CN106675078A - Internal filling material for processing seat of electric freight tricycle - Google Patents
Internal filling material for processing seat of electric freight tricycle Download PDFInfo
- Publication number
- CN106675078A CN106675078A CN201611205694.8A CN201611205694A CN106675078A CN 106675078 A CN106675078 A CN 106675078A CN 201611205694 A CN201611205694 A CN 201611205694A CN 106675078 A CN106675078 A CN 106675078A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber powder
- rice bran
- bran wax
- insulation mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an internal filling material for processing a seat of an electric freight tricycle, relating to the technical field of electro-tricycle accessories processing. The internal filling material is prepared from the following raw materials in parts by weight: 20-25 parts of foam tableware recycling grains, 10-15 parts of plastic beverage bottle regenerated grains, 5-10 parts of coco coir, 5-10 parts of vinyl chloride resins, 3-6 parts of lignocelluloses, 3-6 parts of waste tire rubber powder, 2-4 parts of polyvinyl alcohol resin, 2-4 parts of rice bran wax, 1-2 parts of C9 petroleum resin, 1-2 parts of asbestos wool, 1-2 parts of nanometer rubber powder, 0.5-1 part of vulcanized lard oil, 0.5-1 part of regenerated waste engine oil and 0.1-0.3 part of chromic oxide. The filling material disclosed by the invention has the advantages of high flexibility, high deformation resistance, suitability for bad roads, capability of effectively relieving the impact of the bicycle vibration to a human body under the effect of bumping road, high weather fastness and long service life.
Description
Technical field:
The present invention relates to electro-tricycle accessory processing technique field, and in particular to a kind of electronic shipping tricycle seat adds
Work inside packing material.
Background technology:
Electro-tricycle be to storage battery be power, motor be drive haul goods or holding three-wheel means of transport.Electricity
Dynamic tricycle using tubular type Large Copacity, left and right lining, deep discharge, towed storage battery, want by the continuous discharge that adapts to work long hours
Ask, storage battery is normally used 2 years, and inner capacitiess do not subtract.
At present, electro-tricycle is divided into open type and closed two kinds.Open type electro-tricycle is because the visual field is good and car
Body is gently loved by the people, and is used for shipping.Seat is one of key fitment of electro-tricycle, due to electronic shipping three-wheel
Vehicle-mounted lotus is big, and sometimes for traveling on the rough road in road surface, therefore to the requirement of seat inside packing material
It is higher.On the one hand require that the flexibility of internal packing material is good, sit sense comfortable;On the other hand require that deformation resistance is strong, it is ensured that its
Long run is remained to good elasticity in bumpy sections, to increase the service life.
The content of the invention:
The technical problem to be solved is that a kind of flexibility of offer is good, deformation resistance is strong, long service life
Electronic shipping tricycle seat processing inside packing material.
The technical problem to be solved is realized using following technical scheme:
A kind of electronic shipping tricycle seat processing is made up with internal packing material of the raw material of following parts by weight:
Foam tableware reclaims granule 20-25 parts, plastic beverage bottle regeneration granule 10-15 parts, coconut palm chaff 5-10 part, polrvinyl chloride
Resin 5-10 parts, lignocellulose 3-6 parts, rubber powder of waste tire 3-6 parts, polyvinyl alcohol resin 2-4 parts, rice bran wax 2-4 parts,
C9 Petropols 1-2 parts, asbestos wool 1-2 parts, nanometer rubber powder 1-2 parts, sulfurized lard 0.5-1 parts, used oil regenerated 0.5-1 parts,
Chromic oxide 0.1-0.3 parts;The water content of the coconut palm chaff and lignocellulose is less than 5%.
Its preparation method comprises the steps:
(1) reclaim to foam tableware and add in granule Corvic and rubber powder of waste tire, with the liter of 5 DEG C/min
Warm speed is warming up to 125-130 DEG C of insulation mixing 30min, adds coconut palm chaff, polyvinyl alcohol resin and rice bran wax, continues in 125-
Insulation mixing 10min, then naturally cools to room temperature at 130 DEG C, obtains final product material I;
(2) C9 Petropols and nanometer rubber powder are added in plastic beverage bottle regeneration granule, with the programming rate of 5 DEG C/min
130-135 DEG C of insulation mixing 30min is warming up to, lignocellulose, sulfurized lard and used oil regenerated is added, is continued in 130-
135 DEG C of insulation mixing 10min, then naturally cool to room temperature, obtain final product material II;
(3) material II, asbestos wool and chromic oxide are added in material I, sends in gained mixture after being sufficiently mixed
5min is kneaded in kneading machine, last foamed molding.
