CN106520034A - Pressure-sensitive adhesive for reflection type high-durability polaroid and polaroid with pressure-sensitive adhesive applied - Google Patents
Pressure-sensitive adhesive for reflection type high-durability polaroid and polaroid with pressure-sensitive adhesive applied Download PDFInfo
- Publication number
- CN106520034A CN106520034A CN201610944692.4A CN201610944692A CN106520034A CN 106520034 A CN106520034 A CN 106520034A CN 201610944692 A CN201610944692 A CN 201610944692A CN 106520034 A CN106520034 A CN 106520034A
- Authority
- CN
- China
- Prior art keywords
- weight
- pressure
- sensitive adhesive
- polaroid
- percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pressure-sensitive adhesive for a reflection type high-durability polaroid. The pressure-sensitive adhesive comprises, by weight, 80-85% of acrylate polymer with the weight-average molecular weight being 70000-800000, 14.8-19% of hydroxyethyl acrylate polymer with the weight-average molecular weight being 30000-200000, and 0.2-1.0% of bridging agents. According to the pressure-sensitive adhesive, compared with a formula of traditional pressure-sensitive adhesive, the content of carboxy groups in the adhesive is reduced, the original adhesive force between the adhesive, the polaroid and an aluminum reflecting film and high durability are maintained, and corrosion of H+ ions in the adhesive to the aluminum reflecting film is reduced. The invention further discloses the polaroid provided with the pressure-sensitive adhesive. The aluminum reflecting film is bonded to a polaroid layer through the pressure-sensitive adhesive. As for the pressure-sensitive adhesive, the adhesive force of the adhesive is larger than 500gf/25 cm, the viscosity ranges from 2000cps to 8000 cps, the weather resistance is improved from 80 DEG C*500hr, 60 DEG C*90%*500hr to 105 DEG C*500hr, 85 DEG C*85%*500hr, pin-hole corrosion to the reflecting layer aluminum film is avoided, the reflecting performance of the polaroid remains the same, and the using effect can be achieved.
Description
Technical field
The present invention relates to optics polarization element technical field, more particularly to it is a kind of high durable with reflection function for LCD
Polaroid pressure sensitive adhesive and the polaroid using the pressure sensitive adhesive.
Background technology
Polaroid main usess are used on LCD liquid crystal displays, are had through pattern, semi-permeable pattern and reflective-mode.
Reflective-mode typically uses aluminium mirror coating, and generally aluminium mirror coating is metallic aluminium coating by vaporization to PET base material (Polyethylene
Terephthalate, abbreviation PET, polyethylene terephthalate, chemical formula are COC6H4COOCH2CH2O, are a kind of normal
The resin seen) up, then by the side with aluminum PSA glue (abbreviation of pressure sensitive adhesive, custom
Claim pressure sensitive adhesive) it is compound on polaroid.
The synthesis of traditional polaroid PSA virgin rubber water is by about 80% acrylate (Acrylate ester) peace treaty
The component such as 20% acrylic acid (Acrylic acid) and 2- hydroxyethylmethacry,ates (2-Hydroxyethyl acrylate) is mixed
React what is produced by certain condition after conjunction, in the glue after organic reaction, also contain certain carboxyl (carboxyl)-COOH,
It is hot and humid (85 DEG C × 85%RH × 500H, 85 degrees Celsius, relative humidity be 500 hours in the environment of 85%) in environment,
Hydroxy-acid group can discharge H+, there is aluminium lamination and bores a hole bad, affect using effect in ion etching aluminium film.
The content of the invention
For weak point present in above-mentioned technology, the technical problem to be solved in the present invention is to provide a kind of to reflection-type
The little pressure sensitive adhesive of polaroid aluminium mirror coating corrosive nature, there is also provided the polaroid made using this pressure sensitive adhesive.
