CN106518081A - 多用途微创外科手术刀 - Google Patents
多用途微创外科手术刀 Download PDFInfo
- Publication number
- CN106518081A CN106518081A CN201611204185.3A CN201611204185A CN106518081A CN 106518081 A CN106518081 A CN 106518081A CN 201611204185 A CN201611204185 A CN 201611204185A CN 106518081 A CN106518081 A CN 106518081A
- Authority
- CN
- China
- Prior art keywords
- blade
- knife
- parts
- shaped handle
- multipurpose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种多用途微创外科手术刀,其条形刀柄前端具有供插接部嵌入的插孔;所述条形刀柄的前部沿周向依次开有上螺纹孔、中螺纹孔和下螺纹孔,一锁紧螺丝旋入中螺纹孔并压紧插接部,一上螺栓杆旋入上螺纹孔并嵌入插接部的上凹孔内,将超细碳化钨、碳化钛、碳化铬、二硅化钼、氮化钛、碳化钒和石墨粉投入粉碎机内进行粉碎处理,形成直径小于20微米的混合粉末;将制得的混合粉末置于真空条件中加热至850℃,加热4小时,然后加入酚醛树脂4~6份充分搅拌均匀,制得混合物后冷却。本发明多用途微创外科手术刀避免了刀体易松动、晃动的问题,也方便手术中医生观察伤口情况,有利于提高手术的精度。
Description
技术领域
本发明涉及医疗器械领域,尤其涉及一种多用途微创外科手术刀。
背景技术
手术刀是进行外科手术的必备工具,其安全性对于执刀医生和病患来说至关重要。以往传统手术刀通常有两种类型:一种是塑柄手术刀,另一种是钢柄手术刀。塑柄手术刀主要由一次性使用的刀片和一次性使用的塑柄组成,塑柄前部设有刀片座,刀片安装在刀片座上。钢柄手术刀主要由一次性使用的刀片和非一次性使用的钢柄组成,使用前需要将刀片安装到刀柄上,使用后将刀片从刀柄上移除;现有技术存在在使用过程中难以避免晃动、松动的问题,还可能会发生刀头在外力左右下脱落的情况,危险性极高。
发明内容
本发明提供一种多用途微创外科手术刀,此多用途微创外科手术刀避免了刀体易松动、晃动的问题,也方便手术中医生观察伤口情况,有利于提高手术的精度。
为达到上述目的,本发明采用的技术方案是:一种多用途微创外科手术刀,包括:刀片、条形刀柄,所述刀片的一端为刀刃,另一端为插接部,此插接部上端面和下端面分别开有上凹孔和下凹孔,所述条形刀柄前端具有供插接部嵌入的插孔;所述条形刀柄的前部沿周向依次开有上螺纹孔、中螺纹孔和下螺纹孔,一锁紧螺丝旋入中螺纹孔并压紧插接部,一上螺栓杆旋入上螺纹孔并嵌入插接部的上凹孔内,一下螺栓杆旋入下螺纹孔并嵌入插接部的下凹孔内;所述刀刃上开有若干个吸血孔,此吸血孔通过分导管与集液管连通,此集液管通过到导管连接到吸液接口,所述分导管与集液管位于刀片内,此刀刃上部具有一倒角斜面,一用于套在手上的套绳安装于所述条形刀柄的后部;
所述刀片通过以下步骤获得:
步骤一、将超细碳化钨50~60份、碳化钛 8~10份、碳化铬 6~8份、二硅化钼4~8份、氮化钛7~9份、碳化钒1~2份和石墨粉3~4份投入粉碎机内进行粉碎处理,形成直径小于20微米的混合粉末;
步骤二、将步骤一制得的混合粉末置于真空条件中加热至850℃,加热4小时,然后加入酚醛树脂4~6份充分搅拌均匀,制得混合物后冷却;
步骤三、通过压力机对混合物进行成型压制形成压坯;
步骤四、将压坯放置烧结炉进行烧结形成刀片毛坯,具体步骤如下:
步骤4-1、先升温至260℃,再以每小时4~6℃的速率升温至 500℃,保温1~2小时,此阶段采用真空条件烧结;
步骤4-2、再以每小时8~12℃的速率升温至1260℃,保温1~2小时,此阶段气氛为氩气和氮气形成的混合气体,此时的烧结压力为 6Mpa;
