CN106544189A - A kind of bath of glass processing technology - Google Patents
A kind of bath of glass processing technology Download PDFInfo
- Publication number
- CN106544189A CN106544189A CN201610890357.0A CN201610890357A CN106544189A CN 106544189 A CN106544189 A CN 106544189A CN 201610890357 A CN201610890357 A CN 201610890357A CN 106544189 A CN106544189 A CN 106544189A
- Authority
- CN
- China
- Prior art keywords
- bath
- glass
- processing technology
- carries out
- emulsifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bath of glass processing technology, the processing technology is comprised the following steps:Prepare the deionized water of 62 mass parts;Put into ethylene glycol and be stirred;The Borax of input carries out emulsifying;Put into sodium nitrite and be stirred;Input tributyl phosphate carries out emulsifying;Input BTA carries out emulsifying;Input triethanolamine carries out emulsifying;Input sodium benzoate carries out emulsifying;Input colorant is stirred and emulsifying, that is, obtain bath of glass.Bath of glass prepared by a kind of bath of glass processing technology of the present invention is formed by kinds of surface activating agent and additive compound, surfactant generally has the functions such as moistening, infiltration, solubilising, so as to play a part of clean dirt, compared with common bath of glass, the bath of glass of the present invention has cleaning faster, the less advantage of consumption.
Description
Technical field
The present invention relates to daily chemical products production technology field, more particularly to a kind of bath of glass processing technology.
Background technology
So-called bath of glass is exactly being commonly called as windshield cleanout fluid.Belong to the easily-consumed products in automobile use.High-quality
Windshield water is mainly made up of water, ethanol, ethylene glycol, corrosion inhibiter and kinds of surface activating agent.Windshield water
It is commonly called as bath of glass (i.e. vehicle window is net).Some car owners think to clean front windshield in fact very simply, do not need to make a fuss over a trifling matter.In fact
It is wrong.There is car owner select " folk prescription "-homemade bath of glass.Liquid detergent, detergent, detergent etc. are converted little water by them
To substitute special glass water, it is believed that not only cheap but also save worry;Also the car owner having directly substitutes bath of glass with clear water.Expert points out these
Way has certain hidden danger.Detergent is converted with water:Some precipitate are had in detergent water, time length not only can be rotten
Erosion rubber tube, and can block.Replace bath of glass with water:This risk is relative
It is smaller.But need to pay attention to, common tap water equally contains more impurity, and time length, impurity can be attached to rubber
In pipe, normal water spray is affected.Life-time service increases may frictional force between glass surface and wiper, and glass is produced to be drawn
Trace.In fact, clear water can only simply clean dust, to dirty, the worm corpse that adhere on vehicle window, the not ability of thoroughly cleaning.
And the bath of glass majority of poor quality is to be converted to form with water and ethanol etc., automobile finish glossiness, rubber strip are not only damaged
Hardness, it is serious also to cause rubber parts or other working of plasticss to produce aberration, swollen molten etc..And bath of glass is cleaning glass
Afterwards, can flow near air-conditioning air inlet, the abnormal smells from the patient of bath of glass volatilization also can enter into driving along the ventilation shaft of air conditioning for automobiles
It is indoor.The gas of bath of glass volatilization inferior is harmful, can become the stealthy killer of harm car owner's health.Existing common glass
Glass water has that cleaning speed is slow, the defect that consumption is excessive.
The content of the invention
In order to overcome defect of the prior art, there is provided a kind of bath of glass processing technology.
The present invention is realized by following proposal:
A kind of bath of glass processing technology, the processing technology are comprised the following steps:
The first step:Prepare the deionized water of 62 mass parts;
Second step:The ethylene glycol of 38 mass parts is put in deionized water and is stirred;
3rd step:The Borax that 1.5 mass parts are put in the solution obtained to second step carries out emulsifying;
4th step:The solution obtained to the 3rd step puts into the sodium nitrite of 1.5 mass parts and is stirred;
5th step:The tributyl phosphate that 0.1 mass parts are put in the solution obtained to the 4th step carries out emulsifying;
6th step:The BTA that 0.1 mass parts are put in the solution obtained to the 5th step carries out emulsifying;
7th step:The triethanolamine that 1.5 mass parts are put in the solution obtained to the 6th step carries out emulsifying;
8th step:The sodium benzoate that 2.5 mass parts are put in the solution obtained to the 7th step carries out emulsifying;
9th step:The colorant that 0.01 mass parts are put in the solution obtained to the 8th step is stirred and emulsifying, that is, obtain
Bath of glass.
In second step, the persistent period of the stirring is 5-10 minutes.
In the third step, the emulsification times are 5-10 minutes.