For achieving the above object, the invention provides a kind of high durable pressure-sensitive adhesive for polaroid of reflection-type, pressure-sensitive glue host
Including acrylate component unit as the acrylate polymer of essential building blocks, 2-(Acryloyloxy)ethanol as primary structure
The 2-(Acryloyloxy)ethanol polymer of unit and bridging agent;The percentage by weight of the acrylate polymer is 80%-
85%;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer is 14.8%-19%;The percentage by weight of the bridging agent
0.2%-1.0%.
Wherein, the weight average molecular weight of acrylate polymer is 100000-900000;The 2-(Acryloyloxy)ethanol polymer
Weight average molecular weight 100000-200000.
The viscoelasticity of pressure-sensitive adhesive agent itself and to by the wettability of viscous material surface be produce to pressure-sensitive master
Want reason.As a good pressure-sensitive adhesive agent, it is necessary to meet fast viscous force (A)<Bonding force (B)<Cohesiveness (C)<Glutinous base power (D).
The molecular weight for reducing pressure sensitive adhesive can reduce its bulk viscosity, be conducive to flowing and moistening, so as to improve interface cohesive force.But
When molecular weight is low, cohesive strength is poor, and cohesional failure easily occurs during stripping.Increasing molecular weight can increase the cohesiveness of material, and have
Beneficial to raising adhesive strength, but molecular weight crosses conference retardance moistening and dispersion, so impact and material of the molecular weight to adhesive strength
The property of material is relevant.The adhesive strength of acrylic copolymer increases with the increase of molecular weight, therefore the molecular weight of pressure sensitive adhesive must
Must keep within the specific limits, can just obtaining preferable adhesive property.Main body is done using the polymer elastomer of higher molecular,
Coordinate appropriate low-molecular-weight solvent misture to reduce bulk viscosity, problem above can be solved well.Low-molecular-weight it is poly-
Compound, its mechanical property are typically bad.Pressure-sensitive adhesive agent made by low-molecular weight polymer, although initial bonding strength is sometimes all well and good,
But their peel strength and bonding force be not general high, for electronic beam curing graft polypropylene acid esters, when putting down for polymer
When average molecular weight increases, solidifying the peel strength of post-consumer polymer, bonding force and initial bonding strength all increases, this is because polymer point
Subchain segment length increases, and is conducive to the infiltration with adherend surface.When molecular weight is relatively low, due to peel strength and fast viscous force all
It is low, and all there is cohesional failure when peeling off, actually cannot use as pressure sensitive adhesive, the increase of the performance of pressure sensitive adhesive with molecular weight
And increase, it is therefore necessary to improve molecular weight.Since the bonding force of polymer adhesive increases with molecular weight in low-molecular-weight region
Plus, then peel strength is expected by improving molecular weight to improve.After maximum, peel strength drastically declines, and glues
Connect failure mode and interfacial failure is turned to by cohesional failure, no adhesive stays in base material side.This is because adhesive is cohesion
Power has exceeded adhesive with the bonding force between substrate interface, and under final peeling rate, peel strength is slight with the change of molecular weight, and
It is obvious at high speeds.The adhesive of any molecular weight, for two kinds of failure modes, peel strength is all with peeling rate
And increase.It can thus be seen that must be by the molecular weight control of high polymer in certain scope when pressure-sensitive adhesive agent is prepared.
The composition of high polymer is different, and structure is different, and the optimum range of molecular weight is also different.
In actual production, the weight average molecular weight of general acrylate polymer is 100000-900000, acrylic acid hydroxyl second
During weight average molecular weight 100000-200000 of ester polymer, viscosity can be made between 2000CPS to 8000CPS, can meet fast
Viscous force (A)<Bonding force (B)<Cohesiveness (C)<Glutinous base power (D), is appropriate pressure-sensitive adhesive formula.
Used as a preferred embodiment of the present invention, the percentage by weight of the acrylate polymer is 80%, is divided equally again
Son amount is 100000;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer is 19.0%, and weight average molecular weight is 200000;Institute
The percentage by weight for stating bridging agent is 1.0%.
