CN106637903A - Technology for dyeing and finishing cloth for garments - Google Patents
Technology for dyeing and finishing cloth for garments Download PDFInfo
- Publication number
- CN106637903A CN106637903A CN201610880923.XA CN201610880923A CN106637903A CN 106637903 A CN106637903 A CN 106637903A CN 201610880923 A CN201610880923 A CN 201610880923A CN 106637903 A CN106637903 A CN 106637903A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- agent
- technology
- finishing
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a technology for dyeing and finishing cloth for garments. The technology includes steps of firstly, carrying out singeing; secondly, carrying out desizing; thirdly, carrying out bleaching; fourthly, carrying out heat setting; fifthly, carrying out dyeing; sixthly, carrying out after-finishing; seventhly, carrying out stentering setting. The technology has the advantages that common universal chemical auxiliaries in markets are used for centering in the technology, high-end equipment can be omitted, the integral technology is simple, and technological conditions are easy to control and are safe and environmentally friendly; large quantities of fabrics can be dyed and finished by the aid of the technology at one step, and accordingly the processing efficiency can be guaranteed; original excellent characteristics of the fabrics can be reserved, the fabrics are good in waterproof, oil-proof, dirt-proof and ultraviolet-proof performance, low in strength loss and high in dye fastness and have breathable functions, the technology is reasonable, and requirements can be met by various chemical indexes of products according to detection.
Description
Technical field
The present invention relates to textile technology field, more particularly to a kind of dyeing and finishing technology of clothes cloth material.
Background technology
The mankind using garment material generally include leather, the feather class that can be directly obtained, which has larger size, can
Suitable shape is obtained with cutting out by simple concatenation.And as the mostly textile fabric of garment material, that is, pass through
The various clothes that pair warp and weft is worked out.In today that garment technology industry is increasingly flourishing, requirement of the people to clothing quality
Improve therewith, constantly in the highest quality for pursuing clothing, so as to higher requirement is it is also proposed to garment material, garment material
Make also rigorous therewith, more pay attention to detail.
Knitting fabric is widely used in the product such as garment material and lining, home textile, is liked by consumers in general.It is logical
Often, knitting fabric is mutually worn by coil, as coil can change shapes and sizes, therefore knitting fabric have it is larger
Extensibility and certain elasticity.With the development of sports, the leotard sewed with elastic knitted fabric fabric, leisure
Clothes, including various swimming suits, gym outfit, anorak, jersey etc., demand is increasing, and with people's living standard not
It is disconnected to improve, prescription more and more higher of the people to above-mentioned knitted apparel.
A kind of knitting fabric being loved by the people, generally with good extensibility and recovery, excellent elasticity and
Soft comfortable effect, while also abundant color effect, and the dyeing and finishing technology breath breath represented with fabric of these premium properties
It is related.The whole dyeing technique of traditional fabric, including desizing, boiling-off, chlorine drift, preboarding, dyeing, drying, shaping process, first,
Before desizing operation, remove impurity process is not done, the surface of fabric is more coarse, can affect whole dye effect;Secondly, in drying dyeing face
After material, directly shaped, gauffer easily occurs in the fabric being easily caused after dyeing, further affects the whole dye effect of fabric.
There is more defect in the dyeing and finishing technology of many knitting fabrics, such as:The process links unreasonable, Color of arrangement is not good, normal appearance
The defect such as wrinkle and rope form fine wrinkle, carbon brush and raising process bad etc..These defects have had a strong impact on the product matter of knitting fabric
Amount and wearability, therefore be necessary to be optimized the dyeing and finishing technology of knitting fabric improvement, to overcome drawbacks described above.
The content of the invention
The invention aims to overcome above-mentioned technological deficiency, there is provided a kind of process is simple, safety and environmental protection, and process effect
The dyeing and finishing technology of the good garment material of rate.
