CN106519335A - Medical latex film - Google Patents
Medical latex film Download PDFInfo
- Publication number
- CN106519335A CN106519335A CN201611012243.2A CN201611012243A CN106519335A CN 106519335 A CN106519335 A CN 106519335A CN 201611012243 A CN201611012243 A CN 201611012243A CN 106519335 A CN106519335 A CN 106519335A
- Authority
- CN
- China
- Prior art keywords
- medical latex
- thin film
- water
- medical
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a medical latex film. The medical latex film comprises, by weight, 0.01-1% of nano-silver, 0.2-3% of water-soluble chitosan, 0.5-5% of sericin, 10-40% of waterborne polyurethane and the balance natural latex. According to the medical latex film, the escaping concentration of extractable protein can be obviously reduced, the film has a compact structure, and the surface is more flat and smoother.
Description
Technical field
A kind of the present invention relates to field of material technology, more particularly to medical latex thin film.
Background technology
Natural emulsion is a kind of water-base disperse system of natural reproducible, and the rubber with natural emulsion as raw material has
Excellent combination property and irreplaceability, are widely used to medicine and hygiene fieldses, such as medical catheter, glove and condom
Deng.However, natural latex products still have some performance deficiencies, for example, natural latex products compactness, resistance to ag(e)ing, anti-
Bacterium property is poor.More seriously contain some allergic protein matter in latex, easily induce contact dermatitis, urticaria, anaphylaxis
The property the sent out anaphylaxiss of asthma constant speed, can cause anaphylactic shock when serious, or even dead.
Many researchs in recent years show, in the infection caused by biomaterial for medical purpose, are because life the reason for 45%
When thing material is with human contact, the fiber laminins, glass laminins in blood and tissue, Fibrinogen can adsorb
Material surface, forms one layer of albuminous coat, and this layer of albuminous coat is that the hotbed of growth of microorganism, especially antibacterial are easy in this layer of egg
Stick on tunica albuginea, then growth and breeding, gradually form the bioactive film of one layer of obstinate hydration polysaccharide property.This layer biological
Film can absorb nutrient substance, with certain thickness, produce very strong medicine resistance ability, and traditional antibacterial therapy is to eradicate
's.Thus the infection and other symptoms for causing causes clinical operation and patient significant burden economically.
Therefore, how to improve anti-microbial property and the desensitization performance of medical latex material, be one of difficult problem that this area faces.
The content of the invention
It is an object of the invention to propose a kind of medical latex thin film, enable to leachable albumen effusion concentration it is notable under
Drop, thin film have compact texture, surface more flat smooth.
It is that, up to this purpose, the present invention is employed the following technical solutions:
A kind of medical latex thin film, its percentage composition by weight contain:
Nanometer silver 0.01-1%
Water-soluble chitosan 0.2-3%
Sericin 0.5-5%
Aqueous polyurethane 10-40%
Natural emulsion surplus.
Preferably, the consumption of the nanometer silver is 0.01-0.1.
Preferably, the sericin consumption is 0.5-3%.
Preferably, water-soluble chitosan content is 0.5-2%.
Silver ion and antibacterial haptoreaction, cause cell proper constituent destroyed or produce dysfunction and dead.When micro-
When amount silver ion is met with microbial cell, as silver ion has higher oxidation-reduction potential (± 0.798V, 25 DEG C), and
The latter carries negative charge, by Coulomb attraction, makes the two be closely linked, and silver ion can also the entrance of penetration cell wall
In antibacterial body, and react with the sulfydryl in antibacterial, make protein coagulating, destroy the activity of cell synzyme, make cell loss point
Split multiplication capacity and dead:Simultaneously silver ion can also destroy microorganism electric transmission system, respiratory system, substance delivery system,
Cause microbial cell dead, play bactericidal action.After thalline loses activity, silver ion again can from thalline separate out,
Fungicidal property, therefore its durable antibacterial effect is carried out again and again.Meanwhile, in the presence of light, micro silver ion can be played
The effect of catalytic active center, can activate air or the oxygen in water, produce hydroxyl radical free radical and active oxygen ion, and they have very
Strong oxidability, can destroy the multiplication capacity of microbial cell, suppress or kill antibacterial, play bactericidal action.Due to silver from
Son plays catalytic active center, is not consumed in itself, has illumination just can constantly press down bactericidal, thus can reach it is efficient, lasting,
The antibacterial action of wide spectrum.
