CN106732849B - 一种熔剂坩埚盖的制备方法 - Google Patents
一种熔剂坩埚盖的制备方法 Download PDFInfo
- Publication number
- CN106732849B CN106732849B CN201611183831.2A CN201611183831A CN106732849B CN 106732849 B CN106732849 B CN 106732849B CN 201611183831 A CN201611183831 A CN 201611183831A CN 106732849 B CN106732849 B CN 106732849B
- Authority
- CN
- China
- Prior art keywords
- crucible cover
- flux
- polyethylene film
- preparation
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明具体涉及一种熔剂坩埚盖的制备方法。其技术方案是：将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物30~50wt%的纯水，混合0.5~2小时，在10~40℃的条件下密封静置1~120小时，制得四硼酸锂浆料。将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在10~100℃条件下干燥，制得熔剂坩埚盖。所述圆筒模具的衬底亦为一层聚乙烯膜。所述一层聚乙烯膜的厚度为0.005~0.01mm。所述硼酸粉末的H3BO3含量≥99.9wt%，硼酸粉末的粒度小于0.5mm。所述碳酸锂粉末的Li2CO3含量≥99.9wt%，碳酸锂粉末的粒度小于0.5mm。本发明具有操作简便、防迸溅效果好、节约时间和效率高的特点。
Description
技术领域
本发明属于熔剂坩埚技术领域。具体涉及一种熔剂坩埚盖的制备方法。
背景技术
目前，在XRF熔融制备玻璃片样品时，需要用熔剂（四硼酸锂或四硼酸锂偏硼酸锂）在铂金坩埚内熔融试样。其方法是现将熔剂与试样混合后，置于铂金坩埚中。再均匀覆盖一层熔剂，防止熔融过程中的迸溅。用粉末熔剂覆盖时，由于同种粉末熔剂融化速度高于块状熔剂，在熔融反应开始后，很短的时间内随熔剂一起融化，因此，覆盖效率低。由于粉末颗粒间没有结合力，局部熔解反应的一个微小的体积变化就使覆盖层破坏失效。
上述技术缺陷在于：1、均匀铺撒熔剂耗时长；2、覆盖层厚度很难控制；3、熔剂用量很难控制；4、覆盖操作无法批量完成，效率低。
发明内容
本发明旨在克服现有技术缺陷，目的是提供一种制作简单、使用方便、防迸溅效果好和节约时间的熔剂坩埚盖的制备方法。
为实现上述目的，本发明采用的技术方案的步骤是：
步骤一、将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物30~50wt%的纯水，混合0.5~2小时，在10~40℃的条件下，密封静置1~120小时，制得四硼酸锂浆料。
步骤二、将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在10~100℃条件下干燥，制得熔剂坩埚盖。
所述圆筒模具的衬底亦为一层聚乙烯膜。
所述一层聚乙烯膜的厚度为0.005~0.01mm。
所述硼酸粉末的H3BO3含量≥99.9wt%，硼酸粉末的粒度小于0.5mm。
所述碳酸锂粉末的Li2CO3含量≥99.9wt%，碳酸锂粉末的粒度小于0.5mm。
所述圆筒模具的内径为铂金坩埚内经的0.9~0.95倍；所述圆筒模具的材质为塑料、木质和钢质中的一种。
本发明充分利用四硼酸锂微溶于水的特点，以四硼酸锂和水为结合剂使四硼酸锂粘黏在聚乙烯膜表面，脱水中成型，直接制得熔剂坩埚盖。使用所制备熔剂坩埚盖与现有技术相比具有如下积极效果：
1、本发明无需仔细铺撒四硼酸锂，将所制备的熔剂坩埚盖直接覆盖即可，节约时间。
2、熔剂坩埚盖厚度一致，防护效果好。
3、熔剂坩埚盖比粉状四硼酸锂熔解速度低，局部强度高，故熔剂坩埚盖的覆盖效率高。