Using front through pretreatment, its processing method is the rice bran wax:Polyvinylpolypyrrolidone and hydrogen are added in rice bran wax
Change rosin glyceride, microwave treater microwave treatment 5min is utilized after being sufficiently mixed, proceed in 10-15 DEG C of environment and stand 30min
Continue microwave treatment 3min afterwards, add hexakis(hydroxymethyl)melamine pregnancy ether and 2- imidazolidinones, continue after mix homogeneously micro-
Ripple processes 5min, finally proceeds to gained mixture and 1h is stood in 0-5 DEG C of environment, that is, complete the pretreatment of rice bran wax.
The rice bran wax, polyvinylpolypyrrolidone, hydrogenated rosin glyceride, hexakis(hydroxymethyl)melamine pregnancy ether and 2- imidazolidines
The quality amount ratio of ketone is 15-20:1-2:0.5-1:0.5-1:0.1-0.3.
The specified microwave frequency of the microwave treater is 2450MHz, output is 700W.
Rice bran wax can not only significantly increase its comixing compatibility with macromolecule resin after above-mentioned pretreatment, moreover it is possible to
Improve its thickening property and weatherability.
The nanometer rubber powder is made up of the raw material of following parts by weight:Rosin modified phenolic resin 5-10 parts, gas phase Linesless charcoal
Black 3-5 parts, active hargil 3-5 parts, PAMA 3-5 parts, flake asbestos 2-3 parts, trimethylolpropane tris acrylic acid
Ester 2-3 parts, sepiolite fibre 1-2 parts, epoxy soybean oil 1-2 parts, glass powder 0.5-1 parts, its preparation method is:To Abietyl modified
Active hargil and epoxy soybean oil are added in phenolic resin, is sufficiently mixed, 125-130 is warming up to the programming rate of 5 DEG C/min
DEG C insulation mixing 15min, add gas-phase silica, PAMA and trimethylolpropane trimethacrylate, after
Continue the insulation mixing 15min at 125-130 DEG C, then 55-60 DEG C of sealing thermal insulation is cooled to the cooling rate of 5 DEG C/min and is stood
30min, and flake asbestos, sepiolite fibre and glass powder are added, then 115-125 DEG C of guarantor is warming up to the programming rate of 10 DEG C/min
Temperature mixing 10min, finally while hot by gained mixture send into nano-level grinder in, ground prepared nanometer rubber powder.
Above-mentioned made nanometer rubber powder permeability is extremely strong, and energy uniformly penetrating plays enhancing filling in grease preparing raw material
The effect of material wear ability, impact resistance and weatherability.
The invention has the beneficial effects as follows:The present invention with foam tableware reclaim granule, plastic beverage bottle regeneration granule, coconut palm chaff,
Rubber powder of waste tire and used oil regenerated for raw material, realizes the reasonable recycling of resource, reduces cost and environmental protection, and
It is aided with various auxiliary agents and electronic shipping tricycle seat processing inside packing material is obtained, the packing material flexibility is good, resistance
Shape is strong, it is adaptable to the bad road of road conditions, can effectively mitigate the impact shaken because of the vehicle body of road bumps initiation to human body;And
And weatherability is strong, can for a long time used in the environment blocked without awning, long service life, as long as five years more than.
Specific embodiment:
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) reclaim to 25 parts of foam tablewares and add in granule 5 parts of Corvics and 3 parts of rubber powder of waste tire, with 5
DEG C/programming rate of min is warming up to 125-130 DEG C of insulation mixing 30min, adds 5 parts of coconut palm chaffs, 2 parts of polyvinyl alcohol resins and 2
Part rice bran wax, continues the insulation mixing 10min at 125-130 DEG C, then naturally cools to room temperature, obtains final product material I;
(2) 1 part of C9 Petropols and 1 part of nanometer rubber powder are added in 15 parts of plastic beverage bottle regeneration granules, with 5 DEG C/min
Programming rate be warming up to 130-135 DEG C insulation mixing 30min, add 3 parts of lignocellulose, 0.5 part of sulfurized lard and 0.5
Part is used oil regenerated, continues, in 130-135 DEG C of insulation mixing 10min, then to naturally cool to room temperature, obtains final product material II;
(3) material II, 2 parts of asbestos wools and 0.2 part of chromic oxide are added in material I, mixes gained after being sufficiently mixed
Compound is sent in kneading machine and kneads 5min, last foamed molding.
Wherein, the water content of coconut palm chaff and lignocellulose is less than 5%.
