CN106566349A - Low-temperature damping paint - Google Patents
Low-temperature damping paint Download PDFInfo
- Publication number
- CN106566349A CN106566349A CN201610994146.1A CN201610994146A CN106566349A CN 106566349 A CN106566349 A CN 106566349A CN 201610994146 A CN201610994146 A CN 201610994146A CN 106566349 A CN106566349 A CN 106566349A
- Authority
- CN
- China
- Prior art keywords
- parts
- damping paint
- low temperature
- temperature damping
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides low-temperature damping paint. The low-temperature damping paint comprises the following raw materials, by weight, 95-105 parts of a waterproof acrylic emulsion, 290-310 parts of a pure acrylic emulsion, 90-110 parts of a functional filler, 70-80 parts of a fire retardant, 45-55 parts of an anticorrosive filler, 4-6 parts of pigments and 1.5-2.5 parts of a binder. The damping paint solves the low-temperature self-drying and fast film formation problem and has excellent performances such as acid and alkali resistance and salt fog resistance.
Description
Technical field
The invention belongs to damping paint technical field, and in particular to a kind of low temperature damping paint from dry film forming.
Background technology
High molecular polymer damping material is a kind of functional material for being vibrated as substrate inhibition with polymer and reducing noise,
This new vibration and noise reducing damping material, in the every field such as vehicles such as aircraft, automobile, rolling stock and steamer and
Engineering machinery, is widely used on precision instrument and equipment.Damping paint can be divided into solvent-borne type damping according to decentralized medium
Coating and aqueous damping coating.The early stage damping paint of application is solvent-borne type damping paint, mainly there is coal tar-pitch resistance
Damping paint, solvent borne polyurethane damping paint etc..With the requirement and the raising of people's environmental consciousness of national industrial policies, contain
The solvent-borne type damping paint of a large amount of organic solvents is gradually replaced by the aqueous damping coating of safety and environmental protection.
However, the drying that the aqueous damping coating of domestic production at present is mostly drying-type, i.e. paint film needs high temperature to dry
It is roasting, ability film-forming, this brings certain restriction to construction.
The content of the invention
The present invention proposes a kind of low temperature damping paint, and the damping paint solves the problems, such as low temperature from dry fast filming, and has
There are the performances such as excellent acid and alkali-resistance and salt spray resistance.
The technical scheme is that what is be achieved in that：
A kind of low temperature damping paint, calculates by weight, including following raw material：
95～105 parts of polyacrylic water-proof emulsion, 290～310 parts of pure-acrylic emulsion, 90～110 parts of functional stuffing, fire retardant 70
1.5～2.5 parts of～80 parts, 45～55 parts of anticorrosive packing, 4～6 parts of pigment and adhesive.
Further, the pure-acrylic emulsion is BA-200 pure-acrylic emulsions, and its solid content is 30 ± 1%, and vitrification point is 6
DEG C, MFT is 0 DEG C, and viscosity is less than 20cps.The moon of BA-200 systems epoxy resin modification acrylic ester copolymer from
Sub- emulsion, due to very little particle diameter, in can penetrate matrix, enclosing concrete pore, can make outstanding back cover
Material, is widely used in timber, concrete, metal surface etc..
Further, the polyacrylic water-proof emulsion is German BASF water-proof emulsion S 400F.
Further, the functional stuffing is floating bead and talcous mixture, and wherein floating bead is each 45～55 parts with talcum powder.
Further, the one kind of the fire retardant selected from aluminium hydroxide, magnesium hydroxide, Firebrake ZB, aluminum phosphate and ammonium octamolybdate
Or any several mixture.
Further, the anticorrosive packing is that nano imvite/polyaniline composite powder or nano imvite/polypyrrole are multiple
Close powder.
Further, the pigment is black slurry.
Further, described adhesive is alkaline silica sol.
Further, also including 23～27 parts of preservative.
The preparation method of the low temperature damping paint of the present invention, comprises the following steps：
Weigh 95～105 parts of polyacrylic water-proof emulsion to mix for 290～310 parts with pure-acrylic emulsion, rotating speed is 80r/
Min, time 10min or so, are subsequently adding fire retardant and adhesive, stirring 5min or so, are subsequently adding functional filler, anti-corrosion
Filler and pigment, stirring 60min or so.
Beneficial effect of the present invention：
The solid content of low temperature damping paint of the present invention is 63% or so, and acidproof, salt spray resistance ability is good.Storage stability：Easily
Again stir evenly, 15～17mm of denseness.With good anti-stoning energy, the anti-stones of ENISO20567 are hit as 1, protect paint film；Impact
Intensity >=50kg*cm, flawless, the phenomenon such as come off.Solve the problems, such as low temperature (0 DEG C) from dry fast filming.
