CN106746649A - The light yellow glaze of high temperature light and its ceramic and preparation method - Google Patents
The light yellow glaze of high temperature light and its ceramic and preparation method Download PDFInfo
- Publication number
- CN106746649A CN106746649A CN201611149841.4A CN201611149841A CN106746649A CN 106746649 A CN106746649 A CN 106746649A CN 201611149841 A CN201611149841 A CN 201611149841A CN 106746649 A CN106746649 A CN 106746649A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- high temperature
- light
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to ceramic technology field, and in particular to the light yellow glaze of high temperature light and its ceramic and preparation method.The light yellow glaze of high temperature light with Suzhou soil, feldspar, aluminum oxide, calcite, zinc oxide, burn talcum, spodumene, boron frit, parcel yellow material and carry out dispensing as raw material.This method is with unique novel blank glaze colorant formulas, from the raw material of high-quality, by rational ceramic production technology and calcining system, so that product has high intensity, high compactness, anti-aging, it is corrosion-resistant, anti-leakage, heat endurance is good, do not ftracture, it is indeformable, it is pin-free, the defects such as contracting glaze, glaze colours presents bright-coloured beautiful, pure and honest elegance, it is dignified, it is dignified, it is rich in third dimension, more artistic characteristics, simplify production technology, improve production efficiency, reduce production cost, the large batch of production of ceramic wine bottle can be met, obtain the favor of numerous clients.
Description
Technical field
The present invention relates to ceramic technology field, and in particular to the light yellow glaze of high temperature light and its ceramic and preparation method.
Background technology
Traditional ceramic light yellow glaze of light typically using 700-800 DEG C of low-temperature glaze, need to repeatedly burn till, and produce
Technics comparing is cumbersome, and glaze planar defect is more, and if any pin hole, contracting glaze etc., and color is thin, low in glossiness, colour generation are dull, product
It is difficult to propose shelves upgrading, it is impossible to meet cultural demand of multi-level, the multi-field consumer group to ceramic wine bottle.Glaze paint system defective
Product are defective work, both waste resource, and the performance of enterprises is reduced again, do not meet the requirement of low-carbon environment-friendly production.With people
Living standard and aesthetic raising, have to the appearance luster of ceramic wine bottle requirement higher, particularly bright yellow decoration and
More people are interspersed to be liked, at present prepare yellow glaze be also difficult to meet require, no matter in terms of preparation technology or into
Color effect aspect is required for further research and improves.
The content of the invention
The purpose of the present invention is, in order to solve the above problems, using rational glaze colorant formulas, prepares and burns till work
Skill, there is provided a kind of ceramic wine bottle light yellow glaze of high temperature light and its ceramic.Particularly make bottle, ceramic wine bottle high temperature
The making of the light yellow glaze of light is innovated on the basis of traditional yellow glaze, with unique novel blank glaze colorant formulas, choosing
With the raw material of high-quality, by rational ceramic production technology and calcining system so that product have high intensity, high compactness,
The defect such as anti-aging, corrosion-resistant, anti-leakage, heat endurance is good, do not ftracture, indeformable, pin-free, contracting glaze, glaze colours presents bright-coloured
It is beautiful, pure and honest it is elegant, dignified, dignity, be rich in third dimension, more artistic characteristics, simplify production technology, improve production effect
Rate, reduces production cost, can meet the large batch of production of ceramic wine bottle, obtains the favor of numerous clients.
Technical scheme is as follows：
The light yellow glaze of high temperature light, by following raw material glaze by weight：5~7 parts of Suzhou soil, 11~14 parts of feldspar,
2~4 parts of aluminum oxide, 9~12 parts of calcite, 6~9 parts of zinc oxide, 3~5 parts of talcum of burning, 17~20 parts of spodumene, boron frit 28
~31 parts, 9~11 parts of parcel yellow material.
Described parcel yellow material, by following raw material by weight, 8~12 parts of cadmium sulfide, acetic acid zirconium 52~
56 parts, 5~8 parts of vulcanized sodium, 23~26 parts of waterglass, 2~3 parts of lithium fluoride.
Wrap up the preparation method of yellow material, including procedure below：Cadmium sulfide and acetic acid zirconium are respectively prepared the aqueous solution, then mutually
Mix to form mixed liquor, vulcanized sodium forms sodium sulfide solution with water dissolves, by described mixed liquor and sodium sulfide solution
At the uniform velocity to import and be stirred mixing in mixing apparatus, produce co-precipitation, sediment is scrubbed, dry, fine grinding, to allocate use water into again dilute
The water glass solution stirring mixing released, with acid adjustment pH value to acidity, congeal into colloid, then through washing, filtering, decationizing,
Drying simultaneously mixes with lithium fluoride, then through temperature calcination 15-20 minutes of 1020-1030 DEG C, obtains wrapping up yellow material.
