CN106634335A - General coating and preparation method for preparing light-color and dark-color general coating - Google Patents
General coating and preparation method for preparing light-color and dark-color general coating Download PDFInfo
- Publication number
- CN106634335A CN106634335A CN201611090934.4A CN201611090934A CN106634335A CN 106634335 A CN106634335 A CN 106634335A CN 201611090934 A CN201611090934 A CN 201611090934A CN 106634335 A CN106634335 A CN 106634335A
- Authority
- CN
- China
- Prior art keywords
- preparation
- colour paint
- weight
- acrylic emulsion
- dark
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a general coating and a preparation method for preparing a light-color and dark-color general coating. The general coating comprises the following components by weight percent: 10-18% of water, 0.3-3% of texanol, 0.35-3% of propylene glycol, 0.05-0.5% of organic silicon, 0.05-1% of polycarboxylic ammonium, 0.05-1.1% of isothiazolinone, 0.05-1.1% of sodium alkylarylsulfonate, 0.1-0.5% of cellulose, 0-30% of titanium dioxide, 5-35% of acrylate emulsion, 5-35% of acrylic emulsion, 0.24-1% of polyacrylate, 5-36% of modified talcum powder and 0-20% of color paste. The general coating provided by the invention is suitable for the substrate surface decoration of indoor and outdoor concrete structures, bamboo structure and steel structure and has the advantages of excellent weather fastness, pollution resistance, brushing resistance, wide application scope, simple preparation method, easiness in production and easiness in popularization.
Description
Technical field
The present invention relates to paint field, and in particular to a kind of universal lacquer, preparation light color universal lacquer preparation method with
And the preparation method of the dark universal lacquer of preparation.
Background technology
With the development of social economy, the living standard more and more higher of the people, the quality to living also increasingly is paid close attention to, right
It is consequently increased in beautiful pursuit, the people are also increasing to the demand of decorative paint, and decorative paint can be with beautifying constructure
Surface, so as to reach the purpose of beautifying city and protection building wall.
Due to the existing decorative paint scope of application it is little, it is impossible to be common to xoncrete structure, bamboo-wood structure and steel construction etc.
The substrate surface decoration of different structure, it is also difficult to accomplish outdoor and indoor universal；So using decorative paint decorative architecture thing
The matrix structure of building surface need to be considered during surface, it is also contemplated that indoor or outdoor use, according to different matrix structures
Corresponding coating is selected with use occasion, causes work progress to need frequently to change different coating and instrument, construction working is numerous
Weight, inefficiency.
Therefore, the selection of coating and the decorative effect of building global consistency is readily available during construction for convenience,
Need a kind of coating of the substrate surface decoration of xoncrete structure for being common to indoor and outdoor, bamboo-wood structure and steel construction.
The content of the invention
It is an object of the invention to solve shortcoming and defect present in above-mentioned prior art, there is provided a kind of universal lacquer,
The preparation method for preparing light universal lacquer and the preparation method for preparing dark universal lacquer.The universal lacquer is applied to interior
The substrate surface decoration of outer xoncrete structure, bamboo-wood structure and steel construction, preparation method is simple, it is easy to produce.
The technical solution adopted for the present invention to solve the technical problems is：A kind of universal lacquer, by weight calculating, it is wrapped
Include following components：
Water 10-18%, the 0.3-3% of alcohol ester 12, propane diols 0.35-3%, organosilicon 0.05-0.5%, polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%, sodium alklyarylsulfonate 0.05-1.1%, cellulose 0.1-0.5%, titanium dioxide 0-30%, silicon third
Emulsion 5-35%, acrylic emulsion 5-35%, polyacrylate 0.24-1%, modified talc powder 5-36%, mill base 0-20%.
For the demand of light paint toning, in order to cost-effective and color in order to be able to easily recall various gorgeous light color,
Special light colour paint pulp.
