CN106587951A - High-strength purple clay material - Google Patents
High-strength purple clay material Download PDFInfo
- Publication number
- CN106587951A CN106587951A CN201611158308.4A CN201611158308A CN106587951A CN 106587951 A CN106587951 A CN 106587951A CN 201611158308 A CN201611158308 A CN 201611158308A CN 106587951 A CN106587951 A CN 106587951A
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- strength
- purple clay
- high intensity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength purple clay material which comprises the following components in parts by weight: 30-40 parts of alumina, 10-20 parts of strontia, 10-15 parts of bentonite, 5-10 parts of silicon carbide and 5-10 parts of mica powder. Compared with the traditional technology, the high-strength purple clay material disclosed by the invention is compounded by utilizing the various components and has high strength compared with that of general purple clay materials.
Description
Technical field
The invention belongs to electrothermal dark-red pottery field, and in particular to a kind of high intensity boccaro material.
Background technology
The origin cause of formation of violet sand earthenware clay, category inland lake and strand liminetic facies sedimentary deposit, by external force sedimentary mineralization, it is buried in
Among middle of a mountain.Purple mud and green mud are all originated in Jia Nikuang.First mud is a kind of ridge clay, aubergine, color chalybeate first, therefore named first
Mud.In first mud ore deposit, at most, purple mud, green mud reserves are less, and purple mud only accounts for the 3-4% of gross reserves for first mud reserves.During purple mud is first mud
One interlayer, green mud is the interlayer in purple interburden layer, therefore has the title of " mud, Yan Zhongyan in mud ".So, the pug of boccaro, also only
Have and could obtain under conditions of a large amount of produces days pottery.Because this depth is hidden under rock stratum among " the first mud " of hundreds of meters depths
Purple mud, it is necessary to sort out from first mud, use in a large number the first mud, purple mud of no daily pottery also just have no way of obtaining.Therefore, such as
It is the problem for being worth research that what is re-dubbed using boccaro material and is suitable for various conditions.
The content of the invention
Goal of the invention:Present invention aims to the deficiencies in the prior art, there is provided a kind of high intensity boccaro material.
Technical scheme:In order to reach foregoing invention purpose, the present invention is specifically achieved like this:A kind of high intensity boccaro
Material, including the component of following parts by weight:30 ~ 40 parts of aluminium oxidies, 10 ~ 20 parts of strontium oxide, 10 ~ 15 parts of bentonite, 5 ~ 10 parts of carbon
SiClx, 5 ~ 10 parts of mica powders.
Wherein, the fineness of each raw material is less than 200 mesh.
A kind of preferred version, is made up of the component of following parts by weight:30 parts of aluminium oxidies, 20 parts of strontium oxide, 10 parts of swellings
Soil, 5 parts of carborundums, 10 parts of mica powders.
Beneficial effect:The present invention is compounded using each component compared with conventional art, and the more general boccaro material of intensity is more
It is high.
Specific embodiment
Embodiment 1:
A kind of high intensity boccaro material, is made up of the component of following parts by weight:30 parts of aluminium oxidies, 10 parts of strontium oxide, 10 parts of swellings
Soil, 5 parts of carborundums, 5 parts of mica powders.
Embodiment 2:
A kind of high intensity boccaro material, is made up of the component of following parts by weight:40 parts of aluminium oxidies, 20 parts of strontium oxide, 15 parts of swellings
Soil, 10 parts of carborundums, 10 parts of mica powders.
Embodiment 3:
A kind of high intensity boccaro material, is made up of the component of following parts by weight:35 parts of aluminium oxidies, 15 parts of strontium oxide, 11 parts of swellings
Soil, 6 parts of carborundums, 6 parts of mica powders.
Embodiment 4:
A kind of high intensity boccaro material, is made up of the component of following parts by weight:38 parts of aluminium oxidies, 16 parts of strontium oxide, 14 parts of swellings
Soil, 9 parts of carborundums, 8 parts of mica powders.
Claims (3)
1. a kind of high intensity boccaro material, it is characterised in that including the component of following parts by weight:30 ~ 40 parts of aluminium oxidies, 10 ~ 20
Part strontium oxide, 10 ~ 15 parts of bentonite, 5 ~ 10 parts of carborundums, 5 ~ 10 parts of mica powders.
2. high intensity boccaro material according to claim 1, it is characterised in that the fineness of each raw material is less than 200 mesh.
3. high intensity boccaro material according to claim 1, it is characterised in that be made up of the component of following parts by weight:30
Part aluminium oxide, 20 parts of strontium oxide, 10 parts of bentonite, 5 parts of carborundums, 10 parts of mica powders.