The main performance index of the low temperature damping paint prepared in the embodiment of the present invention is as shown in table 1：
The main performance index of the low temperature damping paint of table 1
Specific embodiment
Embodiment 1
A kind of low temperature damping paint, calculates by weight, including following raw material：
100 parts of polyacrylic water-proof emulsion, 300 parts of pure-acrylic emulsion, 25 parts of preservative, 50 parts of floating bead, 50 parts of talcum powder, boric acid
2 parts of 75 parts of zinc, nano imvite/50 parts of polyaniline composite powder, 5 parts of black slurry and alkaline silica sol.
Wherein, pure-acrylic emulsion is BA-200 pure-acrylic emulsions, and its solid content is 30 ± 1%, and vitrification point is 6 DEG C, minimum
Film-forming temperature is 0 DEG C, and viscosity is less than 20cps.The anionic emulsion of BA-200 systems epoxy resin modification acrylic ester copolymer,
Due to very little particle diameter, in can penetrate matrix, enclosing concrete pore, outstanding back cover material can be done, extensively
It is general for timber, concrete, metal surface etc..
Polyacrylic water-proof emulsion is German BASF water-proof emulsion S 400F.
Embodiment 2
A kind of low temperature damping paint, calculates by weight, including following raw material：
95 parts of polyacrylic water-proof emulsion, 310 parts of pure-acrylic emulsion, 23 parts of preservative, 45 parts of floating bead, 45 parts of talcum powder, hydrogen-oxygen
Change 1.5 parts of 70 parts of magnesium, nano imvite/45 parts of polyaniline composite powder, 4 parts of black slurry and alkaline silica sol.
Wherein, pure-acrylic emulsion is BA-200 pure-acrylic emulsions, and its solid content is 30 ± 1%, and vitrification point is 6 DEG C, minimum
Film-forming temperature is 0 DEG C, and viscosity is less than 20cps.The anionic emulsion of BA-200 systems epoxy resin modification acrylic ester copolymer,
Due to very little particle diameter, in can penetrate matrix, enclosing concrete pore, outstanding back cover material can be done, extensively
It is general for timber, concrete, metal surface etc..
Polyacrylic water-proof emulsion is German BASF water-proof emulsion S 400F.
Embodiment 3
A kind of low temperature damping paint, calculates by weight, including following raw material：
105 parts of polyacrylic water-proof emulsion, 290 parts of pure-acrylic emulsion, 27 parts of preservative, 55 parts of floating bead, 55 parts of talcum powder, hydrogen-oxygen
Change 30 parts of magnesium, 50 parts of aluminium hydroxide, nano imvite/55 parts of polypyrrole composite powder, 6 parts of black slurry and alkaline silica sol 2.5
Part.
Wherein, pure-acrylic emulsion is BA-200 pure-acrylic emulsions, and its solid content is 30 ± 1%, and vitrification point is 6 DEG C, minimum
Film-forming temperature is 0 DEG C, and viscosity is less than 20cps.The anionic emulsion of BA-200 systems epoxy resin modification acrylic ester copolymer,
Due to very little particle diameter, in can penetrate matrix, enclosing concrete pore, outstanding back cover material can be done, extensively
It is general for timber, concrete, metal surface etc..
Polyacrylic water-proof emulsion is German BASF water-proof emulsion S 400F.
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all essences in the present invention
Within god and principle, any modification, equivalent substitution and improvements made etc. should be included within the scope of the present invention.
Claims (9)
1. a kind of low temperature damping paint, it is characterised in that calculate by weight, including following raw material：
95～105 parts of polyacrylic water-proof emulsion, 290～310 parts of pure-acrylic emulsion, 90～110 parts of functional stuffing, fire retardant 70～80
1.5～2.5 parts of part, 45～55 parts of anticorrosive packing, 4～6 parts of pigment and adhesive.
2. low temperature damping paint according to claim 1, it is characterised in that the pure-acrylic emulsion is BA-200 pure third newborn
Liquid, its solid content is 30 ± 1%, and vitrification point is 6 DEG C.
3. low temperature damping paint according to claim 1 and 2, it is characterised in that the polyacrylic water-proof emulsion is Germany
The F of BASF water-proof emulsion S 400.
4. low temperature damping paint according to claim 1 and 2, it is characterised in that the functional stuffing is floating bead and talcum
The mixture of powder, wherein floating bead are each 45～55 parts with talcum powder.
5. low temperature damping paint according to claim 1 and 2, it is characterised in that the fire retardant is selected from aluminium hydroxide, hydrogen
One kind of magnesia, Firebrake ZB, aluminum phosphate and ammonium octamolybdate or arbitrarily several mixtures.
6. low temperature damping paint according to claim 1 and 2, it is characterised in that the anticorrosive packing be nano imvite/
Polyaniline composite powder or nano imvite/polypyrrole composite powder.
7. low temperature damping paint according to claim 1 and 2, it is characterised in that the pigment is black slurry.
8. low temperature damping paint according to claim 1 and 2, it is characterised in that described adhesive is alkaline silica sol.
9. low temperature damping paint according to claim 1, it is characterised in that also including 23～27 parts of preservative.