步骤4-3、再以每小时2~4℃的速率升温至1380℃,保温1~2小时,此阶段气氛为氩气,此时的烧结压力为4Mpa;
步骤4-4、随炉冷却;
步骤五、对刀片毛坯进行精磨加工,载开锋和打磨处理形成初步刀片;
步骤六、将步骤五的初步刀片进行液氮深冷处理从而获得所述刀片。
上述技术方案中进一步改进的技术方案如下:
作为优选,所述条形刀柄的截面为圆形。
作为优选,所述导管由位于刀片内的第一导管和位于条形刀柄内的第二导管贯通组成。
作为优选,所述步骤四的深冷处理的温度低于零下80℃。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
1、本发明多用途微创外科手术刀,其采用超细碳化钨50~60份、碳化钛 8~10份、碳化铬6~8份、二硅化钼4~8份、氮化钛7~9份和碳化钒1~2份进行烧结,使得手术刀的刀片拥有超高的硬度,而且开锋后的刀片十分锋利,且极高的强度不容易出现弯曲;其烧结过程三个阶段压力由真空依次切换到高压烧结、次高压烧结,并伴随特定组分气氛切换,有利于碳化物弥散析出,进而使刀片的材质组织更加紧密,增加了抗弯强度和抗崩刃性;再次,其混合粉末置于真空条件中加热至850℃,加热4小时,然后加入酚醛树脂4~6份充分搅拌均匀,有利于提高耐磨性。
2、本发明多用途微创外科手术刀,其刀片的一端为刀刃,另一端为插接部,此插接部上端面和下端面分别开有上凹孔和下凹孔,所述条形刀柄前端具有供插接部嵌入的插孔;所述条形刀柄的前部沿周向依次开有上螺纹孔、中螺纹孔和下螺纹孔,一锁紧螺丝旋入中螺纹孔并压紧插接部,一上螺栓杆旋入上螺纹孔并嵌入插接部的上凹孔内,一下螺栓杆旋入下螺纹孔并嵌入插接部的下凹孔内,拆装方便、稳定可靠,实现了立体三维定位,避免了刀体易松动、晃动的问题,具有很好的推广应用前景;其次,其医务人员的手腕穿过套绳后,可以防止手术刀滑落,避免了条形刀柄表面光滑,在手术过程中很容易滑脱的缺陷,从而大大降低了医疗事故率。
附图说明
附图1为本发明多用途微创外科手术刀结构示意图;
附图2为附图1的局部示意图。
以上附图中:1、刀片;2、条形刀柄;21、上螺纹孔;22、中螺纹孔;23、下螺纹孔;3、刀刃;4、插接部;41、上凹孔;42、下凹孔;5、插孔;6、锁紧螺丝;7、上螺栓杆;8、下螺栓杆;9、吸血孔;10、分导管;11、集液管;12、导管;121、第一导管;122、第二导管;13、吸液接口;14、套绳。
具体实施方式
下面结合附图及实施例对本发明作进一步描述:
实施例1~4:一种多用途微创外科手术刀,包括:刀片1、条形刀柄2,所述刀片1的一端为刀刃3,另一端为插接部4,此插接部4上端面和下端面分别开有上凹孔41和下凹孔42,所述条形刀柄2前端具有供插接部4嵌入的插孔5;所述条形刀柄2的前部沿周向依次开有上螺纹孔21、中螺纹孔22和下螺纹孔23,一锁紧螺丝6旋入中螺纹孔22并压紧插接部4,一上螺栓杆7旋入上螺纹孔21并嵌入插接部4的上凹孔41内,一下螺栓杆8旋入下螺纹孔23并嵌入插接部4的下凹孔42内;所述刀刃3上开有若干个吸血孔9,此吸血孔9通过分导管10与集液管11连通,此集液管11通过到导管12连接到吸液接口13,所述分导管10与集液管11位于刀片1内,此刀刃3上部具有一倒角斜面9,一用于套在手上的套绳10安装于所述条形刀柄2的后部。
所述刀片1通过以下步骤获得:
步骤一、将超细碳化钨50~60份、碳化钛 8~10份、碳化铬 6~8份、二硅化钼4~8份、氮化钛7~9份、碳化钒1~2份和石墨粉3~4份投入粉碎机内进行粉碎处理,形成直径小于20微米的混合粉末;具体由以下重量份组分组成,如表1所示:
表1
步骤二、将步骤一制得的混合粉末置于真空条件中加热至850℃,加热4小时,然后加入酚醛树脂5份充分搅拌均匀,制得混合物后冷却;
步骤三、通过压力机对混合物进行成型压制形成压坯;
步骤四、将压坯放置烧结炉进行烧结形成刀片毛坯,具体步骤如下:
