CN106543644A - A kind of carbon anticorrosion composite material, and preparation method thereof - Google Patents
A kind of carbon anticorrosion composite material, and preparation method thereof Download PDFInfo
- Publication number
- CN106543644A CN106543644A CN201610888166.0A CN201610888166A CN106543644A CN 106543644 A CN106543644 A CN 106543644A CN 201610888166 A CN201610888166 A CN 201610888166A CN 106543644 A CN106543644 A CN 106543644A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon
- epoxy resin
- present
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The related a kind of carbon composite of the present invention, by following weight than constituting:60 70 parts of anti-corrosion epoxy resin, 10 18 parts of carbon, 5 10 parts of super polyethylene, Gu tough dose 5 12 parts, 58 parts of bulking agent, 58 parts of Gypsum Fibrosum powder.Present invention also offers a kind of preparation method of carbon composite.The carbon composite that the present invention is provided have wear-resisting, impact resistance, it is corrosion-resistant, absorb the combination properties such as impact energy, low temperature resistant, not hygroscopic, density is less.
Description
Technical field
Supra polymer of the present invention is related to technical field of composite materials, the anti-corrosion epoxy of carbon of more particularly to a kind of polynary purposes
Resin composite materials, and preparation method thereof.
Background technology
Carbon composite is based on the comprehensive contribution in polynary field so as to become the function material with property
Material.
As a kind of new structural timber, it is excellent thermosetting resin based on anti-corrosion epoxy resin, with other
Unsaturated polyester resin is compared, and with more excellent physics electro-chemical properties, and it is multiple to add the anti-corrosion epoxy resin of carbon enhancing to make
Condensation material, the aggregative indicator such as its intensity, wear-resisting are higher than existing structure material.Have strictly in rigidity, weight, fatigue properties etc.
The field of requirement, under high temperature resistant, the requirement of chemical stability, carbon composite has much advantage.By additional proportion carbon,
And ultra high molecular polyethylene composition, the combination property of material is improve, based on demand of the polynary field to above-mentioned elastomeric material,
A kind of carbon anticorrosion composite material of this technology team plan offer, and preparation method thereof, and nontoxic pollution-free, its preparation process letter
It is single, it is with low cost, perhaps have great importance for the sustainable development of human settlement, promotion economic society is protected, it is easy to
Socialization application.
The content of the invention
Based on above-mentioned present situation, it is an object of the invention to provide a kind of carbon anticorrosion composite material, and preparation method thereof, should
It is, based on anti-corrosion epoxy resin, with ratio carbon and ultra high molecular polyethylene composition as radix, to improve with the material
The combination property of material, can effectively be lifted the characteristic of carbon anticorrosion composite material and be reached satisfied with time saving and energy saving
Effect.
For achieving the above object, the technical solution adopted in the present invention is:Above-mentioned anti-corrosion epoxy resin using bisphenol A-type,
Above-mentioned solid tough dose adopts alkenes additive using amine nitrile rubber complex, above-mentioned bulking agent;Gypsum Fibrosum powder after process is added
Enter in nonionic aqueous solution, make the mixed liquor that homogenizes, then by above-mentioned bisphenol A-type anti-corrosion epoxy resin, carbon, super polyethylene,
Gu tough dose, after bulking agent, Gypsum Fibrosum powder mixed, be molded, be dried, that is, make carbon anticorrosion composite material.Prepared by the present invention
Carbon composite has wear-resisting, impact resistance, corrosion-resistant, to absorb impact energy, low temperature resistant, not hygroscopic, density less etc. comprehensive
Performance;And technique is brief, low cost, environment friendly and pollution-free, is conducive to social production and people's application.
Improvement, development, research for the demand present situation, the invention has benefit that, the one of present invention offer
Kind carbon anticorrosion composite material, and preparation method thereof, in the presence of solving the preparation method of existing carbon resin material
Technique is miscellaneous, poor repeatability, problem with high costs, by additional proportion carbon and ultra high molecular polyethylene composition, improves
The combination property of material;Can with time saving and energy saving, effectively can be lifted wear-resisting, impact resistance, it is corrosion-resistant, absorb impact energy, resistance to low
The combination property such as warm, not hygroscopic, density is less;And reach satisfied effect.
