CN106626167A - Long-acting environment-friendly release agent and preparing method thereof - Google Patents
Long-acting environment-friendly release agent and preparing method thereof Download PDFInfo
- Publication number
- CN106626167A CN106626167A CN201510736280.7A CN201510736280A CN106626167A CN 106626167 A CN106626167 A CN 106626167A CN 201510736280 A CN201510736280 A CN 201510736280A CN 106626167 A CN106626167 A CN 106626167A
- Authority
- CN
- China
- Prior art keywords
- releasing agent
- release agent
- long
- environmental protection
- protection type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a long-acting environment-friendly release agent and a preparing method thereof. The release agent comprises the following components including NiSO4.6H2O, NaH2PO2.H2O, Na3C6H5O7.2H2O, C2H3NaO2CH3COONa, CuSO4, CH4N2S, PTFE particles, graphite particles, octadecyl trimethyl ammonium chloride and deionized water. According to the long-acting environment-friendly release agent, a composite film formed in the using process can achieve the excellent demoulding effect, and can achieve the effects of protecting a mold and prolonging the service life of the mold. The long-acting environment-friendly release agent overcomes the defects that a traditional release agent is prone to transferring and polluting a product are overcome, so that the long-acting environment-friendly release agent is more suitable for the fields, such as optical products, medical products or food products with high requirements; and the excellent demolding performance can be played for a long time after the release agent is sprayed one time.
Description
【Technical field】
The present invention relates to a kind of long-acting environment friendly releasing agent and preparation method thereof.
【Background technology】
Plastic mould accounts for consequence in modern industrial system, and with Design of Dies, advancing by leaps and bounds for process technology and continually developing for new material, increasing highly difficult, high accuracy, the product of high request are produced by the way of plastic mould injection.Diversified releasing agent is exactly to continue to bring out under such background, but existing releasing agent product suffers from following defect.1st, poor heat resistance, easily carbonization are decomposed so as to fail.2nd, pH value is presented acid, there is certain corrosiveness to mould.3rd, easily transfer, pollutes plasthetics, especially to the optics that has high demands or medicine equipment component.4th, environment is polluted, there is threat to the health of operating personnel.So a kind of permanent type releasing agent of environment-friendly high-efficiency has highly important meaning for the development for solving existing issue acceleration plastic mould.
【The content of the invention】
The present invention seeks to solve existing releasing agent pollution environment, easily failure, the easily shortcoming of transfer, there is provided a kind of to strengthen the corrosion-resistant and wear-resistant performance long-acting environment friendly releasing agent of mould.
Another object of the present invention is to provide a kind of preparation method of above-mentioned releasing agent.
The present invention is achieved by the following technical solutions:
A kind of long effective environmental protection type releasing agent, it is characterised in that including following components:NiSO4·6H2O, NaH2PO2·H2O, Na3C6H5O7·2H2O, C2H3NaO2CH3COONa, CuSO4, CH4N2S, PTFE particulate, graphite particulate, OTAC and deionized water.
The pH value of obtained releasing agent of the invention is 7.0, and corrosion will not be caused to die surface.
Octadecyl in the present invention can be such that the graphite particulate and PTFE particulates of addition is evenly distributed in releasing agent to be not susceptible to precipitate or chromatograph, make system more stable as emulsifying agent.
The particle diameter of PTFE particulates and graphite particulate in the present invention is 0.1-0.8 μm, 0.2 μm of preferable particle size.
In the present invention, PTF PARTICLE Es and graphite particulate suffer from high temperature resistant, self-lubricating, do not adhere to, the advantage of acid and alkali-resistance.Various composition in releasing agent generates composite bed under interaction, and both particulates are firmly fixed on into die surface so as to play the good demoulding and corrosion resistant effect.Specifically action principle is the present invention:Graphite particulate and PTFE particulates are uniformly suspended in releasing agent in the presence of stabilizer OTAC, and when releasing agent is directed onto heated die surface, graphite particulate and PTFE particulates are covered in die surface due to physisorption.At the same time NiSO4·6H2O and CuSO4By NaH2PO2·H2O is reduced, and generates one layer of laminated film being made up of Ni-P-Cu and by these particle encapsulations in die surface rapidly.These particulates are just become by physical absorption and are embedded in die surface.
The content of each component of the present invention is as follows:
Further, the concrete content of each component of the present invention is as follows:
The concrete consumption from water is removed in the present invention to be settled to aequum as principle.
Releasing agent in the present invention is used with nitrogen as propellant is canned, and pressure inside the tank is 0.3-0.5MPa.
A kind of preparation method of above-mentioned long effective environmental protection type releasing agent, it is characterised in that comprise the following steps:
After weighing each component, deionized water is heated in water-bath 45-55 DEG C, it is initially charged OTAC to be dissolved, and be sufficiently stirred for, it is subsequently adding graphite particulate and the stirring of PTFE particles is abundant, it is eventually adding remaining medicament, stop heating and persistently stir, liquid temp to be mixed dropped to and be distributed into after room temperature in pressurized tank, and pour high pure nitrogen makes pressure inside the tank reach 0.3-0.5MPa as propellant, you can.
