CN106751109A - One kind weaving plastic tube composite - Google Patents
One kind weaving plastic tube composite Download PDFInfo
- Publication number
- CN106751109A CN106751109A CN201510812701.XA CN201510812701A CN106751109A CN 106751109 A CN106751109 A CN 106751109A CN 201510812701 A CN201510812701 A CN 201510812701A CN 106751109 A CN106751109 A CN 106751109A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic tube
- tube composite
- resin
- weaving plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides one kind weaving plastic tube composite, belong to plastic products production field.The composite is made up of the raw material that following parts by weight are matched：100 parts, ABS resin 15-25 parts, epoxy resin 5-15 parts, polyether-ether-ketone 8-14 parts, polytetrafluoroethylene (PTFE) 3-5 parts, graphite 1-3 parts, polyphenylene sulfide 3-7 parts, glass fibre 1-2 parts, butyronitrile emulsion 7-11 parts, aluminosilicate 1-5 parts, dodecyldimethylammonium hydroxide inner salt 2-5 parts, activated carbon 1-3 parts of polyvinyl chloride resin.This material has good physics, a mechanical integrated performance, and high mechanical strength, electrical insulating property be good, using noise is low, good flame resistance.
Description
Technical field
The invention belongs to plastic products production field, specifically a kind of weaving plastic tube composite.
Background technology
Since plastic bobbin is promoted since 20 century 70s, because its workability, high speed spin stabilization,
The distinctive advantage such as firm, long service life, obtains rapidly approval with popularization in textile industry.According to should
Difference, the pattern and material of plastic bobbin are had nothing in common with each other.What traditional textile plastic bobbin raw material were commonly used
It is divided into polypropylene (PP), RPP (GF-PP), polycarbonate (PC), nylon (PA), propionitrile alkene
- BS (ABS) etc., and weaving plastic tube prepared by these materials, static electricity resistance
Can be not so good, and noise is very big during textile production, damages human ear.Along with plastics industry
Development, manufacturer is more and more, causes the quality of in the market bobbin uneven.Because major part is used
Producer does not possess the relevant knowledge of plastic process, and some problems occur in often purchasing.
The content of the invention
The technical problems to be solved by the invention are directed to the defect of prior art presence, there is provided a kind of intensity is high,
Electrical insulating property is good, using noise is low, good flame resistance weaving plastic tube composite.
To achieve these goals, the present invention is achieved using following technical scheme：
One kind weaving plastic tube composite, the raw material matched by following parts by weight is constituted：Polyvinyl chloride resin 100
Part, ABS resin 15-25 parts, epoxy resin 5-15 parts, polyether-ether-ketone 8-14 parts, polytetrafluoroethylene (PTFE) 3-5
Part, graphite 1-3 parts, polyphenylene sulfide 3-7 parts, glass fibre 1-2 parts, butyronitrile emulsion 7-11 parts, sial
It is sour 1-5 parts, dodecyldimethylammonium hydroxide inner salt 2-5 parts, activated carbon 1-3 parts.
Preferably, described weaving plastic tube composite, the raw material matched by following parts by weight is constituted：
100 parts of polyvinyl chloride resin, 20 parts of ABS resin, 10 parts of epoxy resin, 11 parts of polyether-ether-ketone, polytetrafluoroethyl-ne
4 parts of alkene, 2 parts of graphite, 5 parts of polyphenylene sulfide, 1.5 parts of glass fibre, 9 parts of butyronitrile emulsion, aluminosilicate 3
Part, 3.5 parts of dodecyldimethylammonium hydroxide inner salt, 2 parts of activated carbon.
The preparation method of described weaving plastic tube composite is thrown after each material component is weighed well by proportioning
Enter in high-speed mixer and be well mixed, be re-fed into double screw extruder, temperature control at 210~225 DEG C,
Screw speed control carries out cool drying afterwards in 350~400rpm, extrusion, granulation.
Advantageous Effects of the invention：This material has good physics, mechanical integrated performance, and machinery is strong
Degree is high, electrical insulating property is good, using noise is low, good flame resistance.
Specific embodiment
With reference to embodiment, specific embodiment of the invention is further described.Following examples are only
For clearly illustrating technical scheme, and can not be limited the scope of the invention with this.