For achieving the above object, the present invention is achieved by the following scheme:
A kind of dyeing and finishing technology of clothes cloth material, described dyeing and finishing technology are divided into following steps:
The first step:Singe:Fabric is carried out front to singe twice, regulation speed 75m/min, and burner requires uniformly have
Power;
Second step:Desizing:Cloth immersion 0.2-1.5g/L BF-7658 desizing enzyme liquids after singing, 3g/L tripolyphosphates
Sodium, sodium silicate 3-6g/L, 2.4g/L fatty alcohol ether, 2g/L chelated dispersants SR, the soda bath of the pH value 8 of 8g/L, 5-6g/L
Alkali-resistant penetrant and 6g/L refining agent in, under conditions of pick-up 100%, and material temperature be 110 DEG C, 80 points of decatize
Clock;Wherein, the refining agent is the mixture of soda and iodate dioctyl succinate sodium salt, and the ratio of the two is 1:1;
3rd step:Bleaching:Cloth immersion after desizing is added the sodium hypochlorite of the pH value 9.7-10 of 5g/L, 3-6g/L connect
Sodium sulfite, 7g/L fatty alcohol-polyoxyethylene ether, 12g/L stabilizers rinse 65-70 minutes at 120 DEG C;
4th step:Thermal finalization:60-80 DEG C of one section of drying 5-8min in dehydrator;160-220 DEG C of two-stage nitration dries 10- again
15min;
5th step:Dyeing:The cloth of the 4th step thermal finalization is first carried out into disperse dyeing, disperse dyeing cleaning is dry
After net, then carry out reactive dyeing;The disperse dyeing process is as follows:By the disperse dyes of 1-4%o.w.f, 2g/L
Chelated dispersants 1030,0.8g/L glacial acetic acid, 1g/L terylene Special high-temperature TF-212F levelling agents are configured to dye liquor, will be through heat
The cloth of sizing is placed in above-mentioned dye liquor, adjusts bath raio 1:7, it is warming up to 132-136 DEG C of insulation 50min, after the completion of dyeing, cooling
Draining, carries out reduction cleaning;The technique of the reactive dyeing is as follows:By the reactive dye of 1.5%o.w.f, 1%o.w.f
Migration inhibitor, 200g/L Sodium Chloride are configured to dye liquor, will be placed in above-mentioned active dye liquor through the cloth of dispersion dyeing, adjustment bath
Than 1:8, using the ramp of 10 DEG C/min to 70 DEG C, Matrii Sulfas Exsiccatus are added, be incubated 15min, add 20g/L sodium carbonate, 5g/L
Sodium hydroxide, is incubated 45min, and then draining carries out next step operation;
6th step:Final finishing:Four anti-arrangements are carried out using nanometer finishing agent;
7th step:Stentering forming:Cloth after Final finishing is dried and stentering forming in 80-90 DEG C.
Wherein, in the disperse dyeing, disperse dyes select any one of high temperature modification disperse dyes, including Zhejiang
The black WHTS of dispersion, the black HW-BG of dispersion of Long Sheng dye chemical industries company limited or disperse blue WNBTS.
The reactive dye are the dyestuffs of iso-bifunctional group or vinyl sulfone(RemzaolHuo Xingranliaohuoxingjituan) active group, and the reactive dye fineness of the particles
Less than 1 micron;The migration inhibitor is flat Ma Su.
The nanometer finishing agent that the Final finishing is adopted is by amido silicon oil NSW, waterproofing agent NT-X604A, oil-proofing agent NT-
X604B, anti-fouling agent NT-X603D, resin NT-X603E and composite catalyst NKS composition, adds amido silicon oil in every liter water
15 grams of 40 grams of 40 grams of 2 grams of NSW, waterproofing agent NT-X604A, oil-proofing agent NT-X604B, anti-fouling agent NT-X603D, resin NT-
10 grams of 15 grams of X603E, composite catalyst NKS;With handy glacial acetic acid carwash, fabric is padded with four liquid-proof for preparing, use steam
120-130 degree is heated to, drying cylinder is dried 90 seconds.