The pretreatment of rice bran wax:1 part of polyvinylpolypyrrolidone and 0.5 part of hydrogenated rosin glyceride are added in 20 parts of rice bran waxs,
Specified microwave frequency 2450MHz, microwave treater microwave treatment 5min of output 700W are utilized after being sufficiently mixed, is proceeded to
In 10-15 DEG C of environment stand 30min after continue microwave treatment 3min, add 0.5 part of hexakis(hydroxymethyl)melamine pregnancy ether and
0.2 part of 2- imidazolidinone, continues microwave treatment 5min after mix homogeneously, finally proceed in gained mixture quiet in 0-5 DEG C of environment
1h is put, that is, completes the pretreatment of rice bran wax.
The preparation of nanometer rubber powder:3 parts of active hargil and 1 part of epoxy soybean are added in 10 parts of rosin modified phenolic resins
Oil, is sufficiently mixed, and with the programming rate of 5 DEG C/min 125-130 DEG C of insulation mixing 15min is warming up to, and adds 3 parts of gas phase Linesless charcoal
Black, 5 parts of PAMAs and 2 parts of trimethylolpropane trimethacrylates, continue the insulation mixing at 125-130 DEG C
15min, is then cooled to 55-60 DEG C of sealing thermal insulation and stands 30min with the cooling rate of 5 DEG C/min, and add 2 parts of flake asbestos, 1
Part sepiolite fibre and 0.5 part of glass powder, then 115-125 DEG C of insulation mixing 10min is warming up to the programming rate of 10 DEG C/min,
It is last while hot gained mixture to be sent in nano-level grinder, ground prepared nanometer rubber powder.
Embodiment 2
(1) reclaim to 25 parts of foam tablewares and add in granule 5 parts of Corvics and 3 parts of rubber powder of waste tire, with 5
DEG C/programming rate of min is warming up to 125-130 DEG C of insulation mixing 30min, adds 5 parts of coconut palm chaffs, 3 parts of polyvinyl alcohol resins and 2
Part rice bran wax, continues the insulation mixing 10min at 125-130 DEG C, then naturally cools to room temperature, obtains final product material I;
(2) 1 part of C9 Petropols and 2 parts of nanometer rubber powders are added in 15 parts of plastic beverage bottle regeneration granules, with 5 DEG C/min
Programming rate be warming up to 130-135 DEG C insulation mixing 30min, add 5 parts of lignocellulose, 0.5 part of sulfurized lard and 0.5
Part is used oil regenerated, continues, in 130-135 DEG C of insulation mixing 10min, then to naturally cool to room temperature, obtains final product material II;
(3) material II, 1 part of asbestos wool and 0.2 part of chromic oxide are added in material I, mixes gained after being sufficiently mixed
Compound is sent in kneading machine and kneads 5min, last foamed molding.
Wherein, the water content of coconut palm chaff and lignocellulose is less than 5%.
The pretreatment of rice bran wax:1 part of polyvinylpolypyrrolidone and 1 part of hydrogenated rosin glyceride are added in 20 parts of rice bran waxs, is filled
Divide after mixing and utilize specified microwave frequency 2450MHz, microwave treater microwave treatment 5min of output 700W, proceed to 10-
Stand in 15 DEG C of environment and continue microwave treatment 3min after 30min, add 1 part of hexakis(hydroxymethyl)melamine pregnancy ether and 0.2 part
2- imidazolidinones, continue microwave treatment 5min after mix homogeneously, finally proceed in 0-5 DEG C of environment gained mixture and stand 1h,
Complete the pretreatment of rice bran wax.
The preparation of nanometer rubber powder:3 parts of active hargil and 2 parts of epoxy soybean oils are added in 8 parts of rosin modified phenolic resins,
Be sufficiently mixed, with the programming rate of 5 DEG C/min be warming up to 125-130 DEG C insulation mixing 15min, add 3 parts of gas-phase silicas,
3 parts of PAMAs and 3 parts of trimethylolpropane trimethacrylates, continue the insulation mixing at 125-130 DEG C
15min, is then cooled to 55-60 DEG C of sealing thermal insulation and stands 30min with the cooling rate of 5 DEG C/min, and add 2 parts of flake asbestos, 2
Part sepiolite fibre and 0.5 part of glass powder, then 115-125 DEG C of insulation mixing 10min is warming up to the programming rate of 10 DEG C/min,
It is last while hot gained mixture to be sent in nano-level grinder, ground prepared nanometer rubber powder.
Embodiment 3
Performance test is carried out to embodiment 1 and the made seat of embodiment 2 inside packing material, test result is as shown in table 1.