Embodiment 1
One kind weaving plastic tube composite, the raw material matched by following parts by weight is constituted：Polyvinyl chloride resin 100
Part, 15 parts of ABS resin, 5 parts of epoxy resin, 8 parts of polyether-ether-ketone, 3 parts of polytetrafluoroethylene (PTFE), graphite 1
Part, 3 parts of polyphenylene sulfide, 1 part of glass fibre, 7 parts of butyronitrile emulsion, 1 part of aluminosilicate, dodecyl two
2 parts of methyl betaine, 1 part of activated carbon.
The preparation method of described weaving plastic tube composite is thrown after each material component is weighed well by proportioning
Enter in high-speed mixer and be well mixed, be re-fed into double screw extruder, at 210 DEG C, screw rod turns temperature control
Speed control carries out cool drying afterwards in 350rpm, extrusion, granulation.
Embodiment 2
One kind weaving plastic tube composite, the raw material matched by following parts by weight is constituted：Polyvinyl chloride resin 100
Part, 25 parts of ABS resin, 15 parts of epoxy resin, 14 parts of polyether-ether-ketone, 5 parts of polytetrafluoroethylene (PTFE), graphite
3 parts, 7 parts of polyphenylene sulfide, 2 parts of glass fibre, 11 parts of butyronitrile emulsion, 5 parts of aluminosilicate, dodecyl
5 parts of dimethyl betaine, 3 parts of activated carbon.
The preparation method of described weaving plastic tube composite is thrown after each material component is weighed well by proportioning
Enter in high-speed mixer and be well mixed, be re-fed into double screw extruder, at 225 DEG C, screw rod turns temperature control
Speed control carries out cool drying afterwards in 400rpm, extrusion, granulation.
Embodiment 3
One kind weaving plastic tube composite, the raw material matched by following parts by weight is constituted：Polyvinyl chloride resin 100
Part, 20 parts of ABS resin, 10 parts of epoxy resin, 11 parts of polyether-ether-ketone, 4 parts of polytetrafluoroethylene (PTFE), graphite
2 parts, 5 parts of polyphenylene sulfide, 1.5 parts of glass fibre, 9 parts of butyronitrile emulsion, 3 parts of aluminosilicate, dodecyl
3.5 parts of dimethyl betaine, 2 parts of activated carbon.
The preparation method of described weaving plastic tube composite is thrown after each material component is weighed well by proportioning
Enter in high-speed mixer and be well mixed, be re-fed into double screw extruder, at 220 DEG C, screw rod turns temperature control
Speed control carries out cool drying afterwards in 400rpm, extrusion, granulation.
The above, is only embodiments of the invention, is not to make any other form to the present invention
Limitation, and any modification for being made according to technical spirit of the invention or equivalent variations, still fall within institute of the present invention
Claimed scope.
Claims (3)
1. a kind of weaving plastic tube composite, it is characterised in that the raw material group matched by following parts by weight
Into：100 parts of polyvinyl chloride resin, ABS resin 15-25 parts, epoxy resin 5-15 parts, polyether-ether-ketone 8-14 parts,
Polytetrafluoroethylene (PTFE) 3-5 parts, graphite 1-3 parts, polyphenylene sulfide 3-7 parts, glass fibre 1-2 parts, butyronitrile breast
Liquid 7-11 parts, aluminosilicate 1-5 parts, dodecyldimethylammonium hydroxide inner salt 2-5 parts, activated carbon 1-3 parts.
2. it is according to claim 1 weaving plastic tube composite, it is characterised in that by following weight
The raw material composition of number proportioning：100 parts of polyvinyl chloride resin, 20 parts of ABS resin, 10 parts of epoxy resin, polyethers
11 parts of ether ketone, 4 parts of polytetrafluoroethylene (PTFE), 2 parts of graphite, 5 parts of polyphenylene sulfide, 1.5 parts of glass fibre, fourth
9 parts of nitrile emulsion, 3 parts of aluminosilicate, 3.5 parts of dodecyldimethylammonium hydroxide inner salt, 2 parts of activated carbon.
3. it is according to claim 1 weaving plastic tube composite preparation method, it is characterised in that：
It is to be well mixed in input high-speed mixer after each material component is weighed well by proportioning, is re-fed into twin-screw and squeezes
Go out in machine, at 210~225 DEG C, screw speed control is granulated temperature control in 350~400rpm, extrusion,
Cool drying is carried out afterwards.