CN106590089A - Water-based potassium silicate zinc-rich primer used for surface treatment of long-acting anti-microbial section steel structures and preparation method of water-based potassium silicate zinc-rich primer - Google Patents
Water-based potassium silicate zinc-rich primer used for surface treatment of long-acting anti-microbial section steel structures and preparation method of water-based potassium silicate zinc-rich primer Download PDFInfo
- Publication number
- CN106590089A CN106590089A CN201611142585.6A CN201611142585A CN106590089A CN 106590089 A CN106590089 A CN 106590089A CN 201611142585 A CN201611142585 A CN 201611142585A CN 106590089 A CN106590089 A CN 106590089A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- potassium silicate
- rich primer
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based potassium silicate zinc-rich primer used for surface treatment of long-acting anti-microbial section steel structures. The water-based potassium silicate zinc-rich primer is prepared from, by weight, 100-102 parts of scale zinc powder, 15-17 parts of potassium silicate, 1-2 parts of water-based epoxy resin emulsion, 6-8 parts of styrene-acrylic emulsion, 3-5 parts of methyltrimethoxysilane, 1.2-1.4 parts of ytterbium chloride, 4-6 parts of viscose, 2.1-2.3 parts of single-wall carbon nanotubes, 10-11 parts of potash feldspar powder, 6-8 parts of polyvinyl alcohol, 5-7 parts of chitosan, 0.4-0.7 part of ferrocene and 21-23 parts of deionized water. The zinc-rich primer prepared by adding the styrene-acrylic emulsion in the raw materials after the styrene-acrylic emulsion is modified through the water-based epoxy resin emulsion, compositing the styrene-acrylic emulsion and a potassium silicate solution to be used as a binding agent, using the scale zinc powder modified by doped silence and rare earth together as pigment and combining other valid auxiliaries has the beneficial effects of being antimicrobial, resistant to corrosion, resistant to water, and the like and is suitable for steel long-acting corrosion-resistant coating projects, and the corrosion prevention service life can reach 50 years.
Description
Technical field
The present invention relates to zinc-rich paint technical field, more particularly to a kind of surface treatment of long acting antibiotic formed steel construction is with aqueous
Potassium silicate zinc rich primer and preparation method thereof.
Background technology
Zinc rich primer is a class anticorrosive paint product of the zinc powder to act on sacrificial anode as main rust resisting pigment,
There is cathodic protection to act on steel substrate, steamer, offshore production platform, container, harbour, lock are widely used in for a long time
The protection of door, storage tank, pipeline and bridge etc..It is at present conventional mainly have epoxy zinc rich primer, alcohol-soluble zinc-rich coating and
Waterborne inorganic einc-rich primer.
Waterborne inorganic einc-rich primer be with water as solvent, silicate(Including potassium silicate, sodium metasilicate, lithium metasilicate etc.)For film forming
Base fluid(Binder), zinc powder for pigment anticorrosive paint.Zinc powder generates cancellated zinc silicate with silicate reaction, while
Also zinc silicate iron complex is defined in metal surface with iron and steel reaction, thus form the stronger chemistry of bond energy in steel surface and inhale
It is attached.And cohesive force of the adhesive force of epoxy zinc rich primer from resin to steel surface, belong to physical absorption.Inorganic matter is more organic
Thing conducts electricity very well, therefore the cathodic protection effect of zinc powder is relatively strong, and the corrosion resistance of waterborne inorganic einc-rich primer far superior to has
Machine zinc-rich coating, but equally also there is the common fault of inorganic coating, such as film is more crisp easy to crack, and adhesive force is not strong, and decorative effect is not
It is good etc., and pliability is preferable after organic material film forming, therefore some water-soluble breasts can be added in waterborne inorganic einc-rich primer
Liquid makes organic matter be filled in improve the pliability of coating in "-Si-O-Si-" network structure as auxiliary film forming matter, than
Such as document《Study on the modification of the styrene-acrylic emulsion to zinc-rich coating》Just it is prepared for a kind of styrene-acrylic emulsion as modifying agent with styrene-acrylic emulsion to change
The aqueous inorganic zinc-enriched coating of property.
