CN106626597A - Pressure-resistant fireproof plate and manufacturing method thereof - Google Patents
Pressure-resistant fireproof plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN106626597A CN106626597A CN201611100433.XA CN201611100433A CN106626597A CN 106626597 A CN106626597 A CN 106626597A CN 201611100433 A CN201611100433 A CN 201611100433A CN 106626597 A CN106626597 A CN 106626597A
- Authority
- CN
- China
- Prior art keywords
- mine tailing
- layer
- grain slag
- slag magnesite
- plastic laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pressure-resistant fireproof plate and a manufacturing method thereof. The pressure-resistant fireproof plate comprises a tailing water slag magnesite gelatinizing material, wherein two layers of glass fiber gridding cloth, one layer of glass fiber gridding cloth and one organic silicon waterproof layer are arranged on the upper part of the tailing water slag magnesite gelatinizing material sequentially from bottom to top; the upper surface of the organic silicon waterproof layer adopts a sanding surface; tailing water slag magnesite gel fills between the glass fiber gridding cloth and the organic silicon waterproof layer; two layers of glass fiber gridding cloth, one organic silicon waterproof layer and a nature color face layer are arranged on the lower part of the tailing water slag magnesite gelatinizing material sequentially from top to bottom; the space between the two layers of glass fiber gridding cloth is fixed with nature color face slurry. According to the pressure-resistant fireproof plate provided by the invention, the water absorbing rate of the product is less than 5 percent, the softening coefficient is 1 and the pressure-resistant strength is more than 40 MPa; the pressure-resistant fireproof plate is lightweight, high-strength and widely applied to interior decoration fireproof plates.
Description
Technical field
The present invention relates to building material field, is related specifically to a kind of measuring body PLASTIC LAMINATED and its manufacture method.
Background technology
China's building materials industry resources and energy consumption is high, gross contamination emission is big, at present, mainly takes in surrounding city hole
Depression band sets up interim eliminate-incorporate-land and carries out the mode of simple landfill and disposed, and causes serious environmental pollution and land resource wave
Take.
And mineral products are valuable sources for the survival of mankind.In the development process of mineral resources, can be to a certain in ore
Or multiple components carry out sorting utilization, unemployed component then can be discarded as solid waste, form mine tailing.Usual tail
Ore deposit can be transported to appointed place, and storage of building a dam, and form Tailings Dam.China's mine tailing storage is huge.According to incompletely statistics, only 2013
Year mine tailing is produced just up to 16.49 hundred million tons, iron tailings 51%, copper tailing 20%, remaining is other mineral products mine tailings.Comprehensive utilization of tailing
Amount is only 3.12 hundred million tons, and comprehensive utilization ratio is very low, and only 18.9%, wherein, 53% is accounted for using mine tailing filling, production building materials are accounted for
43%.In addition to relatively low comprehensive utilization ratio, because frequently with the form of air storage, there is very macrohabitat safety in mine tailing
Hidden danger.Industrial residue, mine tailing " turning waste into wealth " so as to " innoxious, resource, minimizing ", improve human settlement, build
Conservation culture, be green building material and green building Industrial Convergence development in the urgent need to.
The PLASTIC LAMINATED that existing open air uses needs substantial amounts of timber with substantial amounts of sawdust as inserts, destroys ecology
Environment, and the product water absorption rate > 10% of fire-proof board, coefficient of softing 0.85, compression strength is low.So causing sheet material at family
Outer Long-Time Service, it may appear that swell seesaw the problems such as.
The content of the invention
The technical problem to be solved in the present invention is:One kind is provided with magnesite material as gelling agent, a large amount of blast furnace granulated slags are added
For inserts, existing PLASTIC LAMINATED, light weight, a kind of measuring body measuring body PLASTIC LAMINATED and its manufacture method are overcome the shortcomings of.
The technical solution adopted for the present invention to solve the technical problems:A kind of measuring body PLASTIC LAMINATED, including mine tailing grain slag water chestnut
Magnesium Binder Materials, the mine tailing grain slag magnesite binding material top be sequentially provided with from bottom to up two-layer fiberglass gridding cloth,
Layer of glass grid cloth and one layer of organic silicon water-proofing layer, the organic silicon water-proofing layer upper surface be sanding face, the glass
Between fibrous mesh cloth and organic silicon water-proofing layer filled with mine tailing grain slag magnesite be gelled, mine tailing grain slag magnesite binding material bottom from
Layer glass fibrous mesh cloth, one layer of organic silicon water-proofing layer and this color surface layer, the gelling of mine tailing grain slag magnesite are up to sequentially provided with down
True qualities starch adhesive material is filled between the layer glass fibrous mesh cloth of material bottom.
