CN106751661A - A kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material and preparation method thereof - Google Patents
A kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material and preparation method thereof Download PDFInfo
- Publication number
- CN106751661A CN106751661A CN201611138769.5A CN201611138769A CN106751661A CN 106751661 A CN106751661 A CN 106751661A CN 201611138769 A CN201611138769 A CN 201611138769A CN 106751661 A CN106751661 A CN 106751661A
- Authority
- CN
- China
- Prior art keywords
- halogen
- free
- flame
- low cost
- retardant polycarbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material and preparation method thereof, the main points of its technical scheme are：Including following mass percent component：The 99wt% of makrolon 85, the 0.4wt% of dispersant 0, the 6wt% of toughener 0, the 10wt% of halogen-free flame retardants 0.2, the 0.6wt% of anti-dripping agent 0.3, the 0.4wt% of antioxidant 0.2, the 0.6wt% of lubricant 0.3.The present invention provides a kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, and with notch impact strength very high, anti-flammability is fine, production cost is relatively low and processing fluidity is good.
Description
【Technical field】
The invention belongs to technical field of macromolecules, and in particular to a kind of low cost, HI high impact, high glaze and halogen-free flameproof are poly-
Carbonate material and preparation method thereof.
【Background technology】
Makrolon is that molecular end is hydroxyl or carboxyl, is connected with aromatic series or aliphatic group by carbonate group
Connect, the chain macromolecule compound that repeated arrangement is formed, abbreviation PC.Makrolon has good rigidity, toughness, low temperature resistant
Property, heat resistance, glossiness, transparency and electrical insulating property etc., but its melt viscosity is big, chemical proofing is poor, be also easy to produce stress
Ftracture and to notch sensitive etc..
The fire retardant of traditional fire-retardant polycarbonate is halogenated flame retardant, although its anti-flammability is very well and addition is few,
But it can produce substantial amounts of toxic smog and carcinogenic bioxin during fire-retardant, and the halocarbon for producing can corrode
Equipment, causes secondary pollution.
As people are to environmental protection and the attention of personal safety, the country such as European Union has limited halogenated flame retardant
Use.At present, the conventional flame retardant thermoplastic resin composition of in the market is mainly phosphoric acid ester, Sulfonates and polysiloxane-based
Deng.Wherein, than larger, production cost is higher, and phosphate ester flame retardants are to poly- carbonic acid for the addition of phosphate ester flame retardants
The notch impact strength and heat distortion temperature of ester are influenceed than larger.Although Sulfonates fire retardant addition is smaller, production cost
Low, mechanical property and the heat distortion temperature influence on makrolon are small, but it causes fire retardant to be degraded due to the easy moisture absorption, fire-retardant
Effect is substantially reduced, and its flame retardant effect to polycarbonate thin wall product is little.
【The content of the invention】
The present invention seeks to overcome deficiency of the prior art, there is provided a kind of low cost, HI high impact, high glaze and Halogen resistance
Combustion makrolon material, with notch impact strength very high, anti-flammability is fine, production cost is relatively low and processing fluidity is good.
It is a further object of the present invention to provide a kind of preparation method of above-mentioned makrolon material.