The invention further relates to a kind of preparation method for preparing light universal lacquer, comprises the steps：
（1）The preparation of active mother liquor：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, alkyl
During aryl sulfonic acid sodium, cellulose are by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of light colour paint pulp：Active mother liquor, titanium dioxide, modified talc powder are carried out by weight the ratio for calculating
Feed intake mixing, is uniformly dispersed at a high speed, checks scraper plate and remains without the sphere of powder on scraper plate, obtains light colour paint pulp；
（3）The preparation of light colour paint base-material：By light colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio mixing of calculation, is uniformly dispersed at a high speed, obtains light colour paint base-material；
（4）The preparation of light colour paint：It is light colour paint base-material stirring at low speed is uniform, you can to obtain light universal lacquer；Or, by weight
Than calculating, the light colour paint base-material above or equal to 90% and the mill base less than or equal to 10%, stirring at low speed is uniform, obtains light color
The ratio sum of universal lacquer, light colour paint base-material and mill base is equal to 100%；
Wherein, each raw material components are as follows by weight the accounting for calculating：
Water 10-18%,
The 0.3-3% of alcohol ester 12,
Propane diols 0.35-3%,
Organosilicon 0.05-0.5%,
Polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%,
Sodium alklyarylsulfonate 0.05-1.1%,
Cellulose 0.1-0.5%,
Titanium dioxide 10-30%,
Silicone acrylic emulsion 5-35%,
Acrylic emulsion 5-35%,
Polyacrylate 0.24-1%,
Modified talc powder 5-36%,
Mill base 0-10%.
Moreover, it relates to a kind of preparation method for preparing dark universal lacquer, comprises the steps：
（1）The preparation of active mother liquor：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, alkyl
During aryl sulfonic acid sodium, cellulose are by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of dark colour paint pulp：Active mother liquor, modified talc powder are carried out into the mixing that feeds intake by weight the ratio for calculating,
It is uniformly dispersed at a high speed, obtains dark colour paint pulp；
（3）The preparation of dark colour paint base-material：By dark colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio of calculation carries out the mixing that feeds intake, and is uniformly dispersed at a high speed, obtains dark colour paint base-material；
（4）The preparation of dark colour paint：Dark colour paint base-material, mill base are carried out into the mixing that feeds intake, stirring at low speed by weight the ratio for calculating
Uniformly, you can the ratio sum for obtaining dark universal lacquer, dark colour paint base-material and mill base is equal to 100%；
Wherein, each raw material components are as follows by weight the accounting for calculating：
Water 10-18%,
The 0.3-3% of alcohol ester 12,
Propane diols 0.35-3%,
Organosilicon 0.05-0.5%,
Polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%,
Sodium alklyarylsulfonate 0.05-1.1%,
Cellulose 0.1-0.5%,
Silicone acrylic emulsion 5-35%,
Acrylic emulsion 5-35%,
Polyacrylate 0.24-1%,
Modified talc powder 5-36%,
Mill base 10-20%.
The universal lacquer of the present invention belongs to water soluble paint category, and directly adds water the coating dilution that just can carry out, convenient construction,
Paint thinner is not required the use of, environment-protective no-smell just can realize dry tack free in brushing half an hour after.
Compared with prior art, beneficial effects of the present invention are：
（1）The universal lacquer that the present invention is provided is applied to the base material table of the xoncrete structure, bamboo-wood structure and steel construction of indoor and outdoor
Face is decorated, applied widely, and preparation method is simple, it is easy to produce；
（2）This universal lacquer can directly cover with paint, lacquer, colour wash, etc. the surface of wall in xoncrete structure and bamboo-wood structure, not require the use of other priming paint,
Save material cost and construction cost；Adhesive force is good, can cover with paint, lacquer, colour wash, etc. in the smooth surface of wall such as mosaic, it is adaptable to ceramic tile wall
Body cover type is renovated, and reduces renovation cost；
（3）This universal lacquer is covered with paint, lacquer, colour wash, etc. when the substrate surface of steel construction, coordinates water-thinned antirust primer to use；Cover with paint, lacquer, colour wash, etc. in antirust sheet material
Then can be used directly during surface, do not require the use of anti-corrosive primer；Folded sheet is not result in the film cracking that this coating is formed, film
Pliability is strong；
（4）The universal lacquer of the present invention also has good weatherability, pollution resistance, brushing resistance, it is easy to promoted.