The invention has the beneficial effects as follows:(1) in the dyeing and finishing technology to and used in all be more common on the market leading to
With chemical assistant, and without the need for high-end devices, integrated artistic is simple, easy control of process conditions, and safety and environmental protection;It is logical in addition
Crossing this kind of technique can disposably carry out larger amount of shell-fabric dyeing and finishing, allow working (machining) efficiency to be ensured.(2) dyeing and finishing technology is not only
The original good characteristic of fabric is remained, and four anti-performances are good, strength loss is little, dyefastness is high, with airing function, work
Rationally, according to detection, every chemical index of product meets the requirements skill.
Specific embodiment
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described enforcement
Example is only a part of embodiment of the invention, rather than the embodiment of whole.Based on the embodiment in the present invention, this area is common
The every other embodiment obtained under the premise of creative work is not made by technical staff, belongs to the model of present invention protection
Enclose.
Embodiment 1
A kind of dyeing and finishing technology of clothes cloth material, described dyeing and finishing technology are divided into following steps:
The first step:Singe:Fabric is carried out front to singe twice, regulation speed 75m/min, and burner requires uniformly have
Power;
Second step:Desizing:Cloth immersion 1g/L BF-7658 desizing enzyme liquids after singing, 3g/L sodium tripolyphosphates, silicon
Sour sodium 4g/L, 2.4g/L fatty alcohol ether, 2g/L chelated dispersants SR, the soda bath of the pH value 8 of 8g/L, the alkaline-resisting infiltration of 5g/L
In the refining agent of agent and 6g/L, under conditions of pick-up 100%, and material temperature is 110 DEG C, decatize 80 minutes;Wherein, institute
The mixture that refining agent is soda and iodate dioctyl succinate sodium salt is stated, and the ratio of the two is 1:1;
3rd step:Bleaching:Cloth immersion after desizing is added the sodium hypochlorite of the pH value 9.8 of 5g/L, that 5g/L connects two is sub-
Sodium sulfate, 7g/L fatty alcohol-polyoxyethylene ether, 12g/L stabilizers are rinsed 65 minutes at 120 DEG C;
4th step:Thermal finalization:70 DEG C of one section of drying 7min in dehydrator;200 DEG C of two-stage nitration dry 12min again;
5th step:Dyeing:The cloth of the 4th step thermal finalization is first carried out into disperse dyeing, disperse dyeing cleaning is dry
After net, then carry out reactive dyeing;The disperse dyeing process is as follows:By the disperse dyes disperse blue of 1-4%o.w.f
WNBTS, 2g/L chelated dispersants 1030,0.8g/L glacial acetic acid, 1g/L terylene Special high-temperature TF-212F levelling agents are configured to dye
Liquid, will be placed in above-mentioned dye liquor through the cloth of thermal finalization, adjust bath raio 1:7,134 DEG C of insulation 50min are warming up to, dyeing is completed
Afterwards, cooling draining, carries out reduction cleaning;The technique of the reactive dyeing is as follows:Will be the reactive dye of 1.5%o.w.f different
Flat Ma Su, 200g/L Sodium Chloride of double-active radical dye, 1%o.w.f migration inhibitors is configured to dye liquor, by the cloth through dispersion dyeing
Material is placed in above-mentioned active dye liquor, adjusts bath raio 1:8, using the ramp of 10 DEG C/min to 70 DEG C, add Matrii Sulfas Exsiccatus, insulation
15min, adds 20g/L sodium carbonate, 5g/L sodium hydroxide, is incubated 45min, and then draining carries out next step operation;
6th step:Final finishing:Four anti-arrangements are carried out using nanometer finishing agent;
7th step:Stentering forming:Cloth after Final finishing is dried and stentering forming in 85 DEG C.