Further, it is additionally provided with least one of which non-woven fabrics on the sanding face.
Further, the non-woven fabrics is per square metre of 12g to 100g.
Further, described mine tailing grain slag magnesite binding material thickness is 6-50mm.
Further, the thickness of this color surface layer is between 0.1mm to 1mm.
Present invention has the advantages that:A kind of measuring body PLASTIC LAMINATED of the present invention, by fiber grain slag magnesite binding material, glass
The cooperation of glass fiber mesh layer of cloth, this color surface layer and nonwoven layer, it is soft compared with common fire prevention panel products water absorption rate < 5%
Change coefficient 1, compression strength > 40Mpa, high-strength light is widely used in interior decoration.It should be noted that a kind of measuring body anti-
Fiery plate consumes a large amount of blast furnace granulated slags, reduces pollution, improves human settlement.
Description of the drawings
Fig. 1 is the structural representation of a kind of measuring body PLASTIC LAMINATED of the present invention;
Fig. 2 is cross-sectional schematics of the Fig. 1 along A-A;
In figure, 1-mine tailing grain slag magnesite binding material, 2-fiberglass gridding cloth, 3-this color surface layer, 4-sanding face,
5-organic silicon water-proofing layer, 6-true qualities starch adhesive material.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that specific embodiment described herein is not used to only to explain the present invention
Limit the present invention.
Embodiment 1:
As shown in Figure 1 and Figure 2, a kind of measuring body PLASTIC LAMINATED of the invention, including mine tailing grain slag magnesite binding material 1, it is described
The top of mine tailing grain slag magnesite binding material 1 is sequentially provided with from bottom to up the fiberglass gridding cloth 2 of two-layer, layer of glass net
Lattice cloth 1 and one layer of organic silicon water-proofing layer 5, the upper surface of organic silicon water-proofing layer 5 be sanding face 4, the fiberglass gridding cloth 1
Between organic silicon water-proofing layer 5 filled with mine tailing grain slag magnesite be gelled, the bottom of mine tailing grain slag magnesite binding material 1 from top to bottom according to
It is secondary to be provided with 1, one layer of organic silicon water-proofing layer 5 of layer glass fibrous mesh cloth and this color surface layer 3, mine tailing grain slag magnesite binding material 1
True qualities starch adhesive material 6 is filled between the layer glass fibrous mesh cloth 1 of bottom.
A kind of measuring body PLASTIC LAMINATED of the present invention, by mine tailing grain slag magnesite binding material 1, fiberglass gridding cloth 2, originally
The cooperation of color surface layer 3, sanding face 4, organic silicon water-proofing layer 5 and true qualities starch adhesive material 6, compared with common fire prevention panel products water absorption rate <
5%, coefficient of softing 1, compression strength > 40Mpa, quality mitigates, but intensity improves, and is widely used in interior decoration, especially
It is office building decoration.It should be noted that a kind of measuring body PLASTIC LAMINATED consumes a large amount of blast furnace granulated slags, pollution is reduced, improved
Human settlement.
Embodiment 2:
As preferred, at least one of which non-woven fabrics is additionally provided with the sanding face 4.The other parts of the present embodiment with it is above-mentioned
Embodiment is identical, repeats no more.
Embodiment 3:
Used as preferred, the non-woven fabrics is per square metre of 12g to 100g.The other parts of the present embodiment and above-mentioned enforcement
Example is identical, repeats no more.
Embodiment 4:
Used as preferred, the thickness of mine tailing grain slag magnesite binding material 1 is 6-50mm.The other parts of the present embodiment with
Above-described embodiment is identical, repeats no more.
