CN106739269A - 一种防护耐蚀复合金属制品 - Google Patents
一种防护耐蚀复合金属制品 Download PDFInfo
- Publication number
- CN106739269A CN106739269A CN201611041787.1A CN201611041787A CN106739269A CN 106739269 A CN106739269 A CN 106739269A CN 201611041787 A CN201611041787 A CN 201611041787A CN 106739269 A CN106739269 A CN 106739269A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- niobium
- zirconium
- metal layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种防护耐蚀复合金属制品,包括表层的第一金属层和内层的第二金属层,所述第一金属层由锆、铌、铁、铬、钼以及钒组成,各成分所占重量份数分别为:所述锆占70‑77份,所述铌占13‑16份,所述铁占5‑8份,所述铬占4‑7份,所述钼占3‑6份,所述钒占2‑5份,所述第二金属层由锆、铌、锡、镍、钽以及钇组成,各成分所占重量份数分别为:所述锆占66‑72份,所述铌占14‑17份,所述锡占10‑14份,所述镍占4‑9份,所述钽占3‑7份,所述钇占1‑5份。本发明采用复合结构设置,具有防护性好、耐蚀性佳、力学强度好的特点。
Description
技术领域
本发明涉及一种防护耐蚀复合金属制品。
背景技术
金属制品行业包括结构性金属制品制造、金属工具制造、集装箱及金属包装容器制造、不锈钢及类似日用金属制品制造等。随着社会的进步和科技的发展,金属制品在工业、农业以及人们的生活各个领域的运用越来越广泛,也给社会创造越来越大的价值。现有技术中使用的各种金属制品在进行生产时往往仅生产单个独立结构,但是使用时往往也存在着很多问题,如单一材料使用时往往性能比较单一,无法达到当下企业的预期使用效果,无法大范围推广使用。
发明内容
本发明的目的在于提供一种采用复合结构设置,具有防护性好、耐蚀性佳、力学强度好的特点的防护耐蚀复合金属制品。
本发明的技术方案是,一种防护耐蚀复合金属制品,包括表层的第一金属层和内层的第二金属层,所述第一金属层由锆、铌、铁、铬、钼以及钒组成,各成分所占重量份数分别为:所述锆占70-77份,所述铌占13-16份,所述铁占5-8份,所述铬占4-7份,所述钼占3-6份,所述钒占2-5份,所述第二金属层由锆、铌、锡、镍、钽以及钇组成,各成分所占重量份数分别为:所述锆占66-72份,所述铌占14-17份,所述锡占10-14份,所述镍占4-9份,所述钽占3-7份,所述钇占1-5份。
在本发明一个较佳实施例中,所述第一金属层各成分所占重量份数具体为:所述锆占71份,所述铌占14份,所述铁占6份,所述铬占5份,所述钼占4份,所述钒占3份,所述第二金属层各成分所占重量份数具体为:所述锆占67份,所述铌占15份,所述锡占11份,所述镍占5份,所述钽占4份,所述钇占2份。
在本发明一个较佳实施例中,所述第一金属层各成分所占重量份数具体为:所述锆占76份,所述铌占15份,所述铁占7份,所述铬占6份,所述钼占5份,所述钒占4份,所述第二金属层各成分所占重量份数具体为:所述锆占71份,所述铌占16份,所述锡占13份,所述镍占8份,所述钽占6份,所述钇占4份。
本发明所述为一种防护耐蚀复合金属制品,本发明采用复合结构设置,具有防护性好、耐蚀性佳、力学强度好的特点。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种防护耐蚀复合金属制品,包括表层的第一金属层和内层的第二金属层,所述第一金属层由锆、铌、铁、铬、钼以及钒组成,各成分所占重量份数分别为:所述锆占70-77份,所述铌占13-16份,所述铁占5-8份,所述铬占4-7份,所述钼占3-6份,所述钒占2-5份,所述第二金属层由锆、铌、锡、镍、钽以及钇组成,各成分所占重量份数分别为:所述锆占66-72份,所述铌占14-17份,所述锡占10-14份,所述镍占4-9份,所述钽占3-7份,所述钇占1-5份。
进一步地,所述第一金属层各成分所占重量份数具体为:所述锆占71份,所述铌占14份,所述铁占6份,所述铬占5份,所述钼占4份,所述钒占3份,所述第二金属层各成分所占重量份数具体为:所述锆占67份,所述铌占15份,所述锡占11份,所述镍占5份,所述钽占4份,所述钇占2份。
进一步地,所述第一金属层各成分所占重量份数具体为:所述锆占76份,所述铌占15份,所述铁占7份,所述铬占6份,所述钼占5份,所述钒占4份,所述第二金属层各成分所占重量份数具体为:所述锆占71份,所述铌占16份,所述锡占13份,所述镍占8份,所述钽占6份,所述钇占4份。
通过各成分不同重量百分比进行配比,使得得到的产品性能高低不一。
本发明所述为一种防护耐蚀复合金属制品,本发明采用复合结构设置,具有防护性好、耐蚀性佳、力学强度好的特点。
以上所述仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种防护耐蚀复合金属制品,包括表层的第一金属层和内层的第二金属层,其特征在于:所述第一金属层由锆、铌、铁、铬、钼以及钒组成,各成分所占重量份数分别为:所述锆占70-77份,所述铌占13-16份,所述铁占5-8份,所述铬占4-7份,所述钼占3-6份,所述钒占2-5份,所述第二金属层由锆、铌、锡、镍、钽以及钇组成,各成分所占重量份数分别为:所述锆占66-72份,所述铌占14-17份,所述锡占10-14份,所述镍占4-9份,所述钽占3-7份,所述钇占1-5份。
2.根据权利要求1所述的防护耐蚀复合金属制品,其特征在于:所述第一金属层各成分所占重量份数具体为:所述锆占71份,所述铌占14份,所述铁占6份,所述铬占5份,所述钼占4份,所述钒占3份,所述第二金属层各成分所占重量份数具体为:所述锆占67份,所述铌占15份,所述锡占11份,所述镍占5份,所述钽占4份,所述钇占2份。
3.根据权利要求1所述的防护耐蚀复合金属制品,其特征在于:所述第一金属层各成分所占重量份数具体为:所述锆占76份,所述铌占15份,所述铁占7份,所述铬占6份,所述钼占5份,所述钒占4份,所述第二金属层各成分所占重量份数具体为:所述锆占71份,所述铌占16份,所述锡占13份,所述镍占8份,所述钽占6份,所述钇占4份。