In order to increase the function of the generation of prior art, there is provided it is a kind of it is workable, provide that design is brief, multiple-effect is common
Enjoy, a kind of convenient and safe carbon anticorrosion composite material for using, and preparation method thereof, properties of product are high, and integrated cost is low, prepare
It is simple with using method and applied widely, the growing production and construction of diversification and life need can be met
Will, it is science, ecology, environmental protection, the multi-effect scheme of sustainable development.
Described above is only the general introduction of technical solution of the present invention, in order to be able to better understand the technological means of the present invention, and
Can be practiced according to the content of description, and be allow the present invention above and other objects, features and advantages can be brighter
It is aobvious understandable, below especially exemplified by preferred embodiment, describe in detail as follows.
Specific embodiment
Further to illustrate the present invention to reach technological means and effect that predetermined goal of the invention is taken, below in conjunction with
Preferred embodiment, to according to a kind of carbon anticorrosion composite material proposed by the present invention, and preparation method thereof, its specific embodiment party
Formula, feature etc., describe in detail as after.
Embodiment
In this case embodiment, first, a kind of carbon anticorrosion composite material proposed by the present invention, and preparation method thereof, press
Following weight is than constituting:Anti-corrosion epoxy resin 60-70 parts, carbon 10-18 parts, super polyethylene 5-10 parts, Gu tough dose of 5-12 part, increases
Hold agent 5-8 parts, Gypsum Fibrosum powder 5-8 parts;Above-mentioned anti-corrosion epoxy resin adopts amine butyronitrile rubber using bisphenol A-type, above-mentioned solid tough dose again
Glue complex, above-mentioned bulking agent adopt alkenes additive;Gypsum Fibrosum powder after process is added in nonionic aqueous solution, homogenizing is made
Change mixed liquor, by above-mentioned bisphenol A-type anti-corrosion epoxy resin 60-70 parts, carbon 10-18 parts, super polyethylene 5-10 parts, Gu tough dose of 5-
12 parts, bulking agent 5-8 parts, Gypsum Fibrosum powder 5-8 parts are mixed, are molded, be dried after, that is, make carbon anticorrosion composite material.This
A kind of carbon anticorrosion composite material of bright preparation is beneficial in that, with wear-resisting, impact resistance, it is corrosion-resistant, absorb impact energy, resistance to
The combination property such as low temperature, not hygroscopic, density is less;It is and process is simple, with low cost, it is environment friendly and pollution-free, for protection people occupies
Environment, the sustainable development of promotion economic society perhaps have great importance, and are conducive to social production and people's livelihood application.
The above, is only presently preferred embodiments of the present invention, not makees any pro forma restriction to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, in the range of without departing from technical solution of the present invention, when making a little change or modification using the technology contents of the disclosure above
For the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention
Any simple modification, equivalent variations and the modification made to above example, still falls within the range of technical solution of the present invention.
Claims (3)
1. a kind of carbon composite, it is characterised in that by following weight than constituting:Anti-corrosion epoxy resin 60-70 parts, carbon
10-18 parts, super polyethylene 5-10 parts, Gu tough dose of 5-12 part, bulking agent 5-8 parts, Gypsum Fibrosum powder 5-8 parts.
2. a kind of carbon composite according to claim 1, it is characterised in that:Above-mentioned anti-corrosion epoxy resin adopts bis-phenol
A types, above-mentioned solid tough dose alkenes additive is adopted using amine nitrile rubber complex, above-mentioned bulking agent.
3. the preparation method of a kind of carbon composite according to claim 1, it is characterised in that:By the Gypsum Fibrosum after process
During powder adds nonionic aqueous solution, the mixed liquor that homogenizes is made, by above-mentioned bisphenol A-type anti-corrosion epoxy resin 60-70 parts, carbon
10-18 parts, super polyethylene 5-10 parts, Gu tough dose of 5-12 part, bulking agent 5-8 parts, Gypsum Fibrosum powder 5-8 parts are mixed, are molded, being dried
Afterwards, that is, make carbon anticorrosion composite material.