When measuring body PLASTIC LAMINATED gross thickness is 8mm, layer glass fibrous mesh cloth 2, rupture strength > 11Mpa, when
When the measuring body PLASTIC LAMINATED gross thickness of kind is 9mm, four-layer glass fibrous mesh cloth 2, rupture strength > 24Mpa, when a kind of measuring body
PLASTIC LAMINATED gross thickness be 10mm when, four-layer glass fibrous mesh cloth 2, rupture strength > 24Mpa, when a kind of measuring body PLASTIC LAMINATED it is total
When thickness is 12mm, four-layer glass fibrous mesh cloth 2, rupture strength > 20Mpa, when a kind of measuring body PLASTIC LAMINATED gross thickness is
Six layers of fiberglass gridding cloth 2 during 16mm, rupture strength > 25Mpa, when a kind of measuring body PLASTIC LAMINATED gross thickness is 20mm six
Layer fiberglass gridding cloth 2, rupture strength > 30Mpa, seven layers of glass fibre when the measuring body fire prevention plate thickness of one kind is 20mm
Grid cloth 2, rupture strength > 35Mpa, seven layers of fiberglass gridding cloth 2 when the measuring body fire prevention plate thickness of one kind is 42mm resist
Folding intensity > 25Mpa.A kind of measuring body fire prevention plate thickness is different, and two to seven layers of glass chopped strand mat layer 2 may be selected.
Embodiment 5:
It is 6-50mm as preferred, the described thickness of mine tailing grain slag magnesite binding material 1.
Described a kind of measuring body PLASTIC LAMINATED, its preparation method is:
(1) 29.4 ° of B é magnesium sulfate waters are prepared:The epsom salt of 850kg, the water of 1000kg is dissolved into magnesium sulfate
29.4 ° of B é magnesium sulfate waters;
(2) way of true qualities starch adhesive material 6 is prepared:
Take 29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the tail of 125kg
Then all of raw material are poured into mixer and are stirred by breeze, the modifying agent of a weight;
(3) making step of mine tailing grain slag magnesite binding material 1:
Take 29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the tail of 125kg
Breeze, 180kg grain slags, the modifying agent of a weight, then pours all of raw material into mixer and stirs;
(4) PLASTIC LAMINATED is made:
One mixer stirs out true qualities starch adhesive material 6, and two mixers stir out mine tailing grain slag magnesite binding material 1 and starch
Material, is then molded on fire prevention board assembly line, and true qualities starch adhesive material 6 is paved on PVC or ABS substrates, and fiberglass gridding cloth 2 is pressed
In entering the slurry of true qualities starch adhesive material 6, the slurry of mine tailing grain slag magnesite binding material 1 is paved on true qualities starch adhesive material 6, and glass is laid again
Fibrous mesh cloth 2, lays again the slurry of mine tailing grain slag magnesite binding material 1, then lays non-woven fabrics, cleaved, leveling, supports
Shield, solidification, form removal, sanding, four side Length-fixing cuttings, maintenance, spraying waterproofing agent of organosilicon, drying.
Preferably, 29.4 ° of B é magnesium sulfate waters of 135kg are taken, the magnesia light burnt powder of 100kg, the dolomite dust of 9kg,
The mine tailing of 130kg, 190kg grain slags, the modifying agent of a weight, then pours all of raw material into mixer and stirs
Make mine tailing grain slag magnesite binding material 1.
Preferably, 29.4 ° of B é magnesium sulfate waters of 145kg are taken, the magnesia light burnt powder of 105kg, the dolomite dust of 7kg,
The mine tailing of 116kg, 165kg grain slags, the modifying agent of a weight, then pours all of raw material into mixer and stirs
Make mine tailing grain slag magnesite binding material 1.
Preferably, 29.4 ° of B é magnesium sulfate waters of 155kg are taken, the magnesia light burnt powder of 110kg, the dolomite dust of 12kg,
The mine tailing of 140kg, 225kg grain slags, the modifying agent of a weight, then pours all of raw material into mixer and stirs
Make mine tailing grain slag magnesite binding material 1.
Preferably, 29.4 ° of B é magnesium sulfate waters of 165kg are taken, the magnesia light burnt powder of 120kg, the dolomite dust of 4kg,
The mine tailing of 115kg, 200kg grain slags, the modifying agent of a weight, then pours all of raw material into mixer and stirs
Make mine tailing grain slag magnesite binding material 1.