Used as another kind of preferred version of the present invention, the percentage by weight of the acrylate polymer is 82.5%, weight
Average molecular weight is 640000;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer is 17.0%, and weight average molecular weight is
160000;The percentage by weight of the bridging agent is 0.5%.
Used as another preferred version of the present invention, the percentage by weight of the acrylate polymer is 85%, and weight is equal
Molecular weight is 900000;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer is 14.8%, and weight average molecular weight is 100000;
The percentage by weight of the bridging agent is 0.2%.
Preferably, bridging agent is ployisocyanate bridging agent, the bridging agent containing epoxy-functional, the frame containing metal chelate
One or more in bridge agent.
It is furthermore preferred that the bridging agent is ployisocyanate bridging agent.Acrylate polymer and propylene in the present invention
Sour hydroxyl ethyl ester polymer mixed, due to not carboxy-containing acid group in polymer, in the environment of ordinary temperature normal temperature and pressure, substantially not
Can dissociate H+Ion.In order to ensure to contain less H in formula+Ion, the ployisocyanate bridging agent in above-mentioned three kinds of bridging agents
In do not contain acidic functionality, will not dissociate in such formula H substantially+Ion, reduces corrosion of the pressure sensitive adhesive to aluminium mirror coating.
Acrylate polymer in the present invention is the acrylate polymer typically used in prior art, including propylene
The polymer that the monomers such as sour methyl ester, butyl acrylate are polymerized.2-(Acryloyloxy)ethanol polymer as cross-linking agent and lubricant,
Be conducive to the crosslinking of acrylate polymer.Acrylate pressure-sensitive adhesive formula is simple, need not using tackifying resin, softening agent,
The auxiliary agents such as age resistor;Bonding is in extensive range simultaneously, is respectively provided with good adhesive property to materials such as metal, ceramics, cement;And
Due to the presence for having unsaturated double bond of having a talk, with weatherability well.These performances are common acrylate pressure-sensitive adhesive
The advantage that can also have more.And the formula of the present invention is in the acrylate pressure-sensitive adhesive formula on existing basis to eliminate acrylic acid
Component, while suitably have adjusted the component ratio of acrylate polymer and 2-(Acryloyloxy)ethanol polymer so that the present invention
Acrylate pressure-sensitive adhesive is while keeping original viscous force, viscosity, weatherability, moreover it is possible to reduce H+The content of ion, is reduced
Corrosion to aluminium mirror coating.The viscous force of prior art acrylate pressure-sensitive adhesive is more than 500gf/25cm, and viscosity is in 2000cps-
Between 8000cps, weatherability more than 80 DEG C × 500hr, 60 DEG C × 90% × 500hr, and the present invention without acid type pressure-sensitive glue
Viscous force be more than 500gf/25cm, viscosity between 2000cps-8000cps, weatherability from 80 DEG C × 500hr, 60 DEG C × 90% ×
500hr bring up to 105 DEG C × 500hr, 85 DEG C × 85% × 500hr, reflecting layer aluminium film is not produced Pinhole-shaped corrosion, can reach send out
Bright purpose.
The present invention also proposes above-mentioned pressure-sensitive glue host for being adhered fixed aluminium mirror coating and polaroid in reflective polaroid
Matrix.
For achieving the above object, present invention also offers a kind of polaroid, including aluminium mirror coating layer 1, the first pressure-sensitive adhesive layer
2nd, polarization matrix layer 3 and the second pressure-sensitive adhesive layer 4;Aluminium mirror coating layer 1 is by the first pressure-sensitive adhesive layer 2 and the one side of polarization matrix layer 3
It is adhered fixed connection;The another side of polarization matrix layer 3 is adhered fixed with liquid-crystalline glasses 5 by the second pressure-sensitive adhesive layer 4 and is connected;First
Pressure-sensitive glue host in pressure-sensitive adhesive layer 2 is the pressure-sensitive glue host described in any one of claim 1-8.