步骤4-1、先升温至260℃,再以每小时4~6℃的速率升温至 500℃,保温1~2小时,此阶段采用真空条件烧结;
步骤4-2、再以每小时8~12℃的速率升温至1260℃,保温1~2小时,此阶段气氛为氩气和氮气形成的混合气体,此时的烧结压力为 6Mpa;
步骤4-3、再以每小时2~4℃的速率升温至1380℃,保温1~2小时,此阶段气氛为氩气,此时的烧结压力为4Mpa;
步骤4-4、随炉冷却;
步骤五、对刀片毛坯进行精磨加工,载开锋和打磨处理形成初步刀片;
步骤六、将步骤五的初步刀片进行液氮深冷处理从而获得所述刀片1。
上述条形刀柄2的截面为圆形,上述导管12由位于刀片1内的第一导管121和位于条形刀柄2内的第二导管122贯通组成。
采用上述多用途微创外科手术刀时,使得手术刀的刀片拥有超高的硬度,而且开锋后的刀片十分锋利,且极高的强度不容易出现弯曲;其烧结过程三个阶段压力由真空依次切换到高压烧结、次高压烧结,并伴随特定组分气氛切换,有利于碳化物弥散析出,进而使刀片的材质组织更加紧密,增加了抗弯强度和抗崩刃性;其次,其拆装方便、稳定可靠,实现了立体三维定位,避免了刀体易松动、晃动的问题,具有很好的推广应用前景;再次,其医务人员的手腕穿过套绳后,可以防止手术刀滑落,避免了条形刀柄表面光滑,在手术过程中很容易滑脱的缺陷,从而大大降低了医疗事故率。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (4)
1.一种多用途微创外科手术刀,其特征在于:包括:刀片(1)、条形刀柄(2),所述刀片(1)的一端为刀刃(3),另一端为插接部(4),此插接部(4)上端面和下端面分别开有上凹孔(41)和下凹孔(42),所述条形刀柄(2)前端具有供插接部(4)嵌入的插孔(5);所述条形刀柄(2)的前部沿周向依次开有上螺纹孔(21)、中螺纹孔(22)和下螺纹孔(23),一锁紧螺丝(6)旋入中螺纹孔(22)并压紧插接部(4),一上螺栓杆(7)旋入上螺纹孔(21)并嵌入插接部(4)的上凹孔(41)内,一下螺栓杆(8)旋入下螺纹孔(23)并嵌入插接部(4)的下凹孔(42)内;所述刀刃(3)上开有若干个吸血孔(9),此吸血孔(9)通过分导管(10)与集液管(11)连通,此集液管(11)通过到导管(12)连接到吸液接口(13),所述分导管(10)与集液管(11)位于刀片(1)内,此刀刃(3)上部具有一倒角斜面(9),一用于套在手上的套绳(14)安装于所述条形刀柄(2)的后部;
所述刀片(1)通过以下步骤获得:
步骤一、将超细碳化钨50~60份、碳化钛 8~10份、碳化铬 6~8份、二硅化钼4~8份、氮化钛7~9份、碳化钒1~2份和石墨粉3~4份投入粉碎机内进行粉碎处理,形成直径小于20微米的混合粉末;
步骤二、将步骤一制得的混合粉末置于真空条件中加热至850℃,加热4小时,然后加入酚醛树脂4~6份充分搅拌均匀,制得混合物后冷却;
步骤三、通过压力机对混合物进行成型压制形成压坯;
步骤四、将压坯放置烧结炉进行烧结形成刀片毛坯,具体步骤如下:
步骤4-1、先升温至260℃,再以每小时4~6℃的速率升温至 500℃,保温1~2小时,此阶段采用真空条件烧结;
步骤4-2、再以每小时8~12℃的速率升温至1260℃,保温1~2小时,此阶段气氛为氩气和氮气形成的混合气体,此时的烧结压力为 6Mpa;
步骤4-3、再以每小时2~4℃的速率升温至1380℃,保温1~2小时,此阶段气氛为氩气,此时的烧结压力为4Mpa;
步骤4-4、随炉冷却;
步骤五、对刀片毛坯进行精磨加工,载开锋和打磨处理形成初步刀片;
步骤六、将步骤五的初步刀片进行液氮深冷处理从而获得所述刀片(1)。
2.根据权利要求1所述的多用途微创外科手术刀,其特征在于:所述条形刀柄(2)的截面为圆形。
3.根据权利要求1所述的多用途微创外科手术刀,其特征在于:所述导管(12)由位于刀片(1)内的第一导管(121)和位于条形刀柄(2)内的第二导管(122)贯通组成。
4.根据权利要求1所述的多用途微创外科手术刀,其特征在于:所述步骤六的深冷处理的温度低于零下80℃。