The present invention is achieved by the following technical solutions：
A kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：Including following matter
Amount percent composition：
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described makrolon is tower husband Long PC IR2200, its melt flow rate (MFR) 14g/10min, Japanese Supreme Being people PC 1225L, and it melts
Body flow rate 24g/10min, husky uncle basis PC 2200R, in its melt flow rate (MFR) 25g/10min one or two
Mixture, two kinds of polycarbonate bodies of raw material mixing composition, can obtain different heat-conducting effects with arbitrary proportion mix and match
Product.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described dispersant be White Mineral Oil, gamma-aminopropyl-triethoxy-silane, ethylene-acrylic acid copolymer in one or two
Mixture, two kinds of dispersants of raw material mixing composition, it is 1 to match:1.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described toughener is acrylic ester grafted vinyl elastomer, and Shenyang section leads to, and KT-18, grafting rate is 15-20%；Fourth two
Alkene-styrol copolymer grafting polymethyl methacrylate, U.S.'s ROHM AND HAAS, the one kind in EXL2620.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described halogen-free flame retardants is sulfonate halogen-free flame retardants, still curtain chemical industry, FR-3110, active constituent content >=99.7%；Sulfonic acid
Salt halogen-free flame retardants, still curtain chemical industry, FR-400B, active constituent content >=99.7%；Poly aryl phosphate ester, Zhejiang ten thousand is contained,
PX-220, phosphorus content>10.5%；Triphenyl phosphate, Lang Sheng, TPP, phosphorus content be in 9.5% one or two, two kinds of raw materials are mixed
The halogen-free flame retardants being combined into, it is 1 to match:1 or 1:2.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
The anti-dripping agent is special modified polytetrafluoroethylene (PTFE), gloomy match distant health, SN3300B7.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described antioxidant is four [β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid] pentaerythritol esters (1010) or β-(3,5- bis-
Tert-butyl-hydroxy phenyl) the positive octadecanol ester (1076) of propionic acid presses with three (2,4- di-tert-butyl-phenyls) phosphite ester (168)
Mass ratio 1:2 compoundings.
One kind low cost as described above, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：
Described lubricant is stearic acid, calcium stearate, the double stearates of ethylene, special modified ethylene double stearate, pentaerythrites
One or two mixture in stearate or silicone powder.
The preparation method of makrolon material as described above, it is characterised in that：The preparation method is as follows：
A, batch mixing：First by makrolon, dispersant, toughener, halogen-free flame retardants, anti-dripping agent, antioxidant and lubricant
It is added in high-speed mixer, mixes 2-4min；
B, melting extrusion：Then the material that will have been mixed, is added to melting mixing in double screw extruder；
C, cooling, air-dried and pelletizing：After extruded machine melting extrusion and it is water cooled, air-dry, cut drawing.
Preparation method as described above, it is characterised in that：The processing temperature of described double screw extruder is 190-220
DEG C, screw speed is 35-40rpm/min.In actual job, each section of temperature of preferred double screw extruder is as follows：1 area's temperature
It is 60 DEG C；2 area's temperature are 230 DEG C；3 area's temperature are 220 DEG C；4 area's temperature are 210 DEG C；5 area's temperature are 220 DEG C；Die head temperature is
235℃。
Compared with prior art, the present invention has the following advantages：
One kind low cost of the invention, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, collocation different ratio
The combination of dispersant or toughener so that product with notch impact strength very high, excellent anti-flammability is resistance to well
While hot, good effect is obtained in terms of toughness and machining property, also with certain moisture resistance, can meet big
Product, small product and the processing fluidity requirement very high to injected plastics material of complicated product, and to the thickness of halogen-free flameproof product product
Degree requirement is very low, screws and is difficult to explode, and shows good processing fluidity, and production cost aspect is due to most similar
Product, is that product more has the market competitiveness.
【Specific embodiment】
The present invention is further explained with reference to embodiments：
Embodiment 1：
A. according to percentage by weight in table 1, by makrolon and dispersant 1-4 minutes, then toughener, Halogen are hindered
Combustion agent, anti-dripping agent, antioxidant and lubricant are added in the good material of above-mentioned mixing, are mixed 1-4 minutes；
B. and then by mixed material it is added to melting extrusion in double screw extruder hopper.Each section of temperature of double screw extruder
It is as follows：1 area's temperature is 60 DEG C；2 area's temperature are 230 DEG C；3 area's temperature are 220 DEG C；4 area's temperature are 210 DEG C；5 area's temperature are 220
℃；Die head temperature is 235 DEG C.The screw speed of double screw extruder is 38rpm/min.