The invention has the beneficial effects as follows:The pressure sensitive adhesive of the present invention, under the formula of traditional pressure sensitive glue, reduces in glue
Hydroxy-acid group content, makes glue both maintain original adhesion strength and polaroid and aluminium mirror coating between and high-durability, subtracts again
H in glue is lacked+The corrosion of ion pair aluminium mirror coating.The pressure sensitive adhesive of the present invention, glue viscous force are more than 500gf/25cm, and viscosity exists
Between 2000cps-8000cps, weatherability from 80 DEG C × 500hr, 60 DEG C × 90% × 500hr bring up to 105 DEG C × 500hr,
85 DEG C × 85% × 500hr, Pinhole-shaped corrosion is not produced to reflecting layer aluminium film.The polaroid with above-mentioned pressure sensitive adhesive of the present invention,
Aluminium mirror coating by above-mentioned pressure sensitive adhesive and layer of polarizer adhesion, due to reducing the H in pressure sensitive adhesive+Ion, decreases glue
Corrosion to aluminium mirror coating, hot and humid 85 DEG C × 85%RH × 500H or hot and humid, the 80 DEG C × 90%RH × 500H of Jing are durable
Property test, polaroid reflecting properties keep it is constant, can reach using effect.
Description of the drawings
Fig. 1 is the structural representation of polaroid of the present invention:
Main element symbol description is as follows:
1st, aluminium mirror coating layer 2, the first pressure-sensitive adhesive layer
3rd, polarization matrix layer 4, the second pressure-sensitive adhesive layer
5th, liquid-crystalline glasses.
Specific embodiment
In order to more clearly state the present invention, the present invention is further described below with specific embodiment.
In invention bridging agent can for ployisocyanate bridging agent, the bridging agent containing epoxy-functional or, metal chelate
Bridging agent in one or more.In order to reduce the corrosivity to aluminium mirror coating, preferred bridging agent is without acid functional
The ployisocyanate bridging agent of group.In following examples, bridging agent is illustrated from ployisocyanate bridging agent.
Embodiment 1
The percentage by weight of acrylate polymer is 80%-85%, weight average molecular weight is 100000-900000;Propylene
The percentage by weight of sour hydroxyl ethyl ester polymer is 14.8%-19%, weight average molecular weight 100000-200000;Ployisocyanate frame
The percentage by weight 0.2%-1.0% of bridge agent.
Embodiment 2
The percentage by weight of acrylate polymer is 85%, and weight average molecular weight is 900000;2-(Acryloyloxy)ethanol is polymerized
The percentage by weight of thing is 14.8%, and weight average molecular weight is 100000;The percentage by weight of ployisocyanate bridging agent is
0.2%.
Embodiment 3
The percentage by weight of acrylate polymer is 84%, and weight average molecular weight is 860000;2-(Acryloyloxy)ethanol is polymerized
The percentage by weight of thing is 15.7%, and weight average molecular weight is 130000;The percentage by weight of ployisocyanate bridging agent is
0.3%.
Embodiment 4
The percentage by weight of acrylate polymer is 83.5%, and weight average molecular weight is 780000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 16.1%, and weight average molecular weight is 140000;The percentage by weight of ployisocyanate bridging agent is
0.4%.
Embodiment 5
The percentage by weight of acrylate polymer is 82.5%, and weight average molecular weight is 640000;The acrylic acid hydroxyl second
The percentage by weight of ester polymer is 17.0%, and weight average molecular weight is 160000;The percentage by weight of ployisocyanate bridging agent
For 0.5%.
Embodiment 6
The percentage by weight of acrylate polymer is 82.1%, and weight average molecular weight is 500000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 17.3%, and weight average molecular weight is 160000;The percentage by weight of ployisocyanate bridging agent is
0.6%.
