CN106589984A - Rubber powder used for preventing tire from puncturing - Google Patents
Rubber powder used for preventing tire from puncturing Download PDFInfo
- Publication number
- CN106589984A CN106589984A CN201611193676.2A CN201611193676A CN106589984A CN 106589984 A CN106589984 A CN 106589984A CN 201611193676 A CN201611193676 A CN 201611193676A CN 106589984 A CN106589984 A CN 106589984A
- Authority
- CN
- China
- Prior art keywords
- rubber powder
- rubber
- tire
- punctured
- tire according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses rubber powder used for preventing a tire from puncturing, and belongs to the technical field of rubber powder. The problem in the prior art that the rubber powder in the recycled tire is utilized to prepare a new rubber material and the prepared rubber material is poor in toughness, service life and puncture prevention and is not tied to the material inside the tire is solved. The rubber powder used for preventing the tire from puncturing is prepared from, by mass, 5% of natural rubber, 25% of thermoplastic elastomer, 40% of tackifier, 9% of plasticizer, 1% of antioxidant, 2% of a cross-linking agent, 2.5 % of a catalyst and 15.5% of reclaimed rubber and the rubber powder. The rubber powder used for preventing the tire from puncturing is used for preparing the tire.
Description
Technical field
A kind of tire is punctured uses rubber powder, for making tire, belongs to rubber powder technical field.
Background technology
Since the seventies, industrially developed country has a great development in terms of the secondary utilization of waste old.Especially
Since it is the nineties, room temperature has been worked out in succession and cryogenic crushing process manufactures the method for fine vulcanized rubber powder and forms scale
Production.Fine glue powder (80--120 mesh) is a kind of important additive.For example, fine glue powder is added to (one in natural rubber
As rubber incorporation up to 50%), the dynamic properties such as the static properties of rubber powder, endurance can be improved.In Germany, tire
20% rubber powder is added in product, its wearability can be improved, extend the service life of tire, rubber powder is thinner, and the amplitude of raising is got over
Greatly.The price of rubber powder only has the 1/3 1 1/2 of natural rubber, thus can greatly reduce tire cost.Fine glue powder can also add
In being added to plastics, the rubber-plastics material produced, intensity is high, wear-resisting, elasticity range of application that is good, expanding plastics.In tradition
Construction material in add fine glue powder, shockproof, anticracking, leakproof, durable new product building materials can be produced.
By 2010, Chinese junked tire burden up to 200,000,000, and will make us surprised speed with about 65,000,000 every year
Increase, and at present recovery utilization rate only has 30%.China is a rubber applications big country, and the Year's consumption of rubber ranks first in the world
Position;At the same time, China is again the serious deficient country of a rubber sources, and the 60% of Year's consumption needs import, and short
The method of basic solution is not had in time.Damaged tire is a kind of regenerated resources, is in field of new " treasured ", waste and old wheel
Tire process must well, dig a gold mine not to the utmost.Especially in the case where China rubber sources is in short supply, waste rubber goodses
Regeneration has more positive meaning.
Chinese tire recycles industry and obtains the development advanced by leaps and bounds, and has successfully established tire and recycle greatly
The status of state, Chinese rubber powder yield reaches 300,000 tons within 2006, and 50% is increased than last year.
Compared with the tire yield of rapid growth, although the reclaimed rubber and rubber powder of China supplement a part of rubber money
Source, but China remains for many years the big natural rubber importer of the first in the world, more than 70% natural rubber dependence on import, rubber
Industrial Security or even national security receive serious challenge.Therefore, China moves towards wheel in the urgent need to recycling big country from tire
Foetal circulation is using power.
And be all to prepare rubber powder again in order to ensure the quality of rubber powder in prior art, this is just unfavorable for reclaiming in tire
Rubber powder recycling, so as to cause the waste of resource, although in prior art also someone will reclaim tire in rubber powder
Using preparing new sizing material again, the toughness of the sizing material prepared, service life, the material in anti-tie effect on driving birds is not good and tire
The problems such as matter is not fitted.
The content of the invention
The present invention is punctured for above-mentioned weak point there is provided a kind of tire uses rubber powder, solves to be reclaimed in prior art
Rubber powder in tire using preparing new sizing material again, the toughness of the sizing material prepared, service life, anti-tie effect on driving birds is not good,
The problems such as not fitting with the material in tire.
To achieve these goals, the technical solution used in the present invention is as follows:
A kind of tire is punctured uses rubber powder, it is characterised in that:Including natural rubber, thermoplastic elastomer (TPE), viscosifier, plasticising
Agent, antioxidant, cross-linking agent, catalyst, reclaimed rubber and rubber powder;
Wherein mass ratio is:5%, thermoplastic elastomer (TPE) being accounted for including natural rubber and accounting for 25%, viscosifier account for 40%, plasticizer
Account for 9%, antioxidant and account for 1%, cross-linking agent and account for that 2%, catalyst accounts for 2.5%, reclaimed rubber and rubber powder accounts for 15.5%.
Further, the main component of the natural rubber is the natural polymer of cis- Isosorbide-5-Nitrae-polyisoprene.
Further, the composition of the cis- Isosorbide-5-Nitrae-polyisoprene is 91%~94%, protein, fatty acid, ash, sugar
The composition of class is 9%~6%.
Further, the thermoplastic elastomer (TPE) is lactoprene or synthetic rubber.
Further, the viscosifier are modified rosin resin.