Specific embodiment
Embodiment 1
A kind of preparation method for preparing light universal lacquer described by the present embodiment 1, comprises the steps：（1）Active mother liquor
Preparation：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, sodium alklyarylsulfonate, fiber
During element is by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of light colour paint pulp：Active mother liquor, titanium dioxide, modified talc powder are carried out by weight the ratio for calculating
Feed intake mixing, is uniformly dispersed at a high speed, checks scraper plate and remains without the sphere of powder on scraper plate, obtains light colour paint pulp；
（3）The preparation of light colour paint base-material：By light colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio mixing of calculation, is uniformly dispersed at a high speed, obtains light colour paint base-material；
（4）The preparation of light colour paint：It is light colour paint base-material stirring at low speed is uniform, you can to obtain light universal lacquer.
The each component of the light universal lacquer is specific as follows by by weight calculating：
Water 10%, alcohol ester ten two 0.5%, propane diols 0.6%, organosilicon 0.1%, polycarboxylic acids ammonium salt 0.5%, OIT 1.1%, alkane
Base aryl sulfonic acid sodium 1.1%, cellulose 0.5%, titanium dioxide 10%, silicone acrylic emulsion 27%, acrylic emulsion 26.1%, polyacrylic acid
Ester 0.9%, modified talc powder 21.6%.
Embodiment 2
A kind of preparation method for preparing light universal lacquer described by the present embodiment 2, comprises the steps：（1）Active mother liquor
Preparation：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, sodium alklyarylsulfonate, fiber
During element is by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of light colour paint pulp：Active mother liquor, titanium dioxide, modified talc powder are carried out by weight the ratio for calculating
Feed intake mixing, is uniformly dispersed at a high speed, checks scraper plate and remains without the sphere of powder on scraper plate, obtains light colour paint pulp；
（3）The preparation of light colour paint base-material：By light colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio mixing of calculation, is uniformly dispersed at a high speed, obtains light colour paint base-material；
（4）The preparation of light colour paint：Light colour paint base-material and mill base are mixed by weight the ratio for calculating, stirring at low speed is equal
Even, the ratio sum for obtaining light universal lacquer, light colour paint base-material and mill base is equal to 100%.
The each component of the light universal lacquer is specific as follows by by weight calculating：
Water 18%, alcohol ester ten two 3%, propane diols 3%, organosilicon 0.5%, polycarboxylic acids ammonium salt 1%, OIT 1.1%, alkylaryl
Sodium sulfonate 1.1%, cellulose 0.5%, titanium dioxide 30%, silicone acrylic emulsion 5%, acrylic emulsion 5%, polyacrylate 0.24% changes
Property talcum powder 21.56%, mill base 10%.
Embodiment 3
A kind of preparation method for preparing dark universal lacquer described by the present embodiment 3, comprises the steps：（1）Active mother liquor
Preparation：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, sodium alklyarylsulfonate, fiber
During element is by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of dark colour paint pulp：Active mother liquor, modified talc powder are carried out into the mixing that feeds intake by weight the ratio for calculating,
It is uniformly dispersed at a high speed, obtains dark colour paint pulp；
（3）The preparation of dark colour paint base-material：By dark colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio of calculation carries out the mixing that feeds intake, and is uniformly dispersed at a high speed, obtains dark colour paint base-material；
（4）The preparation of dark colour paint：Dark colour paint base-material, mill base are carried out into the mixing that feeds intake, stirring at low speed by weight the ratio for calculating
Uniformly, you can the ratio sum for obtaining dark universal lacquer, dark colour paint base-material and mill base is equal to 100%.
The each component of the dark universal lacquer is specific as follows by by weight calculating：
Water 10%, alcohol ester ten two 0.5%, propane diols 0.6%, organosilicon 0.1%, polycarboxylic acids ammonium salt 0.5%, OIT 1.1%, alkane
Base aryl sulfonic acid sodium 1.1%, cellulose 0.5%, silicone acrylic emulsion 27%, acrylic emulsion 26.1%, polyacrylate 0.9% is modified and slides
Stone flour 21.6%, mill base 10%.
Embodiment 4
The present embodiment 4 is changed on the basis of embodiment 3, and the weight ratio of each component of specially dark universal lacquer is not
Together, it is specific as follows：
The each component of the dark universal lacquer is specific as follows by by weight calculating：
Water 18%, alcohol ester ten two 3%, propane diols 3%, organosilicon 0.5%, polycarboxylic acids ammonium salt 1%, OIT 1.1%, alkylaryl
Sodium sulfonate 1.1%, cellulose 0.5%, silicone acrylic emulsion 5%, acrylic emulsion 10.76%, polyacrylate 0.24%, modified talc powder
35.8%, mill base 20%.