Embodiment 7
The percentage by weight of acrylate polymer is 81.5%, and weight average molecular weight is 400000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 17.8%, and weight average molecular weight is 170000;The percentage by weight of ployisocyanate bridging agent is
0.7%.
Embodiment 8
The percentage by weight of acrylate polymer is 81%, and weight average molecular weight is 300000;2-(Acryloyloxy)ethanol is polymerized
The percentage by weight of thing is 18.2%, and weight average molecular weight is 180000;The percentage by weight of ployisocyanate bridging agent is
0.8%.
Embodiment 9
The percentage by weight of acrylate polymer is 80.5%, and weight average molecular weight is 200000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 18.6%, and weight average molecular weight is 190000;The percentage by weight of ployisocyanate bridging agent is
0.9%.
Embodiment 10
The percentage by weight of acrylate polymer is 80%, and weight average molecular weight is 100000;2-(Acryloyloxy)ethanol is polymerized
The percentage by weight of thing is 19.0%, and weight average molecular weight is 200000;The percentage by weight of ployisocyanate bridging agent is
1.0%.
Embodiment 11
The percentage by weight of acrylate polymer is 78.8%, and weight average molecular weight is 100000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 20.0%, and weight average molecular weight is 210000;The percentage by weight of ployisocyanate bridging agent is
1.2%.
Embodiment 12
The percentage by weight of acrylate polymer is 85.9%, and weight average molecular weight is 920000;2-(Acryloyloxy)ethanol gathers
The percentage by weight of compound is 14.0%, and weight average molecular weight is 80000;The percentage by weight of ployisocyanate bridging agent is
0.1%.
Table 1 below is performance parameter of the pressure-sensitive glue host containing above-described embodiment formula under isodose solvent:
Table 1:
Note:In table 1, weatherability is compared with the condition of 60 DEG C × 90%RH × 500H, 85 DEG C × 85%RH × 500H
Compared with, by it is weather-proof evaluation be evaluated as from low to high it is excellent, good, in, differ from four grades.
From table 1 it follows that using the pressure-sensitive glue of inventive formulation, the corrosion journey to aluminium mirror coating can be reduced
Degree, while glue viscous force is all higher than 500gf/25cm, weatherability is brought up to from 80 DEG C × 500hr, 60 DEG C × 90% × 500hr
105 DEG C × 500hr, 85 DEG C × 85% × 500hr.Consider the solid content and viscosity of glue, the pressure-sensitive glue host of the present invention
Weight average molecular weight 2000cps-8000cps between meet the present invention in 15%-33%, viscosity in 30-100 ten thousand, solid content
Purpose.Wherein preferably pressure-sensitive glue host weight average molecular weight exists in 27%-29%, viscosity in 80-100 ten thousand, solid content
Between 4500cps-6000cps.I.e. the percentage by weight of acrylate polymer is 82.5%-84.0%, and weight average molecular weight is
640000-860000;The percentage by weight of 2-(Acryloyloxy)ethanol polymer is 15.7%-17.0%, and weight average molecular weight is
130000-160000;The percentage by weight of ployisocyanate bridging agent is 0.3%-0.5%, is preferred formula, i.e., specifically
In embodiment, 1-10 can reach the goal of the invention of the present invention, wherein optimal embodiment is specific embodiment 3-5.
Advantage of the invention is that:
1st, the formula of traditional pressure sensitive glue is have adjusted, the hydroxy-acid group content in glue is reduced, makes glue both maintain original
The adhesion strength having between polaroid and aluminium mirror coating and high-durability, reduce H in glue again+The corruption of ion pair aluminium mirror coating
Erosion.The pressure sensitive adhesive of the present invention, glue viscous force are more than 500gf/25cm, and, between 2000cps-8000cps, weatherability is from 80 for viscosity
DEG C × 500hr, 60 DEG C × 90% × 500hr bring up to 105 DEG C × 500hr, 85 DEG C × 85% × 500hr, to reflecting layer aluminium film
Pinhole-shaped corrosion is not produced.