因此，本发明具有操作简便、防迸溅效果好、节约时间和效率高的特点。
具体实施方式
下面结合具体实施方式对本发明做进一步描述，并非对其保护范围的限制。
本具体实施方式中：所述硼酸粉末的H3BO3含量≥99.9wt%，硼酸粉末的粒度小于0.5mm；所述碳酸锂粉末的Li2CO3含量≥99.9wt%，碳酸锂粉末的粒度小于0.5mm；所述圆筒模具的内径为铂金坩埚内经的0.9~0.95倍。实施例中不再赘述。
实施例1
一种熔剂坩埚盖的制备方法。本实施例所述制备方法是：
步骤一、将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物30~40wt%的纯水，混合0.5~1.4小时，在10~40℃的条件下，密封静置1~80小时，制得四硼酸锂浆料。
步骤二、将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在10~60℃条件下干燥，制得熔剂坩埚盖。
所述圆筒模具的衬底亦为一层聚乙烯膜；所述一层聚乙烯膜的厚度为0.005~0.008mm。
所述圆筒模具的材质为塑料。
实施例2
一种熔剂坩埚盖的制备方法。本实施例所述制备方法是：
步骤一、将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物35~45wt%的纯水，混合0.8~1.7小时，在10~40℃的条件下，密封静置20~100小时，制得四硼酸锂浆料。
步骤二、将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在30~80℃条件下干燥，制得熔剂坩埚盖。
所述圆筒模具的衬底亦为一层聚乙烯膜；所述一层聚乙烯膜的厚度为0.006~0.009mm。
所述圆筒模具的材质为木质。
实施例3
一种熔剂坩埚盖的制备方法。本实施例所述制备方法是：
步骤一、将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物40~50wt%的纯水，混合1.1~2小时，在10~40℃的条件下，密封静置40~120小时，制得四硼酸锂浆料。
步骤二、将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在50~100℃条件下干燥，制得熔剂坩埚盖。
所述圆筒模具的衬底亦为一层聚乙烯膜；所述一层聚乙烯膜的厚度为0.007~0.01mm。
所述圆筒模具的材质为钢质。
本具体实施方式充分利用四硼酸锂微溶于水的特点，以四硼酸锂和水为结合剂使四硼酸锂粘黏在聚乙烯膜表面，脱水中成型，直接制得熔剂坩埚盖。使用所制备熔剂坩埚盖与现有技术相比具有如下积极效果：
1、本具体实施方式无需仔细铺撒四硼酸锂，将所制备的熔剂坩埚盖直接覆盖即可，节约时间。
2、熔剂坩埚盖厚度一致，防护效果好。
3、熔剂坩埚盖比粉状四硼酸锂熔解速度低，局部强度高，故熔剂坩埚盖的覆盖效率高。
因此，本具体实施方式具有操作简便、防迸溅效果好、节约时间和效率高的特点。
Claims (4)
1.一种熔剂坩埚盖的制备方法，其特征在于所述制备方法的步骤是：
步骤一、将硼酸和碳酸锂按摩尔比为4∶1混合均匀，得到混合物，再加入所述混合物30~50wt%的纯水，混合0.5~2小时，在10~40℃条件下，密封静置1~120小时，制得四硼酸锂浆料；
步骤二、将所述四硼酸锂浆料转入圆筒模具中，再覆盖一层聚乙烯膜，加压成型，然后在10~100℃条件下干燥，制得熔剂坩埚盖；
所述圆筒模具的衬底亦为一层聚乙烯膜；
所述一层聚乙烯膜的厚度为0.005~0.01mm。
2.根据权利要求1所述熔剂坩埚盖的制备方法，其特征在于所述硼酸粉末的H3BO3含量≥99.9wt%，所述硼酸粉末的粒度小于0.5mm。
3.根据权利要求1所述熔剂坩埚盖的制备方法，其特征在于所述碳酸锂粉末的Li2CO3含量≥99.9wt%，所述碳酸锂粉末的粒度小于0.5mm。
4.根据权利要求1所述熔剂坩埚盖的制备方法，其特征在于所述圆筒模具的内径为铂金坩埚内经的0.9~0.95倍；所述圆筒模具的材质为塑料、木质和钢质中的一种。