The above is only presently preferred embodiments of the present invention, every structure according to described in present patent application scope
Make, the equivalence changes that feature and principle are done or modification, should be included within the scope of the present invention.
Claims (3)
1. a kind of universal lacquer, it is characterised in that by weight calculating, it includes following components：
Water 10-18%,
The 0.3-3% of alcohol ester 12,
Propane diols 0.35-3%,
Organosilicon 0.05-0.5%,
Polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%,
Sodium alklyarylsulfonate 0.05-1.1%,
Cellulose 0.1-0.5%,
Titanium dioxide 0-30%,
Silicone acrylic emulsion 5-35%,
Acrylic emulsion 5-35%,
Polyacrylate 0.24-1%,
Modified talc powder 5-36%,
Mill base 0-20%.
2. a kind of preparation method for preparing light universal lacquer described in universal lacquer according to claim 1, it is characterised in that
Comprise the steps：
（1）The preparation of active mother liquor：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, alkyl
During aryl sulfonic acid sodium, cellulose are by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of light colour paint pulp：Active mother liquor, titanium dioxide, modified talc powder are carried out by weight the ratio for calculating
Feed intake mixing, is uniformly dispersed at a high speed, checks scraper plate and remains without the sphere of powder on scraper plate, obtains light colour paint pulp；
（3）The preparation of light colour paint base-material：By light colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio mixing of calculation, is uniformly dispersed at a high speed, obtains light colour paint base-material；
（4）The preparation of light colour paint：It is light colour paint base-material stirring at low speed is uniform, you can to obtain light universal lacquer；Or, by weight
Than calculating, the light colour paint base-material above or equal to 90% and the mill base less than or equal to 10%, stirring at low speed is uniform, obtains light color
The ratio sum of universal lacquer, light colour paint base-material and mill base is equal to 100%；
Wherein, each raw material components are as follows by weight the accounting for calculating：
Water 10-18%,
The 0.3-3% of alcohol ester 12,
Propane diols 0.35-3%,
Organosilicon 0.05-0.5%,
Polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%,
Sodium alklyarylsulfonate 0.05-1.1%,
Cellulose 0.1-0.5%,
Titanium dioxide 10-30%,
Silicone acrylic emulsion 5-35%,
Acrylic emulsion 5-35%,
Polyacrylate 0.24-1%,
Modified talc powder 5-36%,
Mill base 0-10%.
3. a kind of preparation method for preparing dark universal lacquer described in universal lacquer according to claim 1, it is characterised in that
Comprise the steps：
（1）The preparation of active mother liquor：By water, alcohol ester 12, propane diols, organosilicon, polycarboxylic acids ammonium salt, OIT, alkyl
During aryl sulfonic acid sodium, cellulose are by weight the ratio input dispersion slot for calculating, it is uniformly dispersed at a high speed, obtains active mother liquor；
（2）The preparation of dark colour paint pulp：Active mother liquor, modified talc powder are carried out into the mixing that feeds intake by weight the ratio for calculating,
It is uniformly dispersed at a high speed, obtains dark colour paint pulp；
（3）The preparation of dark colour paint base-material：By dark colour paint pulp, silicone acrylic emulsion, acrylic emulsion, polyacrylate by weight
The ratio of calculation carries out the mixing that feeds intake, and is uniformly dispersed at a high speed, obtains dark colour paint base-material；
（4）The preparation of dark colour paint：Dark colour paint base-material, mill base are carried out into the mixing that feeds intake, stirring at low speed by weight the ratio for calculating
Uniformly, you can the ratio sum for obtaining dark universal lacquer, dark colour paint base-material and mill base is equal to 100%；
Wherein, each raw material components are as follows by weight the accounting for calculating：
Water 10-18%,
The 0.3-3% of alcohol ester 12,
Propane diols 0.35-3%,
Organosilicon 0.05-0.5%,
Polycarboxylic acids ammonium salt 0.05-1%,
OIT 0.05-1.1%,
Sodium alklyarylsulfonate 0.05-1.1%,
Cellulose 0.1-0.5%,
Silicone acrylic emulsion 5-35%,
Acrylic emulsion 5-35%,
Polyacrylate 0.24-1%,
Modified talc powder 5-36%,
Mill base 10-20%.