CN106637965A - Regenerable cotton yarn textile material for flexible, skin-friendly and bamboo-fiber-containing towel and preparation method thereof - Google Patents
Regenerable cotton yarn textile material for flexible, skin-friendly and bamboo-fiber-containing towel and preparation method thereof Download PDFInfo
- Publication number
- CN106637965A CN106637965A CN201610998138.4A CN201610998138A CN106637965A CN 106637965 A CN106637965 A CN 106637965A CN 201610998138 A CN201610998138 A CN 201610998138A CN 106637965 A CN106637965 A CN 106637965A
- Authority
- CN
- China
- Prior art keywords
- cotton
- textile material
- bamboo
- towel
- skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a regenerable cotton yarn textile material for a flexible, skin-friendly and bamboo-fiber-containing towel and a preparation method thereof. The regenerable cotton yarn textile material is prepared from, by weight, 60-80 parts of all cotton fabric strips, 15-25 parts of polyester-mixed cotton fabric strips with the cotton content of 40-60%, 5-10 parts of bamboo fiber, 0.5-1 part of glutenin, 3-5 parts of silicon sol, 5-10 parts of soluble starch, 0.5-1 part of N-sodium lauroyl sarcosine, 2-4 parts of polyvinyl alcohol, 0.5-1 part of sodium alginate and 0.5-1 part of water-soluble wool fat. The regenerable cotton yarn textile material has excellent wholesomeness, comfort, strength and durability and good flexibility, air permeability and skin friendliness and serves as a towel processing raw material.
Description
Technical field
The present invention relates to textile material technical field, more particularly to a kind of towel regeneration cotton of flexible pro-skin bamboo-containing fiber
Yarn textile material and preparation method thereof.
Background technology
China is that fabric clothing maximum in the world is produced and exported country.With economic level and people's living standard
Improve, textile waste is in increase trend, not only waste of resource but also has caused environmental pollution.Regeneration cotton yarn is by process of textile production, clothes
The particle pieces of cloth produced during dress cutting and the waste material such as textile fabric abandoned in daily routines re-work made by yarn
Line.By the way that textile waste cycling and reutilization is made into regeneration cotton yarn, to enterprise considerable economic benefit can be brought, and for ring
Border is administered and is contributed.
The of many uses of cotton yarn is regenerated, is usually used in making mop, gloves, towel, bedding, clothing item etc..Due to
Towel is people's frequent routine amenities for using of contact, and people will to the wholesomeness of towel, comfort level and durability etc.
Ask very high.However, regeneration cotton yarn is the cotton yarn re-worked using the textile raw material for reclaiming, not only raw material contains impurity,
And the intermediate treatment technique such as bleach and can bring pollution to regeneration cotton yarn product, the wholesomeness and comfort of impact finished product,
Also have that fiber is short, the low problem of strength, durability is inadequate.Therefore, it is the requirement that meets towel textile fabrics, needs to again
The performance of raw cotton yarn is improved.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of wholesomeness, comfort type are good, strength is high,
The towel of durability strong flexible pro-skin bamboo-containing fiber regeneration cotton yarn textile material and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of towel of flexible pro-skin bamboo-containing fiber regeneration cotton yarn textile material, it is obtained by the raw material of following weight parts:
Cotton cloth 60-80, cotton content is the polyester-cotton blend cloth 15-25 of 40-60%, and bamboo fibre 5-10, sericin 0.5-1, silicon is molten
Glue 3-5, soluble starch 5-10, N- sodium lauroyl sarcosine 0.5-1, polyvinyl alcohol 2-4, sodium alginate 0.5-1, water-soluble sheep
Hair fat 0.5-1.
A kind of towel of the flexible pro-skin bamboo-containing fiber preparation method of regeneration cotton yarn textile material, comprises the following steps:
(1)Will cotton cloth, polyester-cotton blend cloth bleaching after mix, be then split into regeneration cotton, through cleaning impurity, combing sliver with
And combing obtains fiber sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with bamboo fibre, then obtains through spinning manufacturing procedures
To yarn fabric;
(3)Polyvinyl alcohol is added into 1:100-1:0.5-1h is stirred in the water of 150 times of weight and in 85-95 DEG C, sea is subsequently adding
Mosanom and soluble starch stir 10-15min in 50-60 DEG C, add step(2)The yarn fabric for obtaining is at same temperature
6-12h is processed, is cleaned up with water after cooling, obtain pre-treating textile thing;
(4)First Ludox is added dispersed with stirring in the water of 10-15 times of weight uniformly, add N- sodium lauroyl sarcosines, silk
Glue protein, water-soluble lanolin stir 10-15min in 50-60 DEG C, then to step(3)The yarn fabric dipping 12-24h for obtaining
After 60-80 DEG C of drying, the towel regeneration cotton yarn textile material of flexible pro-skin bamboo-containing fiber is obtained final product.
