CN106694788A - Gh4169合金空心轴颈锻件近等温锻造成形方法 - Google Patents
Gh4169合金空心轴颈锻件近等温锻造成形方法 Download PDFInfo
- Publication number
- CN106694788A CN106694788A CN201611093428.0A CN201611093428A CN106694788A CN 106694788 A CN106694788 A CN 106694788A CN 201611093428 A CN201611093428 A CN 201611093428A CN 106694788 A CN106694788 A CN 106694788A
- Authority
- CN
- China
- Prior art keywords
- forging
- alloy
- hollow shaft
- shaft neck
- forged piece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种GH4169合金空心轴颈锻件近等温锻造成形方法,其步骤为:先将GH4169合金棒材按照一定的方式加热后,经镦粗、冲孔、预轧、倒角后,得到矩形环坯;再将该矩形环坯置入胎膜中,按照一定的变形速度,对其进行成形,获得GH4169合金空心轴颈锻件。该方法能够合理的分配各区域的变形量,获得最佳匹配的组织性能。该方法用于空心轴颈锻件挤压成形。
Description
技术领域
本发明涉及一种近等温锻造成形方法,特别是涉及了GH4169合金空心轴颈锻件近等温锻造成形方法。
背景技术
GH4169合金空心轴颈锻件为空心薄壁异形件,形状上端是一个大喇叭口,下端带有一个圆柱筒体,喇叭口处壁薄,而直径较大,筒体壁厚较薄。由于该锻件为飞机发动机关键转动件,工作条件十分恶劣,要求锻件具有较高的强度、断裂韧性以及较好的低周疲劳性能等,采用普通模锻和自由锻很难满足这些性能要求。目前该类锻件主要采用棒坯闭式模锻成形,再通过机加掏孔的方式生产,但该方法一方面在模锻时,会出现变形不均匀、杆部变形量小,导致锻件组织不理想;另一方面机加掏孔会切断锻件的锻造流线,从而影响锻件质量。
发明内容
本发明要解决的技术问题是提供一种采用环形坯料近等温锻造挤压成形方法,挤压成形过程中,模具型腔中间变化台阶处起到挤压模作用,而上端最大外径型腔起到挤压筒的作用,极大地改善了空心轴颈锻件杆部的变形,坯料变形量大,有利于获得细小均匀的锻态组织。
为解决上述技术问题,本发明所述GH4169合金空心轴颈锻件近等温锻造成形方法,其技术方案包括以下步骤:
把按规格下料的GH4169合金棒材在锻造加热炉内加热,先将棒材加热到880℃~900℃保温,保温时间按0.4min/mm~0.6min/mm计算;再升温至990℃~1020℃保温,保温时间按0.6min/mm~0.8min/mm计算;保温后,对棒材进行镦粗、冲孔、预轧以及内径上部和外径下部倒角后得到矩形环坯;
把矩形环坯置入成形模具中,驱动上模具以v1=1.5mm/s~2mm/s的下压速度进行挤压,当上模具与下模具闭合时,将下压速度降低至v2=(0.3~0.5)v1,对中间坯进行挤压,直到成形完全,获得GH4169合金空心轴颈锻件。
与现有技术相比,本发明的有益效果如下:
本发明所述GH4169合金空心轴颈锻件近等温锻造成形方法,提高了锻件成形时的变形量,使原始晶粒充分破碎,获得细小均匀组织;下压速度先采用v1=1.5mm/s~2mm/s,当上模具与下模具闭合时,将下压速度降低至v2=(0.3~0.5)v1,既防止了温升现象产生,同时也能合理分配锻件各部位的变形量,获得最佳匹配的组织性能。提高锻后降温均匀性,有利于提高锻件组织的均匀性,得到锻件截面状态一致高的锻态组织。而且在矩形环坯的内径上部与外径下部进行倒角,使矩形环坯能够与成形模具能够更好的贴合。
附图说明
下面结合附图和具体实施方式对本发明作进一步详细说明。
图1是矩形环坯的结构示意图。
图2是矩形环坯装模示意图。
图3是上模具与下模具闭合示意图。
图4是锻件成形示意图。
图5是空心轴颈锻件结构示意图。
具体实施方式
实施本发明所述的GH4169合金空心轴颈锻件近等温锻造成形方法需要提供锻造加热炉、压力机、机械手等设备。其具体实施方式:
该GH4169合金的主要化学元素含量(重量百分比)为:含C量≤0.08%、含Cr量17.0%~21.0%、含Ni量50.0%~55.0%、含Co量≤1.0%、含Mo量2.80%~3.30%、含Al量0.30%~0.70%、含Ti量0.75%~1.15%、含Nb量4.75%~5.50%、含B量≤0.006%、含Mg量≤0.01%、含Mn量≤0.35%、含Si量≤0.35%、含P量≤0.015%、含S量≤0.015%、含Cu量≤0.30%、含Ca量≤0.01%、含Pb量≤0.0005%、含Se量≤0.0003%、余量为Fe。
本方法的步骤如下:
把按规格下料的GH4169合金棒材在锻造加热炉内加热,先将棒材加热到880℃~900℃保温,保温时间按0.4min/mm~0.6min/mm计算;再升温至990℃~1020℃保温,保温时间按0.6min/mm~0.8min/mm计算;保温后,对棒材进行镦粗、冲孔、预轧、倒角后得到矩形环坯3,如图1所示;
如图2所示,把矩形环坯3置入成形模具中,驱动上模具1以v1=1.5mm/s~2mm/s的下压速度进行挤压,当上模具1与下模具2闭合时,如图3所示,将下压速度降低至v2=(0.3~0.5)v1,对中间坯4进行挤压,直到成形完全,如图4所示,获得GH4169合金空心轴颈锻件5,如图5所示。
Claims (1)
1.一种GH4169合金空心轴颈锻件近等温锻造成形方法,其特征在于,包括以下步骤:
把按规格下料的GH4169合金棒材在锻造加热炉内加热,先将棒材加热到880℃~900℃保温,保温时间按0.4min/mm~0.6min/mm计算;再升温至990℃~1020℃保温,保温时间按0.6min/mm~0.8min/mm计算;保温后,对棒材进行镦粗、冲孔、预轧以及内径上部和外径下部倒角后得到矩形环坯;
把矩形环坯置入成形模具中,驱动上模具以v1=1.5mm/s~2mm/s的下压速度进行挤压,当上模具与下模具闭合时,将下压速度降低至v2=(0.3~0.5)v1,对中间坯进行挤压,直到成形完全,获得GH4169合金空心轴颈锻件。