Preferably, the proportioning of true qualities starch adhesive material 6:Take 29.4 ° of B é magnesium sulfate waters of 130kg, the magnesia light burnt powder of 95kg,
Then all of raw material are poured into mixer and are stirred by the dolomite dust of 8kg, the mine tailing of 115kg, the modifying agent of a weight
Mix uniform.
Non-woven fabrics is reduced according to measuring body per square metre of the fire prevention plate thickness different choice 33g to 69g of one kind, its Main Function
Product surface porosity, facilitates vacuum cup product offline.
Semi-finished product Jing leveling, maintenance, solidification, form removal, reach intensity after by production line enter four side sizing cutting machines, enter
Row Length-fixing cutting, product is offline.
Above example only to illustrate technical scheme, rather than a limitation;Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that:Its in specification still can be right
Technical scheme described in foregoing embodiments is modified, or carries out equivalent to which part technical characteristic, not
Make the spirit and scope of the essence disengaging various embodiments of the present invention technical scheme of appropriate technical solution.
Claims (6)
1. a kind of measuring body PLASTIC LAMINATED, it is characterised in that:Including mine tailing grain slag magnesite binding material (1), the mine tailing grain slag water chestnut
Magnesium Binder Materials (1) top is sequentially provided with from bottom to up fiberglass gridding cloth (2), the layer of glass grid cloth of two-layer
(1) and one layer of organic silicon water-proofing layer (5), organic silicon water-proofing layer (5) upper surface is sanding face (4), the glass fiber mesh
It is gelled filled with mine tailing grain slag magnesite between Ge Bu (1) and organic silicon water-proofing layer (5), the mine tailing grain slag magnesite binding material
(1) bottom is sequentially provided with from top to bottom layer glass fibrous mesh cloth (1), one layer of organic silicon water-proofing layer (5) and this color surface layer
(3) true qualities starch adhesive, is filled between the layer glass fibrous mesh cloth (1) of mine tailing grain slag magnesite binding material (1) bottom
Material (6).
2. a kind of measuring body PLASTIC LAMINATED according to claim 1, it is characterised in that:Be additionally provided with the sanding face (4) to
Few layer of non-woven fabric.
3. a kind of measuring body PLASTIC LAMINATED according to claim 2, it is characterised in that:The non-woven fabrics is that 12g to 100g is every
Square metre.
4. according to the arbitrary described a kind of measuring body PLASTIC LAMINATED of claims 1 to 3, it is characterised in that:The mine tailing grain slag magnesite
Binder Materials (1) thickness is 6-50mm.
5. according to the arbitrary described a kind of measuring body PLASTIC LAMINATED of claims 1 to 3, it is characterised in that:Described color surface layer (3)
Thickness is between 0.1mm to 1mm.
6., according to the arbitrary described a kind of measuring body PLASTIC LAMINATED of claim 1-5, its preparation method is:
(1) 29.4 ° of B é magnesium sulfate waters are prepared:The epsom salt of 850kg, the water of 1000kg makes magnesium sulfate be dissolved into 29.4 ° of B é
Magnesium sulfate water;
(2) way of true qualities starch adhesive material (6) is prepared:
Take 29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the mine tailing of 125kg,
The modifying agent of a weight, then all of raw material are poured into mixer stir;
(3) making step of mine tailing grain slag magnesite binding material (1):
Take 29.4 ° of B é magnesium sulfate waters of 125kg, the magnesia light burnt powder of 100kg, the dolomite dust of 4kg, the mine tailing of 125kg,
The modifying agent of 180kg grain slags, a weight, then pours all of raw material into mixer and stirs;
(4) PLASTIC LAMINATED is made:
One mixer stirs out true qualities starch adhesive material (6), and two mixers stir out mine tailing grain slag magnesite binding material slurry, so
It is molded on fire prevention board assembly line afterwards, true qualities starch adhesive material (6) are paved on PVC or ABS substrates, fiberglass gridding cloth (6) pressure
In entering true qualities starch adhesive material (6), mine tailing grain slag magnesite binding material slurry is paved in true qualities starch adhesive material (6), and glass is laid again
Fibrous mesh cloth (2), lays again mine tailing grain slag magnesite binding material slurry, then lays non-woven fabrics, cleaved, leveling, supports
Shield, solidification, form removal, sanding, four side Length-fixing cuttings, maintenance, spraying waterproofing agent of organosilicon, drying.