Described glaze presses 1.28-1.3 parts of You Liao ﹕ Qiu ﹕ water=1 ﹕ 1.27-1.32 ﹕, the proportioning of the ﹕ 1.3 of preferably 1 ﹕ 1.29, ball
It is 42 ~ 48 hours to consume time, preferably 43 hours, the sieving of 120 mesh is crossed after ball milling and obtains final product the light yellow glaze of high temperature light.
The preparation method of the light yellow glaze ceramic of high temperature light, including procedure below：
Ceramic body is carried out into biscuiting, biscuiting temperature is 1020 DEG C；
Ceramic body after biscuiting applies the light yellow glaze of high temperature light using the method for leaching glaze, and the glaze firing after dry, glaze firing uses roller kilns
Oxidizing flame burns till, and maximum sintering temperature is 1205-1208 DEG C.
Described glaze firing firing period is 4.5 ~ 5 hours, and sintering curve is：Kiln temperature is in 1 ~ 1.5 hour by kiln temperature
At the uniform velocity rise to 840 DEG C, then maximum sintering temperature at the uniform velocity risen in 1 ~ 1.5 hour, fire insulation high 8-10 minutes, then again 20 ~
1012 DEG C are down in 30 minutes, then quickly 850 DEG C were down in 20 minutes, be then down to 560 DEG C at a slow speed in 0.5 ~ 1 hour again,
Room temperature is finally naturally cooled to again, kiln discharge is burnt till, and is after the assay was approved qualified products.
Described ceramic body, is made up, 58 parts of water-washed kaoline, Changxing white clay of following raw material according to parts by weight proportioning
18 parts, 11 parts of Fujian porcelain stone, 12 parts of feldspar, 1 part of talcum.
The beneficial effects of the invention are as follows：This method use the light yellow glaze colorant of high temperature light and glaze formula of unique novelty with
And specific preparation technology and calcining system, cadmium sulfide, acetic acid zirconium, vulcanized sodium, waterglass, five kinds of materials of lithium fluoride are used pioneeringly
Material, chromophoric mechanism is gone out by science matched combined according to a certain percentage, and with cadmium as chromogen, acetic acid zirconium is inclusion enclave, and its is heat-resisting
Good, the good stability of property, it is less sensitive to glaze and atmosphere, using lithium fluoride as mineralizer, in colour-stable, coated yellow material
The blank that high temperature lacks light yellow glaze is filled up, on the premise of parcel citrine lattice are not destroyed, it is harmless that powder is contacted with people's table body
, it is rational to burn because of the uniqueness of its technique so that the light yellow glaze of high temperature light most environment-friendly advantage prepared by coated yellow material
Base glaze is promoted to combine closely into system, glaze paint is smooth bright and clean, glaze colours presents bright-coloured beautiful, smooth soft, simple and honest generous, rich vertical
Body-sensing, more artistic characteristics, the light yellow glaze of new type high temperature light with ornamental value very high.Improve product specification and meet city
The new demand in field, the product being made using the method has high intensity, and high compactness, anti-aging is corrosion-resistant, anti-leakage, and heat is steady
It is qualitative good, do not ftracture, indeformable, pin-free, contracting glaze, glaze bubble etc. defect, lead, quantity of cadmium release be respectively smaller than 0.1ppm and
0.01ppm, reaches international most stringent of standard regulation, can ensure that user health, and with preferable presentation quality and performance
Index, is a kind of ideal product increased economic efficiency.And saved by the production technology and calcining system that adjust product
Many valuable energy, reduce enterprise's production capacity, and meet the requirement of low-carbon environment-friendly production.
Specifically in technical solution of the present invention：
1st, feldspar：Chemical analysis is water-free alkali metal or alkaline earth metal aluminosilicate, mainly potassium, sodium, calcium and a small amount of barium
Aluminosilicate, in ceramic batch as flux act on, mainly make flux in glaze, be to be formed glass phase it is main into
Point, increase transparency.
2nd, Suzhou soil：It is purity kaolin very high, its chemical composition is sufficiently close to kaolinic theory value, and color is pure white,
Refractoriness is high.
3rd, calcite：Natural calcium carbonate mineral, chemical formula is CaCO3, generally white, sometimes in pelletized form or tabular,
Play flux after decomposition, glossiness and translucency can be improved in glaze.
4th, boron frit：A kind of ceramics frit being made of quartz and borax, plays flux in Production of Ceramics.