It is an advantage of the invention that:
The present invention by textile waste cotton strap raw material mix bamboo fibre spinned, improve textile material intensity,
Toughness and gas permeability;The slurry obtained by polyvinyl alcohol, sodium alginate and soluble starch compounding carries out pre- to textile material
Process, effectively remove the pollutant produced during soluble impurity and bleaching in raw material, improve textile material
Sanitation performance;By the way that the raw materials such as Ludox and sericin are carried out into impregnation process to textile material, textile material is improved
Intensity and soft skin-friendly, by the selection of above-mentioned raw materials and technique, have obtained regeneration cotton yarn textile material concurrently excellent
Wholesomeness, comfort type and intensity, durability, pliability, good permeability, skin-friendly is good, is suitable for towel and processes raw material.
Specific embodiment
The towel of a kind of flexible pro-skin bamboo-containing fiber regeneration cotton yarn textile material, by the component raw material of following weight (kg)
It is prepared from:
Cotton cloth 60, cotton content is 40% polyester-cotton blend cloth 15, bamboo fibre 5, sericin 0.5, Ludox 3, soluble starch
5, N- sodium lauroyl sarcosines 0.5, polyvinyl alcohol 2, sodium alginate 0.5, water-soluble lanolin 0.5.
A kind of towel of the flexible pro-skin bamboo-containing fiber preparation method of regeneration cotton yarn textile material, comprises the following steps:
(1)Will cotton cloth, polyester-cotton blend cloth bleaching after mix, be then split into regeneration cotton, through cleaning impurity, combing sliver with
And combing obtains fiber sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with bamboo fibre, then obtains through spinning manufacturing procedures
To yarn fabric;
(3)Polyvinyl alcohol is added into 1:0.5h are stirred in the water of 100 times of weight and in 85 DEG C, sodium alginate and solvable is subsequently adding
Property starch in 50 DEG C stir 10min, add step(2)The yarn fabric for obtaining processes 6h at same temperature, and water is used after cooling
Clean up, obtain pre-treating textile thing;
(4)First Ludox is added dispersed with stirring in the water of 10 times of weight uniformly, add N- sodium lauroyl sarcosines, silk gum egg
In vain, water-soluble lanolin stirs 10min in 50 DEG C, then to step(3)The yarn fabric dipping 12h for obtaining is dried after 60 DEG C,
Obtain final product the towel regeneration cotton yarn textile material of flexible pro-skin bamboo-containing fiber.
Regeneration cotton yarn textile material obtained above tears strong compared with the textile material that common cotton Jing weavings are obtained
Power improves 25%.
Claims (2)
1. a kind of towel of flexible pro-skin bamboo-containing fiber is used and regenerates cotton yarn textile material, it is characterised in that it is by following weight
The raw material of part is obtained:
Cotton cloth 60-80, cotton content is the polyester-cotton blend cloth 15-25 of 40-60%, and bamboo fibre 5-10, sericin 0.5-1, silicon is molten
Glue 3-5, soluble starch 5-10, N- sodium lauroyl sarcosine 0.5-1, polyvinyl alcohol 2-4, sodium alginate 0.5-1, water-soluble sheep
Hair fat 0.5-1.
2. a kind of towel use of flexible pro-skin bamboo-containing fiber according to claim 1 regenerates the preparation side of cotton yarn textile material
Method, it is characterised in that comprise the following steps:
(1)Will cotton cloth, polyester-cotton blend cloth bleaching after mix, be then split into regeneration cotton, through cleaning impurity, combing sliver with
And combing obtains fiber sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with bamboo fibre, then obtains through spinning manufacturing procedures
To yarn fabric;
(3)Polyvinyl alcohol is added into 1:100-1:0.5-1h is stirred in the water of 150 times of weight and in 85-95 DEG C, sea is subsequently adding
Mosanom and soluble starch stir 10-15min in 50-60 DEG C, add step(2)The yarn fabric for obtaining is at same temperature
6-12h is processed, is cleaned up with water after cooling, obtain pre-treating textile thing;
(4)First Ludox is added dispersed with stirring in the water of 10-15 times of weight uniformly, add N- sodium lauroyl sarcosines, silk
Glue protein, water-soluble lanolin stir 10-15min in 50-60 DEG C, then to step(3)The yarn fabric dipping 12-24h for obtaining
After 60-80 DEG C of drying, the towel regeneration cotton yarn textile material of flexible pro-skin bamboo-containing fiber is obtained final product.