The performance test results of the made seat inside packing material of the embodiment of the present invention of table 1
The ultimate principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and description this
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (6)
1. a kind of electronic shipping tricycle seat is processed with internal packing material, it is characterised in that by the original of following parts by weight
Material is made:
Foam tableware reclaims granule 20-25 parts, plastic beverage bottle regeneration granule 10-15 parts, coconut palm chaff 5-10 part, Corvic
5-10 parts, lignocellulose 3-6 parts, rubber powder of waste tire 3-6 parts, polyvinyl alcohol resin 2-4 parts, rice bran wax 2-4 parts, C9 stones
Oleoresin 1-2 parts, asbestos wool 1-2 parts, nanometer rubber powder 1-2 parts, sulfurized lard 0.5-1 parts, used oil regenerated 0.5-1 parts, three oxygen
Change two chromium 0.1-0.3 parts;The water content of the coconut palm chaff and lignocellulose is less than 5%.
2. electronic shipping tricycle seat according to claim 1 is processed with internal packing material, it is characterised in that its system
Preparation Method comprises the steps:
(1) reclaim to foam tableware and add in granule Corvic and rubber powder of waste tire, with the intensification speed of 5 DEG C/min
Degree is warming up to 125-130 DEG C of insulation mixing 30min, adds coconut palm chaff, polyvinyl alcohol resin and rice bran wax, continues in 125-130
Insulation mixing 10min, then naturally cools to room temperature at DEG C, obtains final product material I;
(2) C9 Petropols and nanometer rubber powder are added in plastic beverage bottle regeneration granule, is heated up with the programming rate of 5 DEG C/min
To 130-135 DEG C of insulation mixing 30min, lignocellulose, sulfurized lard and used oil regenerated are added, continued in 130-135
DEG C insulation mixing 10min, then naturally cool to room temperature, obtain final product material II;
(3) material II, asbestos wool and chromic oxide are added in material I, gained mixture is sent into after being sufficiently mixed is kneaded
5min is kneaded in machine, last foamed molding.
3. electronic shipping tricycle seat according to claim 1 and 2 is processed with internal packing material, it is characterised in that:
Using front through pretreatment, its processing method is the rice bran wax:Add polyvinylpolypyrrolidone and hydrogenated rosin sweet in rice bran wax
Grease, utilizes microwave treater microwave treatment 5min after being sufficiently mixed, proceed in 10-15 DEG C of environment and continue micro- after standing 30min
Ripple processes 3min, adds hexakis(hydroxymethyl)melamine pregnancy ether and 2- imidazolidinones, and microwave treatment is continued after mix homogeneously
5min, gained mixture finally being proceeded to, 1h is stood in 0-5 DEG C of environment, that is, complete the pretreatment of rice bran wax.
4. electronic shipping tricycle seat according to claim 3 is processed with internal packing material, it is characterised in that:It is described
The quality consumption of rice bran wax, polyvinylpolypyrrolidone, hydrogenated rosin glyceride, hexakis(hydroxymethyl)melamine pregnancy ether and 2- imidazolidinones
Than for 15-20:1-2:0.5-1:0.5-1:0.1-0.3.
5. electronic shipping tricycle seat according to claim 3 is processed with internal packing material, it is characterised in that:It is described
The specified microwave frequency of microwave treater is 2450MHz, output is 700W.
6. electronic shipping tricycle seat according to claim 1 is processed with internal packing material, it is characterised in that described
Nanometer rubber powder is made up of the raw material of following parts by weight:Rosin modified phenolic resin 5-10 parts, gas-phase silica 3-5 parts, activity
Hargil 3-5 parts, PAMA 3-5 parts, flake asbestos 2-3 parts, trimethylolpropane trimethacrylate 2-3 parts, Hai Pao
Mineral wool 1-2 parts, epoxy soybean oil 1-2 parts, glass powder 0.5-1 parts, its preparation method is:Add in rosin modified phenolic resin
Enter active hargil and epoxy soybean oil, be sufficiently mixed, 125-130 DEG C of insulation mixing is warming up to the programming rate of 5 DEG C/min
15min, adds gas-phase silica, PAMA and trimethylolpropane trimethacrylate, continues in 125-130
Insulation mixing 15min at DEG C, is then cooled to 55-60 DEG C of sealing thermal insulation and stands 30min with the cooling rate of 5 DEG C/min, and adds
Enter flake asbestos, sepiolite fibre and glass powder, then 115-125 DEG C of insulation mixing is warming up to the programming rate of 10 DEG C/min
10min, finally while hot by gained mixture send into nano-level grinder in, ground prepared nanometer rubber powder.