5th, aluminum oxide：White or blush, water insoluble, relative density 3.5-3.9.
6th, zinc oxide：White hex crystal or powder, it is water insoluble, the firing temperature of high-temperature glaze is reduced, to the mechanical strength of glaze,
Elastic melting behaviour and heat resistance can play good effect.The glossiness of glaze can also be increased, whiteness increases burning till for glaze
Scope.
7th, talcum is burnt：Talcum is a kind of natural hydrosilicate mineral, and its preferable chemical formula is：3MGO-4SiO2-
H2O,Pure talcum is white, burns talcum and destroys the original laminated structure of talcum, prevents from causing ceramic to be opened when burning till
Split.Increase glaze paint without light effect, the generation of body-glaze intermediate layer can be promoted, improve hardness of glaze surface.
8th, spodumene：Crystal is thick, and often in long column shape, aggregate is plate-like or compact massive, and color is shallow white, hardness
It is 6.5-7, is acted on as strong flux in ceramics, reduce firing temperature, improve vitreous degree, line is reduced in sintering process and is received
Contracting, so as to reduce dimensional discrepancy.
9th, acetic acid zirconium：For paint drier and building materials waterproofing agent etc..
10th, cadmium sulfide：Amorphous powder, lemon yellow to orange-yellow, in water insoluble, acid and alkali.
11st, vulcanized sodium：It is inorganic compound, colorless crystalline powder, hygroscopicity is strong, soluble in water, and the aqueous solution is in alkalescence.
12nd, waterglass：It is sodium silicate solution state, colourless, slightly transparent or semitransparent viscous liquid.
13rd, lithium fluoride：It is alkali halide, is at room temperature white crystal, is insoluble in water.
Specific embodiment
It is described in conjunction with the embodiments specific embodiment of the invention.
Embodiment 1：
（1）Parcel yellow material is prepared, by following raw material by weight, 10.8 parts of cadmium sulfide, 56 parts of acetic acid zirconium, vulcanization
5 parts of sodium, 24.5 parts of waterglass, 3 parts of lithium fluoride.
Cadmium sulfide and acetic acid zirconium are respectively prepared the aqueous solution, then are mutually mixed, vulcanized sodium water dissolves are molten by above two
Liquid is at the uniform velocity imported and be stirred in special mixing apparatus mixing, produces co-precipitation, and sediment is scrubbed, dry, fine grinding, match somebody with somebody again
Enter the water glass solution stirring mixing of dilute with water, with acid adjustment pH value to acidity, congeal into colloid, then through washing, filtering, go
Cation, drying simultaneously mixes with lithium fluoride, then through temperature calcination 15-20 minutes of 1025 DEG C, obtains preparing ceramic wine bottle use
The parcel yellow material of the light yellow glaze of high temperature light.
（2）The light yellow glaze of high temperature light, by following raw material glaze by weight：5.6 parts of Suzhou soil, feldspar 14
Part, 4 parts of aluminum oxide, 9.4 parts of calcite, 6 parts of zinc oxide, 3 parts of talcum of burning, 18.6 parts of spodumene, 28 parts of boron frit, parcel yellow
9 parts of material.
（3）To above-mentioned dispensing by material：Ball：Water=1：1.3：1.29 proportioning enters a ball milling, through 48 hours ball millings, goes out a mistake
Sieve series obtains the ceramic wine bottle light yellow glaze of high temperature light.
（4）Ceramic body is carried out into biscuiting, biscuiting temperature is 1020 DEG C；
Ceramic body after biscuiting applies the light yellow glaze of high temperature light using the method for leaching glaze, and the glaze firing after dry, glaze firing uses roller kilns
Oxidizing flame burns till, and maximum sintering temperature is 1206 DEG C.
Described glaze firing firing period is 4.5 ~ 5 hours, and sintering curve is：Kiln temperature is in 1 ~ 1.5 hour by kiln temperature
At the uniform velocity rise to 840 DEG C, then maximum sintering temperature at the uniform velocity risen in 1 ~ 1.5 hour, fire insulation high 8-10 minutes, then again 20 ~
1012 DEG C are down in 30 minutes, then quickly 850 DEG C were down in 20 minutes, be then down to 560 DEG C at a slow speed in 0.5 ~ 1 hour again,
Room temperature is finally naturally cooled to again, kiln discharge is burnt till, and is after the assay was approved qualified products.
Described ceramic body, is made up, 58 parts of water-washed kaoline, Changxing white clay of following raw material according to parts by weight proportioning
18 parts, 11 parts of Fujian porcelain stone, 12 parts of feldspar, 1 part of talcum.