2nd, the polaroid with above-mentioned pressure sensitive adhesive of the invention, aluminium mirror coating are glued with layer of polarizer by above-mentioned pressure sensitive adhesive
Even, due to reducing the H in pressure sensitive adhesive+Ion, decreases corrosion of the glue to aluminium mirror coating, and Jing is hot and humid 85 DEG C ×
85%RH × 500H or hot and humid 80 DEG C × 90%RH × 500H durability tests, polaroid reflecting properties keep constant, can
Reach using effect.
3rd, the ployisocyanate bridging agent of acidic functionality is not preferably contained, H is further reduced+The corruption of ion pair aluminium mirror coating
Corrosion.
Disclosed above is only several specific embodiments of the present invention, but the present invention is not limited to this, any this area
Technical staff can think change should all fall into protection scope of the present invention.
Claims (9)
1. the high durable pressure-sensitive adhesive for polaroid of a kind of reflection-type, it is characterised in that pressure-sensitive glue host includes acrylate component list
Unit as the acrylate polymer of essential building blocks, 2-(Acryloyloxy)ethanol as essential building blocks 2-(Acryloyloxy)ethanol
Polymer and bridging agent;The percentage by weight of the acrylate polymer is 80%-85%;The 2-(Acryloyloxy)ethanol
The percentage by weight of polymer is 14.8%-19%;The percentage by weight 0.2%-1.0% of the bridging agent.
2. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to claim 1, it is characterised in that the acrylate gathers
The weight average molecular weight of compound is 100000-900000;Weight average molecular weight 100000- of the 2-(Acryloyloxy)ethanol polymer
200000。
3. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to claim 1, it is characterised in that the acrylate gathers
It is 100000 that the percentage by weight of compound is 80%, weight average molecular weight;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer
It is 200000 for 19.0%, weight average molecular weight;The percentage by weight of the bridging agent is 1.0%.
4. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to claim 1, it is characterised in that the acrylate gathers
The percentage by weight of compound is 82.5%, and weight average molecular weight is 640000;The weight percent of the 2-(Acryloyloxy)ethanol polymer
Than for 17.0%, weight average molecular weight is 160000;The percentage by weight of the bridging agent is 0.5%.
5. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to claim 1, it is characterised in that the acrylate gathers
The percentage by weight of compound is 85%, and weight average molecular weight is 900000;The percentage by weight of the 2-(Acryloyloxy)ethanol polymer
For 14.8%, weight average molecular weight is 100000;The percentage by weight of the bridging agent is 0.2%.
6. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to any one of claim 1-5, it is characterised in that the frame
Bridge agent is ployisocyanate bridging agent, the bridging agent containing epoxy-functional, the one kind or several in the bridging agent containing metal chelate
Kind.
7. the high durable pressure-sensitive adhesive for polaroid of reflection-type according to claim 6, it is characterised in that the bridging agent is poly-
Carbimide bridging agent.
8. the pressure-sensitive glue host described in any one of claim 1-7 be used for reflective polaroid in be adhered fixed aluminium mirror coating with it is inclined
Light sheet matrix.
9. a kind of polaroid, it is characterised in that pressure-sensitive including aluminium mirror coating layer, the first pressure-sensitive adhesive layer, polarization matrix layer and second
Glue-line;The aluminium mirror coating layer is adhered fixed with the one side of polarization matrix layer by the first pressure-sensitive adhesive layer and is connected;The polarisation base
The another side of body layer is adhered fixed with liquid-crystalline glasses by the second pressure-sensitive adhesive layer and is connected;Pressure sensitive adhesive in first pressure-sensitive adhesive layer
Host is the pressure-sensitive glue host described in any one of claim 1-7.