But only have been introduced to styrene-acrylic emulsion addition and to the pliability of coating in document, with production technology and
That what is filled a prescription continues to optimize, discovery flake zinc powder advantage in terms of covering power, floating capacity and screening ability compared with spherical zinc powder
It is prominent, thus flake zinc powder is increasingly becoming zinc-rich paint first-selection filler, but it is living in aqueous inorganic silicate alkalescence coating
The too strong, resistance to settling of property is poor, easy reunion, causes that coating failure is too fast, surface irregularity, and coating is limited to a certain extent
Using.The aqueous inorganic zinc-rich anti-corrosion bottom of Multifunction of the problems such as therefore research can overcome zinc powder free settling, bad dispersibility
Paint formula is the problem of urgent need to resolve at this stage.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of long acting antibiotic formed steel construction surface treatment
With aqueous silicic acid potassium zinc rich primer and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of long acting antibiotic formed steel construction surface treatment aqueous silicic acid potassium zinc rich primer, is prepared by the raw materials in:
Scale zinc powder 100-102, potassium silicate 15-17, aqueous epoxy resin emulsion 1-2, styrene-acrylic emulsion 6-8, MTMS
3-5, ytterbium chloride 1.2-1.4, viscose rayon 4-6, SWNT 2.1-2.3, feldspar in powder 10-11, polyvinyl alcohol 6-8,
Shitosan 5-7, ferrocene 0.4-0.7, deionized water 21-23.
The preparation method that aqueous silicic acid potassium zinc rich primer is used in a kind of described long acting antibiotic formed steel construction surface treatment, including
Following steps:
(1)Aqueous epoxy resin emulsion is slowly added dropwise toward styrene-acrylic emulsion, 70-80 DEG C is warming up to, isothermal reaction 20-30 minutes,
50-60 DEG C is cooled to, SWNT ultrasonically treated 25-30 minutes are added, adds ferrocene to continue ultrasonically treated 10-15 point
Clock, obtains modifying cinepazid emulsion;
(2)By deionized water water and absolute ethyl alcohol with the mixing of volume ratio 1: 4, MTMS, ytterbium chloride is added to adjust
Section pH is 4.5 or so, is stirred vigorously at 25-30 DEG C 1 hour, and the constant constant temperature of keeping temperature hydrolyzes 24 hours to obtain modification liquid;
(3)By after scale zinc powder oil removing drying and processing with step(2)Modification liquid mixes, agitation grinding 30 minutes, Jing centrifugations, ethanol
Wash, filter, drying the scale zinc powder that must be modified;
(4)By feldspar in powder at 810-900 DEG C high-temperature calcination 20-30 minutes, be cooled to room temperature add viscose rayon, shitosan
Grinding 1-2 hours;
(5)By potassium silicate solution and step(1)Modifying cinepazid emulsion stirs 30-40 minutes, adds step(3)Modified scale zinc
Powder, step(4)Material and other residual components stir and evenly mix discharging.
It is an advantage of the invention that:The present invention will be added to raw material after styrene-acrylic emulsion aqueous epoxy resin emulsion modification
Neutralization potassium silicate solution is combined, and prevents potassium silicate that shrinkage stress is produced during drying and forming-film, it is to avoid fine fisssure occurs in film
Line, improves the pliability of coating;The rare earth doped jointly modified scale zinc powder of silane of the invention, can form silane on zinc powder surface
Film and rare earth metal oxide-film, enhance repulsion between zinc powder with it is sterically hindered, increase the relative contact angle of zinc powder so that
Zinc powder is difficult to be wetted, and improves dispersiveness of the zinc powder in emulsion, meanwhile, the silane film on zinc powder surface has to zinc powder itself
Have certain protective effect so that the more long time can be continued when zinc powder makees in the coating cathodic protection, and rare earth plus
Enter the crosslinking degree that can promote between emulsion so that the compactness of coating is further enhanced so as to improve the corrosion resistant of coating
Corrosion, then compatibility other zinc rich primers obtained in effective auxiliary agent have the advantages that antibacterial is lasting, corrosion-resistant, waterproof, it is adaptable to steel
Iron long life anti corrosion coating project, the anticorrosion time limit was up to 50 years.
