CN106543568A - EPDM flame retardant rubber and its production method - Google Patents
EPDM flame retardant rubber and its production method Download PDFInfo
- Publication number
- CN106543568A CN106543568A CN201610935712.1A CN201610935712A CN106543568A CN 106543568 A CN106543568 A CN 106543568A CN 201610935712 A CN201610935712 A CN 201610935712A CN 106543568 A CN106543568 A CN 106543568A
- Authority
- CN
- China
- Prior art keywords
- weight portions
- flame retardant
- retardant rubber
- sizing material
- epdm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of EPDM flame retardant rubber and its production method.The EPDM flame retardant rubber includes ethylene propylene diene rubber, reinforced filling, encapsulated red phosphorus, phenolic resin, activator, lubricant, sulfur, accelerator, age resistor.The production method of the EPDM flame retardant rubber includes premix, banburying, mill, molding, sulfuration.Flame retardant rubber tensile property that the EPDM flame retardant rubber and its production method that the present invention is provided solves prior art is poor, smoke toxicity is larger, the technical problem such as expensive.
Description
Technical field
The present invention relates to flame retardant rubber field, and in particular to a kind of EPDM flame retardant rubber and its production method.
Background technology
Existing EPDM flame retardant rubber, what is in general commonly used are divided into two big class.One class is with inorganic combustion inhibitor Al
(OH) 3, Mg (OH) 2 is fire-retardant main body, and Firebrake ZB is smoke suppressant.Environment friendly non-halogen element is characterized in, it is cheap.It is another kind of, adopt
It is fire-retardant main body with organic fire-retardant, including halogen flame, phosphorus flame retardant and nitrogenated flame retardant etc..Wherein halogen flame
For the most fire retardant of present consumption, particularly bromide fire retardant, it is extensively selected by producer.
But need to add substantial amounts of inorganic constituentss using inorganic combustion inhibitor, so the physical property of sizing material can be particularly
Tensile property is impacted;
It is little using halogen flame addition, and good flame retardation effect, but smoke toxicity is larger, and can produce during burning halogen-containing has
Poisonous gas;
Then there is addition greatly using the EPDM flame retardant glue material containing phosphorus flame retardant and nitrogenated flame retardant, and it is expensive,
Smoke density is higher, the general problem of flame retardant effect.
The content of the invention
Flame retardant rubber tensile property to solve prior art is poor, smoke toxicity is larger, the technical problem such as expensive, this
It is bright that a kind of EPDM flame retardant rubber for solving the above problems and its production method are provided.
A kind of EPDM flame retardant rubber, including ethylene propylene diene rubber, the benefit of 60 ~ 80 weight portions of 100 ~ 120 weight portions
Strong filler, the encapsulated red phosphorus of 10 ~ 20 weight portions, the phenolic resin of 30 ~ 40 weight portions, the activator of 2 ~ 5 weight portions, 20 ~ 30 weights
The lubricant of amount part, the sulfur of 1 ~ 3 weight portion, the accelerator of 1 ~ 3 weight portion, the age resistor of 1 ~ 3 weight portion.
In a kind of preferred embodiment of the EPDM flame retardant rubber that the present invention is provided, the reinforced filling is white carbon black,
The activator is Zinc Oxide, and the lubricant is molybdenite powder.
In a kind of preferred embodiment of the EPDM flame retardant rubber that the present invention is provided, the encapsulated red phosphorus are dual packet
Red phosphorus is covered, the phenolic resin is linear phenolic resin.
A kind of production method for producing the ethylene propylene diene rubber, comprises the following steps:
Step one:Premix:The phenolic resin of the encapsulated red phosphorus of 10 ~ 20 weight portions, 30 ~ 40 weight portions is carried out at premix
Reason, the encapsulated red phosphorus are well-dispersed in the phenolic resin, obtain disperse materials;
Step 2:Banburying:By the disperse materials, and ethylene propylene diene rubber, the benefit of 60 ~ 80 weight portions of 100 ~ 120 weight portions
Strong filler, the activator of 2 ~ 5 weight portions, the lubricant of 20 ~ 30 weight portions, the sulfur of 1 ~ 3 weight portion, the promotion of 1 ~ 3 weight portion
Agent, the age resistor of 1 ~ 3 weight portion carry out banburying jointly, and each component is sufficiently mixed uniformly, obtain banburying sizing material;
Step 3:Mill:The banburying sizing material is carried out into mill process, each component is further mixed, mill sizing material is obtained;
Step 4:Molding:According to product needed, the mill sizing material is carried out into the preforming such as tabletting process, molding sizing material is obtained;
Step 5:Sulfuration:The molding sizing material is carried out into vulcanizing treatment, the EPDM flame retardant rubber is obtained.
Compared to prior art, the EPDM flame retardant rubber and its production method that the present invention is provided has and following has
Beneficial effect:
First, the EPDM flame retardant rubber adopts encapsulated red phosphorus as fire retardant, phenolic resin as dispersant, with less
Addition realizes preferable flame retardant effect, not only reduces production cost, and smoke density, smoke toxicity all very littles of product,
Oxygen index (OI) can reach 36.