Embodiment 2
A kind of dyeing and finishing technology of clothes cloth material, described dyeing and finishing technology are divided into following steps:
The first step:Singe:Fabric is carried out front to singe twice, regulation speed 75m/min, and burner requires uniformly have
Power;
Second step:Desizing:Cloth immersion 1.2g/L BF-7658 desizing enzyme liquids after singing, 3g/L sodium tripolyphosphates,
Sodium silicate 4g/L, 2.4g/L fatty alcohol ether, 2g/L chelated dispersants SR, the soda bath of the pH value 8 of 8g/L, 5.6g/L it is alkaline-resisting
In the refining agent of penetrating agent and 6g/L, under conditions of pick-up 100%, and material temperature is 110 DEG C, decatize 80 minutes;Its
In, the refining agent is the mixture of soda and iodate dioctyl succinate sodium salt, and the ratio of the two is 1:1;
3rd step:Bleaching:Cloth immersion after desizing is added the sodium hypochlorite of the pH value 9.9 of 5g/L, that 5g/L connects two is sub-
Sodium sulfate, 7g/L fatty alcohol-polyoxyethylene ether, 12g/L stabilizers are rinsed 70 minutes at 120 DEG C;
4th step:Thermal finalization:80 DEG C of one section of drying 5min in dehydrator;160 DEG C of two-stage nitration dry 15min again;
5th step:Dyeing:The cloth of the 4th step thermal finalization is first carried out into disperse dyeing, disperse dyeing cleaning is dry
After net, then carry out reactive dyeing;The disperse dyeing process is as follows:Will be the disperse dyes dispersion of 1-4%o.w.f black
HW-BG, 2g/L chelated dispersants 1030,0.8g/L glacial acetic acid, 1g/L terylene Special high-temperature TF-212F levelling agents are configured to dye
Liquid, will be placed in above-mentioned dye liquor through the cloth of thermal finalization, adjust bath raio 1:7,136 DEG C of insulation 50min are warming up to, dyeing is completed
Afterwards, cooling draining, carries out reduction cleaning;The technique of the reactive dyeing is as follows:By the reactive dye second of 1.5%o.w.f
Flat Ma Su, 200g/L Sodium Chloride of alkene sulfone active base dye, 1%o.w.f migration inhibitors is configured to dye liquor, by through dispersion dyeing
Cloth is placed in above-mentioned active dye liquor, adjusts bath raio 1:8, using the ramp of 10 DEG C/min to 70 DEG C, Matrii Sulfas Exsiccatus are added, protected
Warm 15min, adds 20g/L sodium carbonate, 5g/L sodium hydroxide, is incubated 45min, and then draining carries out next step operation;
6th step:Final finishing:Four anti-arrangements are carried out using nanometer finishing agent;
7th step:Stentering forming:Cloth after Final finishing is dried and stentering forming in 90 DEG C.