Embodiment 2：
（1）Parcel yellow material is prepared, by following raw material by weight, 8 parts of cadmium sulfide, 54.7 parts of acetic acid zirconium, vulcanization
8 parts of sodium, 23 parts of waterglass, 2.6 parts of lithium fluoride.
Cadmium sulfide and acetic acid zirconium are respectively prepared the aqueous solution, then are mutually mixed, vulcanized sodium water dissolves are molten by above two
Liquid is at the uniform velocity imported and be stirred in special mixing apparatus mixing, produces co-precipitation, and sediment is scrubbed, dry, fine grinding, match somebody with somebody again
Enter the water glass solution stirring mixing of dilute with water, with acid adjustment pH value to acidity, congeal into colloid, then through washing, filtering, go
Cation, drying simultaneously mixes with lithium fluoride, then through temperature calcination 15-20 minutes of 1028 DEG C, obtains preparing ceramic wine bottle use
The parcel yellow material of the light yellow glaze of high temperature light.
（2）The light yellow glaze of high temperature light, by following raw material glaze by weight：5 parts of Suzhou soil, feldspar 12.3
Part, 2 parts of aluminum oxide, 12 parts of calcite, 6.5 parts of zinc oxide, 5 parts of talcum of burning, 17 parts of spodumene, 29.8 parts of boron frit, parcel are yellow
11 parts of colorant.
（3）To above-mentioned dispensing by material：Ball：The proportioning of the ﹕ 1.28 of water=1 ﹕ 1.27 enters a ball milling, through 43 hours ball millings, goes out cylinder
Sieving is obtained the ceramic wine bottle light yellow glaze of high temperature light.
（4）Ceramic body is carried out into biscuiting, biscuiting temperature is 1020 DEG C；
Ceramic body after biscuiting applies the light yellow glaze of high temperature light using the method for leaching glaze, and the glaze firing after dry, glaze firing uses roller kilns
Oxidizing flame burns till, and maximum sintering temperature is 1205 DEG C.
Described glaze firing firing period is 4.5 ~ 5 hours, and sintering curve is：Kiln temperature is in 1 ~ 1.5 hour by kiln temperature
At the uniform velocity rise to 840 DEG C, then maximum sintering temperature at the uniform velocity risen in 1 ~ 1.5 hour, fire insulation high 8-10 minutes, then again 20 ~
1012 DEG C are down in 30 minutes, then quickly 850 DEG C were down in 20 minutes, be then down to 560 DEG C at a slow speed in 0.5 ~ 1 hour again,
Room temperature is finally naturally cooled to again, kiln discharge is burnt till, and is after the assay was approved qualified products.
Described ceramic body, is made up, 58 parts of water-washed kaoline, Changxing white clay of following raw material according to parts by weight proportioning
18 parts, 11 parts of Fujian porcelain stone, 12 parts of feldspar, 1 part of talcum.
Embodiment 3：
（1）Prepare parcel yellow material, 12 parts of cadmium sulfide, 52 parts of acetic acid zirconium, vulcanized sodium by following raw material by weight
7.4 parts, 26 parts of waterglass, 2 parts of lithium fluoride.
Cadmium sulfide and acetic acid zirconium are respectively prepared the aqueous solution, then are mutually mixed, vulcanized sodium water dissolves are molten by above two
Liquid is at the uniform velocity imported and be stirred in special mixing apparatus mixing, produces co-precipitation, and sediment is scrubbed, dry, fine grinding, match somebody with somebody again
Enter the water glass solution stirring mixing of dilute with water, with acid adjustment pH value to acidity, congeal into colloid, then through washing, filtering, go
Cation, drying simultaneously mixes with lithium fluoride, then through temperature calcination 15-20 minutes of 1027 DEG C, obtains preparing ceramic wine bottle use
The parcel yellow material of the light yellow glaze of high temperature light.
（2）The light yellow glaze of high temperature light, by following raw material glaze by weight：7 parts of Suzhou soil, 11 parts of feldspar,
3.8 parts of aluminum oxide, 9 parts of calcite, 9 parts of zinc oxide, 3.7 parts of talcum of burning, 20 parts of spodumene, 31 parts of boron frit, parcel yellow material
10.3 parts.
（3）To above-mentioned dispensing by material：Ball：The proportioning of the ﹕ 1.3 of water=1 ﹕ 1.32 enters a ball milling, through 42 hours ball millings, goes out a mistake
Sieve series obtains the ceramic wine bottle light yellow glaze of high temperature light.