C. after extruded machine melting extrusion and water cooled, air-dried, Qie La, product is obtained.
Table 1：The percentage by weight of each component of embodiment A1 and comparative example B1
Table 2：The percentage by weight of each component of embodiment A2 and comparative example B2
Table 3：The percentage by weight of each component of embodiment A3 and comparative example B3
The performance test results of the product embodiments of table 4 and comparative example
1st, as can be seen from Table 4, compared with the test result of product B1, PX-220 and TPP compounding Halogens hinder product A1
Combustion makrolon material adds the good flame resistance of PX-220, notch impact strength high and low production cost than independent；
2nd, product B2 is compared with the test result of product A2, plus the halogen-free and flame-retardant polycarbonate material of toughener increases than not adding
Tough dose of notch impact strength is high, and plus the halogen-free and flame-retardant polycarbonate material of toughener substantially has degraded；
3rd, compared with product B2, PX-220 and TPP compounds halogen-free and flame-retardant polycarbonate material to the test result of product B1
Than sulfonate compounding halogen-free flameproof processing fluidity it is good, but product B1 difference of the heat resistance than product B2；
4th, embodiment A1-A3 prepare makrolon material heat resistance and glossiness more preferably；
5th, the modified PC prepared using same materials and formula, different preparation methods, uses preparation method system of the invention
The performance of the PC for obtaining is more preferable；
6th, the modified PC prepared using identical preparation method, different flame retardant and toughener, uses fire retardant of the invention
It is more preferable with the flame retardant effect of PC obtained in toughener, mechanical performance and heat resistance.
Claims (10)
1. a kind of low cost, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, it is characterised in that：Including following quality
Percent composition：
2. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described makrolon is tower husband Long PC IR2200, its melt flow rate (MFR) 14g/10min, Japanese Supreme Being people PC
1225L, its melt flow rate (MFR) 24g/10min, husky uncle basis PC 2200R, in its melt flow rate (MFR) 25g/10min one
Kind or two kinds of mixture.
3. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described dispersant be White Mineral Oil, gamma-aminopropyl-triethoxy-silane, ethylene-acrylic acid copolymer in one kind or
Two kinds of mixture.
4. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described toughener is acrylic ester grafted vinyl elastomer, the poly- methyl of BS grafting
One kind in methyl acrylate, EXL2620.
5. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described halogen-free flame retardants is sulfonate halogen-free flame retardants FR-3110, sulfonate halogen-free flame retardants FR-400B, poly
Aryl phosphate ester PX-220, one or two in triphenyl phosphate TPP.
6. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：The anti-dripping agent is special modified polytetrafluoroethylene (PTFE).
7. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described antioxidant be four [β-(3,5- di-tert-butyl-hydroxy phenyls) propionic acid] pentaerythritol esters (1010) or β-
The positive octadecanol ester (1076) of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid and three (2,4- di-tert-butyl-phenyls) phosphite esters
(168) in mass ratio 1:2 compoundings.
8. one kind low cost according to claim 1, HI high impact, high glaze and halogen-free and flame-retardant polycarbonate material, its spy
Levy and be：Described lubricant is stearic acid, calcium stearate, the double stearates of ethylene, special modified ethylene double stearate, seasons
One or two mixture in penta tetrol stearate or silicone powder.
9. the preparation method of makrolon material any one of a kind of claim 1-8, it is characterised in that：The preparation side
Method is as follows：
A, batch mixing：First makrolon, dispersant, toughener, halogen-free flame retardants, anti-dripping agent, antioxidant and lubricant are added to
In high-speed mixer, mix 1-4min；
B, melting extrusion：Then the material that will have been mixed, is added to melting mixing in double screw extruder；
C, cooling, air-dried and pelletizing：It is after extruded machine melting extrusion and water cooled, air-dried and cut drawing.
10. preparation method according to claim 9, it is characterised in that：The processing temperature of described double screw extruder is
190-220 DEG C, screw speed is 35-40rpm/min.