The using method of releasing agent of the present invention is very easy, concrete operation method be after mould is heated to 60 DEG C -80 DEG C as needed with equipped with releasing agent aerosol can die surface is carried out even application 1-2 all over.
Compared with prior art, the present invention has the following advantages:
Releasing agent of the present invention sprays to and redox reaction occurs after heated die surface, one layer of laminated film is formed in die surface, this layer film strength is attached to die surface, and the thickness of film is below 0.5 micron, and mould and die accuracy will not be had any impact.The laminated film does not contain in addition to deionized water and propellant high pure nitrogen are evaporated the various organic solvents in traditional releasing agent in forming process, has prevented the healthy harm to operating personnel, complies fully with the requirement of environmental protection.
The laminated film that formed in use of the present invention have do not glue, self-lubricating, coefficient of friction are low, wear-resisting, corrosion resistant excellent properties; hardness can reach HRC50, therefore can not only play the demoulding effect of brilliance mould can also be played a part of to protect and increase the service life.
The laminated film and the adhesion-tight of die surface, by ASTM tests 4B grades can be reached.Therefore perfectly solve traditional releasing agent easily to transfer the pollution the defect of product.So more suitable for use in the field of the high requests such as optical goods, medical article or food compositions.
The laminated film heat resisting temperature that releasing agent of the present invention is formed can reach 350 DEG C, be not in the phenomenon failed because of charing under the molding technological condition of common plastic cement, and its excellent release property can be played for a long time after once spraying.
Releasing agent of the present invention is simple to operate when using, economical and practical, is suitable to promote.
【Description of the drawings】
Fig. 1 is the structural representation that the present invention is formed in die surface.
【Specific embodiment】
The present invention is described in further detail with reference to specific embodiment:
The proportioning of embodiment 1-4 is as shown in table 1:
Table 1:
The preparation method of embodiment 1-5 is:
Proportionally weigh each component, deionized water is heated in water-bath 45-55 DEG C, it is initially charged OTAC to be dissolved, and be sufficiently stirred for, it is subsequently adding graphite particulate and the stirring of PTFE particles is abundant, it is eventually adding remaining medicament, stop heating and persistently stir, liquid temp to be mixed drops to the amount after room temperature according to per part of 300ml and is distributed in pressurized tank, and pour high pure nitrogen makes pressure inside the tank reach 0.3-0.5MPa as propellant, you can.
The releasing agent measure of merit of the embodiment of the present invention:
The equal dies that 1 set of newest processing is also produced have been selected in test, and mould structure is 20 caves, and product is Inner thread mineral water bottle caps, and injection raw material is polyethylene, and stripping means are forced stripper mechanism.Mould is heated to into 80 DEG C, the releasing agent configured in embodiment 1-5 is sprayed on mold parting surface respectively, the head releasing agent prepared by 1-4 caves spraying embodiment 1, each product position spray time is the 1-2 seconds, is sprayed twice, and each interval time is 5 minutes.Same spraying method it is non-not by the releasing agent prepared by embodiment 2-5 be sprayed on 5-8 caves, 9-10 caves, 11-13 caves, above 14-17 caves.18-20 caves do not spray as a control group
Test result is shown in Table 2:
Table 2:
Can be seen that the releasing agent that the formula and preparation method of the releasing agent of the present invention are obtained not only has good release property from the data of table 2, and long-lasting and corrosion resistance has also obtained good checking.
The structure that the present invention is formed after being sprayed on mould is as shown in Figure 1:
①:Mould base material is 2.:Ni-P-Cu composite beds are 3.:Graphite particulate or PTFE particulates.
Claims (7)
1. a kind of long effective environmental protection type releasing agent, it is characterised in that including following components:
NiSO4·6H2O, NaH2PO2·H2O, Na3C6H5O7·2H2O, C2H3NaO2CH3COONa
, CuSO4, CH4N2S, PTFE particulate, graphite particulate, octadecyl front three
Ammonium chloride and deionized water.
2. a kind of long effective environmental protection type releasing agent according to claim 1, it is characterised in that
The pH value of the releasing agent is 7.0.
3. a kind of long effective environmental protection type releasing agent according to claim 1, it is characterised in that
Described PTFE particulates and the particle diameter of graphite particulate is 0.1-0.8 μm.
4. a kind of long effective environmental protection type releasing agent according to claim 1, it is characterised in that
The content of each component is as follows:
5. a kind of long effective environmental protection type releasing agent according to claim 1, it is characterised in that
The concrete content of each component is as follows:
6. a kind of long effective environmental protection type releasing agent according to any one of claim 1-5,
It is characterized in that described releasing agent is used with nitrogen as propellant is canned, pressure inside the tank is
0.3-0.5MPa。
7. the preparation method of the long effective environmental protection type releasing agent described in a kind of claim 6, it is special
Levy is to comprise the following steps:
Deionized water is heated in water-bath 45-55 DEG C, octadecyl trimethyl is initially charged
Ammonium chloride is dissolved, and is sufficiently stirred for, and is subsequently adding graphite particulate and PTFE particles
Stirring is abundant, is eventually adding remaining medicament, stops heating and persistently stirs, liquid temp to be mixed
Drop to and be distributed into after room temperature in pressurized tank, pour high pure nitrogen reaches pressure inside the tank as propellant
To 0.3-0.5MPa, you can.