（4）Ceramic body is carried out into biscuiting, biscuiting temperature is 1020 DEG C；
Ceramic body after biscuiting applies the light yellow glaze of high temperature light using the method for leaching glaze, and the glaze firing after dry, glaze firing uses roller kilns
Oxidizing flame burns till, and maximum sintering temperature is 1208 DEG C.
Described glaze firing firing period is 4.5 ~ 5 hours, and sintering curve is：Kiln temperature is in 1 ~ 1.5 hour by kiln temperature
At the uniform velocity rise to 840 DEG C, then maximum sintering temperature at the uniform velocity risen in 1 ~ 1.5 hour, fire insulation high 8-10 minutes, then again 20 ~
1012 DEG C are down in 30 minutes, then quickly 850 DEG C were down in 20 minutes, be then down to 560 DEG C at a slow speed in 0.5 ~ 1 hour again,
Room temperature is finally naturally cooled to again, kiln discharge is burnt till, and is after the assay was approved qualified products.
Claims (7)
1. the light yellow glaze of high temperature light, it is characterised in that by following raw material glaze by weight：5~7 parts of Suzhou soil,
11~14 parts of feldspar, 2~4 parts of aluminum oxide, 9~12 parts of calcite, 6~9 parts of zinc oxide, 3~5 parts of talcum of burning, spodumene 17~
20 parts, 28~31 parts of boron frit, 9~11 parts of parcel yellow material.
2. the light yellow glaze of high temperature light according to claim 1, it is characterised in that described parcel yellow material, by following original
Material by weight, 8~12 parts of cadmium sulfide, 52~56 parts of acetic acid zirconium, 5~8 parts of vulcanized sodium, 23~26 parts of waterglass,
2~3 parts of lithium fluoride.
3. the light yellow glaze of high temperature light according to claim 1, it is characterised in that the preparation method of parcel yellow material, including
Procedure below：Cadmium sulfide and acetic acid zirconium are respectively prepared the aqueous solution, then are mixed to form mixed liquor mutually, vulcanized sodium water dissolves shape
Into sodium sulfide solution, mixing is stirred during described mixed liquor and sodium sulfide solution are at the uniform velocity imported into mixing apparatus, produced
Raw co-precipitation, sediment is scrubbed, drys, fine grinding, the water glass solution stirring mixing of allocating dilute with water into again, adjust pH with acid
It is worth acidity, congeal into colloid, then through washing, filtering, decationizing, drying simultaneously mixes with lithium fluoride, then through 1020-1030
DEG C temperature calcination 15-20 minutes, obtain wrap up yellow material.
4. the light yellow glaze of high temperature light according to claim 1, it is characterised in that preparation method, including procedure below, it is described
Glaze press 1.28-1.3 parts of You Liao ﹕ Qiu ﹕ water=1 ﹕ 1.27-1.32 ﹕, the proportioning of the ﹕ 1.3 of preferably 1 ﹕ 1.29, Ball-milling Time is 42 ~
48 hours, preferably 43 hours, the sieving of 120 mesh is crossed after ball milling and obtains final product the light yellow glaze of high temperature light.
5. the preparation method of the ceramic of the light yellow glaze of high temperature light according to any one of claim 1 to 4, its feature exists
In, including procedure below：
Ceramic body is carried out into biscuiting, biscuiting temperature is 1020 DEG C；
Ceramic body after biscuiting applies the light yellow glaze of high temperature light using the method for leaching glaze, and the glaze firing after dry, glaze firing uses roller kilns
Oxidizing flame burns till, and maximum sintering temperature is 1205-1208 DEG C.
6. the preparation method of the ceramic of the light yellow glaze of high temperature light according to claim 5, it is characterised in that described
Glaze firing firing period is 4.5 ~ 5 hours, and sintering curve is：Kiln temperature was at the uniform velocity risen to 840 DEG C in 1 ~ 1.5 hour by kiln temperature,
Maximum sintering temperature was at the uniform velocity risen in 1 ~ 1.5 hour again, then fire insulation high 8-10 minutes is down in 20 ~ 30 minutes again
1012 DEG C, then 850 DEG C quickly were down in 20 minutes, then 560 DEG C are down at a slow speed in 0.5 ~ 1 hour again, it is finally naturally cold again
But to room temperature, kiln discharge is burnt till, is after the assay was approved qualified products.
7. the preparation method of the ceramic of the light yellow glaze of high temperature light according to claim 5, it is characterised in that described
Ceramic body, is made up, 58 parts of water-washed kaoline, 18 parts of Changxing white clay, Fujian porcelain stone of following raw material according to parts by weight proportioning
11 parts, 12 parts of feldspar, 1 part of talcum.