Shitosan has good biocompatibility, and the special work(with anti-inflammation with the histoorgan and cell of human body
Energy.The present invention utilizes heterocoagulation blend method, and water-soluble chitosan is incorporated in natural emulsion system.Test shows, water-soluble
Property shitosan be attached to the outer surface of natural emulsion microsphere, define a kind of special nucleocapsid structure so that institute is fine and close into thin film
Property has obtained very big improvement, and solvent resistance is significantly improved.Leachable albumen test and cell toxicity test show that water soluble shells are gathered
Sugar effectively prevent the effusion of water-solubility protein, make albumen escaped quantity minimize below sensitization concentration, modified film material peace
Complete not sensitization.
The sericin of the present invention has antioxidation, ultraviolet light, moisture absorption, biocompatibility and antianaphylaxiss, and which individually should
Modified for natural rubber, in the range of the addition of 1%-1.5%, the mechanical performance of natural rubber film is best, in 0.1%-1%
In the range of addition, water-soluble spilling protein content increases to 1.5mg/g from 1.1mg/g, water-soluble spilling protein content between 1%-2%
Increase sharply, during 1% addition, configuration of surface is most smooth.
, with water as solvent, with pollution-free, safe and reliable, good mechanical performance, the compatibility is good, be easy to change for aqueous polyurethane
The advantages of property.Anion aqueous polyurethane micelle and natural emulsion micelle are all negatively charged, and two kinds of emulsions can be with arbitrary proportion phase
Hold blending.Aqueous polyurethane is intended to improve the flatness of modified film, compactness, mechanical strength, drop with the blending of natural emulsion
Low allergic protein effusion, or even the pore defect for making up Cure of Rubber residual.Currently preferred aqueous polyurethane includes, with different
Isophorone diisocyanate and polytetrahydrofuran diol, Polyethylene Glycol, polypropylene glycol have synthesized aqueous polyurethane, with poly- tetrahydrochysene furan
The aqueous polyurethane muttered as soft section, its comprehensive mechanical property are optimal.Which is carried out into physical blending with natural emulsion, into thin film
Tensile strength is slightly reduced apparently higher than natural emulsion thin film, but elongation at break, and leachable albumen effusion concentration is remarkably decreased,
Solvent resistance is tested and atomic force collection of illustrative plates shows that blend film has compact texture, blend film surface more flat smooth.
The medical latex thin film of the present invention, which can suppress the water-soluble content for overflowing albumen, and possess bacteriostasis.
Specific embodiment
Technical scheme is further illustrated below by specific embodiment.
Embodiment 1
A kind of medical latex thin film, its percentage composition by weight contain:
Nanometer silver 0.01%
Water-soluble chitosan 0.2%
Sericin 0.5%
Aqueous polyurethane 10%
Natural emulsion surplus.
Embodiment 2
A kind of medical latex thin film, its percentage composition by weight contain:
Nanometer silver 1%
Water-soluble chitosan 3%
Sericin 5%
Aqueous polyurethane 40%
Natural emulsion surplus.
Embodiment 3
A kind of medical latex thin film, its percentage composition by weight contain:
Nanometer silver 0.05%
Water-soluble chitosan 1%
Sericin 2%
Aqueous polyurethane 30%
Natural emulsion surplus.
Claims (4)
1. a kind of medical latex thin film, its percentage composition by weight contain:
Nanometer silver 0.01-1%
Water-soluble chitosan 0.2-3%
Sericin 0.5-5%
Aqueous polyurethane 10-40%
Natural emulsion surplus.
2. medical latex thin film as claimed in claim 1, it is characterised in that the consumption of the nanometer silver is 0.01-0.1.
3. medical latex thin film as claimed in claim 1 or 2, it is characterised in that the sericin consumption is 0.5-3%.
4. the medical latex thin film as described in one of claim 1-3, it is characterised in that water-soluble chitosan content is 0.5-
2%.