2nd, in the EPDM flame retardant rubber, the addition of the material such as fire retardant is less, the every physical property to sizing material
Can have no adverse effect, the tensile strength of product can reach 16MPa, and elongation at break reaches 500%, and anti-wear performance is excellent.
Description of the drawings
Fig. 1 is the process chart of the production method of the ethylene propylene diene rubber that the present invention is provided.
Specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the present invention, rather than the embodiment of whole.
The EPDM flame retardant rubber include the ethylene propylene diene rubber of 120 weight portions, the white carbon black of 60 weight portions, 15
The encapsulated red phosphorus of weight portion, the phenolic resin of 30 weight portions, the Zinc Oxide of 5 weight portions, the molybdenite powder of 30 weight portions, 2 weight
The sulfur of part, the accelerator of 1 weight portion, the age resistor of 1 weight portion.
The production method of the EPDM flame retardant rubber is comprised the following steps:
S1:Premix:The phenolic resin of the encapsulated red phosphorus of 15 weight portions, 30 weight portions is carried out into premix process, the bag is made
Cover red phosphorus to be well-dispersed in the phenolic resin, obtain disperse materials;
S2:Banburying:By the disperse materials, and the ethylene propylene diene rubber of 120 weight portions, the white carbon black of 60 weight portions, 5 weight portions
Zinc Oxide, the molybdenite powder of 30 weight portions, the sulfur of 2 weight portions, the accelerator of 1 weight portion, 1 weight portion age resistor it is jointly close
Refining certain hour, makes each component be sufficiently mixed uniformly, obtains banburying sizing material;
S3:Mill:The banburying sizing material is carried out into mill and processes certain hour, further mix each component, obtain mill sizing material;
S4:Molding:Compressing tablet process are carried out to the mill sizing material, molding sizing material is obtained;
S5:Sulfuration:The molding sizing material is carried out into vulcanizing treatment, the EPDM flame retardant rubber is obtained.
Compared to prior art, the EPDM flame retardant rubber and its production method that the present invention is provided has and following has
Beneficial effect:
First, the EPDM flame retardant rubber adopts encapsulated red phosphorus as fire retardant, phenolic resin as dispersant, with less
Addition realizes preferable flame retardant effect, not only reduces production cost, and smoke density, smoke toxicity all very littles of product,
Oxygen index (OI) can reach 36.
2nd, in the EPDM flame retardant rubber, the addition of the material such as fire retardant is less, the every physical property to sizing material
Can have no adverse effect, the tensile strength of product can reach 16MPa, and elongation at break reaches 500%, and anti-wear performance is excellent.
Embodiments of the invention are the foregoing is only, the scope of the claims of the present invention is not thereby limited, it is every using this
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of patent protection of the present invention in the same manner.
Claims (4)
1. a kind of EPDM flame retardant rubber, it is characterised in that:Ethylene propylene diene rubber, 60 ~ 80 weights including 100 ~ 120 weight portions
The amount reinforced filling of part, the encapsulated red phosphorus of 10 ~ 20 weight portions, the phenolic resin of 30 ~ 40 weight portions, the activator of 2 ~ 5 weight portions,
The lubricant of 20 ~ 30 weight portions, the sulfur of 1 ~ 3 weight portion, the accelerator of 1 ~ 3 weight portion, the age resistor of 1 ~ 3 weight portion.
2. EPDM flame retardant rubber according to claim 1, it is characterised in that:The reinforced filling is white carbon black, described
Activator is Zinc Oxide, and the lubricant is molybdenite powder.
3. EPDM flame retardant rubber according to claim 1, it is characterised in that:The encapsulated red phosphorus are that dual cladding is red
Phosphorus, the phenolic resin are linear phenolic resin.
4. a kind of production method of the ethylene propylene diene rubber produced described in claim 1, it is characterised in that comprise the following steps:
Step one:Premix:The phenolic resin of the encapsulated red phosphorus of 10 ~ 20 weight portions, 30 ~ 40 weight portions is carried out at premix
Reason, the encapsulated red phosphorus are well-dispersed in the phenolic resin, obtain disperse materials;
Step 2:Banburying:By the disperse materials, and ethylene propylene diene rubber, the benefit of 60 ~ 80 weight portions of 100 ~ 120 weight portions
Strong filler, the activator of 2 ~ 5 weight portions, the lubricant of 20 ~ 30 weight portions, the sulfur of 1 ~ 3 weight portion, the promotion of 1 ~ 3 weight portion
Agent, the age resistor of 1 ~ 3 weight portion carry out banburying jointly, and each component is sufficiently mixed uniformly, obtain banburying sizing material;
Step 3:Mill:The banburying sizing material is carried out into mill process, each component is further mixed, mill sizing material is obtained;
Step 4:Molding:According to product needed, the mill sizing material is carried out into the preforming such as tabletting process, molding sizing material is obtained;
Step 5:Sulfuration:The molding sizing material is carried out into vulcanizing treatment, the EPDM flame retardant rubber is obtained.