon black, 15 parts of crosslinking agent, 0.5 part of Graphene, 10 parts of nano zircite.