Specific embodiment
A kind of long acting antibiotic formed steel construction surface treatment aqueous silicic acid potassium zinc rich primer, by the raw material system of following weight portion
Into:Scale zinc powder 100, potassium silicate 15, aqueous epoxy resin emulsion 1, styrene-acrylic emulsion 6, MTMS 3, ytterbium chloride
1.2nd, viscose rayon 4, SWNT 2.1, feldspar in powder 10, polyvinyl alcohol 6, shitosan 5, ferrocene 0.4, deionized water
21。
The preparation method that aqueous silicic acid potassium zinc rich primer is used in a kind of described long acting antibiotic formed steel construction surface treatment, including
Following steps:
(1)Aqueous epoxy resin emulsion is slowly added dropwise toward styrene-acrylic emulsion, 70-80 DEG C is warming up to, isothermal reaction 20-30 minutes,
50-60 DEG C is cooled to, SWNT ultrasonically treated 25-30 minutes are added, adds ferrocene to continue ultrasonically treated 10-15 point
Clock, obtains modifying cinepazid emulsion;
(2)By deionized water water and absolute ethyl alcohol with the mixing of volume ratio 1: 4, MTMS, ytterbium chloride is added to adjust
Section pH is 4.5 or so, is stirred vigorously at 25-30 DEG C 1 hour, and the constant constant temperature of keeping temperature hydrolyzes 24 hours to obtain modification liquid;
(3)By after scale zinc powder oil removing drying and processing with step(2)Modification liquid mixes, agitation grinding 30 minutes, Jing centrifugations, ethanol
Wash, filter, drying the scale zinc powder that must be modified;
(4)By feldspar in powder at 810-900 DEG C high-temperature calcination 20-30 minutes, be cooled to room temperature add viscose rayon, shitosan
Grinding 1-2 hours;
(5)By potassium silicate solution and step(1)Modifying cinepazid emulsion stirs 30-40 minutes, adds step(3)Modified scale zinc
Powder, step(4)Material and other residual components stir and evenly mix discharging.
Steel structure surface is coated on using aqueous silicic acid potassium zinc rich primer obtained in the present invention, surface drying time shortens 22%,
The time of doing solid work shortens 9.1%, and adhesive force improves 1 grade, and resistance to impact also increases with pencil hardness.
Claims (2)
1. a kind of long acting antibiotic formed steel construction is surface-treated and uses aqueous silicic acid potassium zinc rich primer, it is characterised in that by following weight
The raw material of part is made:Scale zinc powder 100-102, potassium silicate 15-17, aqueous epoxy resin emulsion 1-2, styrene-acrylic emulsion 6-8, methyl
Trimethoxy silane 3-5, ytterbium chloride 1.2-1.4, viscose rayon 4-6, SWNT 2.1-2.3, feldspar in powder 10-11,
Polyvinyl alcohol 6-8, shitosan 5-7, ferrocene 0.4-0.7, deionized water 21-23.
2. a kind of long acting antibiotic formed steel construction according to claim 1 is surface-treated with the system of aqueous silicic acid potassium zinc rich primer
Make method, it is characterised in that comprise the following steps:
(1)Aqueous epoxy resin emulsion is slowly added dropwise toward styrene-acrylic emulsion, 70-80 DEG C is warming up to, isothermal reaction 20-30 minutes,
50-60 DEG C is cooled to, SWNT ultrasonically treated 25-30 minutes are added, adds ferrocene to continue ultrasonically treated 10-15 point
Clock, obtains modifying cinepazid emulsion;
(2)By deionized water water and absolute ethyl alcohol with the mixing of volume ratio 1: 4, MTMS, ytterbium chloride is added to adjust
Section pH is 4.5 or so, is stirred vigorously at 25-30 DEG C 1 hour, and the constant constant temperature of keeping temperature hydrolyzes 24 hours to obtain modification liquid;
(3)By after scale zinc powder oil removing drying and processing with step(2)Modification liquid mixes, agitation grinding 30 minutes, Jing centrifugations, ethanol
Wash, filter, drying the scale zinc powder that must be modified;
(4)By feldspar in powder at 810-900 DEG C high-temperature calcination 20-30 minutes, be cooled to room temperature add viscose rayon, shitosan
Grinding 1-2 hours;
(5)By potassium silicate solution and step(1)Modifying cinepazid emulsion stirs 30-40 minutes, adds step(3)Modified scale zinc
Powder, step(4)Material and other residual components stir and evenly mix discharging.