The examination and test of products:
The dyeing and finishing technology of clothes cloth material prepared by the embodiment of the present invention 1, Jing inspections, reaches following performance indications:
1. washable, perspiration resistance, fastness to rubbing:4-5 levels;
2. elimination of off flavor performance:Abnormal flavour Xia Jiang Shuai≤60% (8 hours);
3. far-infrared textiles, Fa is to Fa She Shuai≤0.90;
4. content of formaldehyde be up to state standards requirement (<55/kg);
5. Ran Shuai≤77% Shang disperse materials;
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of description is only that those skilled in the art should for clarity
Using description as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (5)
1. a kind of dyeing and finishing technology of clothes cloth material, it is characterised in that described dyeing and finishing technology is divided into following steps:
The first step:Singe:Fabric is carried out front to singe twice, regulation speed 75m/min, and burner is required uniformly effectively;
Second step:Desizing:Cloth immersion 0.2-1.5g/L BF-7658 desizing enzyme liquids after singing, 3g/L sodium tripolyphosphates,
Sodium silicate 3-6g/L, 2.4g/L fatty alcohol ether, 2g/L chelated dispersants SR, the soda bath of the pH value 8 of 8g/L, 5-6g/L it is resistance to
In the refining agent of alkali penetrating agent and 6g/L, under conditions of pick-up 100%, and material temperature is 110 DEG C, decatize 80 minutes;
Wherein, the refining agent is the mixture of soda and iodate dioctyl succinate sodium salt, and the ratio of the two is 1:1;
3rd step:Bleaching:Cloth immersion after desizing is added the sodium hypochlorite of the pH value 9.7-10 of 5g/L, that 3-6g/L connects two is sub-
Sodium sulfate, 7g/L fatty alcohol-polyoxyethylene ether, 12g/L stabilizers rinse 65-70 minutes at 120 DEG C;
4th step:Thermal finalization:60-80 DEG C of one section of drying 5-8min in dehydrator;160-220 DEG C of two-stage nitration dries 10- again
15min;
5th step:Dyeing:The cloth of the 4th step thermal finalization is first carried out into disperse dyeing, disperse dyeing is cleaned up
Afterwards, then carry out reactive dyeing;The disperse dyeing process is as follows:By the disperse dyes of 1-4%o.w.f, 2g/L chelas
Close dispersant 1030,0.8g/L glacial acetic acid, 1g/L terylene Special high-temperature TF-212F levelling agents and be configured to dye liquor, will be fixed through heat
The cloth of type is placed in above-mentioned dye liquor, adjusts bath raio 1:7, it is warming up to 132-136 DEG C of insulation 50min, after the completion of dyeing, cooling row
Water, carries out reduction cleaning;The technique of the reactive dyeing is as follows:The reactive dye of 1.5%o.w.f, 1%o.w.f are prevented
Migration agent, 200g/L Sodium Chloride are configured to dye liquor, will be placed in above-mentioned active dye liquor through the cloth of dispersion dyeing, adjust bath raio
1:8, using the ramp of 10 DEG C/min to 70 DEG C, Matrii Sulfas Exsiccatus are added, be incubated 15min, add 20g/L sodium carbonate, 5g/L hydrogen
Sodium oxide, is incubated 45min, and then draining carries out next step operation;
6th step:Final finishing:Four anti-arrangements are carried out using nanometer finishing agent;
7th step:Stentering forming:Cloth after Final finishing is dried and stentering forming in 80-90 DEG C.
2. dyeing and finishing technology according to claim 1, it is characterised in that disperse dyes select high in the disperse dyeing
Any one of warm type disperse dyes, the black WHTS of dispersion including Zhejiang Longsheng Dye Chemical Co., Ltd, disperse black HW-BG or
Disperse blue WNBTS.
3. dyeing and finishing technology according to claim 1, it is characterised in that the reactive dye are iso-bifunctional group or ethylene
The dyestuff of sulfone active group, and the reactive dye fineness of the particles is less than 1 micron.
4. dyeing and finishing technology according to claim 1, it is characterised in that the migration inhibitor is flat Ma Su.
5. dyeing and finishing technology according to claim 1, it is characterised in that the nanometer finishing agent that the Final finishing is adopted is by amino
Silicone oil NSW, waterproofing agent NT-X604A, oil-proofing agent NT-X604B, anti-fouling agent NT-X603D, resin NT-X603E and composite catalyst
NKS is constituted, and 2 grams of amido silicon oil NSW, 40 grams of waterproofing agent NT-X604A, oil-proofing agent NT-X604B 40 are added in every liter water
Gram, 15 grams of anti-fouling agent NT-X603D, 15 grams of resin NT-X603E, 10 grams of composite catalyst NKS;With handy glacial acetic acid carwash,
Fabric being padded with four liquid-proof for preparing, being heated to 120-130 degree with steam, drying cylinder is dried 90 seconds.