Further, the plasticizer is citric acid ester type, epoxy soybean oil plasticiser.
Further, the antioxidant is BHA, BHT or PG.
Further, the cross-linking agent is cross-linking radiation.
In sum, as a result of above-mentioned technical proposal, the invention has the beneficial effects as follows:
First, the present invention is again proportionally added into ground rubber, and freshly prepared other component ratios of laying equal stress on not only can allow
The rubber powder of recovery is reused, and can also allow the rubber powder for remaking identical in quality with the rubber powder that new material makes, by present invention system
The rubber powder of work is coated in the internal layer of tire by fusing, and can play prevents inner tire layer to be punctured, and causes gas leakage or tyre break,
The problem of security incident is caused, the material toxicity of employing is few, can play environmental protection, can protect that staff's is healthy;
2nd, the present invention uses viscosifier, for reducing viscosity, raising when thermoplastic elastomer (TPE) is heated by viscosity, bonding
Intensity, the heat resisting temperature for adjusting hot-melt adhesive powder and open assembly time, improve operability and reduces cost;
3rd, the present invention have selected plasticizer, for increase for automobile tire macromolecule rubber powder ductility (and flowing
Property), reduce hardness, improve elongation at break and its is low temperature resistant, the macromolecule rubber powder for being used in automobile tire adapts to vehicle tyre
Run up in low temperature without departing from and pierced through by sharp object and steel nail or can be self-styled after bullet punctures;
4th, the cross-linking agent that uses of the present invention has and increases the glue-line that hot melting spraying formed and have resistance to elevated temperatures and persistently
Property.
Specific embodiment
In order that the objects, technical solutions and advantages of the present invention become more apparent, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that specific embodiment described herein is not used to limit only to explain the present invention
The fixed present invention.
A kind of tire is punctured uses rubber powder, it is characterised in that:Including natural rubber, thermoplastic elastomer (TPE), viscosifier, plasticising
Agent, antioxidant, cross-linking agent, catalyst, reclaimed rubber and rubber powder;Wherein mass ratio is:5%, thermoplasticity is accounted for including natural rubber
Elastomer accounts for 25%, viscosifier and accounts for 40%, plasticizer and account for 9%, antioxidant and account for 1%, cross-linking agent and account for 2%, catalyst and accounts for
2.5%th, reclaimed rubber and rubber powder account for 15.5%.The main component of the natural rubber is the natural height of cis- Isosorbide-5-Nitrae-polyisoprene
Molecular compound.The composition of the cis- Isosorbide-5-Nitrae-polyisoprene is 91%~94%, protein, fatty acid, ash, saccharide
Composition is 9%~6%.The thermoplastic elastomer (TPE) is lactoprene or synthetic rubber.The viscosifier are modified rosin resin.
The plasticizer is citric acid ester type, epoxy soybean oil plasticiser.The antioxidant is BHA, BHT or PG.The cross-linking agent
For cross-linking radiation;Foaming agent is carbon black.The present invention is again proportionally added into ground rubber, freshly prepared other composition ratios of laying equal stress on
Example, not only can allow the rubber powder of recovery to be reused, and can also allow the rubber powder quality phase that the rubber powder for remaking makes with new material
Together, the rubber powder for the present invention being made is coated in the internal layer of tire by fusing, and can play prevents inner tire layer to be punctured, and causes Lou
Gas or tyre break, cause the problem of security incident, and the material toxicity of employing is few, can play environmental protection, can protect staff's
It is healthy.
Embodiment 1
A kind of tire is punctured uses rubber powder, including natural polymer 50g, lactoprene 250g, modified rosin tree
Fat 400g, citric acid ester type 90g, BHA 10g, cross-linking radiation 20g, catalyst 25g, reclaimed rubber and rubber powder 155g.
Embodiment 2
A kind of tire is punctured uses rubber powder, including natural polymer 50g, synthetic rubber 250g, modified rosin tree
Fat 400g, epoxy soybean oil plasticiser 90g, BHT 10g, cross-linking radiation 20g, catalyst 25g, reclaimed rubber and rubber powder 155g.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all essences in the present invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (8)
1. a kind of tire is punctured and is used rubber powder, it is characterised in that:Including natural rubber, thermoplastic elastomer (TPE), viscosifier, plasticising
Agent, antioxidant, cross-linking agent, catalyst, reclaimed rubber and rubber powder;
Wherein mass ratio is:5%, thermoplastic elastomer (TPE) being accounted for including natural rubber and accounting for 25%, viscosifier and account for 40%, plasticizer account for
9%th, antioxidant accounts for 1%, cross-linking agent and accounts for that 2%, catalyst accounts for 2.5%, reclaimed rubber and rubber powder accounts for 15.5%.
2. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The natural rubber it is main into
It is divided into the natural polymer of cis- Isosorbide-5-Nitrae-polyisoprene.
3. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The cis- Isosorbide-5-Nitrae-poly- isoamyl two
The composition of alkene is 91%~94%, and protein, fatty acid, ash, the composition of saccharide are 9%~6%.
4. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The thermoplastic elastomer (TPE) is behaved
Make rubber or synthetic rubber.
5. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The viscosifier are modified rosin
Resin.
6. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The plasticizer is citrate
Class, epoxy soybean oil plasticiser.
7. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The antioxidant be BHA,
BHT or PG.
8. a kind of tire according to claim 1 is punctured and is used rubber powder, it is characterised in that:The cross-linking agent is irradiation friendship
Connection.