In the 4th step, the persistent period of the stirring is 5-10 minutes.
In the 5th step, the emulsification times are 5-10 minutes.
In the 6th step, the emulsification times are 5-10 minutes.
In the 7th step, the emulsification times are 5-10 minutes.
In the 8th step, the emulsification times are 5-10 minutes.
In the 9th step, the stirring and emulsification times are 5-10 minutes.
Beneficial effects of the present invention are:
Bath of glass prepared by a kind of bath of glass processing technology of the present invention be by kinds of surface activating agent and additive compound and
Into surfactant generally has the functions such as moistening, infiltration, solubilising, so as to play a part of clean dirt, with common glass
Water is compared, and the bath of glass of the present invention has cleaning faster, the less advantage of consumption.
Specific embodiment
With reference to specific embodiment, the present invention is further described:
A kind of bath of glass processing technology, the processing technology are comprised the following steps:
The first step:Prepare the deionized water of 62 mass parts;
Second step:The ethylene glycol of 38 mass parts is put in deionized water and is stirred;
3rd step:The Borax that 1.5 mass parts are put in the solution obtained to second step carries out emulsifying;
4th step:The solution obtained to the 3rd step puts into the sodium nitrite of 1.5 mass parts and is stirred;
5th step:The tributyl phosphate that 0.1 mass parts are put in the solution obtained to the 4th step carries out emulsifying;
6th step:The BTA that 0.1 mass parts are put in the solution obtained to the 5th step carries out emulsifying;
7th step:The triethanolamine that 1.5 mass parts are put in the solution obtained to the 6th step carries out emulsifying;
8th step:The sodium benzoate that 2.5 mass parts are put in the solution obtained to the 7th step carries out emulsifying;
9th step:The colorant that 0.01 mass parts are put in the solution obtained to the 8th step is stirred and emulsifying, that is, obtain
Bath of glass.
In second step, the persistent period of the stirring is 5-10 minutes.
In the third step, the emulsification times are 5-10 minutes.
In the 4th step, the persistent period of the stirring is 5-10 minutes.
In the 5th step, the emulsification times are 5-10 minutes.
In the 6th step, the emulsification times are 5-10 minutes.
In the 7th step, the emulsification times are 5-10 minutes.
In the 8th step, the emulsification times are 5-10 minutes.
In the 9th step, the stirring and emulsification times are 5-10 minutes.
Bath of glass prepared by a kind of bath of glass processing technology of the present invention be by kinds of surface activating agent and additive compound and
Into surfactant generally has the functions such as moistening, infiltration, solubilising, so as to play a part of clean dirt, with common glass
Water is compared, and the bath of glass of the present invention has cleaning faster, the less advantage of consumption.
Although more detailed elaboration having been done to technical scheme and having been enumerated, it will be appreciated that for ability
For field technique personnel, modification or the replacement scheme using equivalent are made to above-described embodiment, this is to those skilled in the art
It is it is clear that these modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the present invention for member
Claimed scope.
Claims (9)
1. a kind of bath of glass processing technology, it is characterised in that the processing technology is comprised the following steps:
The first step:Prepare the deionized water of 62 mass parts;
Second step:The ethylene glycol of 38 mass parts is put in deionized water and is stirred;
3rd step:The Borax that 1.5 mass parts are put in the solution obtained to second step carries out emulsifying;
4th step:The solution obtained to the 3rd step puts into the sodium nitrite of 1.5 mass parts and is stirred;
5th step:The tributyl phosphate that 0.1 mass parts are put in the solution obtained to the 4th step carries out emulsifying;
6th step:The BTA that 0.1 mass parts are put in the solution obtained to the 5th step carries out emulsifying;
7th step:The triethanolamine that 1.5 mass parts are put in the solution obtained to the 6th step carries out emulsifying;
8th step:The sodium benzoate that 2.5 mass parts are put in the solution obtained to the 7th step carries out emulsifying;
9th step:The colorant that 0.01 mass parts are put in the solution obtained to the 8th step is stirred and emulsifying, that is, obtain glass
Water.
2. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In second step, the stirring
Persistent period is 5-10 minutes.
3. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the third step, during the emulsifying
Between be 5-10 minutes.
4. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 4th step, the stirring
Persistent period is 5-10 minutes.
5. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 5th step, during the emulsifying
Between be 5-10 minutes.
6. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 6th step, during the emulsifying
Between be 5-10 minutes.
7. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 7th step, during the emulsifying
Between be 5-10 minutes.
8. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 8th step, during the emulsifying
Between be 5-10 minutes.
9. a kind of bath of glass processing technology according to claim 1, it is characterised in that:In the 9th step, it is described stirring and
Emulsification times are 5-10 minutes.