CN106587810A - Composite foam cement insulation board - Google Patents
Composite foam cement insulation board Download PDFInfo
- Publication number
- CN106587810A CN106587810A CN201611083876.2A CN201611083876A CN106587810A CN 106587810 A CN106587810 A CN 106587810A CN 201611083876 A CN201611083876 A CN 201611083876A CN 106587810 A CN106587810 A CN 106587810A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation board
- sulfate
- cement
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a composite foam cement insulation board. The cement insulation board is made from, by mass, 130-140 parts of Portland cement, 10-15 parts of fly ash, 3-5 parts of expanded perlite, 0.5-0.8 part of pottery clay, 0.3-0.5 part of gypsum powder, 0.1-0.3 part of quartz sand, 2-3 parts of sodium dodecyl sulfate, 0.4-0.6 part of sodium metasilicate, 0.2-0.4 part of calcium sulfate, 0.5-0.8 part of sodium chloride, 2-3 parts of aluminum sulfate, 0.3-0.5 part of a foaming agent, 0.4-0.6 part of a foam stabilizer, 2.5-3.5 parts of a water repellent and 125-130 parts of water. The composite foam cement insulation board is applied to outer-wall external thermal insulation system construction work of house buildings and has the good thermal insulation property; meanwhile, the raw material source is wide, and the preparation method is simple.
Description
Technical field
The present invention relates to a kind of composite foamed cement insulation board.
Background technology
Cement insulation board is the closed pore light-weight inorganic foaming insulations made by technique such as a kind of foamed, maintenance, cutting
Plate, can be used for the construction of exterior wall external heat-preservation system engineering of building construction, and the styrofoam or extruded sheet that replacement was originally commonly used is
The combustable organic insulation material of representative.
The content of the invention
The invention provides a kind of composite foamed cement insulation board, with good heat-insulating property.
The present invention provides a kind of composite foamed cement insulation board, each component of the cement heat preserving plate by following mass fraction
Composition：Portland cement 130-140 parts, flyash 10-15 parts, expanded perlite 3-5 parts, potter's clay 0.5-0.8 parts, Gypsum Fibrosum powder
0.3-0.5 parts, quartz sand 0.1-0.3 parts, dodecyl sodium sulfate 2-3 parts, sodium metasilicate 0.4-0.6 parts, calcium sulfate 0.2-0.4
Part, Sodium Chloride 0.5-0.8 part, aluminum sulfate 2-3 parts, foaming agent 0.3-0.5 parts, foam stabilizer 0.4-0.6 parts, hydrophober 2.5-3.5
Part, water 125-130 parts.
Preferably, the cement heat preserving plate is grouped into by each group of following mass fraction：135 parts of portland cement, powder
12 parts of coal ash, 4 parts of expanded perlite, 0.6 part of potter's clay, 0.4 part of Gypsum Fibrosum powder, 0.2 part of quartz sand, 2.5 parts of dodecyl sodium sulfate,
0.5 part of sodium metasilicate, 0.3 part of calcium sulfate, 0.6 part of Sodium Chloride, 2.5 parts of aluminum sulfate, 0.4 part of foaming agent, 0.5 part of foam stabilizer, hate
3 parts of water preparation, 128 parts of water.
Foaming agent, foam stabilizer and hydrophober are from market to be buied.The foaming agent of arbitrary brand, foam stabilizer and hydrophober are equal
The effect of the present invention can be realized.
The present invention also provides the preparation method of above-mentioned composite foamed cement insulation board, is standby by the weight ratio of above-mentioned each component
Material, is initially charged portland cement, flyash, expanded perlite, potter's clay, Gypsum Fibrosum powder, quartz sand, dodecane in fine material mixer
Base sodium sulfonate, sodium metasilicate, calcium sulfate, Sodium Chloride, aluminum sulfate and water are sufficiently stirred for slurrying, add foaming agent, foam stabilizer and
Hydrophober is thoroughly mixed, and injects mould, not in addition any pressure, quiet to stop paying out bubble, at normal temperatures, after 24 hours, the demoulding, then
Natural curing 28 hours, you can.
The composite foamed cement insulation board of the present invention is used for the construction of exterior wall external heat-preservation system engineering of building construction, with good
Good heat-insulating property；Extensively, preparation method is simple for raw material sources simultaneously.
Specific embodiment
Below example facilitates a better understanding of the present invention, but does not limit the present invention.Experiment in following embodiments
Method, if no special instructions, is conventional method.In following embodiments, test material used, if no special instructions, is city
Sell.
Embodiment 1
The composite foamed cement insulation board of the present invention is grouped into by each group of following mass fraction：
135 parts of portland cement, 12 parts of flyash, 4 parts of expanded perlite, 0.6 part of potter's clay, 0.4 part of Gypsum Fibrosum powder, quartz sand 0.2
Part, 2.5 parts of dodecyl sodium sulfate, 0.5 part of sodium metasilicate, 0.3 part of calcium sulfate, 0.6 part of Sodium Chloride, 2.5 parts of aluminum sulfate, foaming
0.4 part of agent, 0.5 part of foam stabilizer, 3 parts of hydrophober, 128 parts of water.
The preparation method of composite foamed cement insulation board of the present invention is：
Get the raw materials ready by the weight ratio of above-mentioned each component, portland cement, flyash, expanded pearlite are initially charged in fine material mixer
Rock, potter's clay, Gypsum Fibrosum powder, quartz sand, dodecyl sodium sulfate, sodium metasilicate, calcium sulfate, Sodium Chloride, aluminum sulfate and water are fully stirred
Mixing is starched, and is added foaming agent, foam stabilizer and hydrophober and is thoroughly mixed, and injects mould, not in addition any pressure, quiet to stop paying out
Bubble, at normal temperatures, after 24 hours, the demoulding, then natural curing 28 hours, you can.
Embodiment 2
The composite foamed cement insulation board of the present invention is grouped into by each group of following mass fraction：
130 parts of portland cement, 15 parts of flyash, 3 parts of expanded perlite, 0.8 part of potter's clay, 0.3 part of Gypsum Fibrosum powder, quartz sand 0.3
Part, 2 parts of dodecyl sodium sulfate, 0.6 part of sodium metasilicate, 0.4 part of calcium sulfate, 0.5 part of Sodium Chloride, 3 parts of aluminum sulfate, foaming agent
0.3 part, 0.6 part of foam stabilizer, 2.5 parts of hydrophober, 130 parts of water.
The preparation method of the composite foamed cement insulation board of the present embodiment is same as Example 1.
Embodiment 3
The composite foamed cement insulation board of the present invention is grouped into by each group of following mass fraction：
140 parts of portland cement, 10 parts of flyash, 5 parts of expanded perlite, 0.5 part of potter's clay, 0.5 part of Gypsum Fibrosum powder, quartz sand 0.1
Part, 3 parts of dodecyl sodium sulfate, 0.4 part of sodium metasilicate, 0.2 part of calcium sulfate, 0.8 part of Sodium Chloride, 2 parts of aluminum sulfate, foaming agent
0.5 part, 0.4 part of foam stabilizer, 3.5 parts of hydrophober, 125 parts of water.
The preparation method of the composite foamed cement insulation board of the present embodiment is same as Example 1.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, the present invention is not limited to,
Although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, which still may be used
To modify to the technical scheme described in foregoing embodiments, or equivalent is carried out to which part technical characteristic.
All any modification, equivalent substitution and improvements within the spirit and principles in the present invention, made etc., should be included in the present invention's
Within protection domain.
Claims (3)
1. a kind of composite foamed cement insulation board, it is characterised in that：Each component of the cement heat preserving plate by following mass fraction
Composition：Portland cement 130-140 parts, flyash 10-15 parts, expanded perlite 3-5 parts, potter's clay 0.5-0.8 parts, Gypsum Fibrosum powder
0.3-0.5 parts, quartz sand 0.1-0.3 parts, dodecyl sodium sulfate 2-3 parts, sodium metasilicate 0.4-0.6 parts, calcium sulfate 0.2-0.4
Part, Sodium Chloride 0.5-0.8 part, aluminum sulfate 2-3 parts, foaming agent 0.3-0.5 parts, foam stabilizer 0.4-0.6 parts, hydrophober 2.5-3.5
Part, water 125-130 parts.
2. composite foamed cement insulation board according to claim 1, it is characterised in that：The cement heat preserving plate is by following matter
The each group of amount number is grouped into：135 parts of portland cement, 12 parts of flyash, 4 parts of expanded perlite, 0.6 part of potter's clay, Gypsum Fibrosum powder
0.4 part, 0.2 part of quartz sand, 2.5 parts of dodecyl sodium sulfate, 0.5 part of sodium metasilicate, 0.3 part of calcium sulfate, 0.6 part of Sodium Chloride,
2.5 parts of aluminum sulfate, 0.4 part of foaming agent, 0.5 part of foam stabilizer, 3 parts of hydrophober, 128 parts of water.
3. the preparation method of the composite foamed cement insulation board described in claim 1 or 2, it is characterised in that：It is by above-mentioned each group
Point weight ratio get the raw materials ready, be initially charged portland cement, flyash, expanded perlite in fine material mixer, potter's clay, Gypsum Fibrosum powder,
Quartz sand, dodecyl sodium sulfate, sodium metasilicate, calcium sulfate, Sodium Chloride, aluminum sulfate and water are sufficiently stirred for slurrying, add and send out
Infusion, foam stabilizer and hydrophober are thoroughly mixed, and inject mould, not in addition any pressure, quiet to stop paying out bubble, at normal temperatures, 24
After hour, the